Polydispersity vs. Monodispersity. How the Properties of Ni-Ag Core-Shell Nanoparticles Affect the Conductivity of Ink Coatings.

ABSTRACT: The effect of polydispersity of nickel-silver core-shell nanoparticles (Ni-Ag NPs) on the conductivity of ink coatings was studied. Ni-Ag NPs of various average diameters (100, 220, and 420 nm) were synthesized and utilized for the preparation of conductive inks composed of monodisperse NPs and their polydisperse mixtures. The shell thickness of synthesized Ni-Ag NPs was found to be in the range of 10-20 nm and to provide stability of a core metal to oxidation for at least 6 months. The conductivity of metallic films formed by inks with monodisperse Ni-Ag NPs was compared with those formed by polydisperse inks. In all cases, the optimal conditions for the formation of conductive patterns (weight ratio of monodisperse NPs for polydisperse composition, the concentration of the wetting agent, sintering temperature, and duration) were determined. It was found that metallic films formed by polydisperse ink containing 100, 220, and 420 nm Ni-Ag NPs with a mass ratio of 1:1.5:0.5, respectively, are characterized by the lowest resistivity, 10.9 µΩ·cm, after their thermal post-coating sintering at 300 °C for 30 min that is only 1.6 higher than that of bulk nickel.

SUBMITTER: Pajor-Swierzy A

PROVIDER: S-EPMC8125038 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effect of Oxalic Acid Treatment on Conductive Coatings Formed by Ni@Ag Core-Shell Nanoparticles.

Project description:Low-cost metallic nanoink based on nickel-silver core-shell nanoparticles (Ni@Ag NPs) was used for the formation of conductive metallic coatings with low sintering temperature, which can be successfully applied for replacement of currently used silver-based nanoinks in printed electronics. The effect of oxalic acid (OA) on the sintering temperature and conductivity of coatings formed by Ni@Ag NPs was evaluated. It was found that the addition of OA to the ink formulation and post-printing treatment of deposited films with this acid provided a noticeable decrease in the sintering temperature required for obtaining conductive patterns that is especially important for utilizing the polymeric substrates. The obtained resistivity of metallic coatings after sintering at temperature as low as 100 °C was found to be 30 µΩ·cm, only ~4 times higher compared to the resistivity of bulk Ni that is promising for future application of such materials for fabrication of low-cost flexible printed patterns.

| S-EPMC8746183 | biostudies-literature

Facile Preparation of Monodisperse Cu@Ag Core-Shell Nanoparticles for Conductive Ink in Printing Electronics.

Project description:Copper-based nanoinks are emerging as promising low-cost alternatives to widely used silver nanoinks in electronic printing. However, the spontaneous oxidation of copper under ambient conditions poses significant challenges to its broader application. To address this issue, this paper presents an economical, large-scale, and environmentally friendly method for fabricating Cu@Ag nanoparticles (Cu@Ag NPs). The as-prepared nanoparticles exhibit a narrow size distribution of approximately 100 nm and can withstand ambient exposure for at least 60 days without significant oxidation. The Cu@Ag-based ink, with a 60 wt% loading, was screen-printed onto a flexible polyimide substrate and subsequently heat-treated at 290 °C for 15 minutes under a nitrogen atmosphere. The sintered pattern displayed a low electrical resistivity of 25.5 μΩ·cm (approximately 15 times the resistivity of bulk copper) along with excellent reliability and mechanical fatigue strength. The innovative Cu@Ag NPs fabrication method holds considerable potential for advancing large-scale applications of copper-based inks in flexible electronics.

| S-EPMC10383072 | biostudies-literature

A high-conductivity n-type polymeric ink for printed electronics.

Project description:Conducting polymers, such as the p-doped poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS), have enabled the development of an array of opto- and bio-electronics devices. However, to make these technologies truly pervasive, stable and easily processable, n-doped conducting polymers are also needed. Despite major efforts, no n-type equivalents to the benchmark PEDOT:PSS exist to date. Here, we report on the development of poly(benzimidazobenzophenanthroline):poly(ethyleneimine) (BBL:PEI) as an ethanol-based n-type conductive ink. BBL:PEI thin films yield an n-type electrical conductivity reaching 8 S cm-1, along with excellent thermal, ambient, and solvent stability. This printable n-type mixed ion-electron conductor has several technological implications for realizing high-performance organic electronic devices, as demonstrated for organic thermoelectric generators with record high power output and n-type organic electrochemical transistors with a unique depletion mode of operation. BBL:PEI inks hold promise for the development of next-generation bioelectronics and wearable devices, in particular targeting novel functionality, efficiency, and power performance.

| S-EPMC8060302 | biostudies-literature

Role of the particle size polydispersity in the electrical conductivity of carbon nanotube-epoxy composites.

Project description:Carbon nanotubes (CTNs) with large aspect-ratios are extensively used to establish electrical connectedness in polymer melts at very low CNT loadings. However, the CNT size polydispersity and the quality of the dispersion are still not fully understood factors that can substantially alter the desired characteristics of CNT nanocomposites. Here we demonstrate that the electrical conductivity of polydisperse CNT-epoxy composites with purposely-tailored distributions of the nanotube length L is a quasiuniversal function of the first moment of L. This finding challenges the current understanding that the conductivity depends upon higher moments of the CNT length. We explain the observed quasiuniversality by a combined effect between the particle size polydispersity and clustering. This mechanism can be exploited to achieve controlled tuning of the electrical transport in general CNT nanocomposites.

| S-EPMC5624922 | biostudies-literature

Nano-Silver Ink of High Conductivity and Low Sintering Temperature for Paper Electronics.

Project description:Highly conductive ink with low sintering temperature is important for printed electronics on paper substrate. Silver nanoparticles (Ag NPs) of different average radii ranging from 48 to 176?nm were synthesized by adjusting the Ag+ concentration in the reaction process. The electric resistivity of the Ag NP-based ink film in relation to Ag NP size, sintering temperature, amount of PVP capping agent on Ag NP surface, and morphology evolution of the film during heating process was investigated. It was found that the resistivity of the films reduced very rapidly with increasing particle size due above all to reduced amount of protective agent capping on the Ag NPs. A semi-empirical relationship between the resistivity and the particle size was proposed. With the help of this mathematical expression, one gains both systematic and detailed insight to the resistivity evaluation with regard to the Ag particle size. The optimal electric resistivity of 4.6??? cm was achieved at 140?°C for 10?min which was very close to the resistivity value of bulk Ag (1.58??? cm). Mechanical flexibility of the printed electronics with the Ag NP-based ink on paper substrates was investigated. The prints on the art coated paper exhibited better flexibility compared to that on the photopaper. This might be attributed to the surface coating composition, surface morphology of the paper, and their corresponding ink absorption property.

| S-EPMC6554461 | biostudies-literature

Corrosion Resistance of Heat-Treated Ni-W Alloy Coatings.

Project description:The paper presents research on evaluation of corrosion resistance of Ni-W alloy coatings subjected to heat treatment. The corrosion resistance was tested in 5% NaCl solution by the use of potentiodynamic polarization technique and electrochemical impedance spectroscopy. Characteristics of the Ni-W coatings after heat treatment were carried out using scanning electron microscopy, scanning Kelvin probe technique and X-ray diffraction. Suggested reasons for the improvement of properties of the heat treated Ni-W coating, obtained at the lowest current density value (125 mA?cm-2), are the highest tungsten content (c.a. 25 at.%) as well as the smallest and the most homogeneous electrochemically active surface area.

| S-EPMC7085042 | biostudies-literature

Deposition of Ag and Ag-Au nanocrystalline films with tunable conductivity at the water-toluene interface.

Project description:Thin films of Au, Ag and Ag-Au alloy nanocrystals extending to areas of several square centimetres are obtained by deposition at the interface of water and toluene. Toluene containing chlorotris(triphenylphosphine)silver(i) and/or chlorotriphenylphosphine gold(i) is reacted with aqueous tetrakishydroxymethylphosphonium chloride to obtain nanocrystalline films adhered to the interfacial region. Alloying was induced by varying the composition of the toluene layer. The composition change results in regular and reproducible variation in the transport characteristics of the films, with the initially metallic deposits turning non-metallic with increased Au content. The films at the interface were transferred to different substrates and characterised using atomic force microscopy, UV-visible spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, scanning and transmission electron microscopy.

| S-EPMC9078230 | biostudies-literature

Co-electrodeposition of hard Ni-W/diamond nanocomposite coatings.

Project description:Electroplated hard chrome coating is widely used as a wear resistant coating to prolong the life of mechanical components. However, the electroplating process generates hexavalent chromium ion which is known carcinogen. Hence, there is a major effort throughout the electroplating industry to replace hard chrome coating. Composite coating has been identified as suitable materials for replacement of hard chrome coating, while deposition coating prepared using traditional co-deposition techniques have relatively low particles content, but the content of particles incorporated into a coating may fundamentally affect its properties. In the present work, Ni-W/diamond composite coatings were prepared by sediment co-electrodeposition from Ni-W plating bath, containing suspended diamond particles. This study indicates that higher diamond contents could be successfully co-deposited and uniformly distributed in the Ni-W alloy matrix. The maximum hardness of Ni-W/diamond composite coatings is found to be 2249 ± 23 Hv due to the highest diamond content of 64 wt.%. The hardness could be further enhanced up to 2647 ± 25 Hv with heat treatment at 873 K for 1 h in Ar gas, which is comparable to hard chrome coatings. Moreover, the addition of diamond particles could significantly enhance the wear resistance of the coatings.

| S-EPMC4770281 | biostudies-other

Core Size does not Affect Blinking Behavior of Dye-Doped Ag@SiO<sub>2</sub> Core-Shell Nanoparticles for Super-Resolution Microscopy.

Project description:Dye-doped nanoparticles have been investigated as bright, luminescent labels for super -resolution microscopy via localization methods. One key factor in super-resolution is the size of the luminescent label, which in some cases results in a frame shift between the label target and the label itself. Ag@SiO2 core-shell nanoparticles, doped with organic fluorophores, have shown promise as super-resolution labels. One key aspect of these nanoparticles is that they blink under certain conditions, allowing super-resolution localization with a single excitation source in aqueous solution. In this work, we investigated the effects of both the Ag core and the silica (SiO2) shell on the self-blinking properties of these nanoparticles. Both core size and shell thickness were manipulated by altering the reaction time to determine core and shell effects on photoblinking. Size and shell thickness were investigated individually under both dry and hydrated conditions and were then doped with a 1 mM solution of Rhodamine 110 for analysis. We observed that the cores themselves are weakly luminescent and are responsible for the blinking observed in the fully-synthesized metal-enhanced fluorescence nanoparticles. There was no statistically significant difference in photoblinking behavior-both intensity and duty cycle-with decreasing core size. This observation was used to synthesize smaller nanoparticles ranging from approximately 93 nm to 110 nm as measured using dynamic light scattering. The blinking particles were localized via super-resolution microscopy and show single particle self-blinking behavior. As the core size did not impact blinking performance or intensity, the nanoparticles can instead be tuned for optimal size without sacrificing luminescence properties.

| S-EPMC8963217 | biostudies-literature

Synthesis and Performance Evaluation of Pulse Electrodeposited Ni-AlN Nanocomposite Coatings.

Project description:This research work presents the microscopic analysis of pulse electrodeposited Ni-AlN nanocomposite coatings using SEM and AFM techniques and their performance evaluation (mechanical and electrochemical) by employing nanoindentation and electrochemical methods. The Ni-AlN nanocomposite coatings were developed by pulse electrodeposition. The nickel matrix was reinforced with various amounts of AlN nanoparticles (3, 6, and 9?g/L) to develop Ni-AlN nanocomposite coatings. The effect of reinforcement concentration on structure, surface morphology, and mechanical and anticorrosion properties was studied. SEM and AFM analyses indicate that Ni-AlN nanocomposite coatings have dense, homogenous, and well-defined pyramid structure containing uniformly distributed AlN particles. A decent improvement in the corrosion protection performance is also observed by the addition of AlN particles to the nickel matrix. Corrosion current was reduced from 2.15 to 1.29??A?cm-2 by increasing the AlN particles concentration from 3 to 9?g/L. It has been observed that the properties of Ni-AlN nanocomposite coating are sensitive to the concentration of AlN nanoparticles used as reinforcement.

| S-EPMC5830284 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data