Titanium neck-titanium stem taper corrosion in a modular neck stem.

ABSTRACT: An 81-year-old woman presented with progressive groin pain after metal-on-polyethylene total hip arthroplasty with a modular neck stem and was found to have adverse local tissue reaction. As we report for the first time with this implant, we observed titanium neck-titanium stem taper corrosion intraoperatively. We also found head-neck taper corrosion. The patient underwent revision surgery to a modular fluted tapered stem with ceramic head and was asymptomatic at 3-year follow-up visit. In conclusion, consideration should be given to avoiding the routine use of this modular neck stem in total hip arthroplasty. Patients with this prosthesis should be closely monitored for adverse local tissue reaction.

SUBMITTER: Shah R

PROVIDER: S-EPMC6588719 | biostudies-literature | 2019 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Titanium neck-titanium stem taper corrosion in a modular neck stem.

Shah Ronit R Talmo Carl C Nandi Sumon S

Arthroplasty today 20190605 2

An 81-year-old woman presented with progressive groin pain after metal-on-polyethylene total hip arthroplasty with a modular neck stem and was found to have adverse local tissue reaction. As we report for the first time with this implant, we observed titanium neck-titanium stem taper corrosion intraoperatively. We also found head-neck taper corrosion. The patient underwent revision surgery to a modular fluted tapered stem with ceramic head and was asymptomatic at 3-year follow-up visit. In concl ...[more]

PMID: 31286033

Similar Datasets

Project description:BackgroundFemoral stems with dual-taper modularity were introduced to allow additional options for hip-center restoration independent of femoral fixation in total hip arthroplasty. Despite the increasing availability and use of these femoral stems, concerns exist about potential complications arising from the modular neck-body junction.MethodsThis was a multicenter retrospective case series of twelve hips (eleven patients) with adverse local tissue reactions secondary to corrosion at the modular neck-body junction. The cohort included eight women and three men who together had an average age of 60.1 years (range, forty-three to seventy-seven years); all hips were implanted with a titanium-alloy stem and cobalt-chromium-alloy neck. Patients presented with new-onset and increasing pain at a mean of 7.9 months (range, five to thirteen months) following total hip arthroplasty. After serum metal-ion studies and metal artifact reduction sequence (MARS) magnetic resonance imaging (MRI) revealed abnormal results, the patients underwent hip revision at a mean of 15.2 months (range, ten to twenty-three months). Tissue specimens were examined by a single histopathologist, and the retrieved implants were studied with use of light and scanning electron microscopy.ResultsSerum metal levels demonstrated greater elevation of cobalt (mean, 6.0 ng/mL) than chromium (mean, 0.6 ng/mL) or titanium (mean, 3.4 ng/mL). MRI with use of MARS demonstrated adverse tissue reactions in eight of nine patients in which it was performed. All hips showed large soft-tissue masses and surrounding tissue damage with visible corrosion at the modular femoral neck-body junction. Available histology demonstrated large areas of tissue necrosis in seven of ten cases, while remaining viable capsular tissue showed a dense lymphocytic infiltrate. Microscopic analysis was consistent with fretting and crevice corrosion at the modular neck-body interface.ConclusionsCorrosion at the modular neck-body junction in dual-tapered stems with a modular cobalt-chromium-alloy femoral neck can lead to release of metal ions and debris resulting in local soft-tissue destruction. Adverse local tissue reaction should be considered as a potential cause for new-onset pain in patients with these components, and early revision should be considered given the potentially destructive nature of these reactions. A workup including serologic studies (erythrocyte sedimentation rate and C-reactive protein), serum metal levels, and MARS MRI can be helpful in establishing this diagnosis.

Project description:BackgroundThe modular head taper junction has contributed to the success of total hip arthroplasty (THA) greatly. Taper corrosion and wear problems reported for large and extra-large metal-on-metal bearings as well as for bi-modular THA stems have cast doubt on the benefit of the taper interface. Presently, corrosion problems are being reported for nearly all kinds of artificial hip joints incorporating metal heads, questioning taper connections in general.Questions/purposesThis study aimed to review the mechanical and electrochemical relationships that may lead to taper corrosion, which have been reported more commonly in recent literature, and to also review the contribution of patient characteristics and surgical techniques involved in taper assembly that may contribute to the problem.MethodsThe search criteria "(corrosion) AND (hip arthroplasty) AND (taper OR trunnion)" and "(hip arthroplasty) AND ((pseudotumor) OR (pseudo-tumor))" in PubMed and the JAAOS were used for the literature search. In addition, the arthroplasty registers were considered.ResultsMost studies acknowledge the multifactorial nature of the problem but concentrate their analysis on taper and implant design aspects, since this is the only factor that can be easily quantified. The sometimes conflicting results in the literature could be due to the fact that the other two decisive factors are not sufficiently considered: the loading situation in the patient and the assembly situation by the surgeon. All three factors together determine the fate of a taper junction in THA. There is no single reason as a main cause for taper corrosion. The combined "outcome" of these three factors has to be in a "safe range" to achieve a successful long-term taper fixation.ConclusionNo, this is not the beginning of an epidemic. It is rather the consequence of disregarding known mechanical and electrochemical relationships, which in combination have recently caused a more frequent occurrence-and mainly reporting-of corrosion issues.

Dataset Information

Titanium neck-titanium stem taper corrosion in a modular neck stem.

Publications

Titanium neck-titanium stem taper corrosion in a modular neck stem.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets