Formation and Properties of Superhydrophobic Al Coatings on Steel.

ABSTRACT: Thermal sprayed aluminum coatings are widely scalable to corrosion protection of the offshore steel structure. However, the corrosion rate of the Al coating increases considerably due to the severe marine environment. It has remained a challenge to improve the corrosion resistance and protective ability of Al coatings. The superhydrophobic surface provides a potential way to improve the corrosion resistance of metal materials. Hence, the development of superhydrophobic Al coatings with superior corrosion resistance is of great interest. In this work, the feasibility of the preparation of superhydrophobic Al coatings on a steel substrate was explored. First, Al coatings were prepared onto the steel substrate by the arc-spraying process, followed by ultrasonic etching with 0.1 M NaOH solution, and afterward passivated using 1% fluorosilanes. The effects of the etching time on morphology, contact angle, and corrosion resistance of the Al coatings were evaluated. The schematic model of the fluorosilane passivation process on the Al coating surface was provided. The micro/nanoscale surface structure of the low-surface-energy fluorosilanes promotes the wetting angle of 153.4° and a rolling angle to 6.6°, denoting the superhydrophobic properties. The superhydrophobic Al coating surface displays excellent self-cleaning performance due to its weak adhesion to water droplets. The corrosion current density of the superhydrophobic Al coating (1.36 × 10^-8 A cm^-2) is 2 orders of magnitude lower than that of the as-sprayed Al coating (1.18 × 10^-6 A cm^-2). Similarly, the charge-transfer resistance is found to be 12 times larger for the superhydrophobic Al coating and the corresponding corrosion inhibition efficiency reaches 98.9%. The superhydrophobic Al coating displays superior corrosion resistance and promising applications in a marine corrosion environment.

SUBMITTER: Ge Y

PROVIDER: S-EPMC8296599 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Zirconium–Copper-based metallic glass thin films represent promising coatings in the biomedical sector for their combination of antibacterial property and wear resistance. However, finding a Zr–Cu metallic glass composition with desirable cytocompatibility and antibacterial property is extremely challenging. In this work, we have created a cytocompatible and (super-)hydrophobic Zr–Cu–Ag metallic glass coating with ≈95% antifouling properties. First, a range of different chemical compositions were prepared via Physical Vapor Deposition magnetron by co-sputtering Zr, Cu, and Ag onto a Polybutylene terephthalate (PBT) substrate among which Zr93·5Cu6·2Ag0.2, Zr76·7Cu22·7Ag0.5, and Zr69·3Cu30·1Ag0.6 were selected to be further investigate for their surface properties, antibacterial activity, and cytocompatibility. Scanning electron microscopy (SEM) images revealed a micro-roughness fibrous structure holding superhydrophobic properties demonstrated by specimens' static and dynamic contact angle measurements ranging from 130° to 150°. The dynamic contact angle measurements have shown hysteresis below 10° for all coated samples which indicated the superhydrophobicity of the samples. To distinguish between antifouling and bactericidal effect of the coating, ions release from coatings into Luria Bertani Broth (LB), and Dulbecco's Modified Eagle Medium (DMEM) solutions were evaluated by inductively coupled plasma mass spectrometry (ICP-MS) measurements after 24 h and 5 days. Antifouling properties were evaluated by infecting the specimens' surface with the Gram-positive Staphylococcus aureus and the Gram-negative Escherichia coli strain reporting a ≈95% reduction of bacteria adhesion as visually confirmed by FESEM and fluorescent live/dead staining. Human mesenchymal stem cells (hMSC) were used for direct cytocompatibility evaluation of coated samples and their metabolic activity was evaluated via relative fluorescence unit after 24 h and 5 days confirming that it was comparable to the controls (>97% viable cells). The results were further visualized by FESEM, fluorescent staining by Live/Dead Viability/Cytotoxicity Kit and confirmed the cytocompatibility of all coated samples. Finally, hMSC′ cytoplasm was stained by May Grunwald and Giemsa after 5days to detect and visualize the released ions which have diffused through the cells' membrane. Graphical abstract Image 1

Dataset Information

Formation and Properties of Superhydrophobic Al Coatings on Steel.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets