Microstructure and Electrical Properties of Fluorene Polyester Based Nanocomposite Dielectrics.

ABSTRACT: As a new type of dielectric material, the low dielectric constant and corona resistance life of fluorene polyester (FPE) restricts the range of its applications. In order to simultaneously achieve a high dielectric constant and the long corona aging lifetime of FPE, SiO₂ nanoparticles were chosen as additive to prepare FPE-based composite films. The microstructure of the composite film was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), infrared spectroscopy (IR) and small-angle X-ray scattering (SAXS). The dielectric performances of the composites, including the dielectric constant, breakdown strength and corona resistance lifetime, were investigated. The results show that the introduced SiO₂ does not destroy the structure of the FPE molecular chain and that it increases the thickness of the filler-matrix interface. The dielectric constant of SiO₂/FPE composites increased from 3.54 to 7.30 at 1 Hz. Importantly, the corona resistance lifetime increased by about 12 times compared with the pure FPE matrix. In brief, this work shows what possibilities there might be when considering the potential applications of high-strength insulating materials.

SUBMITTER: Zhang W

PROVIDER: S-EPMC8471433 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Fluorene-Based Donor-Acceptor Copolymers Containing Functionalized Benzotriazole Units: Tunable Emission and their Electrical Properties.

Project description:Monomers 4,7-dibromo-2H-benzo[d]1,2,3-triazole (m1) and 4,7-(bis(4-bromophenyl)ethynyl)-2H-benzo[d]1,2,3-triazole (m2) have been synthesized in good yields using different procedures. Monomers m1 and m2 have been employed for building new copolymers of fluorene derivatives by a Suzuki reaction under microwave irradiation using the same conditions. In each case different chain lengths have been achieved, while m1 gives rise to polymers for m2 oligomers have been obtained (with a number of monomer units lower than 7). Special interest has been paid to their photophysical properties due to excited state properties of these D-A units alternates, which have been investigated by density functional theory (DFT) calculations using two methods: (i) An oligomer approach and (ii) by periodic boundary conditions (PBC). It is highly remarkable the tunability of the photophysical properties as a function of the different monomer functionalization derived from 2H-benzo[d]1,2,3-triazole units. In fact, a strong modulation of the absorption and emission properties have been found by functionalizing the nitrogen N-2 of the benzotriazole units or by elongation of the π-conjugated core with the introduction of alkynylphenyl groups. Furthermore, the charge transport properties of these newly synthesized macromolecules have been approached by their implementation in organic field-effect transistors (OFETs) in order to assess their potential as active materials in organic optoelectronics.

| S-EPMC7077272 | biostudies-literature

Evolution of microstructure, strain and physical properties in oxide nanocomposite films.

Project description:We, using LSMO:ZnO nanocomposite films as a model system, have studied the effect of film thickness on the physical properties of nanocomposites. It shows that strain, microstructure, as well as magnetoresistance strongly rely on film thickness. The magnetotransport properties have been fitted by a modified parallel connection channel model, which is in agreement with the microstructure evolution as a function of film thickness in nanocomposite films on sapphire substrates. The strain analysis indicates that the variation of physical properties in nanocomposite films on LAO is dominated by strain effect. These results confirm the critical role of film thickness on microstructures, strain states, and functionalities. It further shows that one can use film thickness as a key parameter to design nanocomposites with optimum functionalities.

| S-EPMC4067618 | biostudies-literature

Enhanced Mechanical Properties and Microstructure of Accumulative Roll-Bonded Co/Pb Nanocomposite.

Project description:Lead composites have been used as anodes in the electrowinning process to produce metals such as copper and zinc. Manufacturing stable lead anodes with appropriate mechanical and chemical properties is required to improve the performance of the electrowinning process. In this study, an accumulative roll bonding (ARB) method was used to fabricate a Co/Pb nanocomposite. Utilizing the ARB method can help us to achieve a uniform structure with enhanced mechanical properties via severe plastic deformation. The results showed that suitable tensile properties were obtained in Pb-0.5%Co-10pass samples. The tensile strength and strain of these samples were 2.51 times higher and 83.7% lower than that of as-cast pure Pb. They also showed creep resistance and hardness up to 1.8 and 2.5 times more than that of as-cast pure Pb. The ARB technique uniformly distributed Co particles in the Pb matrix. The enhanced strength of Pb samples was observed in the composite including grain sizes of less than 50 nm as a result of hindering the recovery phenomenon. The particle size of the Co distributed in the Pb matrix was 353 ± 259 nm. Compared to conventional methods, the ARB process improved the mechanical properties of Co/Pb composites and can open a new horizon to fabricating this composite in metal industries.

| S-EPMC8147126 | biostudies-literature

Dry Spin Graphene Oxide Fibers: Mechanical/Electrical Properties and Microstructure Evolution.

Project description:Dry-spinning method is extensively employed in fiber industry, comparing to the counter-part of wet-spinning process, it has advantages of environmentally friendly, high yield rate and no need for purification. Here, we report the synthesis of graphene oxide (GO) fibers via dry spinning GO inks with extremely high concentrations. The proper rheology properties of such GO inks allow us to dry spin GO fiber directly. Various dry spinning conditions are investigated, and the relationship between mechanical performance and micro-structure of the obtained GO fiber are established. We found that the existence of larger GO liquid crystal domains does not necessarily result to higher mechanical properties, and it is because those large GO liquid crystal domains evolve into thick GO films during drying process and thus prevent the intimate compaction of the whole GOF and leave behind gaps. This is detrimental for the mechanical properties, and thus the dry spin GOF are much weaker than that of wet spin ones. Importantly, Barus effects, that generally arise during the melt spinning of polymers, were not observed, indicating that caution must be taken when classical polymer rheology theories are applied to investigate the dynamic behaviors of GO solution.

| S-EPMC6050277 | biostudies-literature

Microstructure optimization of bioderived polyester nanofilms for antibiotic desalination via nanofiltration.

Project description:The successful implementation of thin-film composite membranes (TFCM) for challenging solute-solute separations in the pharmaceutical industry requires a fine control over the microstructure (size, distribution, and connectivity of the free-volume elements) and thickness of the selective layer. For example, desalinating antibiotic streams requires highly interconnected free-volume elements of the right size to block antibiotics but allow the passage of salt ions and water. Here, we introduce stevioside, a plant-derived contorted glycoside, as a promising aqueous phase monomer for optimizing the microstructure of TFCM made via interfacial polymerization. The low diffusion rate and moderate reactivity of stevioside, together with its nonplanar and distorted conformation, produced thin selective layers with an ideal microporosity for antibiotic desalination. For example, an optimized 18-nm membrane exhibited an unprecedented combination of high water permeance (81.2 liter m-2 hour-1 bar-1), antibiotic desalination efficiency (NaCl/tetracycline separation factor of 11.4), antifouling performance, and chlorine resistance.

| S-EPMC10162667 | biostudies-literature

Microstructure, Mechanical and Electrical Properties of Hybrid Copper Matrix Composites with Fe Microspheres and rGO Nanosheets.

Project description:Copper matrix composites have a wide application as magnetic conductive materials, electromagnetic materials, electrical discharge machining materials, etc. Such materials are expected to have a good combination of excellent electrical conductivity and good mechanical strength. In this work, micro/nano hybrid reinforcements with Fe microspheres and reduced graphene oxide (rGO) nanosheets were developed for copper matrix composites. The rGO/Fe/Cu powders were firstly wet-mixed and then densified by the vacuum hot-pressing sintering to obtain the bulk compacts. Microstructure, electrical conductivity and mechanical properties of such compacts were investigated. Microstructural result of as-sintered compacts shows that the Fe microspheres could distribute in the matrix uniformly, and rGO nanosheets exhibit both agglomerated and dispersed states. The grain size of Cu matrix decreased with the increase of the rGO content. Hardness, compression and tensile 0.2% yield strength of the as-sintered compacts were improved evidently by the addition of the hybrid Fe/rGO, comparing with pure Cu and single Fe-added composites. However, a lower electrical conductivity appeared in the more rGO-added composites, but still reached more than 33.0% international annealing copper standard (IACS). These performance change could be sought in the spatially geometrical distribution and characteristics of such micro/nano Fe/rGO hybrid addition, and the relevant mechanisms were discussed.

| S-EPMC9573056 | biostudies-literature

Local Dielectric Property Detection of the Interface between Nanoparticle and Polymer in Nanocomposite Dielectrics.

Project description:The interface between nanoparticles and polymer matrix is considered to have an important effect on the properties of nanocomposites. In this experimental study, electrostatic force microscopy (EFM) is used to study the local dielectric property of the interface of low density polyethylene (LDPE)/TiO2 nanocomposites at nanometer scale. The results show that the addition of TiO2 nanoparticles leads to a decrease in local permittivity. We then carry out the finite element simulation and confirm that the decrease of local permittivity is related to the effect of interface. According to the results, we propose several models and validate the dielectric effect and range effect of interface. Through the analysis of DSC and solid-state NMR results, we find TiO2 nanoparticles can suppress the mobility of local chain segments in the interface, which influences the dipolar polarization of chain segments in the interface and eventually results in a decrease in local permittivity. It is believed the results would provide important hint to the research of the interface in future research.

| S-EPMC5154196 | biostudies-literature

Effect of Almond Shell Waste on Physicochemical Properties of Polyester-Based Biocomposites.

Project description:Polyester-based biocomposites containing INZEA F2® biopolymer and almond shell powder (ASP) at 10 and 25 wt % contents with and without two different compatibilizers, maleinized linseed oil and Joncryl ADR 4400®, were prepared by melt blending in an extruder, followed by injection molding. The effect of fine (125-250 m) and coarse (500-1000 m) milling sizes of ASP was also evaluated. An improvement in elastic modulus was observed with the addition of< both fine and coarse ASP at 25 wt %. The addition of maleinized linseed oil and Joncryl ADR 4400 produced some compatibilizing effect at low filler contents while biocomposites with a higher amount of ASP still presented some gaps at the interface by field emission scanning electron microscopy. Some decrease in thermal stability was shown which was related to the relatively low thermal stability and disintegration of the lignocellulosic filler. The added modifiers provided some enhanced thermal resistance to the final biocomposites. Thermal analysis by differential scanning calorimetry and thermogravimetric analysis suggested the presence of two different polyesters in the polymer matrix, with one of them showing full disintegration after 28 and 90 days for biocomposites containing 25 and 10 wt %, respectively, under composting conditions. The developed biocomposites have been shown to be potential polyester-based matrices for use as compostable materials at high filler contents.

| S-EPMC7240503 | biostudies-literature

Microstructure and Electrical Properties of AZO/Graphene Nanosheets Fabricated by Spark Plasma Sintering.

Project description:In this study we report on the sintering behavior, microstructure and electrical properties of Al-doped ZnO ceramics containing 0-0.2 wt. % graphene sheets (AZO-GNSs) and processed using spark plasma sintering (SPS). Our results show that the addition of <0.25 wt. % GNSs enhances both the relative density and the electrical resistivity of AZO ceramics. In terms of the microstructure, the GNSs are distributed at grain boundaries. In addition, the GNSs are also present between ZnO and secondary phases (e.g., ZnAl₂O₄) and likely contribute to the measured enhancement of Hall mobility (up to 105.1 cm²·V-1·s-1) in these AZO ceramics. The minimum resistivity of the AZO-GNS composite ceramics is 3.1 × 10-4 Ω·cm which compares favorably to the value of AZO ceramics which typically have a resistivity of 1.7 × 10-3 Ω·cm.

| S-EPMC5509084 | biostudies-other

Facile Fabrication of Environmentally-Friendly Hydroxyl-Functionalized Multiwalled Carbon Nanotubes/Soy Oil-Based Polyurethane Nanocomposite Bioplastics with Enhanced Mechanical, Thermal, and Electrical Conductivity Properties.

Project description:It is challenging to prepare polyurethane bioplastics from renewable resources in a sustainable world. In this work, polyurethane nanocomposite bioplastics are fabricated by blending up to 80 wt % of soy-based polyol and petrochemical polyol with hydroxyl-functionalized multiwalled carbon nanotubes (MWCNTs-OH). The scanning electron microscope (SEM), transmission electron microscope (TEM), and Fourier transform infrared spectroscopy (FTIR) analyses reveal homogeneous dispersion of the MWCNTs-OH in the matrix, as well as interaction or reaction of MWCNTs-OH with the matrix or polymeric methylene diphenyl diisocyanate (pMDI) in forming the organic-inorganic hybrid bioplastic with a three-dimensional (3D) macromolecule network structure. Mechanical properties and electrical conductivity are remarkably enhanced with the increase of the multiwalled carbon nanotube (MWCNTs) loading. Dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA) results show that the bioplastics with MWCNTs-OH have a better thermal stability compared with the bioplastics without MWCNTs-OH. The composition of the nanocomposites, which defines the characteristics of the material and its thermal and electrical conductivity properties, can be precisely controlled by simply varying the concentration of MWCNTs-OH in the polyol mixture solution.

| S-EPMC6572346 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data