Dual Modular Titanium Alloy Femoral Stem Failure Mechanisms and Suggested Clinical Approaches.

ABSTRACT: Titanium (Ti) alloys have been proven to be one of the most suitable materials for orthopaedic implants. Dual modular stems have been introduced to primary total hip arthroplasty (THA) to enable better control of the femoral offset, leg length, and hip stability. This systematic review highlights information acquired for dual modular Ti stem complications published in the last 12 years and offers a conclusive discussion of the gathered knowledge. Articles referring to dual modular stem usage, survivorship, and complications in English were searched from 2009 to the present day. A qualitative synthesis of literature was carried out, excluding articles referring solely to other types of junctions or problems with cobalt-chromium alloys in detail. In total, 515 records were identified through database searching and 78 journal articles or conference proceedings were found. The reasons for a modular neck fracture of a Ti alloy are multifactorial. Even though dual modular stems have not shown any clinical benefits for patients and have been associated with worse results regarding durability than monolithic stems, some designs are still marketed worldwide. Orthopaedic surgeons should use Ti6Al4V dual modular stem designs for primary THA in special cases only.

SUBMITTER: Zajc J

PROVIDER: S-EPMC8200202 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Failure of Emperion modular femoral stem with implant analysis.

Project description:Modularity in total hip arthroplasty provides multiple benefits to the surgeon in restoring the appropriate alignment and position to a previously damaged hip joint. The vast majority of modern implants incorporate modularity into their design with some implants having multiple modular interfaces. There is the potential for failure at modular junctions because of fretting and crevice corrosion in combination with mechanical loading. This case report details the failure of an Emperion (Smith and Nephew, Memphis, TN) femoral stem in a 67-year-old male patient 6 years after total hip replacement. Analysis of the implant revealed mechanically assisted crevice corrosion that likely accelerated fatigue crack initiation in the hip stem. The benefits of modularity come with the potential drawback of a combination of fretting and crevice corrosion at the modular junction, which may accelerate fatigue, crack initiation and ultimately reduce the hip longevity.

| S-EPMC4957168 | biostudies-literature

Corrosion and adverse local tissue reaction after total hip arthroplasty with a modular titanium alloy femoral neck.

Project description:This report describes a case of mechanically assisted crevice corrosion and secondary adverse local tissue reaction in a patient following a total hip arthroplasty, utilizing a modular neck (bi-modular) femoral component. Radiographic evaluation demonstrated a well-positioned, stable, cementless arthroplasty. Upon further evaluation, the patient had elevated serum cobalt and chromium levels, and magnetic resonance imaging demonstrated a periprosthetic pseudotumor. Corrosion of both the neck-stem and head-neck junctions was suspected. At the time of surgery, the neck-body junction was pristine; however, the head-neck junction of the implant demonstrated severe corrosive wear, a problem that has been reported only once previously with this particular bi-modular implant. This serves as a reminder that any modular junction may be susceptible to corrosion and not all bi-modular designs behave similarly.

| S-EPMC5712034 | biostudies-literature

Titanium neck-titanium stem taper corrosion in a modular neck stem.

Project description:An 81-year-old woman presented with progressive groin pain after metal-on-polyethylene total hip arthroplasty with a modular neck stem and was found to have adverse local tissue reaction. As we report for the first time with this implant, we observed titanium neck-titanium stem taper corrosion intraoperatively. We also found head-neck taper corrosion. The patient underwent revision surgery to a modular fluted tapered stem with ceramic head and was asymptomatic at 3-year follow-up visit. In conclusion, consideration should be given to avoiding the routine use of this modular neck stem in total hip arthroplasty. Patients with this prosthesis should be closely monitored for adverse local tissue reaction.

| S-EPMC6588719 | biostudies-literature

Tapered modular fluted titanium stems for femoral fixation in revision total knee arthroplasty.

Project description:Consensus regarding femoral stem fixation options in revision total knee arthroplasty remains controversial. Tapered, modular, fluted titanium (TMFT) stems have an excellent track record in total hip arthroplasty for their ability to provide axial and rotational stability in situations of compromised host bone. We present 3 successfully treated cases in which the Food & Drug Administration granted permission to use custom TMFT stems in situations of failed femoral fixation in multiple revised knees. These stems hold promise to achieve stable fixation in revision total knee arthroplasty where host metadiaphyseal bone is deficient. Implant manufactures should consider dedicating future resources to create adapters that can link existing successful TMFT stems currently used in hip arthroplasty to revision total knee components when host bone is severely compromised.

| S-EPMC5859738 | biostudies-literature

Temperature Effect on Stacking Fault Energy and Deformation Mechanisms in Titanium and Titanium-aluminium Alloy.

Project description:Alloying elements have great influence on mechanical properties of metals. Combining dislocation characterization and in-situ transmission electron microscope straining at ambient and liquid-nitrogen temperature in high-purity titanium and Ti-5at%Al, we investigated the modulation of Al on dislocation behaviours as temperature changed. It reveals that segregation of Al at edge dislocation cores in Ti-5at%Al generates strong obstacles, promoting room temperature cross-slips. However, the effect of Al on reducing stacking-fault energy (SFE) as decreasing temperature is significant. Consequently, the lower SFE in Ti-5at%Al results in ordinary planar dislocation slip while massive dislocation cross-slips occurred in Ti at liquid-nitrogen temperature.

| S-EPMC7033204 | biostudies-literature

In vivo severe corrosion and hydrogen embrittlement of retrieved modular body titanium alloy hip-implants.

Project description:Titanium alloys are widely used in total-joint replacements due to a combination of outstanding mechanical properties, biocompatibility, passivity, and corrosion resistance. Nevertheless, retrieval studies have pointed out that these materials can be subjected to localized or general corrosion in modular interfaces when mechanical abrasion of the oxide film (fretting) occurs. Modularity adds large crevice environments, which are subject to micromotion between contacting interfaces and differential aeration of the surface. Titanium alloys are also known to be susceptible to hydrogen absorption, which can induce precipitation of hydrides and subsequent brittle failure. In this work, the surface of three designs of retrieved hip-implants with Ti-6Al-4V/Ti-6Al-4V modular taper interfaces in the stem were investigated for evidence of severe corrosion and precipitation of brittle hydrides during fretting-crevice corrosion in the modular connections. The devices were retrieved from patients and studied by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), and chemical analysis. The surface qualitative investigation revealed severe corrosion attack in the mating interfaces with evidence of etching, pitting, delamination, and surface cracking. In vivo hydrogen embrittlement was shown to be a mechanism of degradation in modular connections resulting from electrochemical reactions induced in the crevice environment of the tapers during fretting-crevice corrosion.

| S-EPMC2667129 | biostudies-literature

Spontaneous Fractures of a Modern Modular Uncemented Femoral Stem.

Project description:BackgroundFemoral stem fracture following total hip arthroplasty is an uncommon event that requires immediate revision surgery.Questions/purposesWe report on four patients who experienced stem fractures of one design and a review of the US Food and Drug Administration adverse event reports on this design.MethodsFracture surfaces of four EMPERION™ (Smith & Nephew, Memphis, TN) femoral stems were analyzed under optical and scanning electron microscopy. A search of the FDA's Manufacturer and User Facility Device Experience (MAUDE) that reports on all EMPERION™ adverse events was completed.ResultsFracture surfaces exhibited characteristics consistent with a fatigue fracture mechanism. Sixteen MAUDE reports claimed stem fracture or breakage of EMPERION™ stems.ConclusionThe four cases of EMPERION™ stem fractures were likely driven by small stem diameter, high offset, and high patient weight. Modular stem-sleeve femoral systems are susceptible to fatigue failure under high stress and should only be used in appropriate patients, whom are not considered obese.

| S-EPMC5026663 | biostudies-literature

Fracture of the Neck of a Modern Cementless, Titanium Femoral Stem.

Project description:Intraprosthetic fracture of a femoral component is a rare but devastating complication after total hip arthroplasty (THA). We present the case of a 68-year-old man who presented with acute hip pain approximately 8 years after a left THA with a modern cementless, titanium femoral component. Radiographs revealed a fracture of the midportion of the neck of the stem, below the level of the trunnion. The patient underwent an isolated 1-component revision THA with a modular exchange. To our knowledge, this is the only reported case of a catastrophic failure fracture of this particular prosthesis.

| S-EPMC7218161 | biostudies-literature

High temperature rise dominated cracking mechanisms in ultra-ductile and tough titanium alloy.

Project description:Extensive use of titanium alloys is partly hindered by a lack of ductility, strain hardening, and fracture toughness. Recently, several β-metastable titanium alloys were designed to simultaneously activate both transformation-induced plasticity and twinning-induced plasticity effects, resulting in significant improvements to their strain hardening capacity and resistance to plastic localization. Here, we report an ultra-large fracture resistance in a Ti-12Mo alloy (wt.%), that results from a high resistance to damage nucleation, with an unexpected fracture phenomenology under quasi-static loading. Necking develops at a large uniform true strain of 0.3 while fracture initiates at a true fracture strain of 1.0 by intense through-thickness shear within a thin localized shear band. Transmission electron microscopy reveals that dynamic recrystallization occurs in this band, while local partial melting is observed on the fracture surface. Shear band temperatures of 1250-2450 °C are estimated by the fusible coating method. The reported high ductility combined to the unconventional fracture process opens alternative avenues toward Ti alloys toughening.

| S-EPMC7193587 | biostudies-literature

Early fracture of the modular neck of a MODULUS femoral stem.

Project description:We present the case of a 46-year-old woman who underwent revision surgery approximately 4 years after total hip arthroplasty because of a fracture of the modular neck of a MODULUS femoral stem. The fractured surfaces of the retrieved implant were inspected using optical and scanning electron microscopy. Three-dimensional finite element analysis was also performed to identify the stresses that might have caused the failure. We concluded that active, obese patients who are implanted with a high-offset, small-sized modular component could experience stress-induced fractures of the modular neck, with proper fixation and osseointegration of the distal stem, especially if residual bone or tissue is present on the inner surface of the neck that could contribute to micromovement and decreased proximal fixation.

| S-EPMC5859422 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data