Mechanical and Physicochemical Properties of 3D-Printed Agave Fibers/Poly(lactic) Acid Biocomposites.

ABSTRACT: In order to provide a second economic life to agave fibers, an important waste material from the production of tequila, filaments based on polylactic acid (PLA) were filled with agave fibers (0, 3, 5, 10 wt%), and further utilized to produce biocomposites by fused deposition modeling (FDM)-based 3D printing at two raster angles (-45°/45° and 0°/90°). Differential scanning calorimetry, water uptake, density variation, morphology, and composting of the biocomposites were studied. The mechanical properties of the biocomposites (tensile, flexural, and Charpy impact properties) were determined following ASTM international norms. The addition of agave fibers to the filaments increased the crystallinity value from 23.7 to 44.1%. However, the fibers generated porous structures with a higher content of open cells and lower apparent densities than neat PLA pieces. The printing angle had a low significant effect on flexural and tensile properties, but directly affected the morphology of the printed biocomposites, positively influenced the impact strength, and slightly improved the absorption values for biocomposites printed at -45°/45°. Overall, increasing the concentrations of agave fibers had a detrimental effect on the mechanical properties of the biocomposites. The disintegration of the biocomposites under simulated composting conditions was slowed 1.6-fold with the addition of agave fibers, compared to neat PLA.

SUBMITTER: Figueroa-Velarde V

PROVIDER: S-EPMC8201365 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Poly(lactic acid)/Poly(3-hydroxybutyrate) Biocomposites with Differently Treated Cellulose Fibers.

Project description:The growing concern about environmental pollution has generated an increased demand for biobased and biodegradable materials intended particularly for the packaging sector. Thus, this study focuses on the effect of two different cellulosic reinforcements and plasticized poly(3-hydroxybutyrate) (PHB) on the properties of poly(lactic acid) (PLA). The cellulose fibers containing lignin (CFw) were isolated from wood waste by mechanical treatment, while the ones without lignin (CF) were obtained from pure cellulose by acid hydrolysis. The biocomposites were prepared by means of a melt compounding-masterbatch technique for the better dispersion of additives. The effect of the presence or absence of lignin and of the size of the cellulosic fibers on the properties of PLA and PLA/PHB was emphasized by using in situ X-ray diffraction, polarized optical microscopy, atomic force microscopy, and mechanical and thermal analyses. An improvement of the mechanical properties of PLA and PLA/PHB was achieved in the presence of CF fibers due to their smaller size, while CFw fibers promoted an increased thermal stability of PLA/PHB, owing to the presence of lignin. The overall thermal and mechanical results show the great potential of using cheap cellulose fibers from wood waste to obtain PLA/PHB-based materials for packaging applications as an alternative to using fossil based materials. In addition, in situ X-ray diffraction analysis over a large temperature range has proven to be a useful technique to better understand changes in the crystal structure of complex biomaterials.

| S-EPMC9032581 | biostudies-literature

Influence of Reactive Chain Extension on the Properties of 3D Printed Poly(Lactic Acid) Constructs.

Project description:Fused deposition modeling (FDM) is currently the most popular 3D printing method, where thermoplastic polymers are predominantly used. Among them, the biobased poly(lactic acid) (PLA) governs the FDM filament market, with demand higher than supply, since not all grades of PLA are suitable for FDM filament production. In this work, the effect of a food grade chain extender (Joncryl ADR® 4400) on the physicochemical properties and printability of PLA marketed for injection molding was examined. All samples were characterized in terms of their mechanical and thermal properties. The microstructure of the filaments and 3D-printed fractured surfaces following tensile testing were examined with optical and scanning electron microscopy, respectively. Molecular weight and complex viscosity increased, while the melt flow index decreased after the incorporation of Joncryl, which resulted in filaments of improved quality and 3D-printed constructs with enhanced mechanical properties. Dielectric spectroscopy revealed that the bulk properties of PLA with respect to molecular mobility, both local and segmental, were, interestingly, not affected by the modifier. Indirectly, this may suggest that the major effects of the extender are on chain length, without inducing chain branching, at least not to a significant extent.

| S-EPMC8123025 | biostudies-literature

Post-process optimization of 3D printed poly(lactic-co-glycolic acid) dental implant scaffold for enhanced structure and mechanical properties: effects of sonication duration and power.

Project description:We described a technique of a post-process stage to partially remove the poly(vinyl alcohol) (PVA) binder in Poly(lactic-co-glycolic acid) (PLGA) dental scaffolds. The scaffolds were exposed to ultrasonic waves while immersed in an ethanol/acetone solvent mixture that possessed both polar and nonpolar properties. A factorial experiment was conducted in which the scaffolds were treated to three levels of sonication power (pW): 0, 20% (22 W) and 40% (44 W), and soaking duration (t): 5, 15, and 30 min. The treated scaffolds were characterized by FT-IR, optical microscopy, and mechanical (compressive) testing. FT-IR revealed that the amount of PVA decreased with increasing pW and t. Two-way ANOVA revealed that increasing pW and t, respectively, resulted in increasing scaffold surface area to volume (SVR). Sonication and solvent caused structural damage (i.e., unevenness) on the scaffold surface, but the damage was minimal at 20% pW and 30 min. The optimal values of pW and t resulting in enhanced fracture strength, strain and toughness were 20% and 30 min, respectively, which corroborated the findings of minimal structural damage. However, sonication had no significant effects on the scaffold stiffness. Mechanistic analysis of the effects of sonication predicted that the ultrasonic energy absorbed by the scaffold was sufficient to disrupt the van Der Waals bonds between the PVA and PLGA but not high enough to disrupt the covalent bonds within the PLGA. This technique is promising as it can partially remove the PVA from the scaffold, and mitigate problematic issues down the line, such as thermal degradation during sterilization, and undue delay/variability in biodegradation.

| S-EPMC8325663 | biostudies-literature

Mechanical Performance of 3D-Printed Polyethylene Fibers and Their Durability against Degradation.

Project description:Polyethylene (PE), one of the most popular thermoplastic polymers, is widely used in various areas, such as materials engineering and biomedical engineering, due to its superior performance, while 3D printing via fused deposition modeling (FDM) provides a facile method of preparing PE products. To optimize the performance and assess the degradation of FDM-printed PE materials, we systematically investigate the influences of printing parameters, such as fiber diameter (stretching) and printer head temperature, and degradation, such as UV exposure and thermal degradation, on the mechanical performance of FDM-printed PE fibers. When FDM-printed PE fibers with a smaller diameter are prepared under a higher collecting speed, they undergo stronger stretching, and thus, show higher tensile strength and Young's modulus values. Meanwhile, the tensile strength and Young's modulus decrease as the printer head temperature increases, due to the lower viscosity, and thus, weaker shearing at high temperatures. However, degradation, such as UV exposure and thermal degradation, cause a decrease in all four mechanical properties, including tensile strength, Young's modulus, tensile strain and toughness. These results will guide the optimization of FDM-printed PE materials and help to assess the durability of PE products against degradation for their practical application.

| S-EPMC10386389 | biostudies-literature

Multifunctional lignin-poly (lactic acid) biocomposites for packaging applications.

Project description:Lignin is the most abundant aromatic biopolymer with many promising features but also shortcomings as a filler in polymer blends. The main objective of this work was to improve the processability and compatibility of lignin with poly (lactic acid) (PLA) through etherification of lignin. Commercial kraft lignin (KL) and oxypropylated kraft lignin (OPKL) were blended with PLA at different weight percentages (1, 5, 10, 20, and 40%) followed by injection molding. Low lignin contents between 1 and 10% generally had a favorable impact on mechanical strength and moduli as well as functional properties of the PLA-based composites. Unmodified lignin with free phenolic hydroxyl groups rendered the composites with antioxidant activity, as measured by radical scavenging and lipid peroxidation tests. Incorporating 5-10% of KL or OPKL improved the thermal stability of the composites within the 300-350°C region. DSC analysis showed that the glass transition temperature values were systematically decreased upon addition of KL and OPKL into PLA polymer. However, low lignin contents of 1 and 5% decreased the cold crystallization temperature of PLA. The composites of KL and OPKL with PLA exhibited good stabilities in the migration test, with values of 17 mg kg-1 and 23 mg kg-1 even at higher lignin content 40%, i.e., well below the limit defined in a European standard (60 mg kg-1). These results suggest oxypropylated lignin as a functional filler in PLA for safe and functional food packaging and antioxidant applications.

| S-EPMC9574040 | biostudies-literature

Creep Behavior of Poly(lactic acid) Based Biocomposites.

Project description:Polymer composites containing natural fibers are receiving growing attention as possible alternatives for composites containing synthetic fibers. The use of biodegradable matrices obtained from renewable sources in replacement for synthetic ones is also increasing. However, only limited information is available about the creep behavior of the obtained composites. In this work, the tensile creep behavior of PLA based composites, containing flax and jute twill weave woven fabrics, produced through compression molding, was investigated. Tensile creep tests were performed at different temperatures (i.e., 40 and 60 °C). The results showed that the creep behavior of the composites is strongly influenced by the temperature and the woven fabrics used. As preliminary characterization, quasi-static tensile tests and dynamic mechanical tests were carried out on the composites. Furthermore, fabrics (both flax and jute) were tested as received by means of quasi-static tests and creep tests to evaluate the influence of fabrics mechanical behavior on the mechanical response of the resulting composites. The morphological analysis of the fracture surface of the tensile samples showed the better fiber-matrix adhesion between PLA and jute fabric.

| S-EPMC5506976 | biostudies-other

Crystalline Characteristics, Mechanical Properties, Thermal Degradation Kinetics and Hydration Behavior of Biodegradable Fibers Melt-Spun from Polyoxymethylene/Poly(l-lactic acid) Blends.

Project description:A series of polyoxymethylene (POM)/poly(l-lactic acid) (PLLA) blends were prepared by melt extrusion, and their spinnability was confirmed by rheological characterizations, successive self-nucleation, and annealing thermal fractionation analysis. The bicomponent fibers were prepared by means of the melt-spinning and post-drawing technologies using the above-obtained blends, and their morphology, crystalline orientation characteristics, mechanical performance, hydration behavior, and thermal degradation kinetics were studied extensively. The bicomponent fibers exhibited a uniform diameter distribution and compact texture at the ultimate draw ratio. Although the presence of PLLA reduced the crystallinity of the POM domain in the bicomponent fibers, the post-drawing process promoted the crystalline orientation of lamellar folded-chain crystallites due to the stress-induced crystallization effect and enhanced the crystallinity of the POM domain accordingly. As a result, the bicomponent fibers achieved the relatively high tensile strength of 791 MPa. The bicomponent fibers exhibited a partial hydration capability in both acid and alkali media and therefore could meet the requirement for serving as a type of biodegradable fibers. The introduction of PLLA slightly reduced the thermo-oxidative aging property and thermal stability of the bicomponent fibers. Such a combination of two polymers shortened the thermal lifetime of the bicomponent fibers, which could facilitate their natural degradation for ecological and sustainable applications.

| S-EPMC6918227 | biostudies-literature

3D Printed Cartilage-Like Tissue Constructs with Spatially Controlled Mechanical Properties.

Project description:Developing biomimetic cartilaginous tissues that support locomotion while maintaining chondrogenic behavior is a major challenge in the tissue engineering field. Specifically, while locomotive forces demand tissues with strong mechanical properties, chondrogenesis requires a soft microenvironment. To address this challenge, 3D cartilage-like tissue is bioprinted using two biomaterials with different mechanical properties: a hard biomaterial to reflect the macromechanical properties of native cartilage, and a soft biomaterial to create a chondrogenic microenvironment. To this end, a hard biomaterial (MPa order compressive modulus) composed of an interpenetrating polymer network (IPN) of polyethylene glycol (PEG) and alginate hydrogel is developed as an extracellular matrix (ECM) with self-healing properties, but low diffusive capacity. Within this bath supplemented with thrombin, fibrinogen containing human mesenchymal stem cell (hMSC) spheroids is bioprinted forming fibrin, as the soft biomaterial (kPa order compressive modulus) to simulate cartilage's pericellular matrix and allow a fast diffusion of nutrients. The bioprinted hMSC spheroids improve viability and chondrogenic-like behavior without adversely affecting the macromechanical properties of the tissue. Therefore, the ability to print locally soft and cell stimulating microenvironments inside of a mechanically robust hydrogel is demonstrated, thereby uncoupling the micro- and macromechanical properties of the 3D printed tissues such as cartilage.

| S-EPMC8186324 | biostudies-literature

Wirelessly Powered 3D Printed Hierarchical Biohybrid Robots with Multiscale Mechanical Properties.

Project description:The integration of flexible and stretchable electronics into biohybrid soft robotics can spur the development of new approaches to fabricate biohybrid soft machines, thus enabling a wide variety of innovative applications. Inspired by flexible and stretchable wireless-based bioelectronic devices, we have developed untethered biohybrid soft robots that can execute swimming motions, which are remotely controllable by the wireless transmission of electrical power into a cell simulator. To this end, wirelessly-powered, stretchable, and lightweight cell stimulators were designed to be integrated into muscle bodies without impeding the robots' underwater swimming abilities. The cell stimulators function by generating controlled monophasic pulses of up to ∼9 V in biological environments. By differentiating induced pluripotent stem cell-derived cardiomyocytes (iPSC-CMs) directly on the cell stimulators using an accordion-inspired, three-dimensional (3D) printing construct, we have replicated the native myofiber architecture with comparable robustness and enhanced contractibility. Wirelessly modulated electrical frequencies enabled us to control the speed and direction of the biohybrid soft robots. A maximum locomotion speed of ∼580 μm/s was achieved in robots possessing a large body size by adjusting the pacing frequency. This innovative approach will provide a platform for building untethered and biohybrid systems for various biomedical applications.

| S-EPMC9603592 | biostudies-literature

Antibacterial 3D-Printed Silver Nanoparticle/Poly Lactic-Co-Glycolic Acid (PLGA) Scaffolds for Bone Tissue Engineering.

Project description:Infectious bone defects present a major challenge in the clinical setting currently. In order to address this issue, it is imperative to explore the development of bone tissue engineering scaffolds that are equipped with both antibacterial and bone regenerative capabilities. In this study, we fabricated antibacterial scaffolds using a silver nanoparticle/poly lactic-co-glycolic acid (AgNP/PLGA) material via a direct ink writing (DIW) 3D printing technique. The scaffolds' microstructure, mechanical properties, and biological attributes were rigorously assessed to determine their fitness for repairing bone defects. The surface pores of the AgNPs/PLGA scaffolds were uniform, and the AgNPs were evenly distributed within the scaffolds, as confirmed via scanning electron microscopy (SEM). Tensile testing confirmed that the addition of AgNPs enhanced the mechanical strength of the scaffolds. The release curves of the silver ions confirmed that the AgNPs/PLGA scaffolds released them continuously after an initial burst. The growth of hydroxyapatite (HAP) was characterized via SEM and X-ray diffraction (XRD). The results showed that HAP was deposited on the scaffolds, and also confirmed that the scaffolds had mixed with the AgNPs. All scaffolds containing AgNPs exhibited antibacterial properties against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli). A cytotoxicity assay using mouse embryo osteoblast precursor cells (MC3T3-E1) showed that the scaffolds had excellent biocompatibility and could be used for repairing bone tissue. The study shows that the AgNPs/PLGA scaffolds have exceptional mechanical properties and biocompatibility, effectively inhibiting the growth of S. aureus and E. coli. These results demonstrate the potential application of 3D-printed AgNPs/PLGA scaffolds in bone tissue engineering.

| S-EPMC10253518 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data