Magneto-optical borogermanate glasses and fibers containing Tb³.

ABSTRACT: New glass compositions containing high concentrations of Tb³⁺ ions were developed aiming at the production of magneto-optical (MO) fibers. This work reports on the structural and MO properties of a new glass composition based on (100 - x)(41GeO₂-25B₂O₃-4Al₂O₃-10Na₂O-20BaO) - xTb₄O₇. Morphological analysis (HR-TEM) of the sample with the highest concentration of Tb³⁺ ions confirmed the homogeneous distribution of Tb³⁺ ions and the absence of nanoclusters. All the samples presented excellent thermal stability against crystallization (ΔT > 100 °C). An optical fiber was manufactured by a fiber drawing process. The UV-Vis spectra of the glasses showed Tb³⁺ electronic transitions and optical windows varying from 0.4 to 1.6 μm. The magneto-optical properties and the paramagnetic behaviors of the glasses were investigated using Faraday rotation experiments. The Verdet constant (V_B) values were calculated at 500, 650, 880, 1050, 1330, and 1550 nm. The maximum V_B values obtained at 650 and 1550 nm for the glass with x = 18 mol% were -128 and - 17.6 rad T^-1 m^-1, respectively. The V_B values at 500 and 1550 nm for the optical fiber containing 8 mol% of Tb₄O₇ were - 110.2 and - 9.5 rad T^-1 m^-1, respectively, while the optical loss at around 880 nm was 6.4 dB m^-1.

SUBMITTER: Franco DF

PROVIDER: S-EPMC8110553 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Role of Ag+ Ions in Determining Ce3+ Optical Properties in Fluorophosphate and Sulfophosphate Glasses.

Project description:Understanding the interactions among dopant species and the role of the host lattice is of fundamental importance for the chemical formulation of optically active glasses. Here, we consider the archetypal dopant pair of Ag-Ce in complex fluorophosphate (PF) and sulfophosphate (PS) matrices, in which variable bonding environments and ligand selectivity exert distinct effects on dopant properties. The addition of Ag+ to PF glasses blue-shifts the ultraviolet (UV) cutoff wavelength of Ce3+ and enhances its photoluminescence (PL) intensity. In PS matrices, the exact opposite effect is observed: red-shifting the UV cutoff and lowering the PL intensity. No Ag-Ag pairs or cluster species were found in either matrix material; however, in PS, such clustering could be triggered by secondary broad-band UV-visible irradiation. The optical properties of Ag-Ce-codoped glasses are a result of the ionocovalent character of the Ag+-O-Ce3+ bond, the cross-relaxation process between Ag+ and Ce3+, and the redox ratio of Ce3+/Ce4+. In the PF glasses, the enhancement of the Ce3+ PL intensity is due to energy transfer from Ag+ to Ce3+ and a redox shift from Ce4+ to Ce3+. The more covalent Ag+-O-Ce3+ interactions in the PS series decrease the Ce3+/Ce4+ ratio. Moreover, photoinduced Ag clustering is facilitated in the more covalent environment, which indicates that glasses commonly used for Ag nanoparticle formation, such as silicate glasses, also possess more covalent Ag+-O bonding.

| S-EPMC8582266 | biostudies-literature

Magneto-Induced Hyperthermia and Temperature Detection in Single Iron Oxide Core-Silica/Tb3+/Eu3+(Acac) Shell Nano-Objects.

Project description:Multifunctional nano-objects containing a magnetic heater and a temperature emissive sensor in the same nanoparticle have recently emerged as promising tools towards personalized nanomedicine permitting hyperthermia-assisted treatment under local temperature control. However, a fine control of nano-systems' morphology permitting the synthesis of a single magnetic core with controlled position of the sensor presents a main challenge. We report here the design of new iron oxide core-silica shell nano-objects containing luminescent Tb3+/Eu3+-(acetylacetonate) moieties covalently anchored to the silica surface, which act as a promising heater/thermometer system. They present a single magnetic core and a controlled thickness of the silica shell, permitting a uniform spatial distribution of the emissive nanothermometer relative to the heat source. These nanoparticles exhibit the Tb3+ and Eu3+ characteristic emissions and suitable magnetic properties that make them efficient as a nanoheater with a Ln3+-based emissive self-referencing temperature sensor covalently coupled to it. Heating capacity under an alternating current magnetic field was demonstrated by thermal imaging. This system offers a new strategy permitting a rapid heating of a solution under an applied magnetic field and a local self-referencing temperature sensing with excellent thermal sensitivity (1.64%·K-1 (at 40 °C)) in the range 25-70 °C, good photostability, and reproducibility after several heating cycles.

| S-EPMC9503042 | biostudies-literature

Engineering of Solar Energy Harvesting Tb3+-Ion-Doped CdS Quantum Dot Glasses for Photodissociation of Hydrogen Sulfide.

Project description:The photocatalytic properties of CdS quantum dots (Q-dots) and Tb3+-doped CdS Q-dots dispersed in a borosilicate glass matrix were investigated for the photodissociation of hydrogen sulfide (H2S) into hydrogen (H2) gas and elemental sulfur (S). The Q-dot-containing glass samples were fabricated using the conventional melt-quench method and isothermal annealing between 550 and 600 °C for 6 h for controlling the growth of CdS and Tb3+-ion-doped CdS Q-dots. The structure, electronic band gap, and spectroscopic properties of the Q-dots formed in the glass matrix after annealing were analyzed using Raman and UV-visible spectroscopies, X-ray powder diffraction, and transmission electron microscopy. With increasing annealing temperature, the average size range of the Q-dots increased, corresponding to the decrease of electronic band gap from 3.32 to 2.24 eV. For developing the model for photocatalytic energy exchange, the excited state lifetime and photoluminescence emission were investigated by exciting the CdS and Tb3+-doped CdS quantum states with a 450 nm source. The results from the photoluminescence and lifetime demonstrated that the Tb3+-CdS photodissociation energy exchange is more efficient from the excited Q-dot states compared to the CdS Q-dot glasses. Under natural sunlight, the hydrogen production experiment was conducted, and an increase of 26.2% in hydrogen evolution rate was observed from 0.02 wt % Tb3+-doped CdS (3867 μmol/h/0.5 g) heat-treated at 550 °C when compared to CdS Q-dot glass with a similar heat treatment temperature (3064 μmol/h/0.5 g). Furthermore, the photodegradation stability of 0.02 wt % Tb3+-CdS was analyzed by reusing the catalyst glass powders four times with little evidence of degradation.

| S-EPMC10498422 | biostudies-literature

Faraday rotation and photoluminescence in heavily Tb(3+)-doped GeO2-B2O3-Al2O3-Ga2O3 glasses for fiber-integrated magneto-optics.

Project description:We report on the magneto-optical (MO) properties of heavily Tb(3+)-doped GeO2-B2O3-Al2O3-Ga2O3 glasses towards fiber-integrated paramagnetic MO devices. For a Tb(3+) ion concentration of up to 9.7 × 10(21) cm(-3), the reported glass exhibits an absolute negative Faraday rotation of ~120 rad/T/m at 632.8 nm. The optimum spectral ratio between Verdet constant and light transmittance over the spectral window of 400-1500 nm is found for a Tb(3+) concentration of ~6.5 × 10(21) cm(-3). For this glass, the crystallization stability, expressed as the difference between glass transition temperature and onset temperature of melt crystallization exceeds 100 K, which is a prerequisite for fiber drawing. In addition, a high activation energy of crystallization is achieved at this composition. Optical absorption occurs in the NUV and blue spectral region, accompanied by Tb(3+) photoluminescence. In the heavily doped materials, a UV/blue-to-green photo-conversion gain of ~43% is achieved. The lifetime of photoluminescence is ~2.2 ms at a stimulated emission cross-section σem of ~1.1 × 10(-21) cm(2) for ~ 5.0 × 10(21) cm(-3) Tb(3+). This results in an optical gain parameter σem*τ of ~2.5 × 10(-24) cm(2)s, what could be of interest for implementation of a Tb(3+) fiber laser.

| S-EPMC4354094 | biostudies-other

Magneto-optical painting of heat current.

Project description:Active control of heat flow is crucial for the thermal management of increasingly complex electronic and spintronic devices. In addition to conventional heat transport engineering, spin caloritronics has received extensive attention as a heat control principle owing to its high controllability and unique thermal energy conversion symmetry. Here we demonstrate that the direction of heat currents generated by spin-caloritronic phenomena can be changed simply by illuminating magnetic materials with visible light. The optical control of heat currents is realized through a combination of the spin-driven thermoelectric conversion called an anomalous Ettingshausen effect and all-optical helicity-dependent switching of magnetization. This approach enables not only pinpoint manipulation and flexible design of the heat current distribution by patterning the illuminating light but also on/off control of the resulting temperature modulation by tuning the light polarization. These versatile heat control functionalities will open up a pathway for nanoscale thermal energy engineering.

| S-EPMC6946696 | biostudies-literature

Magnetic-field-induced dielectric behaviors and magneto-electrical coupling of multiferroic compounds containing cobalt ferrite/barium calcium titanate composite fibers.

Project description:Multiferroics have broad application prospects in various fields such as multi-layer ceramic capacitors and multifunctional devices owing to their high dielectric constants and coupled magnetic and ferroelectric properties at room temperature. In this study, cobalt ferrite (CFO)/barium calcium titanate (BCT) composite fibers are prepared from BCT and CFO sols by an electrospinning method, and are then oriented by magnetic fields and sintered at high temperatures. The effects of magnetic fields and CFO contents on the nanostructures and magnetoelectric properties of the composites are investigated. Strong coupling between magnetic and ferroelectric properties occurs in CFO/BCT composites with magnetic orientation. More interestingly, the dielectric constants of CFO/BCT composites with magnetic orientation are found to be enhanced (by ∼1.5-3.5 times) as compared with those of BCT and CFO/BCT without magnetic orientation. The boost of dielectric constants of magnetic-field orientated CFO/BCT is attributed to the magneto-electrical coupling between CFO and BCT, where the polar domains of BCT are pinned by the orientated CFO. Therefore, this work not only provides a novel and effective approach in enhancing the dielectric constants of ceramic ferroelectrics, which is of tremendous value for industrial applications, but also elucidates the interaction mechanisms between ferromagnetic phase and ferroelectric phase in multiferroic compounds.

| S-EPMC5806601 | biostudies-literature

Topological magneto-optical effect from skyrmion lattice.

Project description:The magnetic skyrmion is a spin-swirling topological object characterized by its nontrivial winding number, holding potential for next-generation spintronic devices. While optical readout has become increasingly important towards the high integration and ultrafast operation of those devices, the optical response of skyrmions has remained elusive. Here, we show the magneto-optical Kerr effect (MOKE) induced by the skyrmion formation, i.e., topological MOKE, in Gd2PdSi3. The significantly enhanced optical rotation found in the skyrmion phase demonstrates the emergence of topological MOKE, exemplifying the light-skyrmion interaction arising from the emergent gauge field. This gauge field in momentum space causes a dramatic reconstruction of the electronic band structure, giving rise to magneto-optical activity ranging up to the sub-eV region. The present findings pave a way for photonic technology based on skyrmionics.

| S-EPMC10480175 | biostudies-literature

Hydrothermal Synthesis and Optical Properties of Magneto-Optical Na3FeF6:Tb3+ Octahedral Particles.

Project description:Sodium iron hexafluoride (Na3FeF6), as a colorless iron fluoride, is expected to be an ideal host for rare earth ions to realize magneto-optical bi-functionality. Herein, monodispersed terbium ions (Tb3+) doped Na3FeF6 particles are successfully synthesized by a facile one-pot hydrothermal process. X-ray diffraction (XRD) and Field emission scanning electron microscopy (FESEM) reveal that the Tb3+ doped Na3FeF6 micro-particles with regular octahedral shape can be assigned to a monoclinic crystal structure (space group P21/c). Under ultraviolet light excitation, the Na3FeF6:Tb3+ octahedral particles given orange-red light emission originated from the 5D4?7FJ transitions of the Tb3+ ions. In addition, the magnetism measurement indicates that Na3FeF6:Tb3+ octahedral particles are paramagnetic with high magnetization at room temperature. Therefore, the Na3FeF6:Tb3+ powders may find potential applications in the biomedical field as magnetic-optical bi-functional materials.

| S-EPMC7013557 | biostudies-literature

Plasmon-mediated magneto-optical transparency.

Project description:Magnetic field control of light is among the most intriguing methods for modulation of light intensity and polarization on sub-nanosecond timescales. The implementation in nanostructured hybrid materials provides a remarkable increase of magneto-optical effects. However, so far only the enhancement of already known effects has been demonstrated in such materials. Here we postulate a novel magneto-optical phenomenon that originates solely from suitably designed nanostructured metal-dielectric material, the so-called magneto-plasmonic crystal. In this material, an incident light excites coupled plasmonic oscillations and a waveguide mode. An in-plane magnetic field allows excitation of an orthogonally polarized waveguide mode that modifies optical spectrum of the magneto-plasmonic crystal and increases its transparency. The experimentally achieved light intensity modulation reaches 24%. As the effect can potentially exceed 100%, it may have great importance for applied nanophotonics. Further, the effect allows manipulating and exciting waveguide modes by a magnetic field and light of proper polarization.

| S-EPMC3717503 | biostudies-other

Influences of copper-potassium ion exchange process on the optical bandgaps and spectroscopic properties of Cr3+/Yb3+ co-doped in lanthanum aluminosilicate glasses.

Project description:In this study, lanthanum aluminosilicate glasses with compositions of 45SiO2-20Al2O3-12.5LaF3-10BaF2-9K2O-1Cr2O3-2.5Yb2O3 (SALBK) were prepared using the conventional melting method and copper-potassium ion exchange process. Influences of the ion exchange process between copper and potassium on the visible, upconversion, and near-infrared luminescence spectra of Cr3+/Yb3+ co-doped under excitations of 343, 490, and 980 nm LD were investigated. The EDS analysis of SALBK glasses was measured to confirm the presence of atoms in the glasses. The values of direct and indirect bandgaps of Cr3+/Yb3+ co-doped SALBK glasses were calculated and analyzed. Besides, the energy exchange processes between Cu+, Cu2+ ions, and Cr3+, Yb3+ ions were also proposed and discussed.

| S-EPMC8695246 | biostudies-literature