Electrical Resistivity of Cu and Au at High Pressure above 5 GPa: Implications for the Constant Electrical Resistivity Theory along the Melting Curve of the Simple Metals.

ABSTRACT: The electrical resistivity of solid and liquid Cu and Au were measured at high pressures from 6 up to 12 GPa and temperatures ∼150 K above melting. The resistivity of the metals was also measured as a function of pressure at room temperature. Their resistivity decreased and increased with increasing pressure and temperature, respectively. With increasing pressure at room temperature, we observed a sharp reduction in the magnitude of resistivity at ∼4 GPa in both metals. In comparison with 1 atm data and relatively lower pressure data from previous studies, our measured temperature-dependent resistivity in the solid and liquid states show a similar trend. The observed melting temperatures at various fixed pressure are in reasonable agreement with previous experimental and theoretical studies. Along the melting curve, the present study found the resistivity to be constant within the range of our investigated pressure (6-12 GPa) in agreement with the theoretical prediction. Our results indicate that the invariant resistivity theory could apply to the simple metals but at higher pressure above 5 GPa. These results were discussed in terms of the saturation of the dominant nuclear screening effect caused by the increasing difference in energy level between the Fermi level and the d-band with increasing pressure.

SUBMITTER: Ezenwa IC

PROVIDER: S-EPMC8509151 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Hydromechanical and structural properties of compacted loess have a significant impact on the stability and reliability of subbase and subgrade, which needs to be quickly determined in the field and laboratory. Hence, an electrical resistivity method was used to characterize the hydromechanical and structural properties of compacted loess during constant rate of strain compression. In the present work, compacted loess samples with a dry density of 1.7 g/cm3, a diameter of 64 mm, a height of 10 mm and different water content ranging from 5-25% were prepared. The constant rate of strain (CRS) tests were conducted by a developed oedometer cell equipped with a pair of horizontal circular electrodes (diameter of 20 mm) and vertical rectangular electrodes (width of 3.5 mm) to determine the electrical resistivity of compacted loess. The results showed that as average water content increases, plastic compression indices increase from 0.220 to 0.350 and the elastic compression indices increase from 0.0152 to 0.030, but they decrease to 0.167 and 0.010 and yield stress decreases from 381.28 kPa to 72.35 kPa. Moreover, as vertical strain increases, the variation trend of average formation factor and average shape factor for the lower water content decreases but increases for the maximum water content, and the anisotropy index first decrease and then tend to increase slightly, which indicates that the structural properties of unsaturated and saturated samples during compression exhibits different trend and the anisotropy of samples tend to be stable as vertical strain increases. As the water content increases, the average formation factor and average shape factor decrease, but the anisotropy index first decreases then increases, suggesting that water content has a significant impact on these electrical indices. More important, The coefficients of average formation factor decrease from 33.830 to -1.698 and the coefficients of average shape factor decrease from 8.339 to -0.398 as water content increases, whereas there is less variation for the coefficient of anisotropic index with a value of 2.190. An equation correlating average formation factor and water content and vertical strain is regressed to characterize the hydromechanical properties of compacted loess by measuring its impedance, which can be used to evaluate the stability of compacted loessic ground and subgrade.

Dataset Information

Electrical Resistivity of Cu and Au at High Pressure above 5 GPa: Implications for the Constant Electrical Resistivity Theory along the Melting Curve of the Simple Metals.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets