Interactions of boron released from surface pre-reacted glass ionomer with enamel/dentin and its effect on pH.

ABSTRACT: This study investigated the interaction of borate ions released from surface pre-reacted glass ionomer (S-PRG) fillers with the biological apatites of enamel and dentin using solid-state (SS) magic-angle spinning nuclear magnetic resonance (MAS-NMR) spectroscopy analysis. We further evaluated the effect of borate ions on the pH change. Bovine enamel and dentin powder were submerged in S-PRG eluate (with borate ion concentration of 100 mM) for 3 h, then washed with deionized water (DW). The dried enamel and dentin specimens were used for ¹¹B SS-NMR and Fourier transform infrared spectroscopy (FT-IR) analysis. Enamel and dentin blocks were treated with three solutions: DW (control), S-PRG eluent and borate solution (100 mM). The treated samples were submerged in the demineralization solution and the pH was measured using a pH meter daily for 6 days. The surfaces of the enamel and dentin blocks were then observed using field emission scanning electron microscopy (FE-SEM). SS-NMR analysis revealed the presence of adsorbed borate ions in the enamel and dentin samples in a tetra-coordinated form. The pH results demonstrated an increase in pH values in the S-PRG and borate groups. SEM images showed that the surfaces of the control group were demineralized, whereas the surfaces of the S-PRG and borate groups were intact. These results concluded that borate ions could be adsorbed to enamel and dentin in the tetra-coordinated form. Borate ions possess a buffer capacity which may help to protect the tooth structure against acid attacks and promote remineralization.

SUBMITTER: Hiraishi N

PROVIDER: S-EPMC8333262 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:ObjectivesSurface pre-reacted glass-ionomer (S-PRG) fillers release antibacterial borate and fluoride ions. We fabricated nanoscale S-PRG fillers (S-PRG nanofillers) for antibacterial coating of tooth surfaces and assessed the antibacterial effects of this coating in vitro. In addition, we creating a canine model of periodontitis to evaluate the effectiveness of S-PRG nanofiller application on tooth roots and improvement of periodontal parameters.MethodsHuman dentin blocks were coated with S-PRG nanofiller (average particle size: 0.48 μm) and then characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectrometer (EDX), and ion-releasing test. Antibacterial effects of dentin blocks coated with S-PRG nanofiller were examined using bacterial strains, Streptococcus mutans and Actinomyces naeslundii. Next, we created an experimental model of periodontitis in furcation of premolars of beagle dogs. Then, S-PRG nanofiller coating was applied onto exposed tooth root surfaces. Periodontal parameters, gingival index (GI), bleeding on probing (BOP), probing pocket depth (PPD), and clinical attachment level (CAL), were measured from baseline until 4 weeks. In addition, bone healing was radiographically and histologically examined.ResultsSEM and EDX revealed that S-PRG nanofillers uniformly covered the dentin surface after coating. Dentin blocks coated with S-PRG nanofiller showed ion-releasing property, bacterial growth inhibition, and sterilization effects. In the experimental periodontitis model, S-PRG nanofiller coating significantly reduced clinical inflammatory parameters, such as GI (P < 0.01) and BOP (P < 0.05), compared to uncoated samples. In addition, PPD and CAL significantly decreased by S-PRG nanofiller coating (2 weeks: P < 0.05; 3 and 4 weeks: P < 0.01), suggesting the improvement of periodontitis. Micro-CT and histology revealed that bone healing of furcation defects was enhanced by S-PRG nanofiller coating.ConclusionS-PRG nanofiller coating provides antibacterial effects to tooth surfaces and improves clinical parameters of periodontitis.

Dataset Information

Interactions of boron released from surface pre-reacted glass ionomer with enamel/dentin and its effect on pH.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets