In vivo study of light-driven naproxen release from gated mesoporous silica drug delivery system.

ABSTRACT: A drug delivery system based on mesoporous particles MCM-41 was post-synthetically modified by photo-sensitive ligand, methyl-(2E)-3-(4-(triethoxysilyl)-propoxyphenyl)-2-propenoate (CA) and the pores of MCM-41 particles were loaded with Naproxen sodium salt (NAP). The CA was used as a photoactive molecule that can undergo a reversible photo-dimerization by [2π + 2π] cycloaddition when irradiated with UV light of specific wavelengths. Thus, it has a function of gate-keeper that is responsible for opening/closing the pores and minimizing premature release of NAP. The physicochemical properties of the prepared system were studied by infrared spectroscopy (IR), nitrogen adsorption measurements, thermogravimetric analysis (TGA), scanning transmission electron microscopy (STEM) and energy dispersive X-ray spectroscopy (EDX). The mechanism of the opening/closing pores was confirmed by UV measurements. In vitro and in vivo drug release experiments and the concentration of released NAP was determined by UV spectroscopy and high-performance liquid chromatography (HPLC). In vivo drug release in the blood circulatory system of rats has demonstrated the effective photo-cleavage reaction of CA molecules after UV-light stimulation. The localization and morphological changes of the particles were studied in the blood and liver of rats at different time intervals. The particles in the blood have been shown to retain their original rod-like shape, and the particles in the liver have been hydrolysed, which has resulted in spherical shape with a reduced size.

SUBMITTER: Almasi M

PROVIDER: S-EPMC8511123 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Tunable glutathione (GSH)-sensitive hollow mesoporous silica nanoparticles (HMSiO2 NPs) were developed using a structural difference-based selective etching strategy. These organosilica hollow nanoparticles contained disulfide linkages (S-S) in the outer shell which were degraded by GSH. The particles were compared with their nonGSH-sensitive tetraethyl orthosilicate (TEOS) HMSiO2 counterparts in terms of their synthesis method, characterization, doxorubicin (DOX) release profile, and in vitro cytotoxicity in MCF-7 breast cancer cells. Transmission electron microscopy (TEM) of the particles indicated that the fabricated HMSiO2 NPs had an average diameter of 130?±?5?nm. Thermogravimetric analysis (TGA) revealed that GSH-sensitive particles had approximately 5.3% more weight loss than TEOS HMSiO2 NPs. Zeta potential of these redox-responsive particles was -23?±?1?mV at pH?6 in deionized (DI) water. Nitrogen adsorption-desorption isotherm revealed that the surface area of the hollow mesoporous nanoreservoirs was roughly 446?±?6?m2?g-1 and the average diameter of the pores was 2.3?±?0.5?nm. TEM images suggest that the nanoparticles started to lose mass integrity from Day 1. The particles showed a high loading capacity for DOX (8.9?±?0.5%) as a model drug, due to the large voids existing in the hollow structures. Approximately 58% of the incorporated DOX released within 14?days in phosphate buffered saline (PBS) at pH?6 and in the presence of 10?mM of GSH, mimicking intracellular tumor microenvironment while release from TEOS HMSiO2 NPs was only c.a. 18%. The uptake of these hollow nanospheres by MCF-7 cells and RAW 264.7 macrophages was evaluated using TEM and confocal microscopy. The nanospheres were shown to accumulate in the endolysosomal compartments after incubation for 24?h with the maximum uptake of c.a. 2.1?±?0.3% and 5.2?±?0.4%, respectively. Cytotoxicity of the nanospheres was investigated using CCK-8 assay. Results indicate that intact hollow particles (both GSH-sensitive and TEOS HMSiO2 NPs) were nontoxic to MCF-7 cells after incubation for 24?h within the concentration range of 0-1000??g?ml-1. DOX-loaded GSH-sensitive nanospheres containing 6??g?ml-1 of DOX killed c.a. 51% of MCF-7 cells after 24?h while TEOS HMSiO2 NPs killed c.a. 20% with the difference being statistically significant. Finally, cytotoxicity data in RAW 264.7 macrophages and NIH 3?T3 fibroblasts shows that intact GSH-sensitive HMSiO2 NPs did not show any toxic effects on these cells with the concentrations equal or <125??g?ml-1.

Dataset Information

In vivo study of light-driven naproxen release from gated mesoporous silica drug delivery system.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets