One-step synthesis of black TiO_2-x microspheres by ultrasonic spray pyrolysis process and their visible-light-driven photocatalytic activities.

ABSTRACT: Black TiO_2-x has recently emerged as one of the most promising visible-light-driven photocatalysts, but current synthesis routes that require a reduction step are not compatible with cost-effective mass production and a relatively large particle such as microspheres. Herein, we demonstrate a simple, fast, cost-effective and scalable one-step process based on an ultrasonic spray pyrolysis for the synthesis of black TiO_2-x microspheres. The process utilizes an oxygen-deficient environment during the pyrolysis of titanium precursors to directly introduce oxygen vacancies into synthesized TiO₂ products, and thus a reduction step is not required. Droplets of a titanium precursor solution were generated by ultrasound energy and dragged with continuous N₂ flow into a furnace for the decomposition of the precursor and crystallization to TiO₂ and through such a process spherical black TiO_2-x microspheres were obtained at 900 °C. The synthesized black TiO_2-x microsphere with trivalent titanium/oxygen vacancy clearly showed the variation of physicochemical properties compared with those of white TiO₂. In addition, the synthesized microspheres presented the superior photocatalytic activity for degradation of methylene blue under visible light irradiation. This work presents a new methodology for a simple one-step synthesis of black metal oxides microspheres with oxygen vacancies for visible-light-driven photocatalysts with a higher efficiency.

SUBMITTER: Ji M

PROVIDER: S-EPMC8094901 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

TiO2 thin films by ultrasonic spray pyrolysis as photocatalytic material for air purification.

Project description:In this study, we showed that the TiO2 thin films deposited onto window glass are practicable for air purification and self-cleaning applications. TiO2 films were deposited onto window glass by ultrasonic spray pyrolysis method. Different deposition temperatures were used in the range of 250-450°C. The structural, morphological, optical properties and surface chemical composition were investigated to understand probable factors affecting photocatalytic performance and wettability of the TiO2 thin films. The TiO2 thin films were smooth, compacted and adhered adequately on the substrate with a thickness in the range of 100-240 nm. X-ray diffraction patterns revealed that all the TiO2 thin films consisted of anatase phase structure with the mean crystallite size in the range of 13-35 nm. The optical measurements showed that the deposited films were highly transparent (approx. 85%). The wettability test results showed that the TiO2 thin films sprayed at 350°C and 450°C and annealed at 500°C for 1 h were superhydrophilic. The photocatalytic activity of the films was tested for the degradation of methyl tert-butyl ether (MTBE) in multi-section plug-flow reactor. The TiO2 film deposited at 350°C exhibited the highest amount of conversion of MTBE, approximately 80%.

| S-EPMC6408371 | biostudies-literature

Enhanced Photocatalytic Activity of Nanoparticle-Aggregated Ag-AgX(X = Cl, Br)@TiO2 Microspheres Under Visible Light.

Project description:Ag-AgX(X = Cl, Br)@TiO2 nanoparticle-aggregated spheres with different mass ratio of R = TiO2/Ag(X) from 35:1 to 5:1 were synthesized by a facile sol-gel technique with post-photoreduction. The photocatalytic activities of both Ag-AgCl@TiO2 and Ag-AgBr@TiO2 under visible light are effectively improved by ~3 times relative to TiO2 NPAS under the simulated sunlight for the decomposition of methyl orange (MO). Ag-AgBr@TiO2 showed 30% improvement and less stable in photocatalytic activity than that of AgCl@TiO2. The role of Ag and AgX nanoparticles on the surface of Ag-AgX(X = Cl, Br)@TiO2 was discussed. Ag on these samples not only can efficiently harvest visible light especially for AgCl, but also efficiently separate excited electrons and holes via the fast electron transfer from AgX(X = Cl, Br) to metal Ag nanoparticles and then to TiO2-aggregated spheres on the surface of heterostructure. On the basis of their efficient and stable photocatalytic activities under visible-light irradiation, these photocatalysts could be widely used for degradation of organic pollutants in aqueous solution.

| S-EPMC6199042 | biostudies-literature

Visible-Light-Active Black TiO2 Nanoparticles with Efficient Photocatalytic Performance for Degradation of Pharmaceuticals.

Project description:Special attention has recently been paid to surface-defective titanium dioxide and black TiO2 with advanced optical, electrical, and photocatalytic properties. Synthesis of these materials for photodegradation and mineralization of persistent organic pollutants in water, especially under visible radiation, presents interest from scientific and application points of view. Chemical reduction by heating a TiO2 and NaBH4 mixture at 350 °C successfully introduced Ti3+ defects and oxygen vacancies at the surface of TiO2, with an increase in the photocatalytic degradation of amoxicillin-an antibiotic that is present in wastewater due to its intense use in human and animal medicine. Three TiO2 samples were prepared at different annealing temperatures to control the ratio between anatase and rutile and were subjected to chemical reduction. Electron paramagnetic resonance investigations showed that the formation of surface Ti3+ defects in a high concentration occurred mainly in the anatase sample annealed at 400 °C, contributing to the bandgap reduction from 3.32 eV to 2.92 eV. The reduced band gap enhances visible light absorption and the efficiency of photocatalysis. The nanoparticles of ~90 m2/g specific surface area and 12 nm average size exhibit ~100% efficiency in the degradation of amoxicillin under simulated solar irradiation compared with pristine TiO2. Mineralization of amoxicillin and by-products was over 75% after 48 h irradiation for the anatase sample, where the Ti3+ defects were present in a higher concentration at the catalyst's surface.

| S-EPMC9330099 | biostudies-literature

Photocatalytic degradation of tetracycline using surface defective black TiO2-ZnO heterojunction photocatalyst under visible light.

Project description:Fabrication of heterojunction and surface defective engineering, through the formation of oxygen vacancies, are among the various photocatalytic enhancement techniques. A combination of these techniques has the prospect of enhancing photocatalytic activities through improved light absorption capabilities and charge separation process of the photocatalysts. In this study, a heterojunction of black titanium oxide-zinc oxide (BTiO2-ZnO) nanocomposite was synthesized using the conventional sol-gel approach, coupled with aluminum foil-assisted NaBH4 reduction. The structure, morphology, surface properties, and optical characteristics of the synthesized material were studied using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), UV-vis absorption spectra, scanning electron microscope (SEM), Energy-dispersive X-ray spectroscopy (EDS), and transmission electron microscope (TEM). The XRD confirmed the successful formation of BTiO2-ZnO heterostructure, while SEM revealed the structural morphology as pseudo-spherical with slight agglomeration. BTiO2-ZnO was found to be more efficient than BTiO2 and BZnO for the removal of tetracycline with degradation efficiencies of 63, 58, and 56 % respectively. The effects of process parameters such as the amount of photocatalyst, pollutant's concentration, and the initial solution pH on photocatalytic degradation study were systematically explored. The results confirm that the formation of the heterostructure from BTiO2 and BZnO could offer a facile route to improving the catalytic degradation of tetracycline. Therefore, this study offers a novel perspective on the design of efficient metal oxide photocatalyst systems that rely on the integration of defect engineering and heterojunction for the removal of organic contaminants.

| S-EPMC10661122 | biostudies-literature

Preparation and visible-light photocatalytic properties of the floating hollow glass microspheres - TiO2/Ag3PO4 composites.

Project description:A novel floating visible-light photocatalyst (HGMs-TiO2/Ag3PO4) composite was prepared using amino modified low-density hollow glass microspheres (HGMs) as carriers to disperse and support TiO2 and Ag3PO4 photocatalysts. The surface morphology, crystal structure and optical properties of the HGMs-TiO2/Ag3PO4 composites were characterized and the Ag3PO4 content on the surface of the microspheres was determined by atomic absorption spectrometry (AAS). Methylene blue (MB) was chose as the organic pollutant to investigate the visible-light catalytic properties of the HGMs-TiO2/Ag3PO4 composites. For HGM composite photocatalysts, when the theoretical mass ratio of TiO2 to Ag3PO4 on the surface of HGMs is 1 : 1.5, the visible-light catalytic activity of the composite is superior to pure Ag3PO4 and a TiO2/Ag3PO4 photocatalyst with a mass ratio of 1 : 1.5 under the same conditions, due to the increased light-contact area and the photocatalytic active sites, since the TiO2 and Ag3PO4 particles can be well dispersed on the surface of the floating HGMs. Furthermore, the deposits of TiO2 and Ag3PO4 on the HGM surface form a heterostructure, facilitating the separation of electron-hole (e- - h+) in the energy band, and elevating the photocatalytic activity and cycle stability of Ag3PO4. This work indicates that floating HGMs-TiO2/Ag3PO4 composites could become a promising photocatalyst for organic dye removal due to the low cost and high visible-light responsiveness.

| S-EPMC9059536 | biostudies-literature

Black TiO2 nanobelts/g-C3N4 nanosheets Laminated Heterojunctions with Efficient Visible-Light-Driven Photocatalytic Performance.

Project description:Black TiO2 nanobelts/g-C3N4 nanosheets laminated heterojunctions (b-TiO2/g-C3N4) as visible-light-driven photocatalysts are fabricated through a simple hydrothermal-calcination process and an in-situ solid-state chemical reduction approach, followed by the mild thermal treatment (350 °C) in argon atmosphere. The prepared samples are evidently investigated by X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, N2 adsorption, and UV-visible diffuse reflectance spectroscopy, respectively. The results show that special laminated heterojunctions are formed between black TiO2 nanobelts and g-C3N4 nanosheets, which favor the separation of photogenerated electron-hole pairs. Furthermore, the presence of Ti3+ and g-C3N4 greatly enhance the absorption of visible light. The resultant b-TiO2/g-C3N4 materials exhibit higher photocatalytic activity than that of g-C3N4, TiO2, b-TiO2 and TiO2/g-C3N4 for degradation of methyl orange (95%) and hydrogen evolution (555.8 μmol h-1 g-1) under visible light irradiation. The apparent reaction rate constant (k) of b-TiO2/g-C3N4 is ~9 times higher than that of pristine TiO2. Therefore, the high-efficient laminated heterojunction composites will have potential applications in fields of environment and energy.

| S-EPMC5292731 | biostudies-literature

Enhanced photocatalytic activity of Se-doped TiO2 under visible light irradiation.

Project description:Anatase TiO2 is a typical photocatalyst, and its excellent performance is limited in ultraviolet light range due to its wide band gap of 3.2?eV. A series of Se-doped TiO2 nanoparticles in anatase structure with various Se concentrations up to 17.1?at.% were prepared using sol-gel method. The doped Se ions are confirmed to be mainly in the valence state of?+?4, which provides extra electronic states in the band gap of TiO2. The band gap is effectively narrowed with the smallest gap energy of 2.17?eV, and the photocatalytic activity is effectively improved due to the extended absorption range. The photocatalytic activity was evaluated by the degradation of Rhodamine B (RhB) in aqueous solution under visible light irradiation. The results show that Se doping significantly improves the photocatalytic activity of TiO2 and 13.63?at.% Se-doped TiO2 has the best performance.

| S-EPMC5993730 | biostudies-literature

Sb2S3 grown by ultrasonic spray pyrolysis and its application in a hybrid solar cell.

Project description:Chemical spray pyrolysis (CSP) is a fast wet-chemical deposition method in which an aerosol is guided by carrier gas onto a hot substrate where the decomposition of the precursor chemicals occurs. The aerosol is produced using an ultrasonic oscillator in a bath of precursor solution and guided by compressed air. The use of the ultrasonic CSP resulted in the growth of homogeneous and well-adhered layers that consist of submicron crystals of single-phase Sb2S3 with a bandgap of 1.6 eV if an abundance of sulfur source is present in the precursor solution (SbCl3/SC(NH2)2 = 1:6) sprayed onto the substrate at 250 °C in air. Solar cells with glass-ITO-TiO2-Sb2S3-P3HT-Au structure and an active area of 1 cm2 had an open circuit voltage of 630 mV, short circuit current density of 5 mA/cm2, a fill factor of 42% and a conversion efficiency of 1.3%. Conversion efficiencies up to 1.9% were obtained from solar cells with smaller areas.

| S-EPMC5238638 | biostudies-literature

Electrical Properties of CZO Films Prepared by Ultrasonic Spray Pyrolysis.

Project description:CuZnO (CZO) films have attracted increasing amounts of attention due to their promising potential applications in semiconductor devices. ZnO shows n-type conductivity, and attempts have been made to dope several elements in ZnO to improve the electrical properties. This study investigated the electrical property transitions of CZO films and determined the copper concentration at which the conductivity of CZO films will change from n-type to p-type. In this study, CZO films were fabricated by ultrasonic spray pyrolysis with copper acetate, zinc acetate, and ammonium acetate precursor solution. The concentrations of Cu ions in the CZO films were controlled by the concentration ratios of copper acetate to zinc acetate in the precursor solutions. In addition, these samples were analyzed by Hall effect measurements, X-ray diffraction, transmittance measurements, and photoluminescence measurements. The results show that the conductivity of the CZO film changes from n-type to p-type when the copper ion concentration in the film is 5%.

| S-EPMC5512636 | biostudies-other

Electro-spray deposited TiO2 bilayer films and their recyclable photocatalytic self-cleaning strategy.

Project description:Recyclable titanium dioxide (TiO2)-based photocatalytic self-cleaning films (SCFs) having a bilayer structure were prepared and assessed. These SCFs comprised two layers of fibers fabricated using an electrospinning process. The self-cleaning layer was made of acrylonitrile-butadiene-styrene (ABS) fibers with embedded TiO2 while the substrate layer was composed of fibers made by simultaneously electrospinning poly (vinyl alcohol) (PVA) and ABS. This substrate improved the mechanical strength of the SCF and provided greater adhesion due to the presence of the PVA. The experimental results showed that the hydrophobicity (as assessed by the water contact angle), photocatalytic properties and self-cleaning efficiency of the SCF were all enhanced with increasing TiO2 content in the ABS/TiO2 fibers. In addition, the introduction of the substrate layer allowed the SCFs to be applied to various surfaces and then peeled off when desired. The ABS fibers effectively improved the strength of the overall film, while deterioration of the ABS upon exposure to UV light was alleviated by the addition of TiO2. These SCFs can potentially be recycled after use in various environments, and therefore have applications in the fields of environmental protection and medical science.

| S-EPMC8799740 | biostudies-literature