Gas Porosimetry by Gas Adsorption as an Efficient Tool for the Assessment of the Shaping Effect in Commercial Zeolites.

ABSTRACT: A set of three commercial zeolites (13X, 5A, and 4A) of two distinct shapes have been characterized: (i) pure zeolite powders and (ii) extruded spherical beads composed of pure zeolite powders and an unknown amount of binder used during their preparation process. The coupling of gas porosimetry experiments using argon at 87 K and CO₂ at 273 K allowed determining both the amount of the binder and its effect on adsorption properties. It was evidenced that the beads contain approximately 25 wt% of binder. Moreover, from CO₂ adsorption experiments at 273 K, it could be inferred that the binder present in both 13X and 5A zeolites does not interact with the probe molecule. However, for the 4A zeolite, pore filling pressures were shifted and strong interaction with CO₂ was observed leading to irreversible adsorption of the probe. These results have been compared to XRD, IR spectroscopy, and ICP-AES analysis. The effect of the binder in shaped zeolite bodies can thus have a crucial impact on applications in adsorption and catalysis.

SUBMITTER: Orsikowsky-Sanchez A

PROVIDER: S-EPMC8147277 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Dataset on the comparison of synthesized and commercial zeolites for potential solar adsorption refrigerating system.

Project description:The purpose of this dataset is to provide a comparison between synthesized and commercial 4A and 13X type zeolites. Metakaolin produced from the calcination of beneficiated kaolin at 750?°C for 4?h was dealuminated using sulphuric acid to get the required silica to alumina ratio for the zeolite synthesis. Zeolite 4A and 13X samples were characterized along-side with the commercial variants using X-ray fluorescence (XRF), X-ray diffraction (XRD), Brunauer, Emmett and Teller (BET) and scanning electron microscopy (SEM) techniques. These analyses revealed that, the zeolites synthesized are of comparatively acceptable quality. The pore size of 120.859?nm, pore volume of 0.0065?cm3/g and surface area of 22?m2/g were obtained from BET analyses for zeolite 4A synthesized from kaolin, while the commercial zeolite 4A used as control gave pore size of 58.143?nm, pore volume of 0.2462?cm3/g and surface area of 559.13?m2/g. In the same vein, the pore size of 10.5059?nm, pore volume of 0.135847?cm3/g and surface area of 324.584?m2/g were obtained from BET analyses for zeolite 13X synthesized from kaolin, while the commercial zeolite 13X gave pore size of 7.2752?nm, pore volume of 0.135951?cm3/g and surface area of 310.0906?m2/g.

| S-EPMC6083001 | biostudies-literature

Designing hierarchical nanoporous membranes for highly efficient gas adsorption and storage.

Project description:Nanoporous membranes with two-dimensional materials such as graphene oxide have attracted attention in volatile organic compounds (VOCs) and H2 adsorption because of their unique molecular sieving properties and operational simplicity. However, agglomeration of graphene sheets and low efficiency remain challenging. Therefore, we designed hierarchical nanoporous membranes (HNMs), a class of nanocomposites combined with a carbon sphere and graphene oxide. Hierarchical carbon spheres, prepared following Murray's law using chemical activation incorporating microwave heating, act as spacers and adsorbents. Hierarchical carbon spheres preclude the agglomeration of graphene oxide, while graphene oxide sheets physically disperse, ensuring structural stability. The obtained HNMs contain micropores that are dominated by a combination of ultramicropores and mesopores, resulting in high VOCs/H2 adsorption capacity, up to 235 and 352 mg/g at 200 ppmv and 3.3 weight % (77 K and 1.2 bar), respectively. Our work substantially expands the potential for HNMs applications in the environmental and energy fields.

| S-EPMC7541071 | biostudies-literature

Competitive Adsorption of Xylenes at Chemical Equilibrium in Zeolites.

Project description:The separation of xylenes is one of the most important processes in the petrochemical industry. In this article, the competitive adsorption from a fluid-phase mixture of xylenes in zeolites is studied. Adsorption from both vapor and liquid phases is considered. Computations of adsorption of pure xylenes and a mixture of xylenes at chemical equilibrium in several zeolite types at 250 °C are performed by Monte Carlo simulations. It is observed that shape and size selectivity entropic effects are predominant for small one-dimensional systems. Entropic effects due to the efficient arrangement of xylenes become relevant for large one-dimensional systems. For zeolites with two intersecting channels, the selectivity is determined by a competition between enthalpic and entropic effects. Such effects are related to the orientation of the methyl groups of the xylenes. m-Xylene is preferentially adsorbed if xylenes fit tightly in the intersection of the channels. If the intersection is much larger than the adsorbed molecules, p-xylene is preferentially adsorbed. This study provides insight into how the zeolite topology can influence the competitive adsorption and selectivity of xylenes at reaction conditions. Different selectivities are observed when a vapor phase is adsorbed compared to the adsorption from a liquid phase. These insight have a direct impact on the design criteria for future applications of zeolites in the industry. MRE-type and AFI-type zeolites exclusively adsorb p-xylene and o-xylene from the mixture of xylenes in the liquid phase, respectively. These zeolite types show potential to be used as high-performing molecular sieves for xylene separation and catalysis.

| S-EPMC8025683 | biostudies-literature

Porosity Measurement of Low Permeable Materials Using Gas Expansion Induced Water Intrusion Porosimetry (GEIWIP).

Project description:Porosity measurement is a key factor to identify the hydraulic performance of low permeable porous materials (e.g. rock or concrete). Porosimetry tests such as Mercury Intrusion Porosimetry (MIP), Nuclear Magnetic Resonance (NMR), or Gas Expansion (GE) are cost-prohibitive, use hazardous materials, or are incapable of accessing all inter-connected pores. An alternative Gas Expansion Induced Water Intrusion Porosimetry (GEIWIP) method was developed to measure the porosity of a low permeable porous medium using a gas/water intrusion apparatus. This method overcomes the previously mentioned porosimetry drawbacks by using distilled de-aired water (DDW) as a hazard-free liquid which is a wetting fluid to intrude the porous structure and fill the pores. As the DDW has the tendency to fill all inter-connected pores, no back-up pressure is required. This method has lower cost and needs less preparation time comparing to MIP test. Additionally, the GEIWIP set-up, the gas/water intrusion apparatus, can be moved to the field site and provide mobile measurement feasibility. The reliability of the test results was obtained by a repetitive testing process. The porosity of concrete samples with different mixtures was obtained and compared to those of MIP and NMR tests.

| S-EPMC6879464 | biostudies-literature

Effect of metal decoration on sulfur-based gas molecules adsorption on phosphorene.

Project description:Based on first-principles calculation, the adsorption of sulfur-based gas molecules (H2S, SO2, SO3) on various metal-decorated phosphorenes is researched systematically. Eleven metals (Li, Na, K, Rb, Cs, Ca, Sr, Ba, Ni, La, Tl) which can avoid the formation of clusters on the phosphorene are considered. Noticeably, all metal decorations can enhance the adsorption strength of phosphorene to sulfur-based gas molecules except for H2S on Tl-decorated phosphorene. Meanwhile, the adsorption energy (Eads) shows the trend of Eads(H2S) < Eads(SO2) < Eads(SO3) for the same metal decoration case. In addition, some metal-decorated phosphorene systems exhibit intriguing magnetic and electrical variation after sulfur-based gas molecule adsorptions, indicating that these systems are promising to be candidates for the detection and removal of sulfur-based gas molecules.

| S-EPMC8438081 | biostudies-literature

Net, excess and absolute adsorption in mixed gas adsorption.

Project description:The formulation of a thermodynamic framework for mixtures based on absolute, excess or net adsorption is discussed and the qualitative dependence with pressure and fugacity is used to highlight a practical issue that arises when extending the formulations to mixtures and to the Ideal Adsorbed Solution Theory (IAST). Two important conclusions are derived: the correct fundamental thermodynamic variable is the absolute adsorbed amount; there is only one possible definition of the ideal adsorbed solution and whichever starting point is used the same final IAST equations are obtained, contrary to what has been reported in the literature.

| S-EPMC7010369 | biostudies-literature

Adsorption of gas molecules on monolayer MoS2 and effect of applied electric field.

Project description:: Using first-principles calculations, we investigate the adsorption of various gas molecules (H2, O2, H2O, NH3, NO, NO2, and CO) on monolayer MoS2. The most stable adsorption configuration, adsorption energy, and charge transfer are obtained. It is shown that all the molecules are weakly adsorbed on the monolayer MoS2 surface and act as charge acceptors for the monolayer, except NH3 which is found to be a charge donor. Furthermore, we show that charge transfer between the adsorbed molecule and MoS2 can be significantly modulated by a perpendicular electric field. Our theoretical results are consistent with the recent experiments and suggest MoS2 as a potential material for gas sensing application.

| S-EPMC4015638 | biostudies-literature

Pore Structure Characterization of Sodium Hydroxide Activated Slag Using Mercury Intrusion Porosimetry, Nitrogen Adsorption, and Image Analysis.

Project description:The pore structure of alkali-activated slag has a significant influence on its performance. However, the literature shows insufficient studies regarding the suitability of different techniques for characterizing the pore structure and the influences of Na₂O and curing age on pore structure development. In pursuit of a better understanding, the pore structure of sodium hydroxide activated slag paste was characterized by multiple techniques, e.g., mercury intrusion porosimetry (MIP), nitrogen (N₂) adsorption, and scanning electron microscopy (SEM) image analysis. The sodium hydroxide activated slag pastes were prepared with three different contents of Na₂O (Na₂O/slag = 4, 6, and 8%) and cured for different times up to 360 days. The microstructure observation reveals that outer C⁻(N⁻)A⁻S⁻H and inner C⁻(N⁻)A⁻S⁻H grow successively around the reacting slag grains, along with crystalline reaction products which are formed in the empty coarse pore space. The increase of Na₂O content and curing age lead to a finer pore structure. The MIP measurements show that the total porosity drops about 70% within the first day, and that one peak at most, corresponding to gel pores, was identified in the differential curves of all the investigated samples from 1 to 360 days. On the contrary, only one peak, corresponding to capillary pores, was identified by SEM-image analysis. The differential curves derived from N₂ adsorption generally reveal two peaks, and the trend that the pore diameters of those two peaks vary with curing age depends on the content of Na₂O. Compared to Portland cement, sodium hydroxide activated slag has a higher pore space filling capacity (χ, Vproducts/Vslag-reacted), while the capacity decreases with increasing Na₂O content and curing age.

| S-EPMC6025311 | biostudies-literature

Gas sorption porosimetry for the evaluation of hard carbons as anodes for Li- and Na-ion batteries.

Project description:Hard carbons are promising candidates for high-capacity anode materials in alkali metal-ion batteries, such as lithium- and sodium-ion batteries. High reversible capacities are often coming along with high irreversible capacity losses during the first cycles, limiting commercial viability. The trade-off to maximize the reversible capacities and simultaneously minimizing irreversible losses can be achieved by tuning the exact architecture of the subnanometric pore system inside the carbon particles. Since the characterization of small pores is nontrivial, we herein employ Kr, N2 and CO2 gas sorption porosimetry, as well as H2O vapor sorption porosimetry, to investigate eight hard carbons. Electrochemical lithium as well as sodium storage tests are compared to the obtained apparent surface areas and pore volumes. H2O, and more importantly CO2, sorption porosimetry turned out to be the preferred methods to evaluate the likelihood for excessive irreversible capacities. The methods are also useful to select the relatively most promising active materials within chemically similar materials. A quantitative relation of porosity descriptors to the obtained capacities remains a scientific challenge.

| S-EPMC7431754 | biostudies-literature

Characterization of Adsorption Enthalpy of Novel Water-Stable Zeolites and Metal-Organic Frameworks.

Project description:Water adsorption is becoming increasingly important for many applications including thermal energy storage, desalination, and water harvesting. To develop such applications, it is essential to understand both adsorbent-adsorbate and adsorbate-adsorbate interactions, and also the energy required for adsorption/desorption processes of porous material-adsorbate systems, such as zeolites and metal-organic frameworks (MOFs). In this study, we present a technique to characterize the enthalpy of adsorption/desorption of zeolites and MOF-801 with water as an adsorbate by conducting desorption experiments with conventional differential scanning calorimetry (DSC) and thermogravimetric analyzer (TGA). With this method, the enthalpies of adsorption of previously uncharacterized adsorbents were estimated as a function of both uptake and temperature. Our characterizations indicate that the adsorption enthalpies of type I zeolites can increase to greater than twice the latent heat whereas adsorption enthalpies of MOF-801 are nearly constant for a wide range of vapor uptakes.

| S-EPMC4726357 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data