Preparation of Crystalline LaFeO₃ Nanoparticles at Low Calcination Temperature: Precursor and Synthesis Parameter Effects.

ABSTRACT: Substantial effort has been devoted to fabricating nanocrystalline lanthanum ferrite (LaFeO₃), and calcination is the crucial process of crystallization in both high-temperature strategies and wet chemical methods. Lowering the calcination temperature gives the ability to resist the growth and agglomeration of nanoparticles, therefore contributing to preserve their unique nanostructures and properties. In this work, we prepared crystalline LaFeO₃ nanoparticles with a calcination process at 500 °C, lower than the calcination temperature required in most wet chemistry methods. Correspondingly, the experimental conditions, including stoichiometric ratios, pH values, precipitants, complexant regent, and the calcination temperatures, were investigated. We found that the crystalline LaFeO₃ was formed with crystalline NaFeO₂ after calcination at 500 °C. Furthermore, the structure of FeO₆ octahedra that formed in coprecipitation was associated with the process of crystallization, which was predominantly determined by calcination temperature. Moreover, an illusion of pure-phase LaFeO₃ was observed when investigated by X-ray diffraction spectroscopy, which involves amorphous sodium ferrite or potassium ferrite, respectively. These findings can help prepare nanostructured perovskite oxides at low calcination temperatures.

SUBMITTER: Jiang W

PROVIDER: S-EPMC8509417 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Organozinc Precursor-Derived Crystalline ZnO Nanoparticles: Synthesis, Characterization and Their Spectroscopic Properties.

Project description:Crystalline ZnO-ROH and ZnO-OR (R = Me, Et, iPr, nBu) nanoparticles (NPs) have been successfully synthesized by the thermal decomposition of in-situ-formed organozinc complexes Zn(OR)? deriving from the reaction of Zn[N(SiMe?)?]? with ROH and of the freshly prepared Zn(OR)? under an identical condition, respectively. With increasing carbon chain length of alkyl alcohol, the thermal decomposition temperature and dispersibility of in-situ-formed intermediate zinc alkoxides in oleylamine markedly influenced the particle sizes of ZnO-ROH and its shape (sphere, plate-like aggregations), while a strong diffraction peak-broadening effect is observed with decreasing particle size. For ZnO-OR NPs, different particle sizes and various morphologies (hollow sphere or cuboid-like rod, solid sphere) are also observed. As a comparison, the calcination of the fresh-prepared Zn(OR)? generated ZnO-R NPs possessing the particle sizes of 5.4~34.1 nm. All crystalline ZnO nanoparticles are characterized using X-ray diffraction analysis, electron microscopy and solid-state ¹H and 13C nuclear magnetic resonance (NMR) spectroscopy. The size effect caused by confinement of electrons' movement and the defect centres caused by unpaired electrons on oxygen vacancies or ionized impurity heteroatoms in the crystal lattices are monitored by UV-visible spectroscopy, electron paramagnetic resonance (EPR) and photoluminescent (PL) spectroscopy, respectively. Based on the types of defects determined by EPR signals and correspondingly defect-induced probably appeared PL peak position compared to actual obtained PL spectra, we find that it is difficult to establish a direct relationship between defect types and PL peak position, revealing the complication of the formation of defect types and photoluminescence properties.

| S-EPMC5791109 | biostudies-literature

Low-Temperature Synthesis of Titanium Oxynitride Nanoparticles.

Project description:The synthesis of transition metal oxynitrides is complicated by extreme reaction conditions such as high temperatures and/or high pressures. Here, we show an unprecedented solution-based synthesis of narrowly dispersed titanium oxynitride nanoparticles of cubic shape and average size of 65 nm. Their synthesis is performed by using titanium tetrafluoride and lithium nitride as precursors alongside trioctylphosphine oxide (TOPO) and cetrimonium bromide (CTAB) as stabilizers at temperatures as low as 250 °C. The obtained nanoparticles are characterized in terms of their shape and optical properties, as well as their crystalline rock-salt structure, as confirmed by XRD and HRTEM analysis. We also determine the composition and nitrogen content of the synthesized particles using XPS and EELS. Finally, we investigate the applicability of our titanium oxynitride nanoparticles by compounding them into carbon fiber electrodes to showcase their applicability in energy storage devices. Electrodes with titanium oxynitride nanoparticles exhibit increased capacity compared to the pure carbon material.

| S-EPMC8065472 | biostudies-literature

Chemical State of Potassium on the Surface of Iron Oxides: Effects of Potassium Precursor Concentration and Calcination Temperature.

Project description:Potassium is used extensively as a promoter with iron catalysts in Fisher-Tropsch synthesis, water-gas shift reactions, steam reforming, and alcohol synthesis. In this paper, the identification of potassium chemical states on the surface of iron catalysts is studied to improve our understanding of the catalytic system. Herein, potassium-doped iron oxide (α-Fe2O3) nanomaterials are synthesized under variable calcination temperatures (400-800 °C) using an incipient wetness impregnation method. The synthesis also varies the content of potassium nitrate deposited on superfine iron oxide with a diameter of 3 nm (Nanocat®) to reach atomic ratios of 100 Fe:x K (x = 0-5). The structure, composition, and properties of the synthesized materials are investigated by X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, Fourier-transform infrared, Raman spectroscopy, inductively coupled plasma-atomic emission spectroscopy, and X-ray photoelectron spectroscopy, as well as transmission electron microscopy, with energy-dispersive X-ray spectroscopy and selected area electron diffraction. The hematite phase of iron oxide retains its structure up to 700 °C without forming any new mixed phase. For compositions as high as 100 Fe:5 K, potassium nitrate remains stable up to 400 °C, but at 500 °C, it starts to decompose into nitrites and, at only 800 °C, it completely decomposes to potassium oxide (K2O) and a mixed phase, K2Fe22O34. The doping of potassium nitrate on the surface of α-Fe2O3 provides a new material with potential applications in Fisher-Tropsch catalysis, photocatalysis, and photoelectrochemical processes.

| S-EPMC9610504 | biostudies-literature

Synthesis of an Alleged Byproduct Precursor in Iodixanol Preparation.

Project description:N 1,N 3-Bis(2,3-dihydroxypropyl)-2,4,6-triiodo-5-(N-(oxiran-2-ylmethyl)acetamido)isophthalamide (1), the alleged precursor of several minor byproducts formed when the X-ray contrast agent iodixanol is synthesized from 5-acetamido-N 1,N 3-bis(2,3-dihydroxypropyl)-2,4,6-triiodoisophthalamide (2), has been successfully prepared with an overall yield of 25%. Epoxide 1 enabled the confirmation of its presence in the reaction mixture during the preparation of iodixanol when amide 2 was used as the starting material.

| S-EPMC6644432 | biostudies-literature

Green synthesis of crystalline bismuth nanoparticles using lemon juice.

Project description:Lemon juice effectively served as a reducing and capping agent for an easy, cost-effective, and green synthesis of crystalline bismuth nanoparticles (BiNPs) in basic aqueous media. Spherical BiNPs with a rhombohedral crystalline structure are capped by phytochemicals and stably dispersible in aqueous media. The BiNPs effectively catalyze the reduction of 4-nitrophenol to 4-aminophenol by NaBH4.

| S-EPMC9037828 | biostudies-literature

Low-Temperature Vapor-Phase Synthesis of Single-Crystalline Gold Nanostructures: Toward Exceptional Electrocatalytic Activity for Methanol Oxidation Reaction.

Project description:Au nanostructures (Au NSs) have been considered promising materials for applications in fuel cell catalysis, electrochemistry, and plasmonics. For the fabrication of high-performance Au NS-based electronic or electrochemical devices, Au NSs should have clean surfaces and be directly supported on a substrate without any mediating molecules. Herein, we report the vapor-phase synthesis of Au NSs on a fluorine-doped tin oxide (FTO) substrate at 120 °C and their application to the electrocatalytic methanol oxidation reaction (MOR). By employing AuCl as a precursor, the synthesis temperature for Au NSs was reduced to under 200 °C, enabling the direct synthesis of Au NSs on an FTO substrate in the vapor phase. Considering that previously reported vapor-phase synthesis of Au NSs requires a high temperature over 1000 °C, this proposed synthetic method is remarkably simple and practical. Moreover, we could selectively synthesize Au nanoparticles (NPs) and nanoplates by adjusting the location of the substrate, and the size of the Au NPs was controllable by changing the reaction temperature. The synthesized Au NSs are a single-crystalline material with clean surfaces that achieved a high methanol oxidation current density of 14.65 mA/cm² when intimately supported by an FTO substrate. We anticipate that this novel synthetic method can widen the applicability of vapor-phase synthesized Au NSs for electronic and electrochemical devices.

| S-EPMC6523424 | biostudies-literature

One-Step Low Temperature Synthesis of CeO<sub>2</sub> Nanoparticles Stabilized by Carboxymethylcellulose.

Project description:An elegant method of one-pot reaction at room temperature for the synthesis of nanocomposites consisting of cerium containing nanoparticles stabilized by carboxymethyl cellulose (CMC) macromolecules was introduced. The characterization of the nanocomposites was carried out with a combination of microscopy, XRD, and IR spectroscopy analysis. The type of crystal structure of inorganic nanoparticles corresponding to CeO2 was determined and the mechanism of nanoparticle formation was suggested. It was demonstrated that the size and shape of the nanoparticles in the resulting nanocomposites does not depend on the ratio of the initial reagents. Spherical particles with a mean diameter 2-3 nm of were obtained in different reaction mixtures with a mass fraction of cerium from 6.4 to 14.1%. The scheme of the dual stabilization of CeO2 nanoparticles with carboxylate and hydroxyl groups of CMC was proposed. These findings demonstrate that the suggested easily reproducible technique is promising for the large-scale development of nanoceria-containing materials.

| S-EPMC10058267 | biostudies-literature

Iron Carbonate Beneficiation Through Reductive Calcination - Parameter Optimization to Maximize Methane Formation.

Project description:Direct iron carbonate reduction through reductive calcination in a hydrogen atmosphere is a high-potential candidate for environmentally benign pig iron production. In addition to the direct formation of elemental iron in one reaction step, carbon dioxide is only partially released from the carbonate. Instead, carbon monoxide, methane, and higher hydrocarbons form as gaseous reaction products. The experimental study described here is based on Mg-Mn substituted iron carbonate ore. First, the chemical thermodynamics of the reductive calcination of iron, magnesium, and manganese carbonate are discussed. The influence of temperature and pressure on equilibrium conversion is reviewed together with the accessible products. Results for the reductive calcination of mineral iron carbonate in a tubular reactor setup are presented. The methane yield was optimized via statistically planned design of experiments. The gauge pressure and temperature showed a statistically significant effect on the total iron carbonate conversion, as well as on carbon monoxide, and methane yield.

| S-EPMC6686975 | biostudies-literature

Monodisperse colloidal gallium nanoparticles: synthesis, low temperature crystallization, surface plasmon resonance and Li-ion storage.

Project description:We report a facile colloidal synthesis of gallium (Ga) nanoparticles with the mean size tunable in the range of 12-46 nm and with excellent size distribution as small as 7-8%. When stored under ambient conditions, Ga nanoparticles remain stable for months due to the formation of native and passivating Ga-oxide layer (2-3 nm). The mechanism of Ga nanoparticles formation is elucidated using nuclear magnetic resonance spectroscopy and with molecular dynamics simulations. Size-dependent crystallization and melting of Ga nanoparticles in the temperature range of 98-298 K are studied with X-ray powder diffraction, specific heat measurements, transmission electron microscopy, and X-ray absorption spectroscopy. The results point to delta (?)-Ga polymorph as a single low-temperature phase, while phase transition is characterized by the large hysteresis and by the large undercooling of crystallization and melting points down to 140-145 and 240-250 K, respectively. We have observed size-tunable plasmon resonance in the ultraviolet and visible spectral regions. We also report stable operation of Ga nanoparticles as anode material for Li-ion batteries with storage capacities of 600 mAh g(-1), 50% higher than those achieved for bulk Ga under identical testing conditions.

| S-EPMC4525770 | biostudies-literature

Preparation and Properties of Organic-Inorganic Hybrid Antireflection Films Made by a Low-Temperature Process Using Hollow Silica Nanoparticles.

Project description:Layers made of hollow silica nanoparticles have potential applications as antireflection films with lower refractive index values compared with existing materials such as silica glass (1.50) and magnesium fluoride (1.38). The advantages of such nanoparticles result from interactions between the solid shell, the cavity phase core, and the voids between particles. To obtain practical antireflection films, it is necessary to control the number of layers of these hollow silica nanoparticles and to fill the gaps between particles with a solid. In the present study, antireflection films were prepared by applying a coating of hollow silica nanoparticles dispersed in a UV-curable monomer solution onto plastic substrates. After film formation and exposure to UV light, the voids between the nanoparticles were completely filled with a polymer matrix. Tuning the particle concentration in the coating solution allowed the formation of antireflection films comprising one to three layers of the hollow silica nanoparticles. The reflectance of the films was dependent on the number of layers, and a 100 nm thick film in which two layers of hollow silica nanoparticles were precisely arranged showed the lowest reflectance of 0.92% at 550 nm wavelength, equivalent to a refractive index of 1.23. Because the voids between particles were filled with the polymer, these films resisted contamination during manual handling and so would be expected to maintain low reflectance during practical applications. This work demonstrates that nanosized inorganic-organic hybrid films composed of hollow silica nanoparticles and a UV-curable resin can exhibit optical properties and structural integrity that cannot be achieved by either substance alone.

| S-EPMC8015096 | biostudies-literature