Enhanced Mechanical Properties and Microstructure of Accumulative Roll-Bonded Co/Pb Nanocomposite.

ABSTRACT: Lead composites have been used as anodes in the electrowinning process to produce metals such as copper and zinc. Manufacturing stable lead anodes with appropriate mechanical and chemical properties is required to improve the performance of the electrowinning process. In this study, an accumulative roll bonding (ARB) method was used to fabricate a Co/Pb nanocomposite. Utilizing the ARB method can help us to achieve a uniform structure with enhanced mechanical properties via severe plastic deformation. The results showed that suitable tensile properties were obtained in Pb-0.5%Co-10pass samples. The tensile strength and strain of these samples were 2.51 times higher and 83.7% lower than that of as-cast pure Pb. They also showed creep resistance and hardness up to 1.8 and 2.5 times more than that of as-cast pure Pb. The ARB technique uniformly distributed Co particles in the Pb matrix. The enhanced strength of Pb samples was observed in the composite including grain sizes of less than 50 nm as a result of hindering the recovery phenomenon. The particle size of the Co distributed in the Pb matrix was 353 ± 259 nm. Compared to conventional methods, the ARB process improved the mechanical properties of Co/Pb composites and can open a new horizon to fabricating this composite in metal industries.

SUBMITTER: Karbasi M

PROVIDER: S-EPMC8147126 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Microstructure Evolution and Mechanical Properties of Al-TiB₂/TiC In Situ Aluminum-Based Composites during Accumulative Roll Bonding (ARB) Process.

Project description:In this study, a kind of Al-TiB₂/TiC in situ composite was successfully prepared using the melt reaction method and the accumulative roll-bonding (ARB) technique. The microstructure evolution of the composites with different deformation treatments was characterized using field emission scanning electron microscopy (FESEM) and a transmission electron microscope (TEM). The mechanical properties of the Al-TiB₂/TiC in situ composite were also studied with tensile and microhardness tests. It was found that the distribution of reinforcement particles becomes more homogenous with an increasing ARB cycle. Meanwhile, the mechanical properties showed great improvement during the ARB process. The ultimate tensile strength (UTS) and microhardness of the composites were increased to 173.1 MPa and 63.3 Hv after two ARB cycles, respectively. Furthermore, the strengthening mechanism of the composite was analyzed based on its fracture morphologies.

| S-EPMC5459192 | biostudies-other

Fabrication of Al/Mg/Al Composites via Accumulative Roll Bonding and Their Mechanical Properties.

Project description:Al(1060)/Mg(AZ31)/Al(1060) multilayered composite was successfully produced using an accumulative roll bonding (ARB) process for up to four cycles at an elevated temperature (400 °C). The microstructure evolution of the composites and the bonding characteristics at the interfaces between Al and Mg layers with increasing ARB cycles were characterized through optical microscopy, field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). It was found that the grains of Al and Mg layers were significantly refined and Al₃Mg₂ and Al12 Mg17 intermetallic compound layers formed at the Al/Mg bonding interfaces. The strength increased gradually and the ultimate tensile strength (UTS) reached a maximum value of about 240 MPa at the third pass. Furthermore, the strengthening mechanism of the composite was analyzed based on the fracture morphologies.

| S-EPMC5457262 | biostudies-other

Effect of Processing Route on Microstructure and Mechanical Properties in Single-Roll Angular-Rolling.

Project description:This paper reports the effect of the processing route on the microstructure and mechanical properties in the pure copper sheets processed by single-roll angular-rolling (SRAR). The SRAR process was repeated up to six passes in two processing routes, called routes A and C in equal-channel angular pressing. As the number of passes increased, the heterogeneous evolution of hardness and microstructural heterogeneities between the core and surface regions gradually became intensified in both processing routes. In particular, route A exhibited more prominent partial grain refinement and dislocation localization on the core region than route C. The finite element analysis revealed that the intense microstructural heterogeneities observed in route A were attributed to effective shear strain partitioning between the core and surface regions by the absence of redundant strain. On the other hand, route C induced reverse shearing and cancellation of shear strain over the entire thickness, leading to weak shear strain partitioning and delayed grain refinement. Ultimately, this work suggests that route A is the preferred option to manufacture reverse gradient structures in that the degree of shear strain partitioning and microstructural heterogeneity between the core and surface regions is more efficiently intensified with increasing the number of passes.

| S-EPMC7321117 | biostudies-literature

Microstructure and Electrical Properties of Fluorene Polyester Based Nanocomposite Dielectrics.

Project description:As a new type of dielectric material, the low dielectric constant and corona resistance life of fluorene polyester (FPE) restricts the range of its applications. In order to simultaneously achieve a high dielectric constant and the long corona aging lifetime of FPE, SiO2 nanoparticles were chosen as additive to prepare FPE-based composite films. The microstructure of the composite film was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), infrared spectroscopy (IR) and small-angle X-ray scattering (SAXS). The dielectric performances of the composites, including the dielectric constant, breakdown strength and corona resistance lifetime, were investigated. The results show that the introduced SiO2 does not destroy the structure of the FPE molecular chain and that it increases the thickness of the filler-matrix interface. The dielectric constant of SiO2/FPE composites increased from 3.54 to 7.30 at 1 Hz. Importantly, the corona resistance lifetime increased by about 12 times compared with the pure FPE matrix. In brief, this work shows what possibilities there might be when considering the potential applications of high-strength insulating materials.

| S-EPMC8471433 | biostudies-literature

Evolution of microstructure, strain and physical properties in oxide nanocomposite films.

Project description:We, using LSMO:ZnO nanocomposite films as a model system, have studied the effect of film thickness on the physical properties of nanocomposites. It shows that strain, microstructure, as well as magnetoresistance strongly rely on film thickness. The magnetotransport properties have been fitted by a modified parallel connection channel model, which is in agreement with the microstructure evolution as a function of film thickness in nanocomposite films on sapphire substrates. The strain analysis indicates that the variation of physical properties in nanocomposite films on LAO is dominated by strain effect. These results confirm the critical role of film thickness on microstructures, strain states, and functionalities. It further shows that one can use film thickness as a key parameter to design nanocomposites with optimum functionalities.

| S-EPMC4067618 | biostudies-literature

Microstructure and mechanical properties of different keratinous horns.

Project description:Animal horns play an important role during intraspecific combat. This work investigates the microstructure and mechanical properties of horns from four representative ruminant species: the bighorn sheep (Ovis canadensis), domestic sheep (Ovis aries), mountain goat (Oreamnos americanus) and pronghorn (Antilocapra americana), aiming to understand the relation between evolved microstructures and mechanical properties. Microstructural similarity is found where disc-shaped keratin cells attach edge-to-edge along the growth direction of the horn core (longitudinal direction) forming a lamella; multiple lamellae are layered face to face along the impact direction (radial direction, perpendicular to horn core growth direction), forming a wavy pattern surrounding a common feature, the tubules. Differences among species include the number and shape of the tubules, the orientation of aligned lamellae and the shape of keratin cells. Water absorption tests reveal that the pronghorn horn has the largest water-absorbing ability due to the presence of nanopores in the keratin cells. The loading direction (compressive and tensile) and level of hydration vary among the horns from different species. The differences in mechanical properties among species may relate to their different fighting behaviours: high stiffness and strength in mountain goat to support the forces during stabbing; high tensile strength in pronghorn for interlocked pulling; impact energy absorption properties in domestic and bighorn sheep to protect the skull during butting. These design rules based on evolutionary modifications among species can be applied in synthetic materials to meet different mechanical requirements.

| S-EPMC6030630 | biostudies-literature

Hybrid Cements: Mechanical Properties, Microstructure and Radiological Behavior.

Project description:The use of more eco-efficient cements in concretes is one of the keys to ensuring construction industry sustainability. Such eco-efficient binders often contain large but variable proportions of industrial waste or by-products in their composition, many of which may be naturally occurring radioactive materials (NORMs). This study explored the application of a new gamma spectrometric method for measuring radionuclide activity in hybrid alkali-activated cements from solid 5 cm cubic specimens rather than powder samples. The research involved assessing the effect of significant variables such as the nature of the alkaline activator, reaction time and curing conditions to relate the microstructures identified to the radiological behavior observed. The findings showed that varying the inputs generated pastes with similar reaction products (C-S-H, C-A-S-H and (N,C)-A-S-H) but different microstructures. The new gamma spectrometric method for measuring radioactivity in solid 5 cm cubic specimens in alkaline pastes was found to be valid. The variables involved in hybrid cement activation were shown to have no impact on specimen radioactive content. The powder samples, however, emanated 222Rn (a descendent of 226Ra), possibly due to the deformation taking place in fly ash structure during alkaline activation. Further research would be required to explain that finding.

| S-EPMC8781129 | biostudies-literature

Annealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding.

Project description:Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mechanical properties was monitored by microhardness measurements. The microhardness increases when the material is annealed up to 160 °C. Above this temperature a fast drop of microhardness occurs followed by a negligible variation at annealing temperatures exceeding 300 °C. In order to map continuously the microstructure changes during annealing, the in situ TEM experiments in the heating stage were performed as a supplement to post-mortem TEM observations.

| S-EPMC5456430 | biostudies-other

Microstructure, mineral and mechanical properties of teleost intermuscular bones.

Project description:There is an increasing interest in understanding teleost bone biomechanics in several scientific communities, for instance as interesting biomaterials with specific structure-function relationships. Intermuscular bones of teleost fish have previously been described to play a role in the mechanical force transmission between muscle and bone, but their biomechanical properties are not yet fully described. Here, we have investigated intermuscular bones (IBs) of the North Atlantic Herring with regard to their structure and micro-architecture, mineral-related properties, and micro-mechanical tensile properties. A total of 115 IBs from 18 fish were investigated. One cohort of IBs, containing 20 bones from 2 smaller fish and 23 bones of 3 larger fish, was used for mechanical testing, wide-angle X-ray scattering, and scanning electron microscopy. Another cohort, containing 36 bones from 7 smaller fish and 36 bones from 6 larger fish, was used for microCT. Results show some astonishing properties of the IBs: (i) IBs present higher ductility, lower Young's modulus but similar strength and TMD (Tissue Mineral Density) compared to mammalian bone, and (ii) IBs from small fish were 49% higher in Young's modulus than fish bones from larger fish while their TMD was not statistically different and crystal length was 8% higher in large fish bones. Our results revealed that teleost IB presents a hybrid nature of soft and hard tissue that differs from other bone types, which might be associated with their evolution from mineralized tendons. This study provides new data regarding teleost fish bone biomechanical and micro-structural properties.

| S-EPMC6995032 | biostudies-literature

Mechanical and biological properties of chitosan/carbon nanotube nanocomposite films.

Project description:In this article, different concentrations of multiwalled carbon nanotube (MWCNT) were homogeneously dispersed throughout the chitosan (CS) matrix. A simple solvent-cast method was used to fabricate chitosan films with 0.1, 0.5, and 1% of MWCNT with the average diameter around 30 nm. The CS/MWCNT films were characterized for structural, viscous and mechanical properties with optical microscopy, wide-angle X-ray diffraction, Raman spectroscopy, tensile test machine, and microindentation testing machine. Murine osteoblasts were used to examine the cell viability and attachment of the nanocomposite films at two time points. In comparison to the pure chitosan film, the mechanical properties, including the tensile modulus and strength of the films, were greatly improved by increasing the percentage of MWCNT. Furthermore, adding MWCNT up to 1% increased the viscosity of the chitosan solution by 15%. However, adding MWCNT decreased the samples ductility and transparency. In biological point of view, no toxic effect on osteoblasts was observed in the presence of different percentages of MWCNT at day 3 and day 7. This investigation suggested MWCNT could be a promising candidate for improving chitosan mechanical properties without inducing remarkable cytotoxicity on bone cells.

| S-EPMC4443444 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data