Multifunctionality of Nanosized Calcium Apatite Dual-Doped with Li⁺/Eu³⁺ Ions Related to Cell Culture Studies and Cytotoxicity Evaluation In Vitro.

ABSTRACT: Li⁺/Eu³⁺ dual-doped calcium apatite analogues were fabricated using a microwave stimulated hydrothermal technique. XRPD, FT-IR, micro-Raman spectroscopy, TEM and SAED measurements indicated that obtained apatites are single-phased, crystallize with a hexagonal structure, have similar morphology and nanometric size as well as show red luminescence. Lithium effectively modifies the local symmetry of optical active sites and, thus, affects the emission efficiency. Moreover, the hydrodynamic size and surface charge of the nanoparticles have been extensively studied. The protein adsorption (lysozyme, LSZ; bovine serum albumin, BSA) on the nanoparticle surface depended on the type of cationic dopant (Li⁺, Eu³⁺) and anionic group (OH^-, Cl^-, F^-) of the apatite matrix. Interaction with LSZ resulted in a positive zeta potential, and the nanoparticles had the lowest hydrodynamic size in this protein medium. The cytotoxicity assessment was carried out on the human osteosarcoma cell line (U2OS), murine macrophages (J774.E), as well as human red blood cells (RBCs). The studied apatites were not cytotoxic to RBCs and J774.E cells; however, at higher concentrations of nanoparticles, cytotoxicity was observed against the U2OS cell line. No antimicrobial activity was detected against Gram-negative bacteria with one exception for P. aeruginosa treated with Li⁺-doped fluorapatite.

SUBMITTER: Sobierajska P

PROVIDER: S-EPMC8466056 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A Study of Vanadate Group Substitution into Nanosized Hydroxyapatite Doped with Eu3+ Ions as a Potential Tissue Replacement Material.

Project description:In this study, nanosized vanadate-substituted hydroxyapatites doped with 1 mol% and 2 mol% Eu3+ ions were obtained via the precipitation method. To evaluate the structure and morphology of the obtained compounds, the XRPD (X-ray powder diffraction) technique, Rietveld refinement, SEM-EDS (scanning electron microscopy-energy-dispersive spectrometry) and TEM (transmission electron microscopy) techniques as well as FTIR (Fourier transform infrared) spectroscopy were performed. Moreover, the chemical formula was confirmed using the ICP-OES (Inductively coupled plasma optical emission spectroscopy spectroscopy). The calculated average grain size for powders was in the range of 25 to 90 nm. The luminescence properties of vanadium-substituted hydroxyapatite were evaluated by recording emission spectra and excitation spectra as well as luminescence kinetics. The crucial step of this research was the evaluation of the biocompatibility of the synthesized nanomaterials. Therefore, the obtained compounds were tested toward sheep red blood cells and normal human dermal fibroblast to confirm the nontoxicity and biocompatibility of new nanosized Eu3+ ion-doped vanadate-hydroxyapatite. Moreover, the final step of the research allowed us to determine the time dependent ion release to the simulated body fluid environment. The study confirmed cytocompatibility of vanadium hydroxyapatite doped with Eu3+ ions.

| S-EPMC8746586 | biostudies-literature

Investigation of Physicochemical Properties of the Structurally Modified Nanosized Silicate-Substituted Hydroxyapatite Co-Doped with Eu3+ and Sr2+ Ions.

Project description:In this paper, a series of structurally modified silicate-substituted apatite co-doped with Sr2+ and Eu3+ ions were synthesized by a microwave-assisted hydrothermal method. The concentration of Sr2+ ions was set at 2 mol% and Eu3+ ions were established in the range of 0.5-2 mol% in a molar ratio of calcium ion amount. The XRD (X-ray powder diffraction) technique and infrared (FT-IR) spectroscopy were used to characterize the obtained materials. The Kröger-Vink notation was used to explain the possible charge compensation mechanism. Moreover, the study of the spectroscopic properties (emission, emission excitation and emission kinetics) of the obtained materials as a function of optically active ions and annealing temperature was carried out. The luminescence behavior of Eu3+ ions in the apatite matrix was verified by the Judd-Ofelt (J-O) theory and discussed in detail. The temperature-dependent emission spectra were recorded for the representative materials. Furthermore, the International Commission on Illumination (CIE) chromaticity coordinates and correlated color temperature were determined by the obtained results.

| S-EPMC7823659 | biostudies-literature

Thermal Evolutions to Glass-Ceramics Bearing Calcium Tungstate Crystals in Borate Glasses Doped with Photoluminescent Eu3+ Ions.

Project description:Thermal evolutions of calcium-tungstate-borate glasses were investigated for the development of luminescent glass-ceramics by using Eu3+ dopant in a borate glass matrix with calcium tungstate, which was expected to have a combined character of glass and ceramics. This study revealed that single-phase precipitation of CaWO4 crystals in borate glass matrix was possible by heat-treatment at a temperature higher than glass transition temperature Tg for (100-x) (33CaO-67B2O3)-xCa3WO6 (x = 8-15 mol%). Additionally, the crystallization of CaWO4 was found by Raman spectroscopy due to the formation of W=O double bondings of WO4 tetrahedra in the pristine glass despite starting with the higher calcium content of Ca3WO6. Eu3+ ions were excluded from the CaWO4 crystals and positioned in the borate glass phase as a stable site for them, which provided local environments in higher symmetry around Eu3+ ions.

| S-EPMC7922195 | biostudies-literature

Enhancement of Eu3+ Emission in YVO4:Eu3+ Nanocrystals by Li+ Codoping: An Oxidant-Resistant Dispersion and Polymer Film.

Project description:The enhancement of red emission of YVO4:Eu3+ nanocrystals by Li+ codoping has been achieved. The effect of Li+ codoping on the crystalline properties and the luminescence of Eu3+ has been thoroughly studied. An increase of the unit cell volume and crystallinity of the nanocrystals is observed as the concentration of Li+ codoping increases. The lattice expansion could be related to occupation of the interstitial sites by the Li+ ions. The nanocrystals appear to be assemblies of rodlike nanostructures along with cube-shaped rough nanostructures of uniform size. The optimum concentration of Li+ codoping for luminescence enhancement is found to be 5 at. % at which Eu3+ emission is increased by about 2.5 times. The fall in Eu3+ emission after codoping of Li+ (7-15 at. %) is observed. Is it the increased crystallinity (i.e., the size) or the lattice expansion that poses a limit to luminescence enhancement? Annealing at 500 and 850 °C increased the luminescence emission by threefold and fivefold, respectively. The samples are readily dispersible in deionized water and incorporated easily in the flexible polymer film made of polyvinylidene fluoride. The dispersion-in-water shows bright red luminescence as low as 50 ?g/mL. The emission intensity of the dispersion decreases linearly with concentration with a slope almost equal to unity. The dispersion and the flexible film do not show luminescence degradation under the influence of oxidizing H2O2 medium. The oxidant-resistant nature with enhanced luminescence could serve as a suitable red emitter for lighting and display applications.

| S-EPMC6714512 | biostudies-literature

Copper-Doped Biphasic Calcium Phosphate Powders: Dopant Release, Cytotoxicity and Antibacterial Properties.

Project description:Cytotoxicity and antibacterial properties associated with the dopant release of Cu-doped Biphasic Calcium Phosphate (BCP) powders, mainly composed of hydroxyapatite mixed with β-tricalcium phosphate powders, were investigated. Twelve BCP ceramics were synthesized at three different sintering temperatures (600 °C, 900 °C and 1200 °C) and four copper doping rates (x = 0.0, 0.05, 0.10 and 0.20, corresponding to the stoichiometric amount of copper in Ca10Cux(PO4)6(OH)2-2xO2x). Cytotoxicity assessments of Cu-doped BCP powders, using MTT assay with human-Mesenchymal Stem Cells (h-MSCs), indicated no cytotoxicity and the release of less than 12 ppm of copper into the biological medium. The antibacterial activity of the powders was determined against both Gram-positive (methicillin-sensitive (MS) and methicillin resistant (MR) Staphylococcus aureus) and Gram-negative (Escherichia coli and Pseudomonas aeruginosa) bacteria. The Cu-doped biomaterials exhibited a strong antibacterial activity against MSSA, MRSA and E. coli, releasing approximatively 2.5 ppm after 24 h, whereas 10 ppm were required to induce an antibacterial effect against P. aeruginosa. This study also demonstrated that the culture medium used during experiments can directly impact the antibacterial effect observed; only 4 ppm of Cu2+ were effective for killing all the bacteria in a 1:500 diluted TS medium, whereas 20 ppm were necessary to achieve the same result in a rich, non-diluted standard marrow cell culture medium.

| S-EPMC8124198 | biostudies-literature

Eu3+, Tb3+- and Er3+, Yb3+-Doped α-MoO3 Nanosheets for Optical Luminescent Thermometry.

Project description:Here we report a novel synthesis approach for the preparation of α-MoO3:Ln3+ materials employing a two-step synthesis. Additionally, in this work the α-MoO3:Ln3+ materials are reported as potential optical thermometers for the first time. In this synthesis approach, first MoS2 2D nanosheets were prepared, which were further heat treated to obtain α-MoO3. These materials were fully characterized by powder X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray fluorescence (XRF), thermogravimetry (TG) and differential thermal analysis (DTA), transmission electron microscopy (TEM), and luminescence spectroscopy. Temperature-dependent luminescence measurements were carried out to determine the optical thermometric properties of two different types of α-MoO3:Ln3+ materials (Eu3+/Tb3+ downshifting and Er3+/Yb3+ upconversion luminescence systems). We demonstrate in this study that this class of material could be a potential candidate for temperature-sensing applications.

| S-EPMC6524054 | biostudies-literature

Eu-Doped Citrate-Coated Carbonated Apatite Luminescent Nanoprobes for Drug Delivery.

Project description:In the field of Nanomedicine, there is an increasing demand for new inorganic nanophosphors with low cytotoxicity and efficient loading-release ability of drugs for applications in bioimaging and drug delivery. This work assesses the potentiality of matured Eu-doped citrate-coated carbonated apatite nanoparticles to be used as theranostic platforms, for bioimaging, as luminescent nanoprobes, and for drug delivery applications, using Doxorubicin as a model drug. The drug adsorption isotherm fits the Langmuir-Freundlich (LF) model, showing that the Eu:cit-cAp nanoparticles can carry a maximum of 0.29 ± 0.02 mg Doxo mg Eu:cit-cAp-1 (Qmax). The affinity constant KFL for this binding is 44 ± 2 mL mg-1, and the cooperativity coefficient r is 6 ± 1. The nanoparticle suspensions presented charge reversion from negative to positive after loading with Doxo as revealed by the ζ-potential versus pH characterization. The release of drug from the loaded nanoparticles was found to be strongly pH-dependent, being around 5 wt % at physiological pH 7.4 and 20 wt % at pH 5, in experiments lasting 24 h. Luminescence spectroscopic measurements of Doxo-loaded nanoparticles revealed the increase of luminescence with a decrease in the amount of adsorbed Doxo, due to the so-called inner filter effect. The nanoparticles free of Doxo were cytocompatible when interacted with two human cell lines derived respectively from a gastric carcinoma (GTL-16), and a hepatocarcinoma (Huh7), while Doxo-loaded nanoparticles displayed significant toxicity in a dose-dependent relationship. Therefore, the new nanoassemblies might have a dual function, as nanoprobes in bioimaging by detecting the fate of the nanoparticles in biological environments, and for monitoring the delivery of the drug in such environments, by measuring the rise of the luminescence provided by the desorption of Doxo.

| S-EPMC7074876 | biostudies-literature

Transformation of amorphous calcium phosphate to bone-like apatite.

Project description:Mineralisation of calcium phosphates in bone has been proposed to proceed via an initial amorphous precursor phase which transforms into nanocrystalline, carbonated hydroxyapatite. While calcium phosphates have been under intense investigation, the exact steps during the crystallisation of spherical amorphous particles to platelet-like bone apatite are unclear. Herein, we demonstrate a detailed transformation mechanism of amorphous calcium phosphate spherical particles to apatite platelet-like crystals, within the confined nanodomains of a bone-inspired nanocomposite. The transformation is initiated under the presence of humidity, where nanocrystalline areas are formed and crystallisation advances via migration of nanometre sized clusters by forming steps at the growth front. We propose that such transformation is a possible crystallisation mechanism and is characteristic of calcium phosphates from a thermodynamic perspective and might be unrelated to the environment. Our observations provide insight into a crucial but unclear stage in bone mineralisation, the origins of the nanostructured, platelet-like bone apatite crystals.

| S-EPMC6177403 | biostudies-literature

BaGdF5 Nanophosphors Doped with Different Concentrations of Eu3+ for Application in X-ray Photodynamic Therapy.

Project description:X-ray photodynamic therapy (XPDT) has been recently considered as an efficient alternative to conventional radiotherapy of malignant tissues. Nanocomposites for XPDT typically consist of two components-a nanophosphor which re-emits X-rays into visible light that in turn is absorbed by the second component, a photosensitizer, for further generation of reactive oxygen species. In this study, BaGdF5 nanophosphors doped with different Eu:Gd ratios in the range from 0.01 to 0.50 were synthesized by the microwave route. According to transmission electron microscopy (TEM), the average size of nanophosphors was ~12 nm. Furthermore, different coatings with amorphous SiO2 and citrates were systematically studied. Micro-CT imaging demonstrated superior X-ray attenuation and sufficient contrast in the liver and the spleen after intravenous injection of citric acid-coated nanoparticles. In case of the SiO2 surface, post-treatment core-shell morphology was verified via TEM and the possibility of tunable shell size was reported. Nitrogen adsorption/desorption analysis revealed mesoporous SiO2 formation characterized by the slit-shaped type of pores that should be accessible for methylene blue photosensitizer molecules. It was shown that SiO2 coating subsequently facilitates methylene blue conjugation and results in the formation of the BaGdF5: 10% Eu3+@SiO2@MB nanocomposite as a promising candidate for application in XPDT.

| S-EPMC8657490 | biostudies-literature

Quantitatively Analyzing Pressure Induced Phase Transformation by Photoluminescence Spectra in Eu3+-doped Sodium Potassium Bismuth Titanate.

Project description:(Na0.8,K0.2)0.5Bi0.497Eu0.003TiO3 (NKBET20) piezoelectric ceramic powders were prepared by the solid-reaction method. The phase structures of the NKBET20 powders under various pressures were investigated by photoluminescence (PL) spectra and X-ray diffraction (XRD). The PL spectra of the doped Eu3+ ions suggest a pressure induced transformation from the tetragonal to rhombohedral phase (R phase), and the phase transformations were confirmed by XRD analyses. Furthermore, the fluorescence intensity ratio of the D 0 5 ? F 2 7 transition to the D 0 5 ? F 1 7 transition (FIR21) could be utilized for the quantitative analyses of the phase transformation. The results from the PL method show that as the pressure increases from 0 to 500 MPa, the fractions of the R phase of the NKBET20 powders increase from about 11% to 58%, while the fractions of the tetragonal phase (T phase) decrease from about 89% to 42%, which are consistent with the XRD Rietveld refinement. Unlike the ceramic bulks, the pressure induced phase transformation in the ceramic powders shows no obvious trigger point and is much gentler. This work suggests a different viewpoint to study the pressure induced phase transformation qualitatively and quantitatively, which can be used for more phase analyses.

| S-EPMC7079660 | biostudies-literature