Synthesis of Tailored Perfluoro Unsaturated Monomers for Potential Applications in Proton Exchange Membrane Preparation.

ABSTRACT: The aim of the present work is the synthesis and characterization of new perfluorinated monomers bearing, similarly to Nafion^®, acidic groups for proton transport for potential and future applications in proton exchange membrane (PEM) fuel cells. To this end, we focused our attention on the synthesis of various molecules with (i) sufficient volatility to be used in vacuum polymerization techniques (e.g., PECVD)), (ii) sulfonic, phosphonic, or carboxylic acid functionalities for proton transport capacity of the resulting membrane, (iii) both aliphatic and aromatic perfluorinated tags to diversify the membrane polarity with respect to Nafion^®, and (iv) a double bond to facilitate the polymerization under vacuum giving a preferential way for the chain growth of the polymer. A retrosynthetic approach persuaded us to attempt three main synthetic strategies: (a) organometallic Heck-type cross-coupling, (b) nucleophilic displacement, and (c) Wittig-Horner reaction (carbanion approach). Preliminary results on the plasma deposition of a polymeric film are also presented. The variation of plasma conditions allowed us to point out that the film prepared in the mildest settings (20 W) shows the maximum monomer retention in its structure. In this condition, plasma polymerization likely occurs mainly by rupture of the π bond in the monomer molecule.

SUBMITTER: Monopoli A

PROVIDER: S-EPMC8470954 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Tailored Porous Carbon Xerogels for Fe-N-C Catalysts in Proton Exchange Membrane Fuel Cells.

Project description:Atomically dispersed Fe-N-C catalysts for the oxygen reduction reaction (ORR) have been synthesized with a template-free method using carbon xerogels (CXG) as a porous matrix. The porosity of the CXGs is easily tunable through slight variations in the synthesis procedure. In this work, CXGs are prepared by formaldehyde and resorcinol polymerization, modifying the pH during the process. Materials with a broad range of porous structures are obtained: from non-porous to micro-/meso-/macroporous materials. The porous properties of CXG have a direct effect on Fe-N-CXG activity against ORR in an acidic medium (0.5 M H2SO4). Macropores and wide mesopores are vital to favor the mass transport of reagents to the active sites available in the micropores, while narrower mesopores can generate additional tortuosity. The role of microporosity is investigated by comparing two Fe-N-C catalysts using the same CXG as the matrix but following a different Fe and N doping procedure. In one case, the carbonization of CXG occurs rapidly and simultaneously with Fe and N doping, whereas in the other case it proceeds slowly, under controlled conditions and before the doping process, resulting in the formation of more micropores and active sites and achieving higher activity in a three-electrode cell and a better durability during fuel cell measurements. This work proves the feasibility of the template-free method using CXG as a carbon matrix for Fe-N-C catalysts, with the novelty of the controlled porous properties of the carbon material and its effect on the catalytic activity of the Fe-N-C catalyst. Moreover, the results obtained highlight the importance of the carbon matrix's porous structure in influencing the activity of Fe-N-C catalysts against ORR.

| S-EPMC10780504 | biostudies-literature

Surface-coupled proton exchange of a membrane-bound proton acceptor.

Project description:Proton-transfer reactions across and at the surface of biological membranes are central for maintaining the transmembrane proton electrochemical gradients involved in cellular energy conversion. In this study, fluorescence correlation spectroscopy was used to measure the local protonation and deprotonation rates of single pH-sensitive fluorophores conjugated to liposome membranes, and the dependence of these rates on lipid composition and ion concentration. Measurements of proton exchange rates over a wide proton concentration range, using two different pH-sensitive fluorophores with different pK(a)s, revealed two distinct proton exchange regimes. At high pH (> 8), proton association increases rapidly with increasing proton concentrations, presumably because the whole membrane acts as a proton-collecting antenna for the fluorophore. In contrast, at low pH (< 7), the increase in the proton association rate is slower and comparable to that of direct protonation of the fluorophore from the bulk solution. In the latter case, the proton exchange rates of the two fluorophores are indistinguishable, indicating that their protonation rates are determined by the local membrane environment. Measurements on membranes of different surface charge and at different ion concentrations made it possible to determine surface potentials, as well as the distance between the surface and the fluorophore. The results from this study define the conditions under which biological membranes can act as proton-collecting antennae and provide fundamental information on the relation between the membrane surface charge density and the local proton exchange kinetics.

| S-EPMC2840142 | biostudies-literature

Preparation and Identification of Optimal Synthesis Conditions for a Novel Alkaline Anion-Exchange Membrane.

Project description:The physicochemical and mechanical properties of new alkaline anion-exchange membranes (AAEMs) based on chitosan (CS) and poly(vinyl alcohol) (PVA) polymers doped with unsupported copper nanoparticles (NPs) and copper exchanged over different porous materials were investigated regarding ion-exchange capacity (IEC), OH- conductivity, water uptake (WU), water vapor permeability (WVP), and thermal and mechanical resistance. The influence of the type of filler included in different morphologies and filler loading has been explored using copper exchanged materials such as the layered porous titanosilicate AM-4, layered stannosilicate UZAR-S3, and zeolites Y, MOR, and BEA. Compared to commercially available anion-exchange membranes, the best performing membranes in terms of WU, IEC, OH- conductivity and WVP in this study were those containing 10 wt % of Cu-AM-4 and Cu-UZAR-S3, although 10 wt % Cu-MOR provided better mechanical strength at close values of WVP and anion conductivity. It was also observed that when Cu was exchanged in a porous silicate matrix, its oxidation state was lower than when embedded as unsupported metal NPs. In addition, the statistical analysis of variance determined that the electrochemical properties of the membranes were noticeably affected by both the type and filler loading, and influenced also by the copper oxidation state and content in the membrane, but their hydrophilic properties were more affected by the polymers. The largest significant effects were noticed on the water sorption and transport properties, which gives scope for the design of AAEMs for electrochemical and water treatment applications.

| S-EPMC6403638 | biostudies-literature

Facile Fabrication and Characterization of Improved Proton Conducting Sulfonated Poly(Arylene Biphenylether Sulfone) Blocks Containing Fluorinated Hydrophobic Units for Proton Exchange Membrane Fuel Cell Applications.

Project description:Sulfonated poly(arylene biphenylether sulfone)-poly(arylene ether) (SPABES-PAE) block copolymers by controlling the molar ratio of SPABES and PAE oligomers were successfully synthesized, and the performances of SPABES-PAE (1:2, 1:1, and 2:1) membranes were compared with Nafion 212. The prepared membranes including fluorinated hydrophobic units were stable against heat, nucleophile attack, and physio-chemical durability during the tests. Moreover, the polymers exhibited better solubility in a variety of solvents. The chemical structure of SPABES-PAEs was investigated by ¹H nuclear magnetic resonance (¹H NMR), Fourier transform infrared spectroscopy (FT-IR), and gel permeation chromatography (GPC). The membrane of SPABES-PAEs was fabricated by the solution casting method, and the membranes were very flexible and transparent with a thickness of 70?90 ?m. The morphology of the membranes was observed using atomic force microscope and the ionic domain size was proved by small angle X-ray scattering (SAXS) measurement. The incorporation of polymers including fluorinated units allowed the membranes to provide unprecedented oxidative and dimensional stabilities, as verified from the results of ex situ durability tests and water uptake capacity, respectively. By the collective efforts, we observed an enhanced water retention capacity, reasonable dimensional stability and high proton conductivity, and the peak power density of the SPABES-PAE (2:1) was 333.29 mW·cm-2 at 60 °C under 100% relative humidity (RH).

| S-EPMC6401750 | biostudies-literature

Synthesis of Poly(glycerol butenedioate)-PGB-Unsaturated Polyester toward Biomedical Applications.

Project description:A new polyester poly(glycerol butenedioate) (PGB) was obtained in the bulk polycondensation of glycerin and maleic anhydride. Glycerol polyesters are new biomaterials commonly used in tissue engineering. PGB, containing the α,β-unsaturated moiety, could be very interesting due to potential modifications such as additions or oxidation. Such modifications are not possible on the heretofore known glycerol polyesters due to their structure without α,β-unsaturated moieties. In this work, the developed process was optimized by applying the design of experiments. The optimization criterium was the minimization of the E/Z isomer ratio. Applying the two-stage process, the E/Z isomer ratio was reduced from 5.5 to 0.5 compared to the one-stage process. The degree of branching was also reduced from 17 to 9%, as well as the degree of esterification from 0.89 to 0.72. The obtained structure can be used in modifying or cross-linking via Michael additions.

| S-EPMC9330079 | biostudies-literature

Highly active nano-sized iridium catalysts: synthesis and <i>operando</i> spectroscopy in a proton exchange membrane electrolyzer.

Project description:A stable and cost effective oxygen evolution reaction (OER) catalyst is crucial for the large-scale market penetration of proton exchange membrane (PEM) water electrolyzers. We show that the synthesis of iridium nanoparticles in either low purity ethanol or water, or in the absence of a surfactant, is detrimental to the electrocatalytic properties of the materials. Adding NaBH4 in excess improves the purity of the catalyst enhancing the OER activity up to 100 A gIr-1 at 1.51 V vs. RHE, the highest value reported so far for high purity Ir nanoparticles. The measured OER activity correlates with the capacitive current rather than with the charge corresponding to the IrIII/IrIV oxidation peak. Operando near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) on membrane electrode assemblies (MEAs) with the synthesized catalysts reveals a metallic core surrounded by a thin layer of IrIII/IV oxides/hydroxides. Oxidation of IrIII leaves behind a porous ultrathin layer of IrIV oxides/hydroxides, which dominate the surface during the OER, while IrV was not detected.

| S-EPMC5934821 | biostudies-literature

Low-Cost and Durable Bipolar Plates for Proton Exchange Membrane Electrolyzers.

Project description:Cost reduction and high efficiency are the mayor challenges for sustainable H2 production via proton exchange membrane (PEM) electrolysis. Titanium-based components such as bipolar plates (BPP) have the largest contribution to the capital cost. This work proposes the use of stainless steel BPPs coated with Nb and Ti by magnetron sputtering physical vapor deposition (PVD) and vacuum plasma spraying (VPS), respectively. The physical properties of the coatings are thoroughly characterized by scanning electron, atomic force microscopies (SEM, AFM); and X-ray diffraction, photoelectron spectroscopies (XRD, XPS). The Ti coating (50 μm) protects the stainless steel substrate against corrosion, while a 50-fold thinner layer of Nb decreases the contact resistance by almost one order of magnitude. The Nb/Ti-coated stainless steel bipolar BPPs endure the harsh environment of the anode for more than 1000 h of operation under nominal conditions, showing a potential use in PEM electrolyzers for large-scale H2 production from renewables.

| S-EPMC5353588 | biostudies-literature

Critical advancements in achieving high power and stable nonprecious metal catalyst-based MEAs for real-world proton exchange membrane fuel cell applications.

Project description:Despite great progress in the development of nonprecious metal catalysts (NPMCs) over the past several decades, the performance and stability of these promising catalysts have not yet achieved commercial readiness for proton exchange membrane fuel cells (PEMFCs). Through rational design of the cathode catalyst layer (CCL), we demonstrate the highest reported performance for an NPMC-based membrane electrode assembly (MEA), achieving a peak power of 570 mW/cm2 under air. This record performance is achieved using a precommercial catalyst for which nearly all pores are <3 nm in diameter, challenging previous beliefs regarding the need for larger catalyst pores to achieve high current densities. This advance is achieved at industrially relevant scales (50 cm2 MEA) using a precommercial NPMC. In situ electrochemical analysis of the CCLs is also used to help gain insight into the degradation mechanism observed during galvanostatic testing. Overall, the performance of this NPMC-based MEA has achieved commercial readiness and will be introduced into an NPMC-based product for portable power applications.

| S-EPMC5866058 | biostudies-literature

Preparation and Characterization of AgNPs In Situ Synthesis on Polyelectrolyte Membrane Coated Sericin/Agar Film for Antimicrobial Applications.

Project description:Antibacterial materials are of great importance in preventing bacterial adhesion and reproduction in daily life. Silver nanoparticle (AgNP) is a broad-spectrum antibacterial nanomaterial that has attracted significant attentions for its ability to endow natural materials with antibacterial ability. Silk sericin (SS) has a great advantage for biomaterial application, as it is a natural protein with excellent hydrophilicity and biodegradability. In this study, we prepared AgNPs and polyelectrolyte membrane (PEM) modified SS/Agar films through the layer-by-layer adsorption technique and ultraviolet-assisted AgNPs synthesis method. The film was well characterized by scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction, fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy. Other properties such as water contact angle, wettability and tensile strength, the release of silver were also studied. The antimicrobial activity of AgNPs-PEM-SS/Agar film was investigated against Escherichia coli and Staphylococcus aureus as the model microorganisms by the inhibition zone and bacterial growth curve assays. The results suggested that the AgNPs-PEM-SS/Agar film had excellent mechanical performance, high hydrophilicity, prominent water absorption ability, as well as outstanding and durable antibacterial activity. Therefore, the prepared novel AgNPs-PEM-SS/Agar composite film is proposed as a potentially favorable antibacterial biomaterial for biomedical applications.

| S-EPMC6073696 | biostudies-literature

Hybrid Composite Membrane of Phosphorylated Chitosan/Poly (Vinyl Alcohol)/Silica as a Proton Exchange Membrane.

Project description:Chitosan is one of the natural biopolymers that has been studied as an alternative material to replace Nafion membranes as proton change membranes. Nevertheless, unmodified chitosan membranes have limitations including low proton conductivity and mechanical stability. The aim of this work is to study the effect of modifying chitosan through polymer blending with different compositions and the addition of inorganic filler on the microstructure and physical properties of N-methylene phosphonic chitosan/poly (vinyl alcohol) (NMPC/PVA) composite membranes. In this work, the NMPC biopolymer and PVA polymer are used as host polymers to produce NMPC/PVA composite membranes with different compositions (30-70% NMPC content). Increasing NMPC content in the membranes increases their proton conductivity, and as NMPC/PVA-50 composite membrane demonstrates the highest conductivity (8.76 × 10-5 S cm-1 at room temperature), it is chosen to be the base membrane for modification by adding hygroscopic silicon dioxide (SiO2) filler into its membrane matrix. The loading of SiO2 filler is varied (0.5-10 wt.%) to study the influence of filler concentration on temperature-dependent proton conductivity of membranes. NMPC/PVA-SiO2 (4 wt.%) exhibits the highest proton conductivity of 5.08 × 10-4 S cm-1 at 100 °C. In conclusion, the study shows that chitosan can be modified to produce proton exchange membranes that demonstrate enhanced properties and performance with the addition of PVA and SiO2.

| S-EPMC8470232 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data