Waterborne Graphene- and Nanocellulose-Based Inks for Functional Conductive Films and 3D Structures.

ABSTRACT: In the vast field of conductive inks, graphene-based nanomaterials, including chemical derivatives such as graphene oxide as well as carbon nanotubes, offer important advantages as per their excellent physical properties. However, inks filled with carbon nanostructures are usually based on toxic and contaminating organic solvents or surfactants, posing serious health and environmental risks. Water is the most desirable medium for any envisioned application, thus, in this context, nanocellulose, an emerging nanomaterial, enables the dispersion of carbon nanomaterials in aqueous media within a sustainable and environmentally friendly scenario. In this work, we present the development of water-based inks made of a ternary system (graphene oxide, carbon nanotubes and nanocellulose) employing an autoclave method. Upon controlling the experimental variables, low-viscosity inks, high-viscosity pastes or self-standing hydrogels can be obtained in a tailored way. The resulting inks and pastes are further processed by spray- or rod-coating technologies into conductive films, and the hydrogels can be turned into aerogels by freeze-drying. The film properties, with respect to electrical surface resistance, surface morphology and robustness, present favorable opportunities as metal-free conductive layers in liquid-phase processed electronic device structures.

SUBMITTER: Gonzalez-Dominguez JM

PROVIDER: S-EPMC8227753 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Fabricating highly crystalline macroscopic films with extraordinary electrical and thermal conductivities from graphene sheets is essential for applications in electronics, telecommunications and thermal management. High-temperature graphitization is the only method known to date for the crystallization of all types of carbon materials, where defects are gradually removed with increasing temperature. However, when using graphene materials as precursors, including graphene oxide, reduced graphene oxide and pristine graphene, even lengthy graphitization at 3000°C can only produce graphene films with small grain sizes and abundant structural disorders, which limit their conductivities. Here, we show that high-temperature defects substantially accelerate the grain growth and ordering of graphene films during graphitization, enabling ideal AB stacking as well as a 100-fold, 64-fold and 28-fold improvement in grain size, electrical conductivity and thermal conductivity, respectively, between 2000°C and 3000°C. This process is realized by nitrogen doping, which retards the lattice restoration of defective graphene, retaining abundant defects such as vacancies, dislocations and grain boundaries in graphene films at a high temperature. With this approach, a highly ordered crystalline graphene film similar to highly oriented pyrolytic graphite is fabricated, with electrical and thermal conductivities (∼2.0 × 104 S cm-1; ∼1.7 × 103 W m-1 K-1) that are improved by about 6- and 2-fold, respectively, compared to those of the graphene films fabricated by graphene oxide. Such graphene film also exhibits a superhigh electromagnetic interference shielding effectiveness of ∼90 dB at a thickness of 10 μm, outperforming all the synthetic materials of comparable thickness including MXene films. This work not only paves the way for the technological application of highly conductive graphene films but also provides a general strategy to efficiently improve the synthesis and properties of other carbon materials such as graphene fibers, carbon nanotube fibers, carbon fibers, polymer-derived graphite and highly oriented pyrolytic graphite.

Dataset Information

Waterborne Graphene- and Nanocellulose-Based Inks for Functional Conductive Films and 3D Structures.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets