Electrospinning of a Copolymer PVDF-co-HFP Solved in DMF/Acetone: Explicit Relations among Viscosity, Polymer Concentration, DMF/Acetone Ratio and Mean Nanofiber Diameter.

ABSTRACT: The process of electrospinning polymer solutions depends on many entry parameters, with each having a significant impact on the overall process and where complexity prevents the expression of their interplay. However, under the assumption that most parameters are fixed, it is possible to evaluate the mutual relations between pairs or triples of the chosen parameters. In this case, the experiments were carried out with a copolymer poly(vinylidene-co-hexafluoropropylene) solved in mixed N,N'-dimethylformamide (DMF)/acetone solvent for eight polymer concentrations (8, 10, 12, 15, 18, 21, 24, and 27 wt.%) and five DMF/acetone ratios (1/0, 4/1, 2/1, 1/1, 1/2). Processing of the obtained data (viscosity, mean nanofiber diameter) aimed to determine algebraic expressions relating both to viscosity and a mean nanofiber diameter with polymer concentration, as well as DMF/acetone ratio. Moreover, a master curve relating these parameters with no fitting factors was proposed continuously covering a sufficiently broad range of concentration as well as DMF/acetone ratio. A comparison of algebraic evaluation with the experimental data seems to be very good (the mean deviation for viscosity was about 2%, while, for a mean nanofiber diameter was slightly less than 10%).

SUBMITTER: Filip P

PROVIDER: S-EPMC8512270 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Electrospinning is a versatile technique to produce nanofibrous membranes with applications in filtration, biosensing, biomedical and tissue engineering. The structural and therefore physical properties of electrospun fibers can be finely tuned by changing the electrospinning parameters. The large parameter window makes it challenging to optimize the properties of fibers for a specific application. Therefore, a fundamental understanding of the multiscale structure of fibers and its correlation with their macroscopic behaviors is required for the design and production of systems with dedicated applications. In this study, we demonstrate that the properties of poly(vinylidene fluoride-co-hexafluoro propylene) (PVDF-HFP) electrospun fibers can be tuned by changing the rotating drum speed used as a collector during electrospinning. Indeed, with the help of multiscale characterization techniques such as scanning electron microscopy (SEM), small-angle X-ray scattering (SAXS), and wide-angle X-ray scattering (WAXS), we observe that increasing the rotating drum speed not only aligns the fibers but also induces polymeric chain rearrangements at the molecular scale. Such changes result in enhanced mechanical properties and an increase of the piezoelectric β-phase of the PVDF-HFP fiber membranes. We detect nanostructural deformation behaviors when the aligned fibrous membrane is uniaxially stretched along the fiber alignment direction, while an increase in the alignment of the fibers is observed for randomly aligned samples. This was analyzed by performing in situ SAXS measurements coupled with uniaxial tensile loading of the fibrous membranes along the fiber alignment direction. The present study shows that fibrous membranes can be produced with varying degrees of fiber orientation, piezoelectric β-phase content, and mechanical properties by controlling the speed of the rotating drum collector during the fiber production. Such aligned fiber membranes have potential applications for neural or musculoskeletal tissue engineering.

Dataset Information

Electrospinning of a Copolymer PVDF-co-HFP Solved in DMF/Acetone: Explicit Relations among Viscosity, Polymer Concentration, DMF/Acetone Ratio and Mean Nanofiber Diameter.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets