Photocatalytic Degradation of Single and Binary Mixture of Brilliant Green and Rhodamine B Dyes by Zinc Sulfide Quantum Dots.

ABSTRACT: We present the preparation of octadecylamine-capped ZnS quantum dots from bis(morpholinyldithiocarbamato)Zn(II) complex. The complex was thermolyzed at 130 °C in octadecylamine at different times, to study the effect of reaction time on the morphological and photocatalytic properties of the ZnS quantum dots. Powder X-ray diffraction patterns confirmed a hexagonal wurtzite crystalline phase of ZnS, while HRTEM images showed particle sizes of about 1-3 nm, and energy band gaps of 3.68 eV (ZnS-1), 3.87 eV (ZnS-2), and 4.16 eV (ZnS-3) were obtained from the Tauc plot for the ZnS nanoparticles. The as-prepared ZnS were used as photocatalysts for the degradation of brilliant green, rhodamine B, and binary dye consisting of a mixture of brilliant green-rhodamine B. The highest photocatalytic degradation efficiency of 94% was obtained from ZnS-3 with low photoluminescence intensity. The effect of catalytic dosage and pH of the dyes solution on the photocatalytic process shows that pH 8 is optimal for the degradation of brilliant green, while pH 6.5 is the best for photocatalytic degradation of rhodamine B. The degradation of the binary dyes followed the same trends. The effect of catalytic dosage shows that 1 mg mL^-1 of the ZnS nano-photocatalyst is the optimum dosage for the degradation of organic dyes. Reusability studies show that the ZnS quantum dots can be reused five times without a significant reduction in degradation efficiency.

SUBMITTER: Ajibade PA

PROVIDER: S-EPMC8704525 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Red green blue emissive lead sulfide quantum dots: heterogeneous synthesis and applications.

Project description:Visible emission colloidal quantum dots (QDs) have shown promise in optical and optoelectronic applications. These QDs are typically composed of relatively expensive elements in the form of indium, cadmium, and gallium since alternative candidate materials exhibiting similar properties are yet to be realized. Herein, for the first time, we report red green blue (RGB) photoluminescences with quantum yields of 18% from earth-abundant lead sulfide (PbS) QDs. The visible emissive property is mainly attributed to a high degree of crystallinity even for the extremely small QD sizes (1-3 nm), which is realized by employing a heterogeneous reaction methodology at high growth temperatures (>170 °C). We demonstrate that the proposed heterogeneous synthetic method can be extended to the synthesis of other metal chalcogenide QDs, such as zinc sulfide and zinc selenide, which are promising for future industrial applications. More importantly, benefiting from the enlarged band gaps, the as-prepared PbS solar cells show an impressive open circuit voltage (∼0.8 V) beyond that reported to date.

| S-EPMC6003545 | biostudies-literature

A genome-wide approach in Arabidopsis thaliana to assess the toxicity of cadmium sulfide quantum dots

Project description:Cadmium sulfide quantum dots (CdS QDs) are widely used in novel equipment. The relevance of the research lies in the need to develop risk assessments for nanomaterials, using as basis a model plant species. Here a screen of Arabidopsis thaliana mutant lines was performed in an attempt to identify plants tolerant to CdS QDs. Two tolerant Ds insertion mutant lines (atnp01 and atnp02) were identified. A whole-genome microarray experiment showed how genes were regulated by CdS QDs. Most of the genes involved in the response to CdS QDs were related to detoxification and general metabolism. The two mutant lines treated with CdS QDs showed different patterns of gene expression. The genome-wide expression profile of seedlings of the two selected resistant mutants were acquired and compared to that of wild type seedlings using the Arabidopsis ATH1 Genome Array. The wild type seedlings were exposed to either 0 mg/L, 40 mg/L (1/2 MIC) or 80 mg/L (MIC wt) CdS QDs, and each of the resistant/tolerant mutant line plants to either 0 mg/L or 80 mg/L CdS QDs for 21 days.

2014-06-15 | E-GEOD-53989 | biostudies-arrayexpress

Atomically dispersed Ni in cadmium-zinc sulfide quantum dots for high-performance visible-light photocatalytic hydrogen production.

Project description:Catalysts with a single atom site allow highly tuning of the activity, stability, and reactivity of heterogeneous catalysts. Therefore, atomistic understanding of the pertinent mechanism is essential to simultaneously boost the intrinsic activity, site density, electron transport, and stability. Here, we report that atomically dispersed nickel (Ni) in zincblende cadmium-zinc sulfide quantum dots (ZCS QDs) delivers an efficient and durable photocatalytic performance for water splitting under sunlight. The finely tuned Ni atoms dispersed in ZCS QDs exhibit an ultrahigh photocatalytic H2 production activity of 18.87 mmol hour-1 g-1. It could be ascribed to the favorable surface engineering to achieve highly active sites of monovalent Ni(I) and the surface heterojunctions to reinforce the carrier separation owing to the suitable energy band structures, built-in electric field, and optimized surface H2 adsorption thermodynamics. This work demonstrates a synergistic regulation of the physicochemical properties of QDs for high-efficiency photocatalytic H2 production.

| S-EPMC7428344 | biostudies-literature

A genome-wide approach in Arabidopsis thaliana to assess the toxicity of cadmium sulfide quantum dots

2014-06-15 | GSE53989 | GEO

Enhanced Photocatalytic Degradation of Ternary Dyes by Copper Sulfide Nanoparticles.

Project description:We report the effect of thermolysis time on the morphological and optical properties of CuS nanoparticles prepared from Cu(II) dithiocarbamate single-source precursor. The as-prepared copper sulfide nanoparticles were used as photocatalysts for the degradation of crystal violet (CV), methylene blue (MB), rhodamine B (RhB), and a ternary mixture of the three dyes (CV/MB/RhB). Powder XRD patterns confirmed the hexagonal covellite phase for the CuS nanoparticles. At the same time, HRTEM images revealed mixed shapes with a particle size of 31.47 nm for CuS1 prepared at 30 min while CuS2 prepared at 1 h consists of mixtures of hexagonal and nanorods shaped particles with an average size of 21.59 nm. Mixed hexagonal and spherically shaped particles with a size of 17.77 nm were obtained for CuS3 prepared at 2 h. The optical bandgaps of the nanoparticles are 3.00 eV for CuS1, 3.26 eV for CuS2 and 3.13 eV for CuS3. The photocatalytic degradation efficiency showed that CuS3 with the smallest particle size is the most efficient photocatalyst and degraded 85% of CV, 100% of MB, and 81% of RhB. The as-prepared CuS showed good stability and recyclability and also degraded ternary dyes mixture (CV/MB/RhB) effectively. The byproducts of the dye degradation were evaluated using ESI-mass spectrometry.

| S-EPMC8398049 | biostudies-literature

Transcriptional profiling of E. coli cultures exposed to green or red CdTe Quantum Dots 50 µg/ml

Project description:E. coli cultures were exposed to green or red CdTe Quantum Dots 50 µg/ml during 15 min. Total RNA was extracted and cDNA labeled probes were generated by reverse transcription using Alexa 555 and Alexa 647 fluorophores. These probes were used to hybridize genomic slides containing genomic arrays to determine global transcriptional changes.

2014-12-01 | GSE58912 | GEO

Transcriptome Profile of Quantum Dots on Saccharomyces cerevisiae

Project description:Transcriptome Profile of CdSe/ZnS and InP/ZnS Quantum Dots on Saccharomyces cerevisiae

2021-01-30 | GSE165805 | GEO

Green polymeric nanomaterials for the photocatalytic degradation of dyes: a review.

Project description:Pure and drinkable water will be rarer and more expensive as the result of pollution induced by industrialisation, urbanisation and population growth. Among the numerous sources of water pollution, the textile industry has become a major issue because effluents containing dyes are often released in natural water bodies. For instance, about two years are needed to biodegrade dye-derived, carcinogenic aromatic amines, in sediments. Classical remediation methods based upon physicochemical reactions are costly and still generate sludges that contain amine residues. Nonetheless, recent research shows that nanomaterials containing biopolymers are promising to degrade organic pollutants by photocatalysis. Here, we review the synthesis and applications of biopolymeric nanomaterials for photocatalytic degradation of azo dyes. We focus on conducting biopolymers incorporating metal, metal oxide, metal/metal oxide and metal sulphide for improved biodegradation. Biopolymers can be obtained from microorganisms, plants and animals. Unlike fossil-fuel-derived polymers, biopolymers are carbon neutral and thus sustainable in the context of global warming. Biopolymers are often biodegradable and biocompatible.

| S-EPMC7293757 | biostudies-literature

Fluorescence modulation of cadmium sulfide quantum dots by azobenzene photochromic switches.

Project description:We have investigated the attachment of azobenzene photochromic switches on the modified surface of cadmium sulfide (CdS) quantum dots (QDs). The modification of CdS QDs is done by varying the concentration of the capping agent (mercaptoacetic acid) and NH3 in order to control the size of the QDs. The X-ray diffraction studies revealed that the crystallite size of CdS QDs ranged from 6 to 10?nm. The azobenzene photochromic derivatives bis(4-hydroxybenzene-1-azo)4,4'(1,1' diphenylmethane) (I) and 4,4'-diazenyldibenzoic acid (II) were synthesized and attached with surface-modified CdS QDs to make fluorophore-photochrome CdS-(I) and CdS-(II) dyad assemblies. Upon UV irradiation, the photochromic compounds (I) and (II) undergo a reversible trans-cis isomerization. The photo-induced trans-cis transformation helps to transfer photo-excited electrons from the conduction band of the CdS QDs to the lowest unoccupied molecular orbital of cis isomer of photochromic compounds (I) and (II). As a result, the fluorescence of CdS-(I) and CdS-(II) dyads is suppressed approximately five times compared to bare CdS QDs. The fluorescence modulation in such systems could help to design luminescent probes for bioimaging applications.

| S-EPMC4841658 | biostudies-literature

Observation of compositional domains within individual copper indium sulfide quantum dots.

Project description:The origin of photoluminescence in copper indium sulfide (CIS) quantum dots (Qdots) has previously been ascribed to a donor-acceptor pair (DAP) recombination, with a crystal lattice defect implicated as the origin of the donor state. In this study, electron energy-loss spectroscopy (EELS) was used to observe defect-rich compositional domains within individual CIS Qdots, supporting a model of defect-state-mediated photoluminescence for these particles, and identifying them as an ideal model system for future study of lattice defects on Qdot properties.

| S-EPMC5048650 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data