Pulsed Laser Deposition of Cs₂AgBiBr₆: from Mechanochemically Synthesized Powders to Dry, Single-Step Deposition.

ABSTRACT: Cs₂AgBiBr₆ has been proposed as a promising lead-free and stable double perovskite alternative to hybrid and lead-based perovskites. However, the low solubility of precursors during wet synthesis, or the distinct volatility of components during evaporation, results in complex multistep synthesis approaches, hampering the widespread employment of Cs₂AgBiBr₆ films. Here, we present pulsed laser deposition of Cs₂AgBiBr₆ films as a dry, single-step and single-source deposition approach for high-quality film formation. Cs₂AgBiBr₆ powders were prepared by mechanochemical synthesis and pressed into a solid target maintaining phase purity. Controlled laser ablation of the double perovskite target in vacuum and a substrate temperature of 200 °C results in the formation of highly crystalline Cs₂AgBiBr₆ films. We discuss the importance of deposition pressure to achieve stoichiometric transfer and of substrate temperature during PLD growth to obtain high-quality Cs₂AgBiBr₆ films with grain sizes > 200 nm. This work demonstrates the potential of PLD, an established technique in the semiconductor industry, to deposit complex halide perovskite materials while being compatible with optoelectronic device fabrication, such as UV and X-ray detectors.

SUBMITTER: Rodkey N

PROVIDER: S-EPMC8482541 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Ultrafast Excited-State Localization in Cs2AgBiBr6 Double Perovskite.

Project description:Cs2AgBiBr6 is a promising metal halide double perovskite offering the possibility of efficient photovoltaic devices based on lead-free materials. Here, we report on the evolution of photoexcited charge carriers in Cs2AgBiBr6 using a combination of temperature-dependent photoluminescence, absorption and optical pump-terahertz probe spectroscopy. We observe rapid decays in terahertz photoconductivity transients that reveal an ultrafast, barrier-free localization of free carriers on the time scale of 1.0 ps to an intrinsic small polaronic state. While the initially photogenerated delocalized charge carriers show bandlike transport, the self-trapped, small polaronic state exhibits temperature-activated mobilities, allowing the mobilities of both to still exceed 1 cm2 V-1 s-1 at room temperature. Self-trapped charge carriers subsequently diffuse to color centers, causing broad emission that is strongly red-shifted from a direct band edge whose band gap and associated exciton binding energy shrink with increasing temperature in a correlated manner. Overall, our observations suggest that strong electron-phonon coupling in this material induces rapid charge-carrier localization.

| S-EPMC8154850 | biostudies-literature

Direct, Indirect, and Self-Trapped Excitons in Cs2AgBiBr6.

Project description:Cs2AgBiBr6 exhibits promising photovoltaic and light-emitting properties, making it a candidate for next-generation solar cells and LED technologies. Additionally, it serves as a model system within the family of halide double perovskites, offering insights into a broader class of materials. Here, we study various possible excited states of this material to understand its absorption and emission properties. We use time-dependent density functional theory (TD-DFT) coupled with nonempirical hybrid functionals, specifically PBE0(α) and dielectric-dependent hybrids (DDH) to explore direct, indirect, and self-trapped excitons in this material. Based on comparison with experiment, we show that these methods can give excellent predictions of the absorption spectrum and that the fundamental band gap has been underestimated in previous computational studies. We connect the experimental photoluminescence signals at 1.9-2.0 eV to the emission from self-trapped excitons and electron polarons. Finally, we reveal a complex landscape with energetically competing direct, indirect, and self-trapped excitons in the material.

| S-EPMC11345835 | biostudies-literature

Highly mobile hot holes in Cs2AgBiBr6 double perovskite.

Project description:Highly mobile hot charge carriers are a prerequisite for efficient hot carrier optoelectronics requiring long-range hot carrier transport. However, hot carriers are typically much less mobile than cold ones because of carrier-phonon scattering. Here, we report enhanced hot carrier mobility in Cs2AgBiBr6 double perovskite. Following photoexcitation, hot carriers generated with excess energy exhibit boosted mobility, reaching an up to fourfold enhancement compared to cold carriers and a long-range hot carrier transport length beyond 200 nm. By optical pump–infrared push-terahertz probe spectroscopy and frequency-resolved photoconductivity measurements, we provide evidence that the conductivity enhancement originates primarily from hot holes with reduced momentum scattering. We rationalize our observation by considering (quasi-)ballistic transport of thermalized hot holes with energies above an energetic threshold in Cs2AgBiBr6. Our findings render Cs2AgBiBr6 as a fascinating platform for studying the fundamentals of hot carrier transport and its exploitation toward hot carrier–based optoelectronic devices.

| S-EPMC8694595 | biostudies-literature

Lead-Free Halide Double Perovskite Cs2 AgBiBr6 with Decreased Band Gap.

Project description:Environmentally friendly halide double perovskites with improved stability are regarded as a promising alternative to lead halide perovskites. The benchmark double perovskite, Cs2 AgBiBr6 , shows attractive optical and electronic features, making it promising for high-efficiency optoelectronic devices. However, the large band gap limits its further applications, especially for photovoltaics. Herein, we develop a novel crystal-engineering strategy to significantly decrease the band gap by approximately 0.26 eV, reaching the smallest reported band gap of 1.72 eV for Cs2 AgBiBr6 under ambient conditions. The band-gap narrowing is confirmed by both absorption and photoluminescence measurements. Our first-principles calculations indicate that enhanced Ag-Bi disorder has a large impact on the band structure and decreases the band gap, providing a possible explanation of the observed band-gap narrowing effect. This work provides new insights for achieving lead-free double perovskites with suitable band gaps for optoelectronic applications.

| S-EPMC7496408 | biostudies-literature

Light-activated Multilevel Resistive Switching Storage in Pt/Cs2AgBiBr6/ITO/Glass Devices.

Project description:High-density Cs2AgBiBr6 films with uniform grains were prepared by a simple one-step and low-temperature sol-gel method on indium tin oxide (ITO) substrates. An explicit tristate bipolar resistance switching behavior was observed in the Pt/Cs2 AgBiBr6/ITO/glass devices under irradiation of 10 mW/cm2 (445 nm). This behavior was stable over 1200 s. The maximum ratio of the high and low resistance states was about 500. Based on the analysis of electric properties, valence variation and absorption spectra, the resistive switching characteristics were attributed to the trap-controlled space charge-limited current mechanism due to the bromine vacancies in the Cs2AgBiBr6 layer. On the other hand, it is suggested that the ordering of the Schottky-like barrier located at Pt/Cs2AgBiBr6 affects the three-state resistance switching behavior under light irradiation. The ability to adjust the photoelectrical properties of Cs2AgBiBr6-based resistive switching memory devices is a promising strategy to develop high-density memory.

| S-EPMC8669091 | biostudies-literature

Heteroepitaxial passivation of Cs2AgBiBr6 wafers with suppressed ionic migration for X-ray imaging.

Project description:X-ray detectors are broadly utilized in medical imaging and product inspection. Halide perovskites recently demonstrate excellent performance for direct X-ray detection. However, ionic migration causes large noise and baseline drift, limiting the detection and imaging performance. Here we largely eliminate the ionic migration in cesium silver bismuth bromide (Cs2AgBiBr6) polycrystalline wafers by introducing bismuth oxybromide (BiOBr) as heteroepitaxial passivation layers. Good lattice match between BiOBr and Cs2AgBiBr6 enables complete defect passivation and suppressed ionic migration. The detector hence achieves outstanding balanced performance with a signal drifting one order of magnitude lower than all previous studies, low noise (1/f noise free), a high sensitivity of 250 µC Gy air-1 cm-2, and a spatial resolution of 4.9 lp mm-1. The wafer area could be easily scaled up by the isostatic-pressing method, together with the heteroepitaxial passivation, strengthens the competitiveness of Cs2AgBiBr6-based X-ray detectors as next-generation X-ray imaging flat panels.

| S-EPMC6491557 | biostudies-literature

The Dawn of Lead-Free Perovskite Solar Cell: Highly Stable Double Perovskite Cs2AgBiBr6 Film.

Project description:Recently, lead-free double perovskites have emerged as a promising environmentally friendly photovoltaic material for their intrinsic thermodynamic stability, appropriate bandgaps, small carrier effective masses, and low exciton binding energies. However, currently no solar cell based on these double perovskites has been reported, due to the challenge in film processing. Herein, a first lead-free double perovskite planar heterojunction solar cell with a high quality Cs2AgBiBr6 film, fabricated by low-pressure assisted solution processing under ambient conditions, is reported. The device presents a best power conversion efficiency of 1.44%. The preliminary efficiency and the high stability under ambient condition without encapsulation, together with the high film quality with simple processing, demonstrate promise for lead-free perovskite solar cells.

| S-EPMC5867041 | biostudies-literature

Hydrogenated Cs2AgBiBr6 for significantly improved efficiency of lead-free inorganic double perovskite solar cell.

Project description:Development of lead-free inorganic perovskite material, such as Cs2AgBiBr6, is of great importance to solve the toxicity and stability issues of traditional lead halide perovskite solar cells. However, due to a wide bandgap of Cs2AgBiBr6 film, its light absorption ability is largely limited and the photoelectronic conversion efficiency is normally lower than 4.23%. In this text, by using a hydrogenation method, the bandgap of Cs2AgBiBr6 films could be tunable from 2.18 eV to 1.64 eV. At the same time, the highest photoelectric conversion efficiency of hydrogenated Cs2AgBiBr6 perovskite solar cell has been improved up to 6.37% with good environmental stability. Further investigations confirmed that the interstitial doping of atomic hydrogen in Cs2AgBiBr6 lattice could not only adjust its valence and conduction band energy levels, but also optimize the carrier mobility and carrier lifetime. All these works provide an insightful strategy to fabricate high performance lead-free inorganic perovskite solar cells.

| S-EPMC9192601 | biostudies-literature

Band-Like Charge Transport in Cs2AgBiBr6 and Mixed Antimony-Bismuth Cs2AgBi1-x Sb x Br6 Halide Double Perovskites.

Project description:Recently, halide double perovskites (HDPs), such as Cs2AgBiBr6, have been reported as promising nontoxic alternatives to lead halide perovskites. However, it remains unclear whether the charge-transport properties of these materials are as favorable as for lead-based perovskites. In this work, we study the mobilities of charges in Cs2AgBiBr6 and in mixed antimony-bismuth Cs2AgBi1-x Sb x Br6, in which the band gap is tunable from 2.0 to 1.6 eV. Using temperature-dependent time-resolved microwave conductivity techniques, we find that the mobility is proportional to T -p (with p ≈ 1.5). Importantly, this indicates that phonon scattering is the dominant scattering mechanism determining the charge carrier mobility in these HDPs similar to the state-of-the-art lead-based perovskites. Finally, we show that wet chemical processing of Cs2AgBi1-x Sb x Br6 powders is a successful route to prepare thin films of these materials, which paves the way toward photovoltaic devices based on nontoxic HDPs with tunable band gaps.

| S-EPMC6166227 | biostudies-literature

Shedding Light on Host-to-Yb3+ Energy Transfer in Cs2AgBiBr6:Yb3+ (nano)crystals.

Project description:The optical properties of Cs2AgBiBr6 double perovskite nanocrystals have attracted considerable attention as lead-free alternatives to lead halide perovskites. A promising strategy to create additional flexibility in the emission color is doping lanthanide ions into Cs2AgBiBr6. Incorporating Yb3+ in the lattice has been shown to give rise to near-infrared (NIR) emission, but the energy transfer mechanism remained unclear. Here, we report on the luminescence and sensitization mechanism of Yb3+ in Cs2AgBiBr6 nano- and microcrystals. We observe that the incorporation of Yb3+ in the host lattice does not strongly affect the broadband red emission of the Cs2AgBiBr6 host but does give rise to an additional and characteristic ∼1000 nm NIR line emission from Yb3+. Temperature-dependent and time-resolved photoluminescence studies of undoped and Yb-doped Cs2AgBiBr6 reveal that the energy transfer does not take place through the red emissive state of the Cs2AgBiBr6 host. Instead, there is a competition between relaxation to the red-emitting state and trapping of the photoexcited charge carriers on Yb3+. Trapping on Yb3+ subsequently results in a charge transfer state that relaxes to the 2F5/2 excited state of Yb3+, followed by NIR narrow line f-f emission to the 2F7/2 ground state.

| S-EPMC10976640 | biostudies-literature