Polarization and Dielectric Properties of BiFeO3-BaTiO3 Superlattice-Structured Ferroelectric Films.

ABSTRACT: Superlattice-structured epitaxial thin films composed of Mn(5%)-doped BiFeO3 and BaTiO3 with a total thickness of 600 perovskite (ABO3) unit cells were grown on single-crystal SrTiO3 substrates by pulsed laser deposition, and their polarization and dielectric properties were investigated. When the layers of Mn-BiFeO3 and BaTiO3 have over 25 ABO3 unit cells (N), the superlattice can be regarded as a simple series connection of their individual capacitors. The superlattices with an N of 5 or less behave as a unified ferroelectric, where the BaTiO3 and Mn-BiFeO3 layers are structurally and electronically coupled. Density functional theory calculations can explain the behavior of spontaneous polarization for the superlattices in this thin regime. We propose that a superlattice formation comprising two types of perovskite layers with different crystal symmetries opens a path to novel ferroelectrics that cannot be obtained in a solid solution system.

SUBMITTER: Noguchi Y

PROVIDER: S-EPMC8308477 | biostudies-literature | 2021 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Polarization and Dielectric Properties of BiFeO3-BaTiO3 Superlattice-Structured Ferroelectric Films.

Noguchi Yuji Y Matsuo Hiroki H

Nanomaterials (Basel, Switzerland) 20210719 7

Superlattice-structured epitaxial thin films composed of Mn(5%)-doped BiFeO3 and BaTiO3 with a total thickness of 600 perovskite (ABO3) unit cells were grown on single-crystal SrTiO3 substrates by pulsed laser deposition, and their polarization and dielectric properties were investigated. When the layers of Mn-BiFeO3 and BaTiO3 have over 25 ABO3 unit cells (N), the superlattice can be regarded as a simple series ...[more]

PMID: 34361243

Similar Datasets

Ferroelectric Polarization-Enhanced Photocatalysis in BaTiO3-TiO2 Core-Shell Heterostructures.

Project description:Suppressing charge recombination and improving carrier transport are key challenges for the enhancement of photocatalytic activity of heterostructured photocatalysts. Here, we report a ferroelectric polarization-enhanced photocatalysis on the basis of BaTiO3-TiO2 core-shell heterostructures synthesized via a hydrothermal process. With an optimal weight ratio of BaTiO3 to TiO2, the heterostructures exhibited the maximum photocatalytic performance of 1.8 times higher than pure TiO2 nanoparticles. The enhanced photocatalytic activity is attributed to the promotion of charge separation and transport based on the internal electric field originating from the spontaneous polarization of ferroelectric BaTiO3. High stability of polarization-enhanced photocatalysis is also confirmed from the BaTiO3-TiO2 core-shell heterostructures. This study provides evidence that ferroelectric polarization holds great promise for improving the performance of heterostructured photocatalysts.

| S-EPMC6722819 | biostudies-literature

Suppression of creep-regime dynamics in epitaxial ferroelectric BiFeO3 films.

Project description:Switching dynamics of ferroelectric materials are governed by the response of domain walls to applied electric field. In epitaxial ferroelectric films, thermally-activated 'creep' motion plays a significant role in domain wall dynamics, and accordingly, detailed understanding of the system's switching properties requires that this creep motion be taken into account. Despite this importance, few studies have investigated creep motion in ferroelectric films under ac-driven force. Here, we explore ac hysteretic dynamics in epitaxial BiFeO3 thin films, through ferroelectric hysteresis measurements, and stroboscopic piezoresponse force microscopy. We reveal that identically-fabricated BiFeO3 films on SrRuO3 or La0.67Sr0.33MnO3 bottom electrodes exhibit markedly different switching behaviour, with BiFeO3/SrRuO3 presenting essentially creep-free dynamics. This unprecedented result arises from the distinctive spatial inhomogeneities of the internal fields, these being influenced by the bottom electrode's surface morphology. Our findings further highlight the importance of controlling interface and defect characteristics, to engineer ferroelectric devices with optimised performance.

| S-EPMC4444839 | biostudies-literature

Multilevel polarization switching in ferroelectric thin films.

Project description:Ferroic order is characterized by hystereses with two remanent states and therefore inherently binary. The increasing interest in materials showing non-discrete responses, however, calls for a paradigm shift towards continuously tunable remanent ferroic states. Device integration for oxide nanoelectronics furthermore requires this tunability at the nanoscale. Here we demonstrate that we can arbitrarily set the remanent ferroelectric polarization at nanometric dimensions. We accomplish this in ultrathin epitaxial PbZr0.52Ti0.48O3 films featuring a dense pattern of decoupled nanometric 180° domains with a broad coercive-field distribution. This multilevel switching is achieved by driving the system towards the instability at the morphotropic phase boundary. The phase competition near this boundary in combination with epitaxial strain increases the responsiveness to external stimuli and unlocks new degrees of freedom to nano-control the polarization. We highlight the technological benefits of non-binary switching by demonstrating a quasi-continuous tunability of the non-linear optical response and of tunnel electroresistance.

| S-EPMC9174202 | biostudies-literature

Giant optical enhancement of strain gradient in ferroelectric BiFeO3 thin films and its physical origin.

Project description:Through mapping of the spatiotemporal strain profile in ferroelectric BiFeO3 epitaxial thin films, we report an optically initiated dynamic enhancement of the strain gradient of 10(5)-10(6) m(-1) that lasts up to a few ns depending on the film thickness. Correlating with transient optical absorption measurements, the enhancement of the strain gradient is attributed to a piezoelectric effect driven by a transient screening field mediated by excitons. These findings not only demonstrate a new possible way of controlling the flexoelectric effect, but also reveal the important role of exciton dynamics in photostriction and photovoltaic effects in ferroelectrics.

| S-EPMC4653733 | biostudies-literature

Enhanced Dielectric Performance of P(VDF-HFP) Composites with Satellite-Core-Structured Fe2O3@BaTiO3 Nanofillers.

Project description:Polymer dielectric materials are extensively used in electronic devices. To enhance the dielectric constant, ceramic fillers with high dielectric constant have been widely introduced into polymer matrices. However, to obtain high permittivity, a large added amount (>50 vol%) is usually needed. With the aim of improving dielectric properties with low filler content, satellite-core-structured Fe2O3@BaTiO3 (Fe2O3@BT) nanoparticles were fabricated as fillers for a poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) matrix. The interfacial polarization effect is increased by Fe2O3 nanoparticles, and thus, composite permittivity is enhanced. Besides, the satellite-core structure prevents Fe2O3 particles from directly contacting each other, so that the dielectric loss remains relatively low. Typically, with 20 vol% Fe2O3@BT nanoparticle fillers, the permittivity of the composite is 31.7 (1 kHz), nearly 1.8 and 3.0 times that of 20 vol% BT composites and pure polymers, respectively. Nanocomposites also achieve high breakdown strength (>150 KV/mm) and low loss tangent (~0.05). Moreover, the composites exhibited excellent flexibility and maintained good dielectric properties after bending. These results demonstrate that composite films possess broad application prospects in flexible electronics.

| S-EPMC6835555 | biostudies-literature

Enhanced Magnetoelectric Coupling in BaTiO3-BiFeO3 Multilayers-An Interface Effect.

Project description:Combining various (multi-)ferroic materials into heterostructures is a promising route to enhance their inherent properties, such as the magnetoelectric coupling in BiFeO3 thin films. We have previously reported on the up-to-tenfold increase of the magnetoelectric voltage coefficient α ME in BaTiO3-BiFeO3 multilayers relative to BiFeO3 single layers. Unraveling the origin and mechanism of this enhanced effect is a prerequisite to designing new materials for the application of magnetoelectric devices. By careful variations in the multilayer design we now present an evaluation of the influences of the BaTiO3-BiFeO3 thickness ratio, oxygen pressure during deposition, and double layer thickness. Our findings suggest an interface driven effect at the core of the magnetoelectric coupling effect in our multilayers superimposed on the inherent magnetoelectric coupling of BiFeO3 thin films, which leads to a giant α ME coefficient of 480 V c m -1 Oe-1 for a 16 × (BaTiO3-BiFeO3) superlattice with a 4 . 8 nm double layer periodicity.

| S-EPMC6982203 | biostudies-literature

Studying the Polarization Switching in Polycrystalline BiFeO3 Films by 2D Piezoresponse Force Microscopy.

Project description:For rhombohedral multiferroelectrics, non-180° ferroelectric domain switching may induce ferroelastic and/or (anti-)ferromagnetic effect. So the determination and control of ferroelectric domain switching angles is crucial for nonvolatile information storage and exchange-coupled magnetoelectric devices. We try to study the intrinsic characters of polarization switching in BiFeO3 by introducing a special data processing method to determine the switching angle from 2D PFM (Piezoresponse Force Microscopy) images of randomly oriented samples. The response surface of BiFeO3 is first plotted using the piezoelectric tensor got from first principles calculations. Then from the normalized 2D PFM signals before and after switching, the switching angles of randomly oriented BiFeO3 grains can be determined through numerical calculations. In the polycrystalline BiFeO3 films, up to 34% of all switched area is that with original out-of-plane (OP) polarization parallel to the poling field. 71° polarization switching is more favorable, with the area percentages of 71°, 109° and 180° domain switching being about 42%, 29% and 29%, respectively. Our analysis further reveals that IP stress and charge migration have comparable effect on switching, and they are sensitive to the geometric arrangements. This work helps exploring a route to control polarization switching in BiFeO3, so as to realize desirable magnetoelectric coupling.

| S-EPMC4507449 | biostudies-literature

Ferroelectricity and Self-Polarization in Ultrathin Relaxor Ferroelectric Films.

Project description:We report ferroelectricity and self-polarization in the (001) oriented ultrathin relaxor ferroelectric PMN-PT films grown on Nb-SrTiO3, SrRuO3 and La0.7Sr0.3MnO3, respectively. Resistance-voltage measurements and AC impedance analysis suggest that at high temperatures Schottky depletion width in a 4 nm thick PMN-PT film deposited on Nb-SrTiO3 is smaller than the film thickness. We propose that Schottky interfacial dipoles make the dipoles of the nanometer-sized polar nanoregions (PNRs) in PMN-PT films grown on Nb-SrTiO3 point downward at high temperatures and lead to the self-polarization at room temperature with the assistance of in-plane compressive strain. This work sheds light on the understanding of epitaxial strain effects on relaxor ferroelectric films and self-polarization mechanism.

| S-EPMC4730210 | biostudies-literature

Giant Dielectric Permittivity in Ferroelectric Thin Films: Domain Wall Ping Pong.

Project description:The dielectric permittivity in ferroelectric thin films is generally orders of magnitude smaller than in their bulk. Here, we discover a way of increasing dielectric constants in ferroelectric thin films by ca. 500% by synchronizing the pulsed switching fields with the intrinsic switching time (nucleation of domain plus forward growth from cathode to anode). In a 170-nm lead zirconate titanate thin film with an average grain size of 850 nm this produces a dielectric constant of 8200 with the maximum nucleus density of 3.8 μm(-2), which is one to three orders of magnitude higher than in other dielectric thin films. This permits smaller capacitors in memory devices and is a step forward in making ferroelectric domain-engineered nano-electronics.

| S-EPMC4594126 | biostudies-literature

Compositionally-graded ferroelectric thin films by solution epitaxy produce excellent dielectric stability.

Project description:The composition in ferroelectric oxide films is decisive for optimizing properties and device performances. Controlling a composition distribution in these films by a facile approach is thus highly desired. In this work, we report a solution epitaxy of PbZrxTi1-xO3 films with a continuous gradient of Zr concentration, realized by a competitive growth at ~220 °C. These intriguing films demonstrate a frequency-independent of dielectric permittivity below 100 kHz from room-temperature to 280 °C. In particular, the permittivity of the films can be largely regulated from 100 to 50 by slightly varying Zr compositional gradient. These results were revealed to arise from a built-in electric field within the films due to a coupling between the composition gradient and unidirectional spontaneous polarization. Our findings may pave a way to prepare compositionally-graded ferroelectric films by a solution approach, which is promising for practical dielectric, pyroelectric and photoelectric technical applications.

| S-EPMC11696802 | biostudies-literature