Mechanochemical generation of acid-degradable poly(enol ether)s.

ABSTRACT: In an effort to develop polymers that can undergo extensive backbone degradation in response to mechanical stress, we report a polymer system that is hydrolytically stable but unmasks easily hydrolysable enol ether backbone linkages when force is applied. These polymers were synthesized by ring-opening metathesis polymerization (ROMP) of a novel mechanophore monomer consisting of cyclic ether fused bicyclohexene. Hydrogenation of the resulting polymers led to significantly enhanced thermal stability (T _d > 400 °C) and excellent resistance toward acidic or basic conditions. Solution ultrasonication of the polymers resulted in up to 65% activation of the mechanophore units and conversion to backbone enol ether linkages, which then allowed facile degradation of the polymers to generate small molecule or oligomeric species under mildly acidic conditions. We also achieved solid-state mechano-activation and polymer degradation via grinding the solid polymer. Force-induced hydrolytic polymer degradability can enable materials that are stable under force-free conditions but readily degrade under stress. Facile degradation of mechanically activated polymechanophores also facilitates the analysis of mechanochemical products.

SUBMITTER: Yang J

PROVIDER: S-EPMC8179558 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Development and Characterization of Degradable Thiol-Allyl Ether Photopolymers.

Project description:Degradable thiol-ene photopolymer networks were formed through radically mediated step growth reactions. Variations in the network structure were used to alter the initial and temporal moduli, mass loss profiles, and equilibrium swelling ratios. Mass loss rates varied with changes in the solvent concentration, monomer molecular weight, average monomer functionality, and concentration of degradable linkages. The time required for the networks to degrade completely ranged from 1.20 ± 0.01 to 24.5 ± 0.1 days, which corresponded to hydrolysis rates of 0.18 ± 0.01 and 0.021 ± 0.0003 days(-1). Initial moduli also varied considerably as a function of network structure, ranging from 150 ± 35 to nearly 5000 ± 100 kPa, and initial equilibrium swelling ratios ranged from 2.5 ± 0.01 to 18.7 ± 2. Collectively, these results demonstrate how the material properties and the mass loss behavior of thiol-ene networks can be independently tuned for specific applications.

| S-EPMC2097961 | biostudies-literature

Intercalated Poly (2-Acrylamido-2-methyl-1-propanesulfonic Acid) into Sulfonated Poly (1,4-Phenylene ether-ether-sulfone) Based Proton Exchange Membrane: Improved Ionic Conductivity.

Project description:A series of hybrid proton exchange membranes were synthesized via in situ polymerization of poly (2-acrylamido-2-methyl-1-propanesulfonic acid) PMPS with sulfonated poly (1,4-phenylene ether-ether-sulfone) (SPEES). The insertion of poly (2-acrylamido-2-methyl-1-propanesulfonic acid) PMPS, between the rigid skeleton of SPEES plays a reinforcing role to enhance the ionic conductivity. The synthesized polymer was chemically characterized by fourier-transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance 1H NMR spectroscopy to demonstrate the successful grafting of PMPS with the pendent polymer chain of SPEES. A variety of physicochemical properties were also investigated such as ion exchange capacity (IEC), proton conductivity, water uptake and swelling ratio to characterize the suitability of the formed polymer for various electrochemical applications. SP-PMPS-03, having the highest concentration of all PMPS, shows excellent proton conductivity of 0.089 S cm-1 at 80 °C which is much higher than SPEES which is ~0.049 S cm-1. Optimum water uptake and swelling ratio with high conductivity is mainly attributed to a less ordered arrangement polymer chain with high density of the functional group to facilitate ionic transport. The residual weight was 93.35, 92.44 and 89.56%, for SP-PMPS-01, 02 and 03, respectively, in tests with Fenton's reagent after 24 h. In support of all above properties a good chemical and thermal stability was also achieved by SP-PMPS-03, owing to the durability for electrochemical application.

| S-EPMC7795994 | biostudies-literature

Turning Spiroketals Inside Out: A Rearrangement Triggered by an Enol Ether Epoxidation.

Project description:Spiroketals organize small molecule structures into well-defined, three-dimensional configurations that make them good ligands of proteins. We recently discovered a tandem cycloisomerization-dimerization reaction of alkynyl hemiketals that delivered polycyclic, enol-ether-containing spiroketals. Here we describe rearrangements of those compounds, triggered by epoxidation of their enol ethers that completely remodel their structures, essentially turning them "inside out". Due to the high level of substitution on the carbon skeletons of the substrates and products, characterization resorted to X-ray crystallography and advanced computation and NMR techniques to solve the structures of representative compounds. In particular, a new proton-detected ADEQUATE NMR experiment (1,1-HD-ADEQUATE) enabled the unequivocal assignment of the carbon skeleton of one of the new compounds. Solution of the structures of the representative compounds allowed for the assignment of product structures for the other compounds in two separate series. Both the rearrangement and the methods used for structural determination of the products are valuable tools for the preparation of characterization of new small molecule compounds.

| S-EPMC4608522 | biostudies-literature

Silyl enol ether Prins cyclization: diastereoselective formation of substituted tetrahydropyran-4-ones.

Project description:A diastereoselective synthesis of cis-2,6-disubstituted tetrahydropyran-4-ones was developed. The key step of this methodology, a silyl enol ether Prins cyclization, was promoted by a condensation reaction between a hydroxy silyl enol ether and an aldehyde to afford substituted tetrahydropyran-4-ones. The cyclization was tolerant of many functional groups, and the modular synthesis of the hydroxy silyl enol ether allowed for the formation of more than 30 new tetrahydropyran-4-ones with up to 97% yield and >95:5 dr. The cyclization step forms new carbon-carbon and carbon-oxygen bonds, as well as a quaternary center with good diastereoselectivity. The method provides a versatile route for the synthesis of substituted tetrahydropyrans.

| S-EPMC4168786 | biostudies-literature

Oxygenated Cyclopentenones via the Pauson-Khand Reaction of Silyl Enol Ether Substrates.

Project description:We report here the application of silyl enol ether moieties as efficient alkene coupling partners within cobalt-mediated intramolecular Pauson-Khand reactions. This cyclization strategy delivers synthetically valuable oxygenated cyclopentenone products in yields of ≤93% from both ketone- and aldehyde-derived silyl enol ethers, incorporates both terminal and internal alkyne partners, and delivers a variety of decorated systems, including more complex tricyclic structures. Facile removal of the silyl protecting group reveals oxygenated sites for potential further elaboration.

| S-EPMC9016766 | biostudies-literature

Poly(ethylene glycol) (PEG)-lactic acid nanocarrier-based degradable hydrogels for restoring the vaginal microenvironment.

Project description:Women with bacterial vaginosis (BV) display reduced vaginal acidity, which make them susceptible to associated infections such as HIV. In the current study, poly(ethylene glycol) (PEG) nanocarrier-based degradable hydrogels were developed for the controlled release of lactic acid in the vagina of BV-infected women. PEG-lactic acid (PEG-LA) nanocarriers were prepared by covalently attaching lactic acid to 8-arm PEG-SH via cleavable thioester bonds. PEG-LA nanocarriers with 4 copies of lactic acid per molecule provided controlled release of lactic acid with a maximum release of 23% and 47% bound lactic acid in phosphate buffered saline (PBS, pH7.4) and acetate buffer (AB, pH4.3), respectively. The PEG nanocarrier-based hydrogels were formed by cross-linking the PEG-LA nanocarriers with 4-arm PEG-NHS via degradable thioester bonds. The nanocarrier-based hydrogels formed within 20 min under ambient conditions and exhibited an elastic modulus that was 100-fold higher than the viscous modulus. The nanocarrier-based degradable hydrogels provided controlled release of lactic acid for several hours; however, a maximum release of only 10%-14% bound lactic acid was observed possibly due to steric hindrance of the polymer chains in the cross-linked hydrogel. In contrast, hydrogels with passively entrapped lactic acid showed burst release with complete release within 30 min. Lactic acid showed antimicrobial activity against the primary BV pathogen Gardnerella vaginalis with a minimum inhibitory concentration (MIC) of 3.6 mg/ml. In addition, the hydrogels with passively entrapped lactic acid showed retained antimicrobial activity with complete inhibition G. vaginalis growth within 48 h. The results of the current study collectively demonstrate the potential of PEG nanocarrier-based hydrogels for vaginal administration of lactic acid for preventing and treating BV.

| S-EPMC4255267 | biostudies-literature

Poly(ethylene glycol)s With a Single Cinnamaldehyde Acetal Unit for Fabricating Acid-Degradable Hydrogel.

Project description:A synthetic route to prepare a poly(ethylene glycol) with a single cinnamaldehyde acetal unit in the polymer chain, was successfully established using a newly synthesized cinnamaldehyde acetal diethylene glycol (CADEG) as initiator. This HO-PEG(ca)-OH is non-toxic and would be degraded into a cinnamaldehyde and two PEG diols in acid environment. A whole polyethylene glycol based hydrogel was easily fabricated by thiol-ene "click" reaction in alkalescence aqueous solution using acrylate-PEG(ca)-acrylate and 4-arm PEG-SH as raw materials at room temperature. The gel time was dependent on the pH of the solution and its alkalinity can promote gel. The hydrogel can be degradable in acidic conditions and the stronger the acidity, the faster the degradation. This HO-PEG(ca)-OH also can be used in synthesis of cinnamaldehyde containing PEG derivatives, block copolymers or other acid degradable materials.

| S-EPMC7522333 | biostudies-literature

Degradable Polymer Films Made from Poly(salicylic-acid-co-sebacic acid) and Poly(sebacic anhydride)/Poly(adipic anhydride) Blends: Degradation Kinetics and Use as Sacrificial Layers for Polymer Multilayer Systems.

Project description:Two approaches to obtain fast-degrading polymer films based on poly(sebacic anhydride) (PSA) are presented, both of which target polymer films with a lower degree of crystallinity than pure PSA homopolymer: first, thin films were prepared from poly(adipic anhydride)/poly(sebacic anhydride) blends at different ratios, and second, films were made from the copolymer poly(salicylic acid-co-sebacic acid). These films are intended as sacrificial layers for self-regenerating functional coatings, for example to regenerate antimicrobial surface activity. The degradation kinetics of these films were analyzed by surface plasmon resonance spectroscopy (SPR). The results of the blends approach indicate that the blend degradation rate was accelerated only in the initial degradation phase (compared to PSA). The degradation kinetics study of the poly(salicylic-acid-co-sebacic acid) film shows that this copolymer degraded faster than poly(sebacic anhydride) initially, releasing antimicrobial salicylic acid in the process. However, its degradation rate slowed down at a mass loss > 60% and approached the PSA degradation curve at longer degradation times. When tested as sacrificial layer in self-regenerating antimicrobial polymer stacks, it was found that the degradation rate was too low for successful layer shedding.

| S-EPMC7611817 | biostudies-literature

Degradable Poly(ether-ester-urethane)s Based on Well-Defined Aliphatic Diurethane Diisocyanate with Excellent Shape Recovery Properties at Body Temperature for Biomedical Application.

Project description:The aim of this study is to offer a new class of degradable shape-memory poly(ether-ester-urethane)s (SMPEEUs) based on poly(ether-ester) (PECL) and well-defined aliphatic diurethane diisocyanate (HBH) for further biomedical application. The prepolymers of PECLs were synthesized through bulk ring-opening polymerization using ?-caprolactone as the monomer and poly(ethylene glycol) as the initiator. By chain extension of PECL with HBH, SMPEEUs with varying PEG content were prepared. The chemical structures of the prepolymers and products were characterized by GPC, 1H NMR, and FT-IR, and the effect of PEG content on the physicochemical properties (especially the shape recovery properties) of SMPEEUs was studied. The microsphase-separated structures of the SMPEEUs were demonstrated by DSC and XRD. The SMPEEU films exhibited good tensile properties with the strain at a break of 483%-956% and an ultimate stress of 23.1-9.0 MPa. Hydrolytic degradation in vitro studies indicated that the time of the SMPEEU films becoming fragments was 4-12 weeks and the introduction of PEG facilitates the degradation rate of the films. The shape memory properties studies found that SMPEEU films with a PEG content of 23.4 wt % displayed excellent recovery properties with a recovery ratio of 99.8% and a recovery time of 3.9 s at body temperature. In addition, the relative growth rates of the SMPEEU films were greater than 75% after incubation for 72 h, indicating good cytocompatibility in vitro. The SMPEEUs, which possess not only satisfactory tensile properties, degradability, nontoxic degradation products, and cytocompatibility, but also excellent shape recovery properties at body temperature, promised to be an excellent candidate for medical device applications.

| S-EPMC6631253 | biostudies-literature

Amino alcohol-based degradable poly(ester amide) elastomers.

Project description:Currently available synthetic biodegradable elastomers are primarily composed of crosslinked aliphatic polyesters, which suffer from deficiencies including (1) high crosslink densities, which results in exceedingly high stiffness, (2) rapid degradation upon implantation, or (3) limited chemical moieties for chemical modification. Herein, we have developed poly(1,3-diamino-2-hydroxypropane-co-polyol sebacate)s, a new class of synthetic, biodegradable elastomeric poly(ester amide)s composed of crosslinked networks based on an amino alcohol. These crosslinked networks feature tensile Young's modulus on the order of 1MPa and reversable elongations up to 92%. These polymers exhibit in vitro and in vivo biocompatibility. These polymers have projected degradation half-lives up to 20 months in vivo.

| S-EPMC2880180 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data