Efficient Removal of Chromium(VI) Using a Novel Waste Biomass Chestnut Shell-Based Carbon Electrode by Electrosorption.

ABSTRACT: Biomass-derived porous carbon materials have a good application prospect in electrosorption because of their low cost, abundant natural resources, and excellent performance. In this work, three-dimensional interconnected structure porous carbon (CPC) was successfully synthesized from waste biomass chestnut shells by carbonization and chemical activation processes. The unique structure of CPC could offer superior double-layer capacitance and excellent conductivity. The as-obtained CPC was applied as an electrosorption electrode. In the deionization experiments, the removal efficiency of the CPC electrode in a 30 mg L^-1 chromium(VI) aqueous solution at 1.0 V was 90.5%. The electrosorption follows pseudo-second-order kinetics. The CPC electrode also presented good regeneration performance in the regeneration test. These results demonstrate that the as-prepared carbonaceous material is an ideal material for capacitive deionization electrodes.

SUBMITTER: Zhang X

PROVIDER: S-EPMC8495849 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A large amount of Cr (VI)-polluted wastewater produced in electroplating, dyeing and tanning industries seriously threatens water ecological security and human health. Due to the lack of high-performance electrodes and the coulomb repulsion between hexavalent chromium anion and cathode, the traditional DC-mediated electrochemical remediation technology possesses low Cr (VI) removal efficiency. Herein, by modifying commercial carbon felt (O-CF) with amidoxime groups, amidoxime-functionalized carbon felt electrodes (Ami-CF) with high adsorption affinity for Cr (VI) were prepared. Based on Ami-CF, an electrochemical flow-through system powered by asymmetric AC was constructed. The mechanism and influencing factors of efficient removal of Cr (VI) contaminated wastewater by an asymmetric AC electrochemical method coupling Ami-CF were studied. Scanning Electron Microscopy (SEM), Fourier Transform Infrared (FTIR), and X-ray photoelectron spectroscopy (XPS) characterization results showed that Ami-CF was successfully and uniformly loaded with amidoxime functional groups, and the adsorption capacity of Cr (VI) was more than 100 times higher than that of O-CF. In particular, the Coulomb repulsion effect and the side reaction of electrolytic water splitting were inhibited by the high-frequency anode and cathode switching (asymmetric AC), the mass transfer rate of Cr (VI) from electrode solution was increased, the reduction efficiency of Cr (VI) to Cr (III) was significantly promoted and a highly efficient removal of Cr (VI) was achieved. Under optimal operating conditions (positive bias 1 V, negative bias 2.5 V, duty ratio 20%, frequency 400 Hz, solution pH = 2), the asymmetric AC electrochemistry based on Ami-CF can achieve fast (30 s) and efficient removal (>99.11%) for 0.5-100 mg·L-1 Cr (VI) with a high flux of 300 L h-1 m-2. At the same time, the durability test verified the sustainability of the AC electrochemical method. For Cr (VI)-polluted wastewater with an initial concentration of 50 mg·L-1, the effluent concentration could still reach drinking water grade (<0.05 mg·L-1) after 10 cycling experiments. This study provides an innovative approach for the rapid, green and efficient removal of Cr (VI) containing wastewater at low and medium concentrations.

Dataset Information

Efficient Removal of Chromium(VI) Using a Novel Waste Biomass Chestnut Shell-Based Carbon Electrode by Electrosorption.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets