Preparation and Application of Fluorine-Free Finishing Agent with Excellent Water Repellency for Cotton Fabric.

ABSTRACT: Water repellent is an important functional finish for cotton fabric. However, cotton fabrics often have poor washing resistance and other performances after actual finishing. In this study, based on the structural characteristics of cotton fiber and durability of water repellent, a cross-linked amino long-chain alkyl polysiloxane (CAHPS) was first prepared, and then reacted with modified silica. Finally, a chemically bonded organic-inorganic nanohybrid cross-linked polysiloxane (rSiO₂-CAHPS) was fabricated. Furthermore, the rSiO₂-CAHPS was emulsified to obtain a durable fluorine-free water repellent. The water repellent finishing for cotton fabric was carried out by the pad-dry-cure process. After finishing, the cotton fabric had good resistance to conventional liquids and excellent washing resistance, and still maintained good water repellency after 30 rounds of soaping. Moreover, properties including air permeability, mechanical property and whiteness are hardly affected after finishing. SEM and XPS characterization show that a layer of dense silicon film is formed on the surface of cotton fabric by rSiO₂-CAHPS water repellent. The existence of nanosilica can improve the surface roughness of cotton fibers. The synergistic effect of fiber matrix, nanoparticles and CAHPS endows the fabric with a micro/nano-multi-scale micro-rough structure, which improves the water repellency of cotton fabric after water repellent finishing.

SUBMITTER: Yu C

PROVIDER: S-EPMC8433999 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Multifunctional Finishing of Cotton Fabric with Curcumin Derivatives Coatings Obtained by Sol-Gel Method.

Project description:Textile materials with fluorescent, repellent, or antimicrobial properties are increasingly used in common applications. Obtaining multi-functional coatings is of wide interest, especially for applications related to signaling or to the medical field. In order to increase the performance (color properties, fluorescence lifetime, self-cleaning or antimicrobial properties) of textile materials with special uses, a series of research was carried out regarding the modification of surfaces with nanosols. In this study, coatings with multiple properties were obtained by depositing nanosols on cotton fabrics generated through sol-gel reactions. These multifunctional coatings are hybrid materials in which the host matrix is generated using tetraethylorthosilicate (TEOS) and network modifying organosilanes:dimethoxydimethylsilane (DMDMS) or dimethoxydiphenylsilane (DMDPS) in a 1:1 mass ratio. Two curcumin derivatives were embedded in siloxane matrices, a yellow one (CY) that is identical to bis-demethoxycurcumin (one of the natural constituents in turmeric) and a red dye (CR) that has a N,N-dimethylamino group grafted in position 4 of the dicinnamoylmethane skeleton of curcumin. The nanocomposites obtained by embedding curcumin derivatives in siloxane matrices were deposited on cotton fabric and studied in relation to the dye and the type of host matrix. Fabrics coated with such systems provide a hydrophobic surface, have fluorescent and antimicrobial properties, change color depending on the pH, and therefore can be used in various fields where textiles provide signaling properties, self-cleaning, or antibacterial protection. The coated fabrics maintained their good multifunctional properties even after several washing cycles.

| S-EPMC10217195 | biostudies-literature

Cross-Linking Strategies for Fluorine-Containing Polymer Coatings for Durable Resistant Water- and Oil-Repellency.

Project description:Functional coatings for application on surfaces are of growing interest. Especially in the textile industry, durable water and oil repellent finishes are of special demand for implementation in the outdoor sector, but also as safety-protection clothes against oil or chemicals. Such oil and chemical repellent textiles can be achieved by coating surfaces with fluoropolymers. As many concerns exist regarding (per)fluorinated polymers due to their high persistence and accumulation capacity in the environment, a durable and resistant coating is essential also during the washing processes of textiles. Within the present study, different strategies are examined for a durable resistant cross-linking of a novel fluoropolymer on the surface of fibers. The monomer 2-((1,1,2-trifluoro-2-(perfluoropropoxy)ethyl)thio)ethyl acrylate, whose fluorinated side-chain is degradable by treatment with ozone, was used for this purpose. The polymers were synthesized via free radical polymerization in emulsion, and different amounts of cross-linking reagents were copolymerized. The final polymer dispersions were applied to cellulose fibers and the cross-linking was induced thermally or by irradiation with UV-light. In order to investigate the cross-linking efficiency, tensile elongation studies were carried out. In addition, multiple washing processes of the fibers was performed and the polymer loss during washing, as well as the effects on oil and water repellency were investigated. The cross-linking strategy paves the way to a durable fluoropolymer-based functional coating and the polymers are expected to provide a promising and sustainable alternative to functional coatings.

| S-EPMC7956606 | biostudies-literature

Application of Plasma Activation in Flame-Retardant Treatment for Cotton Fabric.

Project description:Cotton fabric treated by Pyrovatex CP New (PCN) and Knittex FFRC (K-FFRC) using the Pad-dry-cure method showed an excellent fire-retardant effect. However, it needed to be cured at high temperatures for a long time leading to a high loss of mechanical strength. In this study, atmospheric-pressure dielectric barrier discharge (APDBD) plasma was applied to the cotton fabric, which then was treated by flame retardants (FRs) using the pad-dry-cure method. The purpose was to have a flame-retardant cotton fabric (limiting oxygen index (LOI) ≥ 25) and a mechanical loss of the treated fabric due to the curing step as low as possible. To achieve this goal, 10 experiments were performed. The vertical flammability characteristics, LOI value and tensile strength of the treated fabrics were measured. A response model between the LOI values of the treated fabric and two studied variables (temperature and time of the curing step) was found. It was predicted that the optimal temperature and time-to-cure to achieve LOI of 25 was at 160 °C for 90 s, while the flame-retardant treatment process without plasma pretreatment, was at 180 °C and 114 s. Although the curing temperature and the time have decreased significantly, the loss of mechanical strength of the treated fabric is still high. The tensile strength and scanning electron microscopy (SEM) images of the fabric after plasma activation show that the plasma treatment itself also damages the mechanical strength of the fabric. X-ray photoelectron spectroscopy (XPS) spectra of the fabric after plasma activation and energy-dispersive spectroscopy (EDS) analysis of the flame retardant-treated (FRT) fabric clarified the role of plasma activation in this study.

| S-EPMC7408165 | biostudies-literature

Cost-effective fabrication, antibacterial application and cell viability studies of modified nonwoven cotton fabric.

Project description:In the present work, nonwoven cotton fabric was modified for antibacterial applications using low-cost and eco-friendly precursors. The treatment of fabric with alkali leads to the formation of active sites for surface modification, followed by dip coating with silver nanoparticles and chitosan. The surface was chlorinated in the next step to transform amide (N-H) groups in chitosan into N-halamine (N-Cl). The modified and unmodified surfaces of the nonwoven cotton fabric have been characterized by FTIR, SEM, and XRD. The active chlorine loading is measured with iodine/sodium thiosulphate. The antimicrobial activity and cell toxicity assay were carried out with and without modifications of nonwoven cotton fabric. The antimicrobial efficacies of loaded fabric were evaluated against four bacterial species (Micrococcus luteus, Staphylococcus aureus, Enterobacter aerogenes, and E.coli). It was found that modified fabric exhibited superior efficiency against gram-positive and gram-negative bacterial strains as compared to their bulk counterparts upon exposure without affecting strength and integrity of fabric. The overall process is economical for commercial purposes. The modified fabric can be used for antimicrobial, health, and food packaging industries, and in other biomedical applications.

| S-EPMC8847346 | biostudies-literature

Certain Soil Surfactants Could Become a Source of Soil Water Repellency after Repeated Application.

Project description:Repeated application of soil surfactants, or wetting agents, is a common practice for alleviating soil water repellency associated with soil organic coatings. However, wetting agents are organic compounds that may also coat soil particle surfaces and reduce wettability. For this experiment, hydrophobic sands from the field and fresh, wettable sands were collected and treated with either a polyoxyalkylene polymer (PoAP) or alkyl block polymer (ABP) wetting agent, or water only treatments served as a control. Following repeated treatment application and sequential washings, dissolved and particulate organic carbon (OC) were detected in the leachates of both sand systems. The total amount of OC recovered in leachates was 88% or less than the OC introduced by the wetting agents, indicating sorption of wetting agent monomers to soil particle surfaces regardless of soil hydrophobicity status. While ABP treatment did not alter solid phase organic carbon (SOC) in the sands studied, PoAP application increased SOC by 16% and 45% which was visible in scanning electronic microscopy images, for hydrophobic and wettable sands, respectively. PoAP application also increased the hydrophobicity of both sands that were studied. In contrast, ABP treatment increased the wettability of hydrophobic sand. Our results provide strong evidence that certain wetting agents may increase soil hydrophobicity and exacerbate wettability challenges if used repeatedly over time.

| S-EPMC8538948 | biostudies-literature

The pectinolytic activity of Burkholderia cepacia and its application in the bioscouring of cotton knit fabric.

Project description:BackgroundEnzymatic catalysis in different industrial applications is often preferred over chemical methods due to various advantages, such as higher specificity, greater efficiency, and less environmental footprint. Pectinases are a group of enzymes that catalyze the degradation of pectic compounds, the key components of plant middle lamella and the primary cell wall. Pectinases have found applications in multiple industrial processes, including cotton bioscouring, fruit juice extraction and its clarification, plant fiber degumming, paper making, plant biomass liquefaction, and saccharification, among others. The purpose of this study was to taxonomically characterize a bacterial species exhibiting pectinolytic activities and assess its pectinolytic activity qualitatively and quantitatively, as well as test its bioscouring potential.ResultsHere, we report that Burkholderia cepacia, a previously unknown species with pectinolytic activity, exerts such activity comparable to commercially used pectinase enzymes in the textile industry, but requires less temperature for activity.ConclusionQuantitative evaluation of enzyme activity indicates the potential of the bacterial species for use in the bioscouring of cotton knit fabric.

| S-EPMC10667187 | biostudies-literature

Surface Modification of Cotton Fabric Using TiO2 Nanoparticles for Self-Cleaning, Oil-Water Separation, Antistain, Anti-Water Absorption, and Antibacterial Properties.

Project description:Superhydrophobicity is of interest for practical applications such as water repellency, self-cleaning, stain resistance, antibacterial properties, and oil-water separation. In this work, a superhydrophobic coating on cotton fabric is prepared by simple immersion in TiO2 nanoparticles and perfluorodecyltriethoxysilane solution. Its antiwetting properties, surface morphology, and functionality are characterized. The cotton fabric shows superhydrophobicity with a water static contact angle of 169.3 ± 2.1° and tilt angle of 6.3 ± 2.0°. The coating is also characterized by performing stability tests, and it shows excellent mechanical durability, chemical stability, and thermal stability. Additionally, the water droplet dynamic on the coated surface is also studied. The coated cotton fabric exhibits excellent self-cleaning, stain resistance, rust stain resistance, anti-water absorption, and antibacterial properties. It can also be used in oil-water separation with a high separation efficiency and excellent reusability.

| S-EPMC7160840 | biostudies-literature

Preliminary Studies on the Application of Grape Seed Extract in the Dyeing and Functional Modification of Cotton Fabric.

Project description:Cotton has the shortcomings of having no antibacterial, antioxidant and ultraviolet (UV) protection properties, which are of great importance for health protection purposes. In the present study, grape seed extract (GSE) mainly composed of proanthocyanins (tannins) was employed to simultaneously import pale colors and the three aforementioned functions to cotton fabric. The tests on the application conditions of GSE showed that pH and GSE concentration had great impact on the color depth of cotton fabric, and the color hue of dyed fabric could be controlled in the absence of pH regulators due to the weakly acidic nature of GSE solution. The fabric dyed with 10%owf (on the weight of fabric) GSE exhibited an excellent inhibition effect towards Escherichia coli, whereas the one dyed with 20%owf GSE had high antioxidant activity of 97%. The fabric dyed with 5%owf GSE offered excellent UV protection. This study reveals that GSE can be used as a functional finishing agent for health protection in cotton textiles in addition to coloration capability.

| S-EPMC7072231 | biostudies-literature

Complementary Assessment of Commercial Photoluminescent Pigments Printed on Cotton Fabric.

Project description:The presented study focuses on photoluminescent pigments applied on cotton fabric by a screen-printed procedure using polydimethylsiloxane (PDMS) as a binder. Microscopic data depicts irregular shapes and relatively wide size distribution (3-80 µm) of pigments. Regarding composition, the Energy-Dispersive X-ray (EDX) and Fourier Transform Infrared (FTIR) spectroscopy data complement findings suggesting the presence of Eu-doped strontium aluminate in the yellow-green, calcium aluminate in the violet pigment, and metal oxides in the blue pigment. The optical properties of pigment-enriched PDMS-coated cotton fabric were assessed and reflectance intensity was found to be concentration-dependent only in the blue pigment. The luminescence decay data show that luminescence intensity decreased with the reduction of pigment concentration in the following order, yellow-green > blue > violet pigments. Relying on absorption and emission data of powdered pigments, the confocal microscopy enables visualization of the pigments' distribution within a 3D image projection. This identifies the most homogeneous distribution in the case of the blue pigment, as well as the presence of a continuous fluorescing signal in the z projection when 5% pigment was used. This was, for the first time, presented as a powerful tool for non-destructive visualization of photoluminescent pigments' spatial distribution when printed on textile (cotton) fabric. Finally, the photoluminescent PDMS coating demonstrates high washing and abrasion resistance, contributing to overall functionality of printed cotton fabrics when commercial types of pigments are applied.

| S-EPMC6680420 | biostudies-literature

Environmental-friendly regenerated lignocellulose functionalized cotton fabric to prepare multi-functional degradable membrane for efficient oil-water separation and solar seawater desalination.

Project description:Freshwater pollution and shortage have become an imminent problem. Therefore, it is necessary to develop a multi-functional membrane for the production of fresh water. In this work, the regenerated lignocellulose modified cotton fabric was developed as a novel, multi-functional and degradable membrane (LCPT@CF) for efficient oil-water separation and solar steam generation for the first time. The fabrication method has the merits of simple, environmentally friendly and cost effective. The regenerated lignocellulose was adhered on the surface of cotton fabric by tannic acid and polyvinyl alcohol complexes tightly, and the multilayered structures of the LCPT@CF can be formed, which endowed the membranes with underwater superoleophobic property and durability. The underwater superoleophobic property enabled LCPT@CF to purify various kinds of oil-in-water emulsions with a separation efficiency of more than 99.90%. Moreover, benefiting from the excellent photothermal conversion capacity of regenerated lignocellulose, the LCPT@CF achieved high evaporation rate of 1.39 kg m-2 h-1 and favorable evaporation efficiency of 84% under 1 sun illumination, and the LCPT@CF also presented excellent salt-resistance for evaporating seawater for 20 cycles, without salt accumulation. More importantly, the LCPT@CF could be naturally degradable by microorganisms in the natural condition within 3 months, which had outstanding environmental friendliness. These above results demonstrated that the green and efficient LCPT@CF could play great potential in oil-water separation and sewage purification.

| S-EPMC10066188 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data