Reversible Magnesium Metal Anode Enabled by Cooperative Solvation/Surface Engineering in Carbonate Electrolytes.

ABSTRACT: Magnesium metal anode holds great potentials toward future high energy and safe rechargeable magnesium battery technology due to its divalent redox and dendrite-free nature. Electrolytes based on Lewis acid chemistry enable the reversible Mg plating/stripping, while they fail to match most cathode materials toward high-voltage magnesium batteries. Herein, reversible Mg plating/stripping is achieved in conventional carbonate electrolytes enabled by the cooperative solvation/surface engineering. Strongly electronegative Cl from the MgCl₂ additive of electrolyte impairs the Mg…O = C interaction to reduce the Mg²⁺ desolvation barrier for accelerated redox kinetics, while the Mg²⁺-conducting polymer coating on the Mg surface ensures the facile Mg²⁺ migration and the effective isolation of electrolytes. As a result, reversible plating and stripping of Mg is demonstrated with a low overpotential of 0.7 V up to 2000 cycles. Moreover, benefitting from the wide electrochemical window of carbonate electrolytes, high-voltage (> 2.0 V) rechargeable magnesium batteries are achieved through assembling the electrode couple of Mg metal anode and Prussian blue-based cathodes. The present work provides a cooperative engineering strategy to promote the application of magnesium anode in carbonate electrolytes toward high energy rechargeable batteries.

SUBMITTER: Wang C

PROVIDER: S-EPMC8440703 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Highly reversible Zn metal anode enabled by sustainable hydroxyl chemistry.

Project description:Rechargeable Zn metal batteries (RZMBs) may provide a more sustainable and lower-cost alternative to established battery technologies in meeting energy storage applications of the future. However, the most promising electrolytes for RZMBs are generally aqueous and require high concentrations of salt(s) to bring efficiencies toward commercially viable levels and mitigate water-originated parasitic reactions including hydrogen evolution and corrosion. Electrolytes based on nonaqueous solvents are promising for avoiding these issues, but full cell performance demonstrations with solvents other than water have been very limited. To address these challenges, we investigated MeOH as an alternative electrolyte solvent. These MeOH-based electrolytes exhibited exceptional Zn reversibility over a wide temperature range, with a Coulombic efficiency > 99.5% at 50% Zn utilization without cell short-circuit behavior for > 1,800 h. More important, this remarkable performance translates well to Zn || metal-free organic cathode full cells, supporting < 6% capacity decay after > 800 cycles at -40 °C.

| S-EPMC9214537 | biostudies-literature

Solubility-mediated sustained release enabling nitrate additive in carbonate electrolytes for stable lithium metal anode.

Project description:The physiochemical properties of the solid-electrolyte interphase, primarily governed by electrolyte composition, have a profound impact on the electrochemical cycling of metallic lithium. Herein, we discover that the effect of nitrate anions on regulating lithium deposition previously known in ether-based electrolytes can be extended to carbonate-based systems, which dramatically alters the nuclei from dendritic to spherical, albeit extremely limited solubility. This is attributed to the preferential reduction of nitrate during solid-electrolyte interphase formation, and the mechanisms behind which are investigated based on the structure, ion-transport properties, and charge transfer kinetics of the modified interfacial environment. To overcome the solubility barrier, a solubility-mediated sustained-release methodology is introduced, in which nitrate nanoparticles are encapsulated in porous polymer gel and can be steadily dissolved during battery operation to maintain a high concentration at the electroplating front. As such, effective dendrite suppression and remarkably enhanced cycling stability are achieved in corrosive carbonate electrolytes.

| S-EPMC6128910 | biostudies-literature

A highly reversible lithium metal anode.

Project description:Lithium metal has shown a lot of promise for use as an anode material in rechargeable batteries owing to its high theoretical capacity. However, it does not meet the cycle life and safety requirements of rechargeable batteries owing to electrolyte decomposition and dendrite formation on the surfaces of the lithium anodes during electrochemical cycling. Here, we propose a novel electrolyte system that is relatively stable against lithium metal and mitigates dendritic growth. Systematic design methods that combined simulations, model-based experiments, and in situ analyses were employed to design the system. The reduction potential of the solvent, the size of the salt anions, and the viscosity of the electrolyte were found to be critical parameters determining the rate of dendritic growth. A lithium metal anode in contact with the designed electrolyte exhibited remarkable cyclability (more than 100 cycles) at a high areal capacity of 12 mAh cm(-2).

| S-EPMC5379181 | biostudies-literature

Sensing Leakage of Electrolytes from Magnesium Batteries Enabled by Natural AIEgens.

Project description:The potential for leakage of liquid electrolytes from magnesium (Mg) batteries represents a large hurdle to future application. Despite this, there are no efficient sensing technologies to detect the leakage of liquid electrolytes. Here, we developed a sensor using laccaic acid (L-AIEgen), a naturally occurring aggregation-induced emission luminogen (AIEgens) isolated from the beetle Laccifer lacca. L-AIEgen showed good selectivity and sensitivity for Mg2+, a universal component of electrolytes in Mg batteries. Using L-AIEgen, we then produced a smart film (L-AIE-F) that was able to sense leakage of electrolytes from Mg batteries. L-AIE-F showed a strong "turn-on" AIE-active fluorescence at the leakage point of electrolyte from model Mg batteries. To the best of our knowledge, this is the first time that AIE technology has been used to sense the leakage of electrolytes.

| S-EPMC9499604 | biostudies-literature

A Highly Reversible Room-Temperature Sodium Metal Anode.

Project description:Owing to its low cost and high natural abundance, sodium metal is among the most promising anode materials for energy storage technologies beyond lithium ion batteries. However, room-temperature sodium metal anodes suffer from poor reversibility during long-term plating and stripping, mainly due to formation of nonuniform solid electrolyte interphase as well as dendritic growth of sodium metal. Herein we report for the first time that a simple liquid electrolyte, sodium hexafluorophosphate in glymes (mono-, di-, and tetraglyme), can enable highly reversible and nondendritic plating-stripping of sodium metal anodes at room temperature. High average Coulombic efficiencies of 99.9% were achieved over 300 plating-stripping cycles at 0.5 mA cm(-2). The long-term reversibility was found to arise from the formation of a uniform, inorganic solid electrolyte interphase made of sodium oxide and sodium fluoride, which is highly impermeable to electrolyte solvent and conducive to nondendritic growth. As a proof of concept, we also demonstrate a room-temperature sodium-sulfur battery using this class of electrolytes, paving the way for the development of next-generation, sodium-based energy storage technologies.

| S-EPMC4827673 | biostudies-literature

An ultrastable lithium metal anode enabled by designed metal fluoride spansules.

Project description:The lithium metal anode (LMA) is considered as a promising star for next-generation high-energy density batteries but is still hampered by the severe growth of uncontrollable lithium dendrites. Here, we design "spansules" made of NaMg(Mn)F3@C core@shell microstructures as the matrix for the LMA, which can offer a long-lasting release of functional ions into the electrolyte. By the assistance of cryogenic transmission electron microscopy, we reveal that an in situ-formed metal layer and a unique LiF-involved bilayer structure on the Li/electrolyte interface would be beneficial for effectively suppressing the growth of lithium dendrites. As a result, the spansule-modified anode affords a high Coulombic efficiency of 98% for over 1000 cycles at a current density of 2 mA cm-2, which is the most stable LMA reported so far. When coupling this anode with the Li[Ni0.8Co0.1Mn0.1]O2 cathode, the practical full cell further exhibits highly improved capacity retention after 500 cycles.

| S-EPMC7060059 | biostudies-literature

The solvation structure, transport properties and reduction behavior of carbonate-based electrolytes of lithium-ion batteries.

Project description:Despite the extensive employment of binary/ternary mixed-carbonate electrolytes (MCEs) for Li-ion batteries, the role of each ingredient with regards to the solvation structure, transport properties, and reduction behavior is not fully understood. Herein, we report the atomistic modeling and transport property measurements of the Gen2 (1.2 M LiPF6 in ethylene carbonate (EC) and ethyl methyl carbonate (EMC)) and EC-base (1.2 M LiPF6 in EC) electrolytes, as well as their mixtures with 10 mol% fluoroethylene carbonate (FEC). Due to the mixing of cyclic and linear carbonates, the Gen2 electrolyte is found to have a 60% lower ion dissociation rate and a 44% faster Li+ self-diffusion rate than the EC-base electrolyte, while the total ionic conductivities are similar. Moreover, we propose for the first time the anion-solvent exchange mechanism in MCEs with identified energetic and electrostatic origins. For electrolytes with additive, up to 25% FEC coordinates with Li+, which exhibits a preferential reduction that helps passivate the anode and facilitates an improved solid electrolyte interphase. The work provides a coherent computational framework for evaluating mixed electrolyte systems.

| S-EPMC8597828 | biostudies-literature

Interface solvation regulation stabilizing the Zn metal anode in aqueous Zn batteries.

Project description:The Zn metal anode experiences dendritic growth and side reactions in aqueous zinc batteries. The regulation of the interface environment would provide efficient modification without largely affecting the aqueous nature of bulk electrolytes. Herein, we show that the ethylene carbonate (EC) additive is able to adsorb on the Zn surface from the ZnSO4 electrolyte. Together with the higher dielectric constant of EC than water, Zn2+ preferentially forms EC-rich solvation structures at the interface even with a low overall EC content of 4%. An inorganic-organic solid-electrolyte interface (SEI) is also generated. Thanks to the increased energy levels of the lowest unoccupied molecular orbital of EC-rich solvation structures and the stable SEI, side reactions are suppressed and the Zn2+ transference number increases to allow uniform Zn growth. As a result, the cycle life of Zn stripping/plating in symmetric Zn cells extends from 108 h to 1800 h after the addition of 4% EC. Stable cycling for 180 h is realized with 35% depth of discharge in the 4% EC electrolyte, superior to the initial cell failure with EC-free electrolyte. The capacity retention of the Zn//V6O13·H2O full cell with N/P = 1.3 also increases from 51.1% to 80.5% after 500 cycles with the help of EC.

| S-EPMC10395310 | biostudies-literature

Correlation between Redox Potential and Solvation Structure in Biphasic Electrolytes for Li Metal Batteries.

Project description:The activity of lithium ions in electrolytes depends on their solvation structures. However, the understanding of changes in Li+ activity is still elusive in terms of interactions between lithium ions and solvent molecules. Herein, the chelating effect of lithium ion by forming [Li(15C5)]+ gives rise to a decrease in Li+ activity, leading to the negative potential shift of Li metal anode. Moreover, weakly solvating lithium ions in ionic liquids, such as [Li(TFSI)2 ]- (TFSI = bis(trifluoromethanesulfonyl)imide), increase in Li+ activity, resulting in the positive potential shift of LiFePO4 cathode. This allows the development of innovative high energy density Li metal batteries, such as 3.8 V class Li | LiFePO4 cells, along with introducing stable biphasic electrolytes. In addition, correlation between Li+ activity, cell potential shift, and Li+ solvation structure is investigated by comparing solvated Li+ ions with carbonate solvents, chelated Li+ ions with cyclic and linear ethers, and weakly solvating Li+ ions in ionic liquids. These findings elucidate a broader understanding of the complex origin of Li+ activity and provide an opportunity to achieve high energy density lithium metal batteries.

| S-EPMC9685466 | biostudies-literature

Fluorine-donating electrolytes enable highly reversible 5-V-class Li metal batteries.

Project description:Lithium metal has gravimetric capacity ?10× that of graphite which incentivizes rechargeable Li metal batteries (RLMB) development. A key factor that limits practical use of RLMB is morphological instability of Li metal anode upon electrodeposition, reflected by the uncontrolled area growth of solid-electrolyte interphase that traps cyclable Li, quantified by the Coulombic inefficiency (CI). Here we show that CI decreases approximately exponentially with increasing donatable fluorine concentration of the electrolyte. By using up to 7 m of Li bis(fluorosulfonyl)imide in fluoroethylene carbonate, where both the solvent and the salt donate F, we can significantly suppress anode porosity and improve the Coulombic efficiency to 99.64%. The electrolyte demonstrates excellent compatibility with 5-V LiNi0.5Mn1.5O4 cathode and Al current collector beyond 5 V. As a result, an RLMB full cell with only 1.4× excess lithium as the anode was demonstrated to cycle above 130 times, at industrially significant loading of 1.83 mAh/cm2 and 0.36 C. This is attributed to the formation of a protective LiF nanolayer, which has a wide bandgap, high surface energy, and small Burgers vector, making it ductile at room temperature and less likely to rupture in electrodeposition.

| S-EPMC5819397 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data