Enhanced Photocatalytic Degradation of Ternary Dyes by Copper Sulfide Nanoparticles.

ABSTRACT: We report the effect of thermolysis time on the morphological and optical properties of CuS nanoparticles prepared from Cu(II) dithiocarbamate single-source precursor. The as-prepared copper sulfide nanoparticles were used as photocatalysts for the degradation of crystal violet (CV), methylene blue (MB), rhodamine B (RhB), and a ternary mixture of the three dyes (CV/MB/RhB). Powder XRD patterns confirmed the hexagonal covellite phase for the CuS nanoparticles. At the same time, HRTEM images revealed mixed shapes with a particle size of 31.47 nm for CuS1 prepared at 30 min while CuS2 prepared at 1 h consists of mixtures of hexagonal and nanorods shaped particles with an average size of 21.59 nm. Mixed hexagonal and spherically shaped particles with a size of 17.77 nm were obtained for CuS3 prepared at 2 h. The optical bandgaps of the nanoparticles are 3.00 eV for CuS1, 3.26 eV for CuS2 and 3.13 eV for CuS3. The photocatalytic degradation efficiency showed that CuS3 with the smallest particle size is the most efficient photocatalyst and degraded 85% of CV, 100% of MB, and 81% of RhB. The as-prepared CuS showed good stability and recyclability and also degraded ternary dyes mixture (CV/MB/RhB) effectively. The byproducts of the dye degradation were evaluated using ESI-mass spectrometry.

SUBMITTER: Ajibade PA

PROVIDER: S-EPMC8398049 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Creation of an innovative composite photocatalyst, to advance its performance, has attracted researchers to the field of photocatalysis. In this article, a new photocatalyst based on polyaniline/reduced graphene oxide (PANI/RGO) composites has been prepared via the in situ oxidative polymerization method employing RGO as a template. For thermoelectric applications, though a higher percentage (50 wt %) of RGO has been used, for photocatalytic activity, lesser percentages (2, 5, and 8 wt %) of RGO in the composite have given a significant outcome. Furthermore, photoluminescence (PL) spectra, time-resolved fluorescence spectra, and Brunauer-Emmett-Teller surface area analyses confirmed the improved photocatalytic mechanism. PANI/RGO composites under visible light irradiation exhibit amazingly improved activity toward the degradation of cationic and anionic dyes in comparison with pristine PANI or RGO. Here, a PANI/RGO composite, with 5 wt % RGO(PG2), has emerged as the best combination with the degradation percentages of 99.68, 99.35, and 98.73 for malachite green, rhodamine B, and congo red within 15, 30, and 40 min, respectively. Experimental findings show that the introduction of RGO can relieve the agglomeration of PANI nanoparticles and enhance the light absorption of the materials due to an increased surface area. Moreover, the PG2 composite also showed excellent photocatalytic activity to reduce noxious Cr(VI). The effective removal of Cr(VI) up to 94.7% at pH 2 was observed within only 15 min. With the help of the active species trapping experiment, a plausible mechanism for the photocatalytic degradation has been proposed. The heightened activity of the as-synthesized composite compared to that of neat PANI or RGO was generally because of high concentrations of •OH radicals and partly of •O2 - and holes (h+) as concluded from the nitroblue tetrazolium probe test and photoluminescence experiment. It is hoped that the exceptional photocatalytic performance of our work makes the conducting polymer-based composite an effective alternative in wastewater treatment for industrial applications.

Dataset Information

Enhanced Photocatalytic Degradation of Ternary Dyes by Copper Sulfide Nanoparticles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets