Effect of various dentin disinfection protocols on the bond strength of resin modified glass ionomer restorative material.

ABSTRACT: Disinfection of dentin surface prior to any restorative therapy is important for the longevity of the treatment rendered. However, these dentin disinfection methods should itself not interfere with the adhesion of the restorative material. Therefore the aim of this study was to determine the effect of various dentin disinfection protocols on the shear bond strength (SBS) of resin modified glass ionomer cement (RMGIC).The occlusal surface of 40 extracted premolars were trimmed to obtain a flat dentinal surface and was randomly divided into four groups. CTRL was the control group; NaOCl was 1% sodium hypochlorite disinfection group; CHX was 2% chlorhexidine disinfection group; and PAD was the photo-activated disinfection group. Then a predetermined dimension of RMGIC was bonded to the pre-treated dentin surfaces. Following this, each sample was tested for SBS using universal testing machine at a crosshead speed of 0.5mm/min.Among the test groups, CHX showed the least reduction in SBS and NaOCl the highest reduction in SBS as compared to the control group. PAD on the other hand showed significantly lower SBS than CTRL and CHX groups, but the values were higher than the NaOCl group.Thus, it could be concluded from the present study that use of chlorhexidine based dentin disinfection does interfere with the adhesion of RMGIC. However, photo-activated disinfection should be done with caution. Moreover, sodium hypochlorite based disinfectants should be avoided prior to the use of RMGIC. Key words:Chlorhexidine, Dentin disinfection, Photo-activated disinfection, Resin modified glass ionomer cement, Shear bond strength, Sodium hypochlorite.

SUBMITTER: Sekhar A

PROVIDER: S-EPMC5549579 | biostudies-other | 2017 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Addition of chlorhexidine has enhanced the antimicrobial effect of glass ionomer cement (GIC) indicated to Atraumatic Restorative Treatment (ART); however, the impact of this mixture on the properties of these materials and on the longevity of restorations must be investigated. The aim of this study was to evaluate the effects of incorporating chlorhexidine (CHX) in the in vitro biological and chemical-mechanical properties of GIC and in vivo clinical/ microbiological follow-up of the ART with GIC containing or not CHX.For in vitro studies, groups were divided into GIC, GIC with 1.25% CHX, and GIC with 2.5% CHX. Antimicrobial activity of GIC was analyzed using agar diffusion and anti-biofilm assays. Cytotoxic effects, compressive tensile strength, microhardness and fluoride (F) release were also evaluated. A randomized controlled trial was conducted on 36 children that received ART either with GIC or GIC with CHX. Saliva and biofilm were collected for mutans streptococci (MS) counts and the survival rate of restorations was checked after 7 days, 3 months and one year after ART. ANOVA/Tukey or Kruskal-Wallis/ Mann-Whitney tests were performed for in vitro tests and in vivo microbiological analysis. The Kaplan-Meier method and Log rank tests were applied to estimate survival percentages of restorations (p<0.05).Incorporation of 1.25% and 2.5% CHX improved the antimicrobial/anti-biofilm activity of GIC, without affecting F release and mechanical characteristics, but 2.5% CHX was cytotoxic. Survival rate of restorations using GIC with 1.25% CHX was similar to GIC. A significant reduction of MS levels was observed for KM+CHX group in children saliva and biofilm 7 days after treatment.The incorporation of 1.25% CHX increased the in vitro antimicrobial activity, without changing chemical-mechanical properties of GIC and odontoblast-like cell viability. This combination improved the in vivo short-term microbiological effect without affecting clinical performance of ART restorations.

Dataset Information

Effect of various dentin disinfection protocols on the bond strength of resin modified glass ionomer restorative material.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets