Aging Resistance of Biocomposites Crosslinked with Silica and Quercetin.

ABSTRACT: This research focuses on revealing the double role of quercetin accompanied by silica in epoxidized natural rubber. A crosslinking ability with antioxidative properties exists and reveals the dependence of these functions on quercetin content. Here, the aging resistance of self-healable biocomposites was analyzed. The self-healing properties were presented in our previous work. The stabilizing effect of quercetin applied as a crosslinking agent has been studied in epoxidized natural rubber with a 50 mol% of epoxidation (ENR-50). Some of five -OH moiety groups existing in the quercetin structure are able to react with epoxy rings of ENR-50 and cure this elastomer, whereas other free hydroxyl groups can donate the hydrogen molecule to a radical molecule, stabilizing it. The aging resistance of prepared composites was estimated by mechanical tests conducted before and after different types of aging, as well as by differences in color and surface energy between aged and un-aged samples. Changes within the oxygen function, which occurred as a result of the aging process, were observed using FT-IR absorbance spectroscopy. Furthermore, the impact of quercetin content on composites' thermal stability was investigated by thermogravimetry (TGA). According to the results, a proper dose of quercetin can act as a crosslinker and antioxidant in ENR-50 at the same time.

SUBMITTER: Masek A

PROVIDER: S-EPMC8509444 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:This paper presents the synthesis and physicochemical characterization of a new hybrid composite. Its main goals are evaluating the structure and studying the thermal and mechanical properties of the crosslinked polymeric materials based on varying chemical properties of the compounds. As an organic crosslinking monomer, bisphenol A glycerolate diacrylate (BPA.GDA) was used. Trimethoxyvinylsilane (TMVS) and N-vinyl-2-pyrrolidone (NVP) were used as comonomers and active diluents. The inorganic fraction was the silica in the form of nanoparticles (NANOSiO2). The hybrid composites were obtained by the bulk polymerization method using the UV initiator Irqacure 651 with a constant weight ratio of the tetrafunctional monomer BPA.GDA to TMVS or NVP (7:3 wt.%) and different wt.% of silica nanoparticles (0, 1, 3%). The proper course of polymerization was confirmed by the ATR/FTIR spectroscopy and SEM EDAX analysis. In the composites spectra the signals correspond to the C=O groups from NVP at 1672-1675 cm-1, and the vibrations of Si-O-C and Si-O-Si groups at 1053-1100 cm-1 from TMVS and NANOSiO2 are visible. Thermal stabilities of the obtained composites were studied by a differential scanning calorimetry DSC. Compared to NVP the samples with TMVS degraded in one stage (422.6-425.3 °C). The NVP-derived materials decomposed in three stages (three endothermic effects on the DSC curves). The addition of NANOSiO2 increases the temperature of composites maximum degradation insignificantly. Additionally, the Shore D hardness test was carried out with original metrological measurements of changes in diameter after indentation in relation to the type of material. The accuracy analysis of the obtained test results was based on a comparative analysis of graphical curves obtained from experimental tests. The values of the changes course of similarity in the examined factors, represented by those of characteristic coefficients were determined based on the Fréchet's theory.

Dataset Information

Aging Resistance of Biocomposites Crosslinked with Silica and Quercetin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets