High-Performance Washable PM_2.5 Filter Fabricated with Laser-Induced Graphene.

ABSTRACT: This study demonstrates a novel application of laser-induced graphene (LIG) as a reusable conductive particulate matter (PM) filter. Four types of LIG-based filters were fabricated based on the laser-induced pyrolysis of thin polyimide (PI) sheets, each pyrolyzed on either a single side or both sides, with or without densification. The LIG filters exhibited a high removal efficiency while maintaining minimal pressure drop compared to a commercial fiberglass filter. The densified LIG (dLIG) filters displayed a higher PM_2.5 removal efficiency (>99.86%) than regular LIG filters. The dLIG filters also exhibited excellent durability when tested for washability by ultrasonication in tap water. After being cleaned and left to dry, the structures of the dLIG filters were well-maintained; their filtration efficiencies were also well-maintained (less than a 7% change in PM_2.5 removal efficiency), and their resistances only marginally increased (less than a 7% increase after five uses). These results demonstrate the robustness and reusability of the dLIG filters and the accessibility of their cleaning (not requiring aggressive cleaning agents). These promising features will enable the application of LIG in economical, scalable, and high-performance air cleaning.

SUBMITTER: Nguyen AP

PROVIDER: S-EPMC8509409 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Batch-fabricated high-performance graphene Hall elements.

Project description:Hall elements are by far the most widely used magnetic sensor. In general, the higher the mobility and the thinner the active region of the semiconductor used, the better the Hall device. While most common magnetic field sensors are Si-based Hall sensors, devices made from III-V compounds tend to favor over that based on Si. However these devices are more expensive and difficult to manufacture than Si, and hard to be integrated with signal-processing circuits for extending function and enforcing performance. In this article we show that graphene is intrinsically an ideal material for Hall elements which may harness the remarkable properties of graphene, i.e. extremely high carrier mobility and atomically thin active body, to create ideal magnetic sensors with high sensitivity, excellent linearity and remarkable thermal stability.

| S-EPMC3563039 | biostudies-literature

Laser-Induced Graphene Microsupercapacitors: Structure, Quality, and Performance.

Project description:Laser-induced graphene (LIG) is a graphenic material synthesized from a polymeric substrate through point-by-point laser pyrolysis. It is a fast and cost-effective technique, and it is ideal for flexible electronics and energy storage devices, such as supercapacitors. However, the miniaturization of the thicknesses of the devices, which is important for these applications, has still not been fully explored. Therefore, this work presents an optimized set of laser conditions to fabricate high-quality LIG microsupercapacitors (MSC) from 60 µm thick polyimide substrates. This is achieved by correlating their structural morphology, material quality, and electrochemical performance. The fabricated devices show a high capacitance of 22.2 mF/cm2 at 0.05 mA/cm2, as well as energy and power densities comparable to those of similar devices that are hybridized with pseudocapacitive elements. The performed structural characterization confirms that the LIG material is composed of high-quality multilayer graphene nanoflakes with good structural continuity and an optimal porosity.

| S-EPMC10005378 | biostudies-literature

Flexible and Highly Sensitive Strain Sensor Based on Laser-Induced Graphene Pattern Fabricated by 355 nm Pulsed Laser.

Project description:A laser-induced-graphene (LIG) pattern fabricated using a 355 nm pulsed laser was applied to a strain sensor. Structural analysis and functional evaluation of the LIG strain sensor were performed by Raman spectroscopy, scanning electron microscopy (SEM) imaging, and electrical-mechanical coupled testing. The electrical characteristics of the sensor with respect to laser fluence and focal length were evaluated. The sensor responded sensitively to small deformations, had a high gauge factor of ~160, and underwent mechanical fracture at 30% tensile strain. In addition, we have applied the LIG sensor, which has high sensitivity, a simple manufacturing process, and good durability, to human finger motion monitoring.

| S-EPMC6891597 | biostudies-literature

Luminescent graphene quantum dots fabricated by pulsed laser synthesis.

Project description:Graphene has been the subject of intense research in recent years due to its unique electrical, optical and mechanical properties. Furthermore, it is expected that quantum dots of graphene would make their way into devices due to their structure and composition which unify graphene and quantum dots properties. Graphene quantum dots (GQDs) are planar nano flakes with a few atomic layers thick and with a higher surface-to-volume ratio than spherical carbon dots (CDs) of the same size. We have developed a pulsed laser synthesis (PLS) method for the synthesis of GQDs that are soluble in water, measure 2-6 nm across, and are about 1-3 layers thick. They show strong intrinsic fluorescence in the visible region. The source of fluorescence can be attributed to various factors, such as: quantum confinement, zigzag edge structure, and surface defects. Confocal microscopy images of bacteria exposed to GQDs show their suitability as biomarkers and nano-probes in high contrast bioimaging.

| S-EPMC4999264 | biostudies-literature

Long-lifetime water-washable ceramic catalyst filter for air purification.

Project description:Particulate matter (PM) and volatile organic compounds (VOCs) are recognised as hazardous air pollutants threatening human health. Disposable filters are generally used for air purification despite frequent replacement and waste generation problems. However, the development of a novel regenerable and robust filter for long-term use is a huge challenge. Here, we report on a new class of facile water-washing regenerable ceramic catalyst filters (CCFs), developed to simultaneously remove PM (>95%) and VOCs (>82%) in single-pass and maximized space efficiency by coating the inner and outer filter channels with an inorganic membrane and a Cu2O/TiO2 photocatalyst, respectively. The CCFs reveal four-fold increase in the maximum dust loading capacity (approximately 20 g/L) in relation to conventional filters (5 g/L), and can be reused after ten regeneration capability with simple water washing retaining initial PM and VOC removal performances. Thus, the CCFs can be well-suited for indoor and outdoor air purification for 20 years, which shows a huge increase in lifetime compared to the 6-month lifespan of conventional filters. Finally, we believe that the development and implementation of CCFs for air purification can open new avenues for sustainable technology through renewability and zero-waste generation.

| S-EPMC9932083 | biostudies-literature

Laser Scribed Graphene Cathode for Next Generation of High Performance Hybrid Supercapacitors.

Project description:Hybrid supercapacitors have been regarded as next-generation energy storage devices due to their outstanding performances. However, hybrid supercapacitors remain a great challenge to enhance the energy density of hybrid supercapacitors. Herein, a novel approach for high-energy density hybrid supercapacitors based on a laser scribed graphene cathode and AlPO4-carbon hybrid coated H2Ti12O25 (LSG/H-HTO) was designed. Benefiting from high-energy laser scribed graphene and high-power H-HTO, it was demonstrated that LSG/H-HTO delivers superior energy and power densities with excellent cyclability. Compared to previous reports on other hybrid supercapacitors, LSG/H-HTO electrode composition shows extraordinary energy densities of ~70.8?Wh/kg and power densities of ~5191.9?W/kg. Therefore, LSG/H-HTO can be regarded as a promising milestone in hybrid supercapacitors.

| S-EPMC5970221 | biostudies-literature

Flash healing of laser-induced graphene.

Project description:The advancement of laser-induced graphene (LIG) technology has streamlined the fabrications of flexible graphene devices. However, the ultrafast kinetics triggered by laser irradiation generates intrinsic amorphous characteristics, leading to high resistivity and compromised performance in electronic devices. Healing graphene defects in specific patterns is technologically challenging by conventional methods. Herein, we report the rapid rectification of LIG's topological defects by flash Joule heating in milliseconds (referred to as F-LIG), whilst preserving its overall structure and porosity. The F-LIG exhibits a decreased ID/IG ratio from 0.84 - 0.33 and increased crystalline domain from Raman analysis, coupled with a 5-fold surge in conductivity. Pair distribution function and atomic-resolution imaging delineate a broader-range order of F-LIG with a shorter C-C bond of 1.425 Å. The improved crystallinity and conductivity of F-LIG with excellent flexibility enables its utilization in high-performance soft electronics and low-voltage disinfections. Notably, our F-LIG/polydimethylsiloxane strain sensor exhibits a gauge factor of 129.3 within 10% strain, which outperforms pristine LIG by 800%, showcasing significant potential for human-machine interfaces.

| S-EPMC10995154 | biostudies-literature

Simple fabrication of Co<sub>3</sub>O<sub>4</sub> nanoparticles on N-doped laser-induced graphene for high-performance supercapacitors.

Project description:This study demonstrates a simple strategy to fabricate Co3O4 on N-doped laser-induced graphene (Co3O4-NLIG) based on duplicate laser pyrolysis, enabling the in situ generation of Co3O4 nanoparticles and heteroatom doping in laser-induced graphene (LIG). Morphological analyses reveal the uniform distribution of Co3O4 nanoparticles on the surface of the LIG structure. The modification of NLIG with Co3O4 nanoparticles results in impressive electrochemical performance due to the contributions from electric double-layer capacitance and pseudocapacitance. The optimal Co3O4-NLIG is produced at 20 wt% cobalt precursor loading (Co3O4-NLIG-20). In a three-electrode setup, this electrode exhibits a specific areal capacitance (C A) of 216.3 mF cm-2 at a current density of 0.5 mA cm-2 in a 1 M KOH electrolyte. When the optimal electrodes are assembled into a solid-state supercapacitor (Co3O4-NLIG-SC) using a poly(vinyl alcohol) phosphoric acid (PVA-H3PO4) gel electrolyte, a C A of 17.96 mF cm-2 is obtained with good cycling stability.

| S-EPMC9044152 | biostudies-literature

Kaleidoscopic imaging patterns of complex structures fabricated by laser-induced deformation.

Project description:Complex surface structures have stimulated a great deal of interests due to many potential applications in surface devices. However, in the fabrication of complex surface micro-/nanostructures, there are always great challenges in precise design, or good controllability, or low cost, or high throughput. Here, we present a route for the accurate design and highly controllable fabrication of surface quasi-three-dimensional (quasi-3D) structures based on a thermal deformation of simple two-dimensional laser-induced patterns. A complex quasi-3D structure, coaxially nested convex-concave microlens array, as an example, demonstrates our capability of design and fabrication of surface elements with this method. Moreover, by using only one relief mask with the convex-concave microlens structure, we have gotten hundreds of target patterns at different imaging planes, offering a cost-effective solution for mass production in lithography and imprinting, and portending a paradigm in quasi-3D manufacturing.

| S-EPMC5476795 | biostudies-literature

Laser induced white lighting of graphene foam.

Project description:Laser induced white light emission was observed from porous graphene foam irradiated with a focused continuous wave beam of the infrared laser diode. It was found that the intensity of the emission increases exponentially with increasing laser power density, having a saturation level at ca. 1.5 W and being characterized by stable emission conditions. It was also observed that the white light emission is spatially confined to the focal point dimensions of the illuminating laser light. Several other features of the laser induced white light emission were also discussed. It was observed that the white light emission is highly dependent on the electric field intensity, allowing one to modulate the emission intensity. The electric field intensity ca. 0.5 V/μm was able to decrease the white light intensity by half. Origins of the laser-induced white light emission along with its characteristic features were discussed in terms of avalanche multiphoton ionization, inter-valence charge transfer and possible plasma build-up processes. It is shown that the laser-induced white light emission may be well utilized in new types of white light sources.

| S-EPMC5256029 | biostudies-literature