Indentation Response of Calcium Aluminoborosilicate Glasses Subjected to Humid Aging and Hot Compression.

ABSTRACT: Aluminoborosilicate glasses find a wide range of applications, which require good mechanical reliability such as surface damage resistance. Calcium aluminoborosilicate (CABS) glasses have recently been found to exhibit so-called intermediate behavior in terms of their response to sharp contact loading. That is, these glasses deform with less shear than normal glass and less densification than anomalous glasses. This deformation mechanism is believed to give rise to high crack initiation resistance of certain CABS glasses. In order to further improve and understand the micromechanical properties of this glass family, we studied the indentation response of different CABS glasses subjected to two types of post-treatment, namely hot compression and humid aging. Upon hot compression, density, elastic moduli, and hardness increased. Specifically, elastic modulus increased by as much as 20% relative to the as-made sample, while the largest change in hardness was 1.8 GPa compared to the as-made sample after hot compression. The pressure-induced increase in these properties can be ascribed to the increase in network connectivity and bond density. On the other hand, the crack initiation resistance decreased, as the hot compression increased the residual stress driving the indentation cracking. Humid aging had only a minor impact on density, modulus, and hardness, but an observed decrease in crack initiation resistance. We discuss the correlations between hardness, density, crack resistance, and deformation mechanism and our study thus provides guidelines for tailoring the mechanical properties of oxide glasses.

SUBMITTER: Ren X

PROVIDER: S-EPMC8269477 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:This work aimed to monitor, through the changes in electrical resistance, the evolution of the mechanical properties due to aging caused by water sorption in carbon nanotube-based epoxy composites. The epoxy/CNT nanocomposites were prepared by dispersing the filler in the precursor through the ultra-sonication process and mixing the hardener by mechanical stirring. After an evaluation of the electrical properties, detected through a two-probe electrical measurement method, of nanocomposites at different percentages by weight of the filler (0.025, 0.05, 0.1, 0.3, 0.5, and 1.0), a concentration (0.1% by weight), close to that of the electrical percolation threshold, was chosen to evaluate the resistive response. This specific concentration was selected in order to obtain maximized values of the variation detected for the changes in the electrical resistance resulting from phenomena of structural relaxations/rearrangements due to water absorption. In particular, the electrical conductivity value switched from 8.2 × 10-14 S/m for the unfilled epoxy resin to 6.3 × 10-2 S/m for carbon nanotube-based epoxy composite at 0.1% by weight of the nanofiller. The water sorption caused a reduction in the mechanical properties (storage modulus and tan δ) due to swelling and plasticization phenomena, which caused the structural reorganization of the conductive interparticle contacts in the matrix with a consequent variation in the electrical resistance of the material. The found 'non-Fickian' water diffusion behavior was very similar to the variation in the electrical resistance with time. This last correlation allows the association of the measurement of the electrical resistance with the quantity of absorbed water and, therefore, with the aging of the material to water absorption, through the sensitivity factor (β). The resistive nature of the composite can be used to monitor the amount of water absorption and the changes in the structure of the material subject to water aging.

Dataset Information

Indentation Response of Calcium Aluminoborosilicate Glasses Subjected to Humid Aging and Hot Compression.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets