Compositional Effects on Indentation Mechanical Properties of Chemically Strengthened TiO₂-Doped Soda Lime Silicate Glasses.

ABSTRACT: TiO₂ is an important oxide for property modifications in the conventional soda lime silicate glass family. It offers interesting optical and mechanical properties, for instance, by substituting heavy metals such as lead in consumer glasses. The compositional effects on the hardness, reduced elastic modulus and crack resistance as determined by indentation of chemically strengthened (CS) TiO₂-doped soda lime silicate glass was studied in the current paper. The CS, which was performed by a K⁺ for Na⁺ ion exchange in a molten KNO₃ salt bath at 450 °C for 15 h, yielded significant changes in the indentation mechanical properties. The hardness of the glass samples increased, and this was notably dependent on the SiO₂, CaO and TiO₂ content. The reduced elastic modulus was less affected by the CS but showed decrease for most samples. The crack resistance, an important property in many applications where glasses are subjected to contact damage, showed very different behaviors among the series. Only one of the series did significantly improve the crack resistance where low CaO content, high TiO₂ content, high molar volume and increased elastic deformation favored an increased crack resistance.

SUBMITTER: Karlsson S

PROVIDER: S-EPMC8779215 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Surface relief hologram formed by selective SiO2 deposition on soda-lime silicate glass.

Project description:We propose the fabrication of surface relief holograms via selective SiO2 deposition on soda-lime silicate glass substrates. Initially, the original hologram was recorded on an azobenzene photosensitive polymer film coated on the soda-lime silicate glass by irradiation with a conventional continuous wave Ar+ laser with a wavelength of 514.5 nm. The hologram was transferred to the soda-lime silicate glass surface via a corona discharge treatment as an index modulation hologram, which was created by partial substitution of protons for sodium ions during the corona discharge treatment in air. After the corona discharge treatment, the polymer film was removed from the substrate. The diffraction efficiency of the index hologram on the soda-lime silicate glass was estimated to be 5.8 × 10-2% at a wavelength of 532 nm. Finally, the glass substrate was subjected to corona discharge treatment in air with vaporized cyclic siloxane. A surface relief hologram with the diffraction efficiency of 2.3% was successfully fabricated on the soda-lime silicate glass.

| S-EPMC6345422 | biostudies-literature

Zinc Oxide-Doped Antibacterial Soda Lime Glass Produced as a Glass Container.

Project description:The aim of this study is to produce and characterize glass materials, which have an enhanced antibacterial property by the conventional melting method. Container glass compositions including different amounts of zinc oxide (ZnO) (5.0, 7.5, and 10.0%) were prepared and melted to be able to obtain the antibacterial glass. The Release and antibacterial tests, which were performed after the melting process, showed that the glass doped with 5% ZnO was the most appropriate composition according to test results (99.82% Escherichia coli inactivation) and its raw materials' costs. Physical, thermal, and mechanical properties such as thermal expansion coefficient (86.1 × 10-7/°C), density (2.523 g/cm3), refractive index (1.5191), hardness (596 kg/mm2), and elastic modulus (5.84 GPa) of the glass doped with 5% ZnO were determined, and the results showed that the obtained antibacterial glass sample is suitable to be used as a glass container. HighTemperature Melting Observation System studies were performed on the produced antibacterial glass composition, and it was found that the antibacterial glass can be produced in soda lime glass furnaces without changing any furnace design and production parameters. This antibacterial glass can be a remarkable product for the pharmaceutical and food industries.

| S-EPMC10018712 | biostudies-literature

A Structural Comparison of Ordered and Non-Ordered Ion Doped Silicate Bioactive Glasses.

Project description:One of the key benefits of sol-gel-derived glasses is the presence of a mesoporous structure and the resulting increase in surface area. This enhancement in textural properties has a significant effect on the physicochemical properties of the materials. In this context the aim of this study was to investigate how sol-gel synthesis parameters can influence the textural and structural properties of mesoporous silicate glasses. We report the synthesis and characterization of metal ion doped sol-gel derived glasses with different dopants in the presence or absence of a surfactant (Pluronic P123) used as structure-directing templating agent. Characterization was done by several methods. Using a structure directing agent led to larger surface areas and highly ordered mesoporous structures. The chemical structure of the non-ordered glasses was modified to a larger extent than the one of the ordered glasses due to increased incorporation of dopant ions into the glass network. The results will help to further understand how the properties of sol-gel glasses can be controlled by incorporation of metal dopants, in conjunction with control over the textural properties, and will be important to optimize the properties of sol-gel glasses for specific applications, e.g., drug delivery, bone regeneration, wound healing, and antibacterial materials.

| S-EPMC7078819 | biostudies-literature

Unseen complication of the exhausted soda lime.

Project description: Not available

| S-EPMC6383477 | biostudies-literature

soda lime metagenome

Project description:soda lime metagenome Targeted loci environmental

| PRJNA433081 | ENA

Shear-banding Induced Indentation Size Effect in Metallic Glasses.

Project description:Shear-banding is commonly regarded as the "plasticity carrier" of metallic glasses (MGs), which usually causes severe strain localization and catastrophic failure if unhindered. However, through the use of the high-throughput dynamic nanoindentation technique, here we reveal that nano-scale shear-banding in different MGs evolves from a "distributed" fashion to a "localized" mode when the resultant plastic flow extends over a critical length scale. Consequently, a pronounced indentation size effect arises from the distributed shear-banding but vanishes when shear-banding becomes localized. Based on the critical length scales obtained for a variety of MGs, we unveil an intrinsic interplay between elasticity and fragility that governs the nanoscale plasticity transition in MGs. Our current findings provide a quantitative insight into the indentation size effect and transition mechanisms of nano-scale plasticity in MGs.

| S-EPMC4914989 | biostudies-literature

Production of Soda Lime Glass Having Antibacterial Property for Industrial Applications.

Project description:This study was aimed to produce and characterize the first commercial glass materials with enhanced antibacterial property using conventional melting method. For this purpose, typical container glass composition that contains some specific metal ions, such as silver, strontium, and copper, was used to obtain antibacterial glass samples using classical melting method. After the melting process, antibacterial tests and migration tests were applied to the glasses, and it was found that the glass doped with 2% Ag2O was the best composition. X-rays diffractometer (XRD), thermal expansion coefficient, density, refractive index, hardness, and elastic module results showed that the glass doped with 2% Ag2O was a suitable material as a container glass. High Temperature Melting Observation System studies were performed on the produced antibacterial glass composition, and it was found that the antibacterial glass can be produced in soda lime glass furnaces without changing any furnace design and production parameters. As a result of the characterization studies, it was concluded that the produced container glass doped with silver can be a good candidate for food and pharmaceutical products where bacterial growth is absolutely undesirable.

| S-EPMC7663106 | biostudies-literature

Dynamics of self-reorganization explains passivation of silicate glasses.

Project description:Understanding the dissolution of silicate glasses and minerals from atomic to macroscopic levels is a challenge with major implications in geoscience and industry. One of the main uncertainties limiting the development of predictive models lies in the formation of an amorphous surface layer--called gel--that can in some circumstances control the reactivity of the buried interface. Here, we report experimental and simulation results deciphering the mechanisms by which the gel becomes passivating. The study conducted on a six-oxide borosilicate glass shows that gel reorganization involving high exchange rate of oxygen and low exchange rate of silicon is the key mechanism accounting for extremely low apparent water diffusivity (∼10-21 m2 s-1), which could be rate-limiting for the overall reaction. These findings could be used to improve kinetic models, and inspire the development of new molecular sieve materials with tailored properties as well as highly durable glass for application in extreme environments.

| S-EPMC5986767 | biostudies-literature

Selective Deposition of SiO2 on Ion Conductive Area of Soda-lime Glass Surface.

Project description:Selective deposition of SiO2 nanoparticles was demonstrated on a soda-lime glass surface with a periodic sodium deficient pattern formed using the electrical nanoimprint. Positively charged SiO2 particles generated using corona discharge in a cyclic siloxane vapor, were selectively deposited depending on the sodium pattern. For such phenomena to occur, the sodium ion migration to the cathode side was indispensable to the electrical charge compensation on the glass surface. Therefore, the deposition proceeded preferentially outside the alkali-deficient area. Periodic SiO2 structures with 424?nm and 180?nm heights were obtained using one-dimensional (6??m period) and two-dimensional (500?nm period) imprinted patterns.

| S-EPMC4904222 | biostudies-literature

Indentation Response of Calcium Aluminoborosilicate Glasses Subjected to Humid Aging and Hot Compression.

Project description:Aluminoborosilicate glasses find a wide range of applications, which require good mechanical reliability such as surface damage resistance. Calcium aluminoborosilicate (CABS) glasses have recently been found to exhibit so-called intermediate behavior in terms of their response to sharp contact loading. That is, these glasses deform with less shear than normal glass and less densification than anomalous glasses. This deformation mechanism is believed to give rise to high crack initiation resistance of certain CABS glasses. In order to further improve and understand the micromechanical properties of this glass family, we studied the indentation response of different CABS glasses subjected to two types of post-treatment, namely hot compression and humid aging. Upon hot compression, density, elastic moduli, and hardness increased. Specifically, elastic modulus increased by as much as 20% relative to the as-made sample, while the largest change in hardness was 1.8 GPa compared to the as-made sample after hot compression. The pressure-induced increase in these properties can be ascribed to the increase in network connectivity and bond density. On the other hand, the crack initiation resistance decreased, as the hot compression increased the residual stress driving the indentation cracking. Humid aging had only a minor impact on density, modulus, and hardness, but an observed decrease in crack initiation resistance. We discuss the correlations between hardness, density, crack resistance, and deformation mechanism and our study thus provides guidelines for tailoring the mechanical properties of oxide glasses.

| S-EPMC8269477 | biostudies-literature