Synthesis and Characterization Superabsorbent Polymers Made of Starch, Acrylic Acid, Acrylamide, Poly(Vinyl Alcohol), 2-Hydroxyethyl Methacrylate, 2-Acrylamido-2-methylpropane Sulfonic Acid.

ABSTRACT: Three polymers with excellent absorption properties were synthesized by graft polymerization: soluble starch-g-poly(acrylic acid-co-2-hydroxyethyl methacrylate), poly(vinyl alcohol)/potato starch-g-poly(acrylic acid-co-acrylamide), poly(vinyl alcohol)/potato starch-g-poly(acrylic acid-co-acrylamide-co-2-acrylamido-2-methylpropane sulfonic acid). Ammonium persulfate and potassium persulfate were used as initiators, while N,N'-methylenebisacrylamide was used as the crosslinking agent. The molecular structure of potato and soluble starch grafted by synthetic polymers was characterized by means of Fourier Transform Infrared Spectroscopy (FTIR). The morphology of the resulting materials was studied using a scanning electron microscope (SEM). Thermal stability was tested by thermogravimetric measurements. The absorption properties of the obtained biopolymers were tested in deionized water, sodium chroma solutions of various concentrations and in buffer solutions of various pH.

SUBMITTER: Czarnecka E

PROVIDER: S-EPMC8122658 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Maleic acid as an important monomer in synthesis of stimuli-responsive poly(acrylic acid-co-acrylamide-co-maleic acid) superabsorbent polymer.

Project description:Poly(acrylic acid-co-acrylamide-co-maleic acid) (p(AA-co-AM-co-MA)) superabsorbent polymer was synthesized from acrylic acid (AA), acrylamide (AM), and maleic acid (MA) via free radical copolymerization. Results showed the presence of maleic acid in structure of superabsorbent has the key and superior role in creating a smart superabsorbent. The structure, morphology, and strength of the superabsorbent were characterized using FT-IR, TGA, SEM, and rheology analysis. The effect of different factors was investigated to determine the ability of water absorbency of the superabsorbent. According to optimized conditions, the water absorbency capacity of the superabsorbent in distilled water (DW) was 1348 g/g and in a solution containing 1.0 wt.% NaCl (SCS) was 106 g/g. The water retention ability of the superabsorbent was also investigated. The kinetic swelling of superabsorbent was identified by Fickian diffusion and Schott's pseudo-second-order model. Furthermore, the reusability of superabsorbent was studied in distilled water and saline solution. The ability of superabsorbent was investigated in simulated urea and glucose solutions, and very good results were obtained. The response ability of the superabsorbent was confirmed by swelling and shrinking behavior against changes of temperature, pH, and ionic strength.

| S-EPMC9981600 | biostudies-literature

Differential orientation and conformation of surface-bound keratinocyte growth factor on (hydroxyethyl)methacrylate, (hydroxyethyl)methacrylate/methyl methacrylate, and (hydroxyethyl)methacrylate/methacrylic acid hydrogel copolymers.

Project description:The development of hydrogels for protein delivery requires protein-hydrogel interactions that cause minimal disruption of the protein's biological activity. Biological activity can be influenced by factors such as orientational accessibility for receptor binding and conformational changes, and these factors can be influenced by the hydrogel surface chemistry. (Hydroxyethyl)methacrylate (HEMA) hydrogels are of interest as drug delivery vehicles for keratinocyte growth factor (KGF) which is known to promote re-epithelialization in wound healing. The authors report here the surface characterization of three different HEMA hydrogel copolymers and their effects on the orientation and conformation of surface-bound KGF. In this work, they characterize two copolymers in addition to HEMA alone and report how protein orientation and conformation is affected. The first copolymer incorporates methyl methacrylate (MMA), which is known to promote the adsorption of protein to its surface due to its hydrophobicity. The second copolymer incorporates methacrylic acid (MAA), which is known to promote the diffusion of protein into its surface due to its hydrophilicity. They find that KGF at the surface of the HEMA/MMA copolymer appears to be more orientationally accessible and conformationally active than KGF at the surface of the HEMA/MAA copolymer. They also report that KGF at the surface of the HEMA/MAA copolymer becomes conformationally unfolded, likely due to hydrogen bonding. KGF at the surface of these copolymers can be differentiated by Fourier-transform infrared-attenuated total reflectance spectroscopy and time-of-flight secondary ion mass spectrometry in conjunction with principal component analysis. The differences in KGF orientation and conformation between these copolymers may result in different biological responses in future cell-based experiments.

| S-EPMC6905655 | biostudies-literature

Polymer Electrolyte Membranes Prepared by Graft Copolymerization of 2-Acrylamido-2-Methylpropane Sulfonic Acid and Acrylic Acid on PVDF and ETFE Activated by Electron Beam Treatment.

Project description:Polymer electrolyte membranes (PEM) for potential applications in fuel cells or vanadium redox flow batteries were synthesized and characterized. ETFE (poly (ethylene-alt-tetrafluoroethylene)) and PVDF (poly (vinylidene fluoride)) serving as base materials were activated by electron beam treatment with doses ranging from 50 to 200 kGy and subsequently grafted via radical copolymerization with the functional monomers 2-acrylamido-2-methylpropane sulfonic acid and acrylic acid in aqueous phase. Since protogenic groups are already contained in the monomers, a subsequent sulfonation step is omitted. The mechanical properties were studied via tensile strength measurements. The electrochemical performance of the PEMs was evaluated by electrochemical impedance spectroscopy and fuel cell tests. The proton conductivities and ion exchange capacities are competitive with Nafion 117, the standard material used today.

| S-EPMC6680964 | biostudies-literature

The Thermoviscosifying Behavior of Water-Soluble Polymer Based on Graft Polymerization of Pluronic F127 with Acrylamide and 2-Acrylamido-2-methylpropane Sulfonic Acid Sodium Salt.

Project description:A new concept of thermoviscosifying polymers is proposed to address the problems about decreasing viscosity of polymer solution under high temperatures. However, existing thermoviscosifying polymers have complicated synthesis processes and high costs, and both of them restrict the wide practical applications of thermoviscosifying polymers. Although polyethers have the characteristics of thermal gelatinization, they just display thermoviscosifying behaviors only under extremely high concentrations (>15 wt %). Therefore, the graft copolymerization of the commercialized Pluronic F127 (PEO100-PPO65-PEO100) with acrylamide and 2-acrylamide-methylpropionic acid sodium salt was studied here. A series of graft modified polyether polymers were prepared and it was expected to get thermoviscosifying polymers with high molecular weights and low association temperatures. Several factors on thermoviscosifying behaviors were investigated, such as polymerization condition, polymer concentration, hydrophilic monomer, molecular structure and molecular weight. It was also proven that the apparent viscosity of polymer solution is influenced by polymer concentration, molecular weight of polymer, and content of anion groups.

| S-EPMC6835222 | biostudies-literature

Biodegradable Poly(acrylic acid-<i>co</i>-acrylamide)/Poly(vinyl alcohol) Double Network Hydrogels with Tunable Mechanics and High Self-healing Performance.

Project description:We proposed a novel strategy in the fabrication of biodegradable poly(acrylic acid-co-acrylamide)/poly(vinyl alcohol) (P(AAc-co-Am)/PVA) double network (DN) hydrogels with good mechanical and self-healing properties. In the DN hydrogel system, P(AAc-co-Am) polymers form a network through the ionic coordinates between -COO- and Fe3+ and hydrogen bonding between -COOH and -CONH2, while another network is fabricated by the complexation between PVA and borax. The influences of the composition on the rheological behaviors and mechanical properties of the synthesized DN hydrogels were investigated. The rheological measurements revealed that the viscoelasticity and stiffness of the P(AAc-co-Am)/PVA DN hydrogels increase as the acrylamide and Fe3+ concentrations increase. At 0.05 mmol of Fe3+ and 50% of acrylamide, tensile strength and elongation at break of P(AAc-co-Am)/PVA DN hydrogels could reach 329.5 KPa and 12.9 mm/mm, respectively. These properties arise from the dynamic reversible bonds existed in the P(AAc-co-Am)/PVA DN hydrogels. These reversible bonds also give good self-healing properties, and the maximum self-healing efficiency of P(AAc-co-Am)/PVA DN hydrogels is up to 96.4%. The degradation test of synthesized DN hydrogels was also conducted under simulated physiological conditions and the weight loss could reach 74% in the simulated intestinal fluid. According to the results presented here, the synthesized P(AAc-co-Am)/PVA DN hydrogels have a potential application prospect in various biomedical fields.

| S-EPMC6631433 | biostudies-literature

One-year multicenter evaluation of a new hydrophobic acrylic intraocular lens with hydroxyethyl methacrylate in an automated preloaded delivery system.

Project description:PurposeTo assess a single-piece monofocal hydrophobic acrylic intraocular lens (IOL) with hydroxyethyl methacrylate (HEMA) (Clareon) contained in automated preloaded delivery system (AutonoMe).Setting18 surgical sites in Japan.DesignObservational study.MethodsIn patients undergoing phacoemulsification and IOL implantation of a new hydrophobic acrylic IOL using an automated injector, clinical data were collected preoperatively and at 1 day, 1 week, and 1 month, 6 months, and 12 months postoperatively. The degree of glistenings was graded on a 4-point scale. The surgeons rated usability and performance of the IOL delivery system on a 5-point scale.ResultsThe study enrolled 384 eyes of 384 patients, ranging in age from 41 to 93 (73.8 ± 8.2, mean ± SD) years. The percentage of eyes with corrected distance visual acuity of 20/25 or better at 1 day, 1 week, and 1 month, 6 months, and 12 months postoperatively was 82.6%, 91.9%, 92.8%, 96.6%, and 95.2%, respectively. Refractive error was within 1.0 diopter in approximately 90% of cases. No glistenings were found in all cases throughout the study period. The rate of Nd:YAG laser posterior capsulotomy was 0.9% at 1 year. The IOL delivery system received high ratings on its usability and performance by the surgeons.ConclusionsThe new hydrophobic acrylic IOL with HEMA showed excellent visual and refractive outcomes without developing glistenings throughout the 1-year study period. The surgeons gave high marks for usability and performance of the automated preloaded delivery system.

| S-EPMC8865199 | biostudies-literature

Superabsorbent poly(acrylic acid) and antioxidant poly(ester amide) hybrid hydrogel for enhanced wound healing.

Project description:Wound healing dressing is increasingly needed in clinical owing to the large quantity of skin damage annually. Excessive reactive oxygen species (ROS) produced through internal or external environmental influences can lead to lipid peroxidation, protein denaturation, and even DNA damage, and ultimately have harmful effects on cells. Aiming to sufficiently contact with the wound microenvironment and scavenge ROS, superabsorbent poly (acrylic acid) and antioxidant poly (ester amide) (PAA/PEA) hybrid hydrogel has been developed to enhance wound healing. The physical and chemical properties of hybrid hydrogels were studied by Fourier-transform infrared (FTIR) absorption spectrum, compression, swelling, degradation, etc. Besides, the antioxidant properties of hybrid hydrogels can be investigated through the free radical scavenging experiment, and corresponding antioxidant indicators have been tested at the cellular level. Hybrid hydrogel scaffolds supported the proliferation of human umbilical vein endothelial cells and fibroblasts, as well as accelerated angiogenesis and skin regeneration in wounds. The healing properties of wounds in vivo were further assessed on mouse skin wounds. Results showed that PAA/PEA hybrid hydrogel scaffolds significantly accelerated the wound healing process through enhancing granulation formation and re-epithelialization. In summary, these superabsorbent and antioxidative hybrid hydrogels could be served as an excellent wound dressing for full-thickness wound healing.

| S-EPMC8055781 | biostudies-literature

TRANSCRIPTOME MODIFICATIONS IN HUMAN GINGIVAL FIBROBLASTS EXPOSED TO 2-HYDROXYETHYL-METHACRYLATE (HEMA)

Project description:Objective: 2-Hydroxyethyl methacrylate (HEMA), one of the most common components of tooth filling materials, could diffuse throughout dentine, and in gingival and pulp cells, affecting odontoblast vitality. Design: the aim of this study was to assess the differential transcriptome modulation induced by HEMA treatment in human cultured gingival fibroblasts (HGFs) at different exposure time compared to untreated cells. Materials and methods: Gene expression profile was performed by employing a whole gene microarray approach on RNA extracted from cultured HGFs exposed to 3 mmol/l HEMA for 24 or 96 h. Differentially identified transcripts were analyzed by Ingenuity Pathways Analysis software to disclose genes biological functions. Results: Hierarchical clustering analysis of the data set originated from a total of 8 experiments showed the selective presence of two gene clusters, composed by hundreds trandcripts differentially expressed after 24-h and 96-h HEMA treatment. when compared to untreated controls. Functional analysis showed the transcripts involvement mainly in cell survival, proliferation and death, with an unbalance towards cell growth and inflammatory response. Conclusions: Data analysis showed an overall damage induced by HEMA exposure for both HGFs cultures at 24 and 96-h mainly leading to a proliferation impairement. Interestingly 24-h HEMA exposure could induce the cells to trigger repair mechanisms evidencing an early compensatory response and survive while. 96-h incubation might increase apoptosis as a consequence of the chronic damage.

2014-12-15 | GSE61043 | GEO

Solvent Effects on Radical Copolymerization Kinetics of 2-Hydroxyethyl Methacrylate and Butyl Methacrylate.

Project description:2-Hydroxyethyl methacrylate (HEMA) is an important component of many acrylic resins used in coatings formulations, as the functionality ensures that the chains participate in the cross-linking reactions required to form the final product. Hence, the knowledge of their radical copolymerization kinetic coefficients is vital for both process and recipe improvements. The pulsed laser polymerization (PLP) technique is paired with size exclusion chromatography (SEC) and nuclear magnetic resonance (NMR) to provide kinetic coefficients for the copolymerization of HEMA with butyl methacrylate (BMA) in various solvents. The choice of solvent has a significant impact on both copolymer composition and on the composition-averaged propagation rate coefficient (kp,cop). Compared to the bulk system, both n-butanol and dimethylformamide reduce the relative reactivity of HEMA during copolymerization, while xylene as a solvent enhances HEMA reactivity. The magnitude of the solvent effect varies with monomer concentration, as shown by a systematic study of monomer/solvent mixtures containing 50 vol%, 20 vol%, and 10 vol% monomer. The observed behavior is related to the influence of hydrogen bonding on monomer reactivity, with the experimental results fit using the terminal model of radical copolymerization to provide estimates of reactivity ratios and kp,HEMA.

| S-EPMC6474149 | biostudies-literature

Rapid Accessible Fabrication and Engineering of Bilayered Hydrogels: Revisiting the Cross-Linking Effect on Superabsorbent Poly(acrylic acid).

Project description:Superabsorbent hydrogels are significant not only in materials science but also in industries and daily life, being used in diapers or soil conditioners as typical examples. The main feature of these materials is their capacity to hold considerable amount of water, which is strongly dependent on the cross-linking density. This study focuses on the preparation of hydrogels by reweighing the effect of cross-linking density on physical properties, which provides green fabrication of bilayered hydrogels that consist of homogeneous structural motifs but show programmed responses via sequential radical polymerization. In particular, when two hydrogel layers containing different cross-linking densities are joined together, an integrated linear bilayer shows heterogeneous deformation triggered by water. We monitor the linear hydrogel bilayer bending into a circle and engineer it by incorporating disperse dyes, changing colors as well as physical properties. In addition, we demonstrate an electric circuit switch using a patterned hydrogel. Anisotropic shape change of the polyelectrolyte switch closes an open circuit and lights a light-emitting diode in red. This proposed fabrication and engineering can be expanded to other superabsorbent systems and create smart responses in cross-linked systems for biomedical or environmental applications.

| S-EPMC6641435 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data