Efficient Removal of Chromium(VI) Anionic Species and Dye Anions from Water Using MOF-808 Materials Synthesized with the Assistance of Formic Acid.

ABSTRACT: This study presents a simple approach to prepare MOF-808, an ultra-stable Zr-MOF constructed from 6-connected zirconium clusters and 1,3,5-benzene tricarboxylic acid, with tailored particle sizes. Varying the amount of formic acid as a modulator in the range of 200-500 equivalents results in MOF-808 materials with a crystal size from 40 nm to approximately 1000 nm. Apart from the high specific surface area, a combination of a fraction of mesopore and plenty of acidic centers on the Zr-clusters induces a better interaction with the ionic pollutants such as K₂Cr₂O₇ and anionic dyes. MOF-808 shows uptakes of up to 141.2, 642.0, and 731.0 mg/g for K₂Cr₂O₇, sunset yellow, and quinoline yellow, respectively, in aqueous solutions at ambient conditions. The uptakes for the ionic dyes are significantly higher than those of other MOFs reported from the literature. Moreover, the adsorption capacity of MOF-808 remains stable after four cycles. Our results demonstrate that MOF-808 is a promising ideal platform for removing oxometallates and anionic dyes from water.

SUBMITTER: Nguyen KD

PROVIDER: S-EPMC8226478 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Porous MOF-808@PVDF beads for removal of iodine from gas streams.

Project description:The removal of radioiodine from the exhaust gas streams produced in spent fuel reprocessing plants is of paramount importance for the nuclear fuel cycle's security. Here, millimeter-sized poly(vinylidene fluoride) (PVDF) composites containing zirconium-based metal-organic frameworks, MOF-808, were synthesized by a facile phase inversion method to adsorb the volatile iodine. MOF-808@PVDF composites have inherited the crystallinity and pore accessibility of MOF-808, as well as its outstanding iodine capture performance. The MOF-808@PVDF composite beads containing 70 wt% MOFs, exhibited ultrahigh iodine adsorption capacity, 1.42 g g-1 at 80 °C, much higher than other millimeter-sized adsorbents reported in the literature. Raman mapping suggests that the negative iodine ions were formed at the early stage of iodine adsorption, while the close-packed iodine molecules were subsequently trapped in the frames. Using dynamic adsorption, the influences of iodine concentration, operating temperature and humidity were analyzed to evaluate its application potential in industrial conditions. The iodine adsorption capacity could reach 1.36 g g-1 at 80 °C, 100 °C and 120 °C in flow gas. And the elevated temperature (120 °C) is beneficial to accelerating the mass transfer of iodine vapor, as well as slightly inhibiting the competitive adsorption of water molecules under humidity. Besides, only one-third of the loaded iodine was released in nitrogen purging after saturated adsorption. The remaining majority was trapped firmly by the beads due to their strong interactions with the frameworks. This work highlights the millimeter-sized MOF-808@polymer composite beads with ultrahigh iodine adsorption capacity, providing experimental references for their application in radioiodine removal from hot and moist streams.

| S-EPMC9058509 | biostudies-literature

Tuning the Properties of MOF-808 via Defect Engineering and Metal Nanoparticle Encapsulation.

Project description:Defect engineering and metal encapsulation are considered as valuable approaches to fine-tune the reactivity of metal-organic frameworks. In this work, various MOF-808 (Zr) samples are synthesized and characterized with the final aim to understand how defects and/or platinum nanoparticle encapsulation act on the intrinsic and reactive properties of these MOFs. The reactivity of the pristine, defective and Pt encapsulated MOF-808 is quantified with water adsorption and CO2 adsorption calorimetry. The results reveal strong competitive effects between crystal morphology and missing linker defects which in turn affect the crystal morphology, porosity, stability, and reactivity. In spite of leading to a loss in porosity, the introduction of defects (missing linkers or Pt nanoparticles) is beneficial to the stability of the MOF-808 towards water and could also be advantageously used to tune adsorption properties of this MOF family.

| S-EPMC8251568 | biostudies-literature

MOF-808 as a Highly Active Catalyst for the Diastereoselective Reduction of Substituted Cyclohexanones.

Project description:Zr-containing MOF-808 is an excellent heterogeneous catalyst for the diastereoselective Meerwein-Ponndorf-Verley reduction of substituted cyclohexanones. The presence of substituents at the 2 or 3 position of the cyclohexanone ring strongly drives the reaction towards the formation of one of the two possible isomers. For 3-methyl cyclohexanone, the available space inside the MOF pores allows the formation of the bulkier transition state leading to the thermodynamically stable 3-cis-cyclohexanol. For 2-methyl cyclohexanone, the reaction rate is much slower and the final diastereoselectivity depends on the size of the alcohol used. Finally, reduction of 2-phenyl cyclohexanone is considerable faster over MOF-808 than for any other catalyst reported so far. The large size of the phenyl favors the selective formation (up to 94% selectivity) of the cis-alcohol, which goes through a less hindered transition state.

| S-EPMC9571754 | biostudies-literature

Occurrence and speciation of polymeric chromium(III), monomeric chromium(III) and chromium(VI) in environmental samples.

Project description:Laboratory experiments suggest that polymeric Cr(III) could exist in aqueous solution for a relative long period of time. However, the occurrence of polymeric Cr(III) has not been reported in environmental media due partially to the lack of method for speciating polymeric Cr. We observed an unknown Cr species during the course of study on speciation of Cr in the leachates of chromated-copper-arsenate (CCA)-treated wood. Efforts were made to identify structure of the unknown Cr species. Considering the forms of Cr existed in the CCA-treated woods, we mainly focused our efforts to determine if the unknown species were polymeric Cr(III), complex of Cr/As or complex of Cr with dissolved organic matter (DOM). In order to evaluate whether polymeric Cr(III) largely exist in wood leachates, high performance liquid chromatography coupled with inductively coupled mass spectrometry (HPLC-ICPMS was used) for simultaneous speciation of monomeric Cr(III), polymeric Cr(III), and Cr(VI). In addition to wood leachates where polymeric Cr (III) ranged from 39.1 to 67.4%, occurrence of the unknown Cr species in other environmental matrices, including surface waters, tap and waste waters, was also investigated. It was found that polymeric Cr(III) could exist in environmental samples containing μg/L level of Cr, at a level up to 60% of total Cr, suggesting that polymeric Cr(III) could significantly exist in natural environments. Failure in quantifying polymeric Cr(III) would lead to the underestimation of total Cr and bias in Cr speciation. The environmental implication of the presence of polymeric Cr(III) species in the environment deserves further study.

| S-EPMC5027193 | biostudies-literature

Chromium released from leather - I: exposure conditions that govern the release of chromium(III) and chromium(VI).

Project description:BackgroundApproximately 1-3% of the adult population in Europe is allergic to chromium (Cr). A new restriction in REACH (Registration, Evaluation, Authorization and Restriction of Chemicals) based on the ISO 17075 standard has recently been adopted in the EU to limit Cr(VI) in consumer and occupational leather products.ObjectivesThe aim of this study was to critically assess key experimental parameters in this standard on the release of Cr(III) and Cr(VI) and their relevance for skin exposure.Material and methodsFour differently tanned, unfinished, leather samples were systematically investigated for their release of Cr(III) and Cr(VI) in relation to surface area, key exposure parameters, temperature, ultraviolet irradiation, and time.ResultsAlthough the total release of Cr was largely unaffected by all investigated parameters, except exposure duration and temperature, the Cr oxidation state was highly dynamic, with reduced amounts of released Cr(VI) with time, owing to the simultaneous release of reducing agents from the leather. Significantly more Cr(III) than Cr(VI) was released from the Cr-tanned leather for all conditions tested, and it continued to be released in artificial sweat up to at least 1 week of exposure.ConclusionsSeveral parameters were identified that influenced the outcome of the ISO 17075 test.

| S-EPMC4415597 | biostudies-literature

Removal of diclofenac sodium from water using a polyacrylonitrile mixed-matrix membrane embedded with MOF-808.

Project description:MOF-808, owing to the synergistic effect of its large surface area and surface charge matching, showed a diclofenac sodium (DCF) removal capacity as high as 630 mg g-1, and the ability to adsorb 436 mg g-1 DCF in two hours, outperforming many common Zr-MOFs under the same conditions. Importantly, a series of free-standing mixed-matrix membranes made by combining polyacrylonitrile with MOF-808 were fabricated and exhibited high efficiency of removing DCF from water via an easily accessible filtration method.

| S-EPMC11019406 | biostudies-literature

Chromium(III) and chromium(VI) release from leather during 8 months of simulated use.

Project description:BackgroundChromium (Cr) release from Cr-tanned leather articles is a major cause of Cr contact dermatitis. It has been suggested that Cr(VI) release from leather is not necessarily an intrinsic property of the leather, but is strongly dependent on environmental conditions.ObjectivesTo test this hypothesis for long-term (8?months) simulated use.Materials and methodsThe release of total Cr and Cr(VI) from Cr-tanned, unfinished leather was analysed in subsequent phosphate buffer (pH?8.0) immersions for a period of 7.5?months. The effect of combined ultraviolet treatment and alkaline solution (pH?12.1) was tested. Dry storage [20% relative humidity (RH)] was maintained between immersions. Atomic absorption spectroscopy, X-ray fluorescence and diphenylcarbazide tests were used.ResultsCr(VI) release was dependent on previous dry storage or alkaline treatment, but not on duration or number of previous immersions. Cr(III) release decreased with time. Fifty-two percent of the total Cr released during the last immersion period was Cr(VI). Cr(VI) release exceeded 9?mg/kg in all immersion periods except in the first 10-day immersion (2.6?mg/kg).ConclusionsCr(VI) release is primarily determined by environmental factors (RH prior to immersion, solution pH, and antioxidant content). The RH should be kept low prior to testing Cr(VI) release from leather.

| S-EPMC5084788 | biostudies-literature

Photocatalytic Dye and Cr(VI) Degradation Using a Metal-Free Polymeric g-C₃N₄ Synthesized from Solvent-Treated Urea.

Project description:The development of visible-light-driven polymeric g-C₃N₄ is in response to an emerging demand for the photocatalytic dye degradation and reduction of hexavalent chromium ions. We report the synthesis of g-C₃N₄ from urea treated with various solvents such as methanol, ethanol, and ethylene glycol. The samples were characterized and the Williamson⁻Hall method was applied to investigate the lattice strain of the samples. The activity of the samples was evaluated by observing the degradation of methyl orange and K₂Cr₂O₇ solution under light irradiation. Photocatalytic reaction kinetics were determined as pseudo-first-order and zero-order for the degradation of methyl orange and reduction of hexavalent chromium, respectively. Due to the inhibited charge separation resulting from the small lattice strain, reduced crystal imperfection, and sheet-like structure, g-C₃N₄ obtained from ethanol-treated urea exhibited the highest activity among the evaluated samples.

| S-EPMC6401860 | biostudies-other

Selective chromium(VI) ligands identified using combinatorial peptoid libraries.

Project description:Hexavalent chromium [Cr(VI)] is a worldwide water contaminant that is currently without cost-effective and efficient remediation strategies. This is in part due to a lack of ligands that can bind it amid an excess of innocuous ions in aqueous solution. We present herein the design and application of a peptoid-based library of ligand candidates for toxic metal ions. A selective screening process was used to identify members of the library that can bind to Cr(VI) species at neutral pH and in the presence of a large excess of spectator ions. There were 11 sequences identified, and their affinities were compared using titrations monitored with UV-vis spectroscopy. To identify the interactions involved in coordination and specificity, we evaluated the effects of sequence substitutions and backbone variation in the highest affinity structure. Additional characterization of the complex formed between this sequence and Cr(VI) was performed using NMR spectroscopy. To evaluate the ability of the developed sequences to remediate contaminated solutions, the structures were synthesized on a solid-phase resin and incubated with environmental water samples that contained simulated levels of chromium contamination. The synthetic structures demonstrated the ability to reduce the amount of toxic chromium to levels within the range of the EPA contamination guidelines. In addition to providing some of the first selective ligands for Cr(VI), these studies highlight the promise of peptoid sequences as easily prepared components of environmental remediation materials.

| S-EPMC4136388 | biostudies-literature

Introducing VO<sup>2+</sup> Group in Phosphomolybdic Acid and Supporting on MOF-808 for Efficient Oxidative Desulfurization.

Project description:Herein, by introducing a VO2+ group into the microstructure of phosphomolybdenic acid (PMA) and loading it onto MOF-808, a series of composite catalysts were obtained by reducing the V element with Vitamin C (ascorbic acid). V atoms exist in the secondary structural units of phosphomolybdic acid as [VO(H2O)5]H[PMo12O40]. Surprisingly, the VC-VO-PMA/MOF-808 completely removed DBT and 4,6-DMDBT from the simulated oil in 12 min. The EPR and XPS results verify the electronic structure and valence state of V4+ in the composites. The oxygen vacancy and V4+ generated by VC modification in VC-VO-PMA/MOF-808 have positive effects on the oxidation desulfurization (ODS) activity. Based on the design of the microstructure and electronic structure, this study provides a new paradigm for the development of readily available and efficient ODS catalysts.

| S-EPMC10568600 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data