Characterization of an Experimental Two-Step Self-Etch Adhesive's Bonding Performance and Resin-Dentin Interfacial Properties.
Ontology highlight
ABSTRACT:
SUBMITTER: Chowdhury AFMA
PROVIDER: S-EPMC8036260 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Background: The newly introduced self-adhering flowable resin-composites decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resin composite (Vertise™Flow Self-Adhering Flowable Composite, Kerr Dental, USA) versus a total-etch (Te-Econom Plus) resin composite, using an etching agent (Eco-Etch gel) and bonding agent (Single Bond Universal). Methods: Sixteen freshly extracted sound human posterior teeth were used. The teeth were randomly divided into two groups: 8 specimens per type of composite. Standard-shaped class V cavities were prepared on the buccal surface. One group was restored by Te-Econom Plus resin composite by total-etch technique using Eco-Etch gel, which was applied to dentine for 15 seconds, followed by rinsing, drying and bonding agent application (Single Bond Universal). The other group restored directly with self-adhering resin composite (Vertise-Flow) without application of etch or bond. Curing was done for 20 seconds using a light emitting diode light curing unit. Evaluation of the resin-dentin interface was done microscopically by examination of marginal gap distance in μm using scanning electron microscope (SEM), and chemical analysis of silver particles was observed using SEM with energy-dispersive X-ray spectrometry after 24 hours of specimen storage in ammoniacal silver nitrate. Results: Regarding marginal gap distance (µm) and silver atomic % mean values, teeth restored with self-adhering resin composite (Vertise-Flow) showed significantly higher mean values than the multi-step etch and rinse resin composite group (5.2 vs 0; 12.2 vs 8.2, respectively). Conclusions: Resin-dentin bonding using total-etch resin composite technique was more effective than self-adhering flowable resin composite (Vertise-Flow) regarding marginal gap formation and penetration of silver particles. Further studies for bond strength could be performed.
| S-EPMC5649117 | biostudies-literature
Project description:Based on the frequent application of composite resins as tooth-colored fillings, this method is considered a viable alternative to dental amalgam. However, this method has the low bond strength of the composite to dentin. To solve this issue, various dental adhesive systems with different characteristics have been developed by dentistry experts.To assess the effect of an additional layer of unfilled resin in self-etch and total-etch dentin adhesives on the shear bond strength (SBS) of composite to dentin. Moreover, we assessed the effects of sample storage in artificial saliva on the SBS of composite to dentin.Methods: This experimental study was conducted on 160 freshly extracted human first or second premolar teeth, which were randomly divided into 16 groups. The teeth were prepared from Mashhad University of Medical Sciences, Mashhad, Iran (2008-2009). Scotchbond Multi-purpose (SBMP), single bond (SB), Clearfil SE Bond, and Clearfil S3 Bond were applied to dentin surface with or without the placement of hydrophobic resin (Margin Bond) in accordance with the instructions of the manufacturers. To expose the coronal dentin, the teeth were abraded with 600 grit SiC paper. Immediately after restoration, half of the samples were tested in terms of SBS, while the other samples were evaluated in terms of SBS after three months of storage in artificial saliva. SBS rates of dental composites evaluated by universal testing machine and samples were studied by optical stereomicroscopy to verify the failure type. Data analysis was performed in SPSS V.16 using Kolmogorov-Smirnov test, independent-samples t-test, ANOVA, and Duncan's logistic regression test.In this study, a significant reduction was observed in the SBS rates of SB and S3 bond adhesive systems after storage with and without hydrophobic resin (p>0.000). Without storage in normal saline, a significant increase was observed in the SBS rate of the SE bond (p=0.013). In addition, SBS rate of SBMP significantly increased after storage with hydrophobic resin (p=0.001). Finally, the highest and lowest rates of SBS were observed in the SE and S3 bonds in all the experimental groups, respectively.The effects of using a hydrophobic resin layer on shear bond strength values seem to be effective. The mild self-etch adhesive exhibited the best resin-dentine bond strength after aging.
| S-EPMC5498705 | biostudies-other
Project description:The durability of the resin-dentin bonding interface is a key issue in clinical esthetic dentistry. Inspired by the extraordinary bioadhesive properties of marine mussels in a wet environment, we designed and synthetized N-2-(3,4-dihydroxylphenyl) acrylamide (DAA) according to the functional domain of mussel adhesive proteins. DAA's properties of collagen cross-linking, collagenase inhibition, inducing collagen mineralization in vitro, and as a novel prime monomer for clinical dentin adhesion use, its optimal parameters, and effect on the adhesive longevity and the bonding interface's integrity and mineralization, were evaluated in vitro and in vivo. The results showed that oxide DAA can inhibit the activity of collagenase and cross collagen fibers to improve the anti-enzymatic hydrolysis of collagen fibers and induce intrafibrillar and interfibrillar collagen mineralization. As a primer used in the etch-rinse tooth adhesive system, oxide DAA can improve the durability and integrity of the bonding interface by anti-degradation and mineralization of the exposed collagen matrix. Oxidized DAA (OX-DAA) is a promising primer for improving dentin durability; using 5% OX-DAA ethanol solution and treating the etched dentin surface for 30 s is the optimal choice when used as a primer in the etch-rinse tooth adhesive system.
| S-EPMC10079285 | biostudies-literature
Project description:To test the impact of preheating (25, 37, 54, or 68 °C) of TetricEvoCeram (TEC), FiltekSupremeXT (FSXT), and Venus (V) on flexural strength (FS), shear bond strength (SBS) and interfacial tension (IFT). FS was tested with TEC and FSXT. For SBS, glass-ceramic and human dentin substrate were fabricated and luted with the preheated resin composite (RC). SBSs of 1500 thermal cycled specimens were measured. For IFT, glass slides covered with the non-polymerized RC were prepared and contact angles were measured. Data were analyzed using 2/1-way ANOVA with Scheffé-test, and t-test (p < 0.05). Preheated TEC (37-68 °C) showed higher FS compared to the control-group (25 °C) (p < 0.001). FSXT presented higher FS than TEC (p < 0.001). For SBS to dentin higher values for FSXT than TEC were found. The preheating temperature showed no impact on SBS to dentin. SBS to glass-ceramic revealed a positive influence of temperature for TEC 25-68 °C (p = 0.015). TEC showed higher values than V and FSXT (p < 0.001). IFT values increased with the preheating temperature. A significant difference could be observed in every RC group between 25 and 68 °C (p < 0.001).
| S-EPMC5456469 | biostudies-other
Project description:Degradation of hybrid layers created in primary dentin occurs as early as 6 months in vivo. Biomimetic remineralization utilizes "bottom-up" nanotechnology principles for interfibrillar and intrafibrillar remineralization of collagen matrices. This study examined whether imperfect hybrid layers created in primary dentin can be remineralized. Coronal dentin surfaces were prepared from extracted primary molars and bonded using Adper Prompt L-Pop and a composite. One-millimeter-thick specimen slabs of the resin-dentin interface were immersed in a Portland cement-based remineralization medium that contained two biomimetic analogs to mimic the sequestration and templating functions of dentin noncollagenous proteins. Specimens were retrieved after 1-6 months. Confocal laser scanning microscopy was used for evaluating the permeability of hybrid layers to Rhodamine B. Transmission electron microscopy was used to examine the status of remineralization within hybrid layers. Remineralization at different locations of the hybrid layers corresponded with quenching of fluorescence within similar locations of those hybrid layers. Remineralization was predominantly intrafibrillar in nature as interfibrillar spaces were filled with adhesive resin. Biomimetic remineralization of imperfect hybrid layers in primary human dentin is a potential means for preserving bond integrity. The success of the current proof-of-concept, laterally diffusing remineralization protocol warrants development of a clinically applicable biomimetic remineralization delivery system.
| S-EPMC2860636 | biostudies-literature
Project description:The purpose of this in vitro study was to evaluate the microtensile bond strength of one-step self-etch adhesive to human dentin surface modified with air abrasion and sonic technique and to assess the morphological characteristics of the pretreated dentin surface. The occlusal enamel was removed to obtain a flat dentin surface for thirty-six human molar teeth. The teeth were randomly divided into three experimental groups (n = 12 per group), according to the pretreatment of the dentin: (1) control group, (2) air abrasion group, and (3) sonic preparation group. Microtensile bond strength test was performed on a universal testing machine. Two specimens from each experimental group were subjected to SEM examination. There was no statistically significant difference in bond strength between the three experimental groups (P > 0.05). Mean microtensile bond strength (MPa) values were 35.3 ± 12.8 for control group, 35.8 ± 13.5 for air abrasion group, and 37.7 ± 12.0 for sonic preparation group. The use of air abrasion and sonic preparation with one-step self-etch adhesive does not appear to enhance or impair microtensile bond strength in dentin.
| S-EPMC4386705 | biostudies-other
Project description:In dentistry, the wet-bonding approach relies on water to maintain demineralized collagen expanded for proper resin infiltration; nevertheless, hydrolytic instability of the resin-dentin interface is inevitable with current bonding techniques. Considering dimethyl sulfoxide's (DMSO) ability to "biomodify" collagen and precipitate enzymes, the aim was to test whether the use of DMSO would permit adequate resin bonding to H3PO4-etched dehydrated dentin and assess its impact on collagen degradation by host-derived enzymes. Etched dentin surfaces from extracted sound human molars were randomly bonded in wet or dry conditions using aqueous or ethanolic DMSO solutions as pretreatments and bonding resins with or without DMSO. Bonded teeth were sectioned into resin-dentin slabs for confocal in situ zymography and beams for microtensile bond strength test. Demineralized powdered dentin was incubated in the tested DMSO -media and a hydroxyproline assay evaluated dissolution of collagen peptides. Zymography was performed on protein extracts obtained from dry and wet H3PO4-ecthed dentin powder treated with the DMSO- media. The correlative biochemical analysis demonstrated that reduction of water content during dentin hybridization by the innovative dry-bonding approaches with DMSO is effective to inactivate host-derived MMP-2 and MMP-9 and thus reduce collagen degradation while simultaneously optimizing resin-dentin bonding.
| S-EPMC6237771 | biostudies-literature
Project description:This study was performed to standardize a dentin barrier test with the substitute and evaluate the cytotoxicity of one-step self-etching bonding agents. Each of the natural bovine dentin and polyurethane discs were 500-μm thick and were tested using a perfusion device. Following the treatment with 0.05% phenol on the natural bovine disc or three kinds of polyurethane discs-30, 40, and 50 pcf (pounds per cubic foot)-cell viability of L-929 was measured by the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay and expressed as percentages of non-treated group, respectively. A substitute showing permeability similar to that of bovine dentin was determined based on this result. Cytotoxicity test of bonding agents was performed by the selected substitute, the results of which were expressed as percentages of the control. In addition, SEM images were taken after the tests. The cell viability by 40-pcf polyurethane disc was not statistically different from that by bovine dentin disc (P > 0.05). Futurabond DC resulted in the highest cell viability and Bond force the lowest by the 40-pcf polyurethane disc (P < 0.05). The adhesives on the 40-pcf polyurethane disc changed cellular morphology with different degrees on the SEM images. This standardized test might be useful for assessing the cytotoxicity of dental materials applied to dentin before clinical applications.
| S-EPMC5453160 | biostudies-other
Project description:The aim of the study was to evaluate the stability, reactivity, and bond strength with a lithium disilicate ceramic of a self-etch silane primer (Monobond Etch and Prime/MEP). The stability was evaluated by 1H-,31P-NMR spectroscopy (before/after aging), and the reactivity by micro MIR-FTIR spectroscopy on Ge surfaces (0, 1, 24 h) using a prehydrolyzed silane primer (Calibra Silane Coupling Agent/CLB), as a control. The effect of MEP vs. 5% HF-etching on ceramic roughness was assessed by optical profilometry. The shear bond strength (SBS) of a resin composite bonded to polished ceramic surfaces treated with MEP, HF without silane (HF+NS), HF+CLB, and HF+MEP (n = 20) was evaluated after storage in water (A: 37 °C/1 week, B: 5000×/5-55 °C and C: 100 °C/24 h). Aging did not affect the silanol groups of MEP, but only the phosphate co-monomer. Silanols were reactive forming siloxanes, but exhibited lower consumption rate than CLB. HF-etching induced significantly higher values than MEP, in all the roughness parameters tested (Sa, Sz, Sdr, Sc, Sv), with the greatest differences found in Sdr and Sv. For SBS, MEP was inferior to all treatments/storage conditions, except of HF+NS in A, where the values were similar. However, on a HF-etched substrate, MEP provided highest strength and reliability.
| S-EPMC7040894 | biostudies-literature
Project description:Statement of problemIt has been shown that selective etching improves the bond strength of some self-adhesive resin cements to enamel. The same has yet to be determined with dentin pre-treatment.PurposeTo evaluate the tensile bond strength of two self-adhesive resin cements after two dentin surface pre-treatments, and also to analyze the cement/dentin interface.Material and methodsOne hundred and twelve human third molars were extracted. The teeth were distributed into seven groups (n = 16). Maxcem Elite Chroma (MAX) (Kerr, Scafati, Italy) and Relyx U200 (RLX) (3M ESPE, Neuss, Germany) were used without pre-treatment or with two dentin pre-treatments (polyacrylic acid or phosphoric acid). A conventional etch-and-rinse (EAR) luting cement, NX3 Nexus (NX3) (Kerr, Scafati, Italy), was used as an external control group. Before testing, all specimens were stored in distilled water for 24 hours. Three specimens from each group were prepared for scanning electron microscopy observation (SEM). A tensile bond strength test (TBS) was performed for the remaining samples. The data were statistically analyzed using the Kruskal-Wallis test and Pairwise comparisons using the Wilcoxon rank sum test.ResultsMAX without pre-treatment and with phosphoric acid etching attained statistically similar bond strengths to NX3 (P > 0.05). There was a statistical difference (P = 0.00488) between RLX without pre-treatment (5.62 MPa) and NX3 (10.88 MPa). Phosphoric acid pre-treatment increases the bond strength values of RLX to a strength that is comparable to NX3 (P > 0.05). The lowest tensile bond strength (TBS) was attained after the application of polyacrylic acid with MAX (1.98 MPa). No statistical differences were found between the RLX bond strength values after polyacrylic acid treatment and RLX without pre-treatment or NX3 (P > 0.05). SEM observations disclosed an enhanced potential of the self-adhesive cements to infiltrate into dentin tubules and form resin tags when applied after phosphoric acid pre-treatment. The failure mode was dominantly adhesive.ConclusionsOn dentin, the self-adhesive resin cement MAX might be an effective alternative to conventional resin cement. Etching the dentin with phosphoric acid does not have a negative effect on the bond strength of MAX to dentin. On the other hand, phosphoric acid improved the bond strength of RLX when compared to EAR cement.
| S-EPMC8555495 | biostudies-literature