Tailored Synthesis of Iron Oxide Nanocrystals for Formation of Cuboid Mesocrystals.

ABSTRACT: In this work, we systematically studied the shape- and size-controlled monodisperse synthesis of iron oxide nanocrystals (IONCs) for their use as building blocks in the formation of mesocrystals. For this aim, on understanding the influence of the oleic acid concentration, iron-oleate concentration, and heating rate on the synthesis of robust and reproducible IONCs with desired sizes and shapes, we synthesized highly monodisperse ∼11 nm sized nanocubes and nanospheres. Magnetic measurements of both cubic and spherical IONCs revealed the presence of mixed paramagnetic and superparamagnetic phases in these nanocrystals. Moreover, we observed that the magnetic moments of the nanocubes are more substantial compared to their spherical counterparts. We then demonstrated a simple magnetic-field-assisted assembly of nanocubes into three-dimensional (3D) cuboid mesocrystals while nanospheres did not form any mesocrystals. These findings indicate that small cubic nanocrystals hold great promise as potential building blocks of 3D magnetic hierarchical structures with their superior magnetic properties and mesocrystal assembly capability, which may have high relevance in various fields ranging from high-density data storage to biomedical applications.

SUBMITTER: Soran-Erdem Z

PROVIDER: S-EPMC8358947 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Shape induced symmetry in self-assembled mesocrystals of iron oxide nanocubes.

Project description:Grazing incidence small-angle scattering and electron microscopy have been used to show for the first time that nonspherical nanoparticles can assemble into highly ordered body-centered tetragonal mesocrystals. Energy models accounting for the directionality and magnitude of the van der Waals and dipolar interactions as a function of the degree of truncation of the nanocubes illustrated the importance of the directional dipolar forces for the formation of the initial nanocube clusters and the dominance of the van der Waals multibody interactions in the dense packed arrays.

| S-EPMC3075854 | biostudies-other

Colloidal Synthesis of Bipolar Off-Stoichiometric Gallium Iron Oxide Spinel-Type Nanocrystals with Near-IR Plasmon Resonance.

Project description:We report the colloidal synthesis of ?5.5 nm inverse spinel-type oxide Ga2FeO4 (GFO) nanocrystals (NCs) with control over the gallium and iron content. As recently theoretically predicted, some classes of spinel-type oxide materials can be intrinsically doped by means of structural disorder and/or change in stoichiometry. Here we show that, indeed, while stoichiometric Ga2FeO4 NCs are intrinsic small bandgap semiconductors, off-stoichiometric GFO NCs, produced under either Fe-rich or Ga-rich conditions, behave as degenerately doped semiconductors. As a consequence of the generation of free carriers, both Fe-rich and Ga-rich GFO NCs exhibit a localized surface plasmon resonance in the near-infrared at ?1000 nm, as confirmed by our pump-probe absorption measurements. Noteworthy, the photoelectrochemical characterization of our GFO NCs reveal that the majority carriers are holes in Fe-rich samples, and electrons in Ga-rich ones, highlighting the bipolar nature of this material. The behavior of such off-stoichiometric NCs was explained by our density functional theory calculations as follows: the substitution of Ga3+ by Fe2+ ions, occurring in Fe-rich conditions, can generate free holes (p-type doping), while the replacement of Fe2+ by Ga3+ cations, taking place in Ga-rich samples, produces free electrons (n-type doping). These findings underscore the potential relevance of spinel-type oxides as p-type transparent conductive oxides and as plasmonic semiconductors.

| S-EPMC6105077 | biostudies-literature

In vivo clearance and toxicity of monodisperse iron oxide nanocrystals.

Project description:Thermal decomposition of organometallic precursors has been found to generate highly crystalline iron oxide (IO) nanocrystals that display superior MR contrast and lower polydispersity than IO nanocrystals synthesized by aqueous precipitation. In the present study, the in vivo characteristics of IO nanocrystals prepared by the thermal decomposition route and then coated with a phospholipid containing a pendant poly(ethylene glycol) chain are examined. The size and surface chemistry of the IO nanocrystal influence the biodistibution, the rate of biodegradation and bioclearance, and the biodegradation products. We conclude that the in vivo fate of PEGylated monodisperse IO nanocrystals and the iron, phospholipid, and oleic acid biodegradation products may influence the cellular environments in the organs and blood that can determine their safety in the body.

| S-EPMC3400701 | biostudies-literature

Co-precipitation Synthesis of Near-infrared Iron Oxide Nanocrystals on Magnetically Targeted Imaging and Photothermal Cancer Therapy via Photoablative Protein Denature.

Project description:Near-infrared (NIR)-based nanomaterials that provide efficient tumor ablation for cancer therapy have been reported. However, the issues of biocompatibility of metals or ions in inorganic nanoparticles systems such as copper and gold nanoparticles are still a matter of concern. In this study, we developed a facile and ligand-assisted co-precipitation method to synthesize biocompatible iron oxide (IO) nanocrystals with NIR absorption that provided T2-weighted magnetic resonance (MR) images and photothermal ablation characteristics suitable for cancer theranostics. Our results showed that 150-nm particles can be synthesized and optimized by using different amounts of ligand. NIR-IO nanocrystals of this size showed high photothermal conversion efficiency (21.2%) and T2-weighted MR contrast (transverse relaxivity value approximately 141 S-1 mM-1). The NIR-IO nanocrystals showed no cytotoxicity in HT-29 colorectal cancer cells without irradiation, whereas the viability of cells that received NIR-IO nanocrystals decreased significantly after 808-nm laser irradiation. The mechanism of cell death may involve alterations in protein secondary structure and membrane permeability. For in vivo studies, 4-fold enhanced tumor accumulation was significantly observed of NIR-IO nanocrystals with a magnetic field (MF) application, resulting in a 3-fold higher T2-weighted MR signal than that produced by a commercial T2-weighted MR contrast agent (Resovist®) and excellent photothermal efficacy (approximately 53 °C) for cancer treatment. The innovative NIR-IO nanocrystals showed excellent biocompatibility and have great potential as a theranostic agent against cancer.

| S-EPMC6584136 | biostudies-literature

Synthesis of Shape-Tailored WO₃ Micro-/Nanocrystals and the Photocatalytic Activity of WO₃/TiO₂ Composites.

Project description:A traditional semiconductor (WO₃) was synthesized from different precursors via hydrothermal crystallization targeting the achievement of three different crystal shapes (nanoplates, nanorods and nanostars). The obtained WO₃ microcrystals were analyzed by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and diffuse reflectance spectroscopy (DRS). These methods contributed to the detailed analysis of the crystal morphology and structural features. The synthesized bare WO₃ photocatalysts were totally inactive, while the P25/WO₃ composites were efficient under UV light radiation. Furthermore, the maximum achieved activity was even higher than the bare P25's photocatalytic performance. A correlation was established between the shape of the WO₃ crystallites and the observed photocatalytic activity registered during the degradation of different substrates by using P25/WO₃ composites.

| S-EPMC5502922 | biostudies-other

Tailored Synthesis of Catalytically Active Cerium Oxide for N, N-Dimethylformamide Oxidation.

Project description:Cerium oxide nanopowder (CeOx) was prepared using the sol-gel method for the catalytic oxidation of N, N-dimethylformamide (DMF). The phase, specific surface area, morphology, ionic states, and redox properties of the obtained nanocatalyst were systematically characterized using XRD, BET, TEM, EDS, XPS, H2-TPR, and O2-TPO techniques. The results showed that the catalyst had a good crystal structure and spherelike morphology with the aggregation of uniform small grain size. The catalyst showed the presence of more adsorbed oxygen on the catalyst surface. XPS and H2-TPR have confirmed the reduction of Ce4+ species to Ce3+ species. O2-TPR proved the reoxidability of CeOx, playing a key role during DMF oxidation. The catalyst had a reaction rate of 1.44 mol g-1cat s-1 and apparent activation energy of 33.30 ± 3 kJ mol-1. The catalytic performance showed ~82 ± 2% DMF oxidation at 400 °C. This work's overall results demonstrated that reducing Ce4+ to Ce3+ and increasing the amount of adsorbed oxygen provided more suitable active sites for DMF oxidation. Additionally, the catalyst was thermally stable (~86%) after 100 h time-on-stream DMF conversion, which could be a potential catalyst for industrial applications.

| S-EPMC9867243 | biostudies-literature

Octahedron Iron Oxide Nanocrystals Prohibited Clostridium difficile Spore Germination and Attenuated Local and Systemic Inflammation.

Project description:Clinical management of Clostridium difficile infection is still far from satisfactory as bacterial spores are resistant to many chemical agents and physical treatments. Certain types of nanoparticles have been demonstrated to exhibit anti-microbial efficacy even in multi-drug resistance bacteria. However, most of these studies failed to show biocompatibility to the mammalian host cells and no study has revealed in vivo efficacy in C. difficile infection animal models. The spores treated with 500?µg/mL Fe3-?O4 nanoparticles for 20?minutes, 64% of the spores were inhibited from transforming into vegetative cells, which was close to the results of the sodium hypochlorite-treated positive control. By cryo-electron micro-tomography, we demonstrated that Fe3-?O4 nanoparticles bind on spore surfaces and reduce the dipicolinic acid (DPA) released by the spores. In a C. difficile infection animal model, the inflammatory level triple decreased in mice with colonic C. difficile spores treated with Fe3-?O4 nanoparticles. Histopathological analysis showed a decreased intense neutrophil accumulation in the colon tissue of the Fe3-?O4 nanoparticle-treated mice. Fe3-?O4 nanoparticles, which had no influence on gut microbiota and apparent side effects in vivo, were efficacious inhibitors of C. difficile spore germination by attacking its surface and might become clinically feasible for prophylaxis and therapy.

| S-EPMC5558001 | biostudies-literature

Examining the effect of ions and proteins on the heat dissipation of iron oxide nanocrystals.

Project description:In this paper, the effect and contribution of physiological components like ions and proteins under an applied alternating magnetic field (AMF) towards heat dissipation of superparamagnetic iron oxide nanoparticles (SPIONs) are discussed. Our results have shown that under an applied AMF, magnetic hyperthermia efficiency could be significantly enhanced if SPIONs were suspended in 1× phosphate buffered saline (PBS) compared to a suspension in de-ionized (DI) water. However, no heat enhancement was found when SPIONs were suspended in blood which is an amalgamation of physiological ions and proteins. Closer investigations have revealed that the presence of physiological ions can contribute positively to heating efficiency, and the heating efficiency increases with concentration of ions, ionic mass and solubility. However, the heating efficiency of ions can be suppressed to an insignificant level (comparable with measurement error), in the presence of physiological proteins in 1×PBS. Our electrochemical studies also showed that ionic mobility can be reduced significantly if proteins were present in the solution, thus retarding the heating efficiency.

| S-EPMC9077098 | biostudies-literature

Ligand-mediated formation of Cu/metal oxide hybrid nanocrystals with tunable number of interfaces.

Project description:Combining domains of different chemical nature within the same hybrid material through the formation of heterojunctions provides the opportunity to exploit the properties of each individual component within the same nano-object; furthermore, new synergistic properties will often arise as a result of unique interface interactions. However, synthetic strategies enabling precise control over the final architecture of multicomponent objects still remain scarce for certain classes of materials. Herein, we report on the formation of Cu/MO x (M = Ce, Zn and Zr) hybrid nanocrystals with a tunable number of interfaces between the two domains. We demonstrate that the organic ligands employed during the synthesis play a key role in regulating the final configuration. Finally, we show that the synthesized nanocrystals serve as materials platforms to investigate the impact of the Cu/metal oxide interfaces in applications by focusing on the electrochemical CO2 reduction reaction as one representative example.

| S-EPMC8163200 | biostudies-literature

Mechanochemical Synthesis of Iron and Cobalt Magnetic Metal Nanoparticles and Iron/Calcium Oxide and Cobalt/Calcium Oxide Nanocomposites.

Project description:We report an environmentally benign and cost-effective method to produce Fe and Co magnetic metal nanoparticles as well as the Fe/Cao and Co/CaO nanocomposites by using a novel, dry mechanochemical process. Mechanochemical milling of metal oxides with a suitable reducing agent resulted in the production of magnetic metal nanoparticles. The process involved grinding and consequent reduction of low-costing oxide powders, unlike conventional processing techniques involving metal salts or metal complexes. Calcium granules were used as the reducing agent. Magnetometry measurements were performed over a large range of temperatures, from 10 to 1273?K, to evaluate the Curie temperature, blocking temperature, irreversibility temperature, saturation magnetization, and coercivity. The saturation magnetizations of the iron and cobalt nanoparticles were found to be 191 and 102?emu?g-1, respectively. The heating abilities of these nanoparticles suspended in several liquids under alternating magnetic fields were measured and the specific loss power was determined. Our results suggest that the dry mechanochemical process is a robust method to produce metallic nanoparticles and nanocomposites.

| S-EPMC6080568 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data