Fouling Release Coatings Based on Acrylate-MQ Silicone Copolymers Incorporated with Non-Reactive Phenylmethylsilicone Oil.

ABSTRACT: Copolymers containing MQ silicone and acrylate were synthesized by controlling the additive amount of compositions. Subsequently, fouling release coatings based on the copolymer with the incorporation of non-reactive phenylmethylsilicone oil were prepared. The surface properties of the coating (CAMQ₄₀) were consistent with that of the polydimethylsiloxane (PDMS) elastomer, which ensured good hydrophobicity. Moreover, the seawater volume swelling rate of all prepared coatings was less than 5%, especially for CAMQ₄₀ with only 1.37%. Copolymers enhanced the mechanical properties of the coatings, while the enhancement was proportional to the molar content of structural units from acrylate in the copolymer. More importantly, the adhesion performance between the prepared coatings and substrates indicated that pull-off strength values were more than 1.6 MPa, meaning a high adhesion strength. The phenylmethylsilicone oil leaching observation determined that the oil leaching efficiency increased with the increase in the structural unit's molar content from MQ silicone in the copolymer, which was mainly owing to the decrease in compatibility between oil and the cured coating, as well as the decrease in mechanical properties. High oil leaching efficiency could make up for the decrease in the biofouling removal rate due to the enhancement of the elastic modulus. For CAMQ₄₀, it had an excellent antifouling performance at 30 days of exposure time with more than 92% of biofouling removal rate, which was confirmed by biofilm adhesion assay.

SUBMITTER: Zhou H

PROVIDER: S-EPMC8469071 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

On the mechanism of marine fouling-prevention performance of oil-containing silicone elastomers.

Project description:For many decades, silicone elastomers with oil incorporated have served as fouling-release coating for marine applications. In a comprehensive study involving a series of laboratory-based marine fouling assays and extensive global field studies of up to 2-year duration, we compare polydimethylsiloxane (PDMS) coatings of the same composition loaded with oil via two different methods. One method used a traditional, one-pot pre-cure oil addition approach (o-PDMS) and another method used a newer post-cure infusion approach (i-PDMS). The latter displays a substantial improvement in biofouling prevention performance that exceeds established commercial silicone-based fouling-release coating standards. We interpret the differences in performance between one-pot and infused PDMS by developing a mechanistic model based on the Flory-Rehner theory of swollen polymer networks. Using this model, we propose that the chemical potential of the incorporated oil is a key consideration for the design of future fouling-release coatings, as the improved performance is driven by the formation and stabilization of an anti-adhesion oil overlayer on the polymer surface.

| S-EPMC9276722 | biostudies-literature

Modulated release from implantable ocular silicone oil tamponade drug reservoirs.

Project description:Complicated cases of retinal detachment can be treated with silicone oil tamponades. There is the potential for silicone oil tamponades to have adjunctive drug releasing behaviour within the eye, however the lipophilic nature of silicone oil limits the number of drugs that are suitable, and drug release from the hydrophobic reservoir is uncontrolled. Here, a radiometric technique was developed to accurately measure drug solubility in silicone oil and measure release into culture media. All-trans retinoic acid (atRA), a lipophilic drug known to act as an anti-proliferative within the eye, was used throughout this work. Chain-end modification of polydimethylsiloxane with atRA produced a polydimethylsiloxane retinoate (PDMS-atRA), which was used as an additive to silicone oil to modify the solvent environment within the silicone oil and the distribution coefficient. Blends of PDMS-atRA and silicone oil containing different concentrations of free atRA were produced. The presence of PDMS-atRA in silicone oil had a positive effect on atRA solubility and the longevity of release in vitro. The drug release period was independent of atRA starting concentration and dependent on the PDMS-atRA concentration in the blend. A clinically relevant release period of atRA over 7 weeks from a silicone oil blend with PDMS-atRA was observed. © 2018 The Authors. Journal of Polymer Science Part A: Polymer Chemistry Published by Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018, 56, 938-946.

| S-EPMC5873246 | biostudies-literature

Preparation and Properties of Plant-Oil-Based Epoxy Acrylate-Like Resins for UV-Curable Coatings.

Project description:Novel oil-based epoxy acrylate (EA)-like prepolymers were synthesized via the ring-opening reaction of epoxidized plant oils with a new unsaturated carboxyl acid precursor (MAAMA) synthesized by reacting maleic anhydride (MA) with methallyl alcohol (MAA). Since the employed epoxidized oils including epoxidized soybean oil (ESO), epoxidized rubber seed oil (ERSO), and epoxidized wilsoniana seed oil (EWSO) possessed epoxy values of 7.34-4.38%, the obtained epoxy acrylate (EA)-like prepolymers (MMESO, MMERSO, and MMEWSO) indicated a C=C functionality of 7.81-4.40 per triglyceride. Furthermore, effects of the C=C functionality and the addition of hydroxyethyl methacrylate (HEMA) diluent on the ultimate properties of the resulting UV-cured EA-like materials were investigated and compared with those of commercially available acrylated ESO (AESO) resins. As the C=C functionality increased, the storage modulus at 25 °C (E'25), glass transition temperature (Tg), 5% weight-loss temperature (T5), tensile strength and modulus (σ and E), and hardness of the coating for both the pure EA and EA/HEMA resins increased significantly as well. These properties indicated similar trends when comparing the EA materials with 30% of HEMA with those pure EA materials. Specially, although ERSO had a clearly lower epoxy value that ESO, both the UV-cured pure MMERSO and MMERSO/HEMA materials showed much better E'25, Tg, σ, and E than their AESO counterparts, indicating that the MAAMA modification of epoxidized plant oils was much more effective than the modification of acrylic acid to achieve high-performance oil-based epoxy acrylate resins.

| S-EPMC7570069 | biostudies-literature

Suppression Effect and Mechanism of Amine-Containing MQ Silicone Resin on the Tracking and Erosion Resistance of Silicone Rubber.

Project description:How to effectively enhance the antitracking performance of silicone rubber is a huge challenge in the field of high-voltage insulation. In this contribution, amine-containing MQ silicone resin (A-MQ) was prepared to enhance the tracking and erosion resistance of addition-cure liquid silicone rubber (ALSR). The results showed that A-MQ imparted ALSR with excellent tracking and erosion resistance. When A-MQ content was 4 phr, all test samples passed the inclined plane test at 4.5 kV, and the erosion mass decreased by 67.8%. In addition, the tensile strength and tear strength increased by 13.2 and 13.6%, respectively, compared with that of ALSR without A-MQ. The suppression mechanism was further investigated in the aspects of heat attack and plasma bombardment by laser Raman spectroscopy, thermogravimetry, thermogravimetry-Fourier transform infrared spectrometry, scanning electron microscopy, attenuated total reflection-Fourier transform infrared spectrometry, and X-ray photoelectron spectroscopy. This revealed that at the elevated temperature caused by arc discharge, A-MQ promoted crosslinking of the polysiloxane molecules and suppressed the generation of cyclic oligomers, which reduced the intensity of the electrical arc. Moreover, when suffering from plasma bombardment, which was also produced by arc discharge, A-MQ protected the silicone chains from degradation and eliminated the carbon deposited on the surface.

| S-EPMC6641718 | biostudies-literature

Stable low-fouling plasma polymer coatings on polydimethylsiloxane.

Project description:Polydimethylsiloxane (DMS) is a popular material for microfluidics, but it is hydrophobic and is prone to non-specific protein adsorption. In this study, we explore methods for producing stable, protein resistant, tetraglyme plasma polymer coatings on PDMS by combining extended baking processes with multiple plasma polymer coating steps. We demonstrate that by using this approach, it is possible to produce a plasma polymer coatings that resist protein adsorption (<10 ng/cm(2)) and are stable to storage over at least 100 days. This methodology can translate to any plasma polymer system, enabling the introduction of a wide range of surface functionalities on PDMS surfaces.

| S-EPMC3470602 | biostudies-other

Niobia Nanofiber-Reinforced Protective Niobium Oxide/Acrylate Nanocomposite Coatings.

Project description:In the present study, the corrosion resistance of a new niobium oxide/acrylate hybrid nanocomposite coating doped with niobia nanofibers is investigated. Nanofibers were initially synthesized from niobium(V) chloride precursor in a novel autoclave approach before fabricating the base coating from a two-step process involving the syntheses of acrylate resin via free radical polymerization and niobium oxide gel from niobium ethoxide via a sol-gel technique. Variants of the synthesized nanocomposite coating were incorporated with varying concentrations of niobia nanofibers before spin-coating on Q235 steel substrates to inhibit corrosive electrolytic ion percolation and further enhance corrosion resistance when treated with chloride-enriched corrosive media. The corrosion resistance of these nanocomposite coatings increased with nanofiber content up to an optimum concentration due to the corrosion-inhibiting and protective effects of niobium barrier layers within these coatings. The presence of the niobia nanofibers also promoted improved surface contact angle and toughened mechanical strengths.

| S-EPMC7711932 | biostudies-literature

Composite Slow-Release Fouling Release Coating Inspired by Synergistic Anti-Fouling Effect of Scaly Fish.

Project description:Inspired by the antifouling properties of scaly fish, the conventional silicone coating with phenylmethylsilicone oil (PSO/PDMS) composite coating was fabricated and modified with single layer polystyrene (PS) microsphere (PSO/PDMS-PS) arrays. The fish scale like micro-nano structures were fabricated on the surface of bio-inspired coating, which can reduce the contact area with the secreted protein membrane of fouling organisms effectively and prevent further adhesion between fouling organisms and bio-inspired coating. Meanwhile, PSO exuded to the coating surface has the similar function with mucus secreted by fish epidermis, which make the coating surface slithery and will be polished with the fouling organisms in turbulent waters. Compared to PSO/PDMS coating without any structure and conventional silicone coating, PSO/PDMS-PS showed better antiadhesion activity against both marine bacteria and benthic diatom (Navicula sp.). Additionally, the existence of PS microspheres can reduce the release rate of PSO greatly, which will extend the service life of coating. Compared to PSO/PDMS coating, the sustained release efficiency of PSO/PDMS-PS coating can reach 23.2%. This facile method for fabricating the bio-inspired composite slow-release antifouling coating shows a widely fabricating path for the development of synergistic anti-fouling coating.

| S-EPMC8401683 | biostudies-literature

New Principles of Polymer Composite Preparation. MQ Copolymers as an Active Molecular Filler for Polydimethylsiloxane Rubbers.

Project description:Colorless transparent vulcanizates of silicone elastomers were prepared by mixing the components in a common solvent followed by solvent removal. We studied the correlation between the mechanical behavior of polydimethylsiloxane (PDMS)-rubber compositions prepared using MQ (mono-(M) and tetra-(Q) functional siloxane) copolymers with different ratios of M and Q parts as a molecular filler. The composition and molecular structure of the original rubber, MQ copolymers, and carboxyl-containing PDMS oligomers were also investigated. The simplicity of the preparation of the compositions, high strength and elongation at break, and their variability within a wide range allows us to consider silicone elastomers as a promising alternative to silicone materials prepared by traditional methods.

| S-EPMC8433927 | biostudies-literature

Comparison of anti-fouling surface coatings for applications in bacteremia diagnostics.

Project description:To accurately diagnose microbial infections in blood, it is essential to recover as many microorganisms from a sample as possible. Unfortunately, recovering such microorganisms depends significantly on their adhesion to the surfaces of diagnostic devices. Consequently, we sought to minimize the adhesion of methicillin-sensitive Staphylococcus aureus (MSSA) to the surface of polypropylene- and acrylic-based bacteria concentration devices. These devices were treated with 11 different coatings having various charges and hydrophobicities. Some coatings promoted bacterial adhesion under centrifugation, whereas others were more likely to prevent it. Experiments were run using a simple buffer system and lysed blood, both inoculated with MSSA. Under both conditions, Hydromer's 7-TS-13 and Aqua65JL were most effective at reducing bacterial adhesion.

| S-EPMC4137785 | biostudies-literature

Coral-like silicone nanofilament coatings with extremely low ice adhesion.

Project description:Passive icephobic surfaces can provide a cost and energy efficient solution to many icing problems that are currently handled with expensive active strategies. Water-repellent surface treatments are promising candidates for this goal, but commonly studied systems, such as superhydrophobic surfaces and Slippery Liquid Infused Porous Surfaces (SLIPS), still face challenges in the stability and durability of their properties in icing environments. In this work, environmental icing conditions are simulated using an Icing Wind Tunnel, and ice adhesion is evaluated with a Centrifugal Adhesion Test. We show that superhydrophobic coral-like Silicone Nanofilament (SNF) coatings exhibit extremely low ice adhesion, to the point of spontaneous ice detachment, and good durability against successive icing cycles. Moreover, SNFs-based SLIPS show stably low ice adhesion for the whole duration of the icing test. Stability of surface properties in a cold environment is further investigated with water wettability at sub-zero surface temperature, highlighting the effect of surface chemistry on superhydrophobicity under icing conditions.

| S-EPMC8516905 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data