Vanadia-Zirconia and Vanadia-Hafnia Catalysts for Utilization of Volatile Organic Compound Emissions.

ABSTRACT: Utilization is a sustainable and interesting alternative for the destructive treatment of volatile organic compounds due to avoided CO₂ emission. This work concentrates on the development of active and sulfur-tolerant catalysts for the utilization of contaminated methanol. Impregnated and sol-gel prepared vanadia-zirconia and vanadia-hafnia catalysts were thoroughly characterized by N₂ sorption, analytical (S)TEM, elemental analysis, XRD and Raman spectroscopy, and their performances were evaluated in formaldehyde production from methanol and methanethiol mixture. The results showed higher activity of the sol-gel prepared catalysts due to formation of mono- and polymeric vanadia species. Unfortunately, the most active vanadia sites were deactivated more easily than the metal-mixed oxide HfV₂O₇ and ZrV₂O₇ phases, as well as crystalline V₂O₅ observed in the impregnated catalysts. Metal-mixed oxide phases were formed in impregnated catalysts through formation of defects in HfO₂ and ZrO₂ structure during calcination at 600 °C, which was evidenced by Raman spectroscopy. The sol-gel prepared vanadia-zirconia and vanadia-hafnia catalysts were able to produce formaldehyde from contaminated methanol with high selectivity at temperature around 400 °C, while impregnated catalysts required 50-100 °C higher temperatures.

SUBMITTER: Ojala S

PROVIDER: S-EPMC8467847 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Warming occurs in the Arctic twice as fast as the global average, which in turn leads to a large enhancement in terpenoid emissions from vegetation. Volatile terpenoids are the main class of biogenic volatile organic compounds (VOCs) that play crucial roles in atmospheric chemistry and climate. However, the biochemical mechanisms behind the temperature-dependent increase in VOC emissions from subarctic ecosystems are largely unexplored. Using 13 CO2 -labeling, we studied the origin of VOCs and the carbon (C) allocation under global warming in the soil-plant-atmosphere system of contrasting subarctic heath tundra vegetation communities characterized by dwarf shrubs of the genera Salix or Betula. The projected temperature rise of the subarctic summer by 5°C was realistically simulated in sophisticated climate chambers. VOC emissions strongly depended on the plant species composition of the heath tundra. Warming caused increased VOC emissions and significant changes in the pattern of volatiles toward more reactive hydrocarbons. The 13 C was incorporated to varying degrees in different monoterpene and sesquiterpene isomers. We found that de novo monoterpene biosynthesis contributed to 40%-44% (Salix) and 60%-68% (Betula) of total monoterpene emissions under the current climate, and that warming increased the contribution to 50%-58% (Salix) and 87%-95% (Betula). Analyses of above- and belowground 12/13 C showed shifts of C allocation in the plant-soil systems and negative effects of warming on C sequestration by lowering net ecosystem exchange of CO2 and increasing C loss as VOCs. This comprehensive analysis provides the scientific basis for mechanistically understanding the processes controlling terpenoid emissions, required for modeling VOC emissions from terrestrial ecosystems and predicting the future chemistry of the arctic atmosphere. By changing the chemical composition and loads of VOCs into the atmosphere, the current data indicate that global warming in the Arctic may have implications for regional and global climate and for the delicate tundra ecosystems.

Project description:Fused Deposition Modeling (FDM®), also known as Fused Filament Fabrication (FFF), 3D printers have been shown in numerous studies to emit ultrafine particles and volatile organic compounds (VOCs). Filament extruders, designed to create feedstocks for 3D printers, have recently come onto the consumer market for at-home hobbyists as an alternative to buying 3D printer filaments. These instruments allow for the creation of 3D printer filaments from raw plastic pellets. Given the similarity in processes and materials used by 3D printers and filament extruders, we hypothesized that filament extruders may also release ultrafine particle emissions and VOCs. An off-the-shelf filament extruder was operated in a 2 m3 chamber using three separate feedstocks: acrylonitrile butadiene styrene (ABS) pellets, pulverized poly-lactic acid (PLA), and PLA pellets. Ultrafine particle emissions were measured in real-time using a scanning mobility particle sizer and thermal desorption tubes were used for both non-targeted and targeted analysis of VOCs present in emissions. Ultrafine particle number emission rates were comparable to those found in 3D printer studies with the greatest to least emission rates from ABS pellets, pulverized PLA, and PLA pellets, respectively. In addition, the majority of particles released were found to be ultrafine (1-100 nm), similar to 3D printer studies. A variety of VOCs were identified using the ABS feedstock, including styrene and ethylbenzene, and PLA feedstock. Styrene average mass concentration amounts were found to be near the EPA Integrated Risk Information System Reference Concentration for Inhalation Exposure for 3 min and 5 min samples. Further studies will be needed to determine the impact on emissions of environmental volume, air exchange rate, and extruder settings such as extrusion speed and temperature. The results support the hypothesis that use of a filament extruder may present an additional exposure risk to 3D printer hobbyists.

Dataset Information

Vanadia-Zirconia and Vanadia-Hafnia Catalysts for Utilization of Volatile Organic Compound Emissions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets