Structure validation of oxidized poly (2-hydroxyethyl acrylate) with multiple aldehyde groups and its application for collagen modification.

ABSTRACT: The structural characteristic of oxidized poly (2-hydroxyethyl acrylate) (OP) was confirmed by high-performance liquid chromatography, gel permeation chromatography and hydroxylamine hydrochloride titration. The results demonstrated that OP prepared through 2,2,6,6-tetramethylpiperidine-1-oxyl-mediated oxidation of poly (2-hydroxyethyl acrylate) was featured by multiple aldehyde groups on its side chain, with no free formaldehyde produced during the oxidation process. The computational simulation for the electrophilic reactivity of OP molecule showed that the reactivity of the aldehyde groups in OP with the amino groups of collagen was comparable to that of glutaraldehyde. In this study, OP was chosen as a collagen modifier to investigate the modification effects on the secondary structure, aggregation behaviour and thermal stability of collagen. The covalent cross-linking occurred between the aldehyde groups of OP and the amino groups of collagen under alkaline condition. The covalent binding between OP and collagen was strengthened with the increasing reaction pH and OP dosage, and the triple helix of collagen was altered to some degree. Furthermore, OP promoted the intense aggregation of collagen and enhanced the thermal stability of collagen. This work provides guidance for preparing novel collagen modifier with multiple aldehyde groups.

SUBMITTER: Liu B

PROVIDER: S-EPMC8074665 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The purpose of this work was to investigate the effect of multifunctionality on material properties of synthetic polymer aerogels. For this purpose, we present the synthesis and characterization of monolithic dendritic-type urethane-acrylate monomers based on an aliphatic/flexible (Desmodur N3300), or an aromatic/rigid (Desmodur RE) triisocyanate core. The terminal acrylate groups (three at the tip of each of the three branches, nine in total) were polymerized with 2,2'-azobis(isobutyronitrile) (AIBN) via free radical chemistry. The resulting wet-gels were dried with supercritical fluid (SCF) CO₂. Aerogels were characterized with ATR-FTIR and solid-state 13C NMR. The porous network was probed with N₂-sorption and scanning electron microscopy (SEM). The thermal stability of aerogels was studied with thermogravimetric analysis (TGA). Most aerogels were macroporous materials (porosity > 80%), with high thermal stability (up to 300 °C). Aerogels were softer at low monomer concentrations and more rigid at higher concentrations. The material properties were compared with those of analogous aerogels bearing only one acrylate moiety at the tip of each branch and the same cores, and with those of analogous aerogels bearing norbornene instead of acrylate moieties. The nine-terminal acrylate-based monomers of this study caused rapid decrease of the solubility of the growing polymer and made possible aerogels with much smaller particles and much higher surface areas. For the first time, aliphatic/flexible triisocyanate-based materials could be made with similar properties in terms of particle size and surface areas to their aromatic/rigid analogues. Finally, it was found that with monomers with a high number of crosslinkable groups, material properties are determined by multifunctionality and thus aerogels based on 9-acrylate- and 9-norbornene-terminated monomers were similar. Materials with aromatic cores are carbonizable with satisfactory yields (20⁻30% w/w) to mostly microporous materials (BET surface areas: 640⁻740 m² g-1; micropore surface areas: 360⁻430 m² g-1).

Dataset Information

Structure validation of oxidized poly (2-hydroxyethyl acrylate) with multiple aldehyde groups and its application for collagen modification.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets