Roles of Small Polyetherimide Moieties on Thermal Stability and Fracture Toughness of Epoxy Blends.

ABSTRACT: Bisphenol A diglycidyl ether (DGEBA) was blended with polyetherimide (PEI) as a thermoplastic toughener for thermal stability and mechanical properties as a function of PEI contents. The thermal stability and mechanical properties were investigated using a thermogravimetric analyzer (TGA) and a universal test machine, respectively. The TGA results indicate that PEI addition enhanced the thermal stability of the epoxy resins in terms of the integral procedural decomposition temperature (IPDT) and pyrolysis activation energy (E_t). The IPDT and E_t values of the DGEBA/PEI blends containing 2 wt% of PEI increased by 2% and 22%, respectively, compared to those of neat DGEBA. Moreover, the critical stress intensity factor and critical strain energy release rate for the DGEBA/PEI blends containing 2 wt% of PEI increased by 83% and 194%, respectively, compared to those of neat DGEBA. These results demonstrate that PEI plays a key role in enhancing the flexural strength and fracture toughness of epoxy blends. This can be attributed to the newly formed semi-interpenetrating polymer networks (semi-IPNs) composed of the epoxy network and linear PEI.

SUBMITTER: Lee SY

PROVIDER: S-EPMC8512680 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effect of Ambient Plasma Treatments on Thermal Conductivity and Fracture Toughness of Boron Nitride Nanosheets/Epoxy Nanocomposites.

Project description:With the rapid growth in the miniaturization and integration of modern electronics, the dissipation of heat that would otherwise degrade the device efficiency and lifetime is a continuing challenge. In this respect, boron nitride nanosheets (BNNS) are of significant attraction as fillers for high thermal conductivity nanocomposites due to their high thermal stability, electrical insulation, and relatively high coefficient of thermal conductivity. Herein, the ambient plasma treatment of BNNS (PBNNS) for various treatment times is described for use as a reinforcement in epoxy nanocomposites. The PBNNS-loaded epoxy nanocomposites are successfully manufactured in order to investigate the thermal conductivity and fracture toughness. The results indicate that the PBNNS/epoxy nanocomposites subjected to 7 min plasma treatment exhibit the highest thermal conductivity and fracture toughness, with enhancements of 44 and 110%, respectively, compared to the neat nanocomposites. With these enhancements, the increases in surface free energy and wettability of the PBNNS/epoxy nanocomposites are shown to be attributable to the enhanced interfacial adhesion between the filler and matrix. It is demonstrated that the ambient plasma treatments enable the development of highly dispersed conductive networks in the PBNNS epoxy system.

| S-EPMC9823992 | biostudies-literature

On the Residual Stresses and Fracture Toughness of Glass/Carbon Epoxy Composites.

Project description:The resistance to delamination in polymer composite depends on their constituents, manufacturing process, environmental factors, specimen geometry, and loading conditions. The manufacturing of laminated composites is usually carried out at an elevated temperature, which induces thermal stresses in composites mainly due to a mismatch in the coefficient of thermal expansion (CTE) of fiber and matrix. This work aims to investigate the effect of these process-induced stresses on mode-I interlaminar fracture toughness (GI) of Glass-Carbon-Epoxy (GCE) and Glass-Epoxy (GE) composites. These composites are prepared using a manual layup technique and cured under room temperature, followed by post-curing using different curing conditions. Double cantilever beam (DCB) specimens were used to determine GI experimentally. The slitting technique was used to estimate residual stresses (longitudinal and transverse direction of crack growth) inherited in cured composites and the impact of these stresses on GI was investigated. Delaminated surfaces of composites were examined using a scanning electron microscopy (SEM) to investigate the effect of post-curing on the mode-I failure mechanism. It was found that GI of both GE and GEC composites are sensitive to the state of residual stress in the laminas. The increase in the GI of laminates can also be attributed to an increase in matrix deformation and fiber-matrix interfacial bond with the increase in post-curing temperature.

| S-EPMC9609049 | biostudies-literature

Thermal and Mechanical Characterization of Epoxy/Polyimide Blends via Postcuring Process.

Project description:In this study, the effects of polyimide (PI) content and postcuring on thermal and mechanical properties in PI and epoxy (EP) blending systems were investigated. EP/PI (EPI) blending reduced the crosslinking density and improved the flexural and impact strength due to ductility. On the other hand, in the postcuring of EPI, the thermal resistance improved due to the increased crosslinking density and the flexural strength increased by up to 57.89% due to the enhanced stiffness, but the impact strength decreased by up to 59.54%. EPI blending induced the improvement in the mechanical properties of EP, and the postcuring process of EPI was shown to be an effective method to improve heat resistance. It was confirmed that EPI blending induces improvement in the mechanical properties of EP, and the postcuring process of EPI is an effective method for improving heat resistance.

| S-EPMC10007675 | biostudies-literature

PET/Bio-Based Terpolyester Blends with High Dimensional Thermal Stability.

Project description:To improve the dimensional thermal stability of polyethylene terephthalate (PET), a poly(ethylene glycol 1,4-cyclohexane dimethylene (CHDM) isosorbide (ISB) terephthalate) (PEICT) known as ECOZEN®T110 (EZT) was introduced into PET using a melt blending technique. The miscibility, morphology, and thermal properties of the PET/EZT samples were investigated. The introduction of amorphous EZT into semi-crystalline PET increased the glass transition temperature (Tg) but decreased the crystallinity, which could be related to the transesterification reaction. By adding EZT contents up to 20%, the PET/EZT samples showed a single Tg, which indicated the miscibility between PET and EZT. However, two Tg values were observed in the PET/EZT samples with higher EZT contents (30-70%), indicating partial miscibility. This may have been due to the slightly different rheological and thermodynamic parameters that were affected by a higher ratio of bulky (rigid ISB and ductile CHDM) groups in EZT. However, the heat distortion temperature of the PET/EZT samples remarkably increased, which indicated that the dimensional stability was truly enhanced. Although the crystallinity of the PET/EZT samples decreased with increasing EZT content, the tensile strength and Young's modulus decreased slightly. Based on these results, the as-prepared PET/EZT samples with high dimensional stability can be used as a high-temperature polymeric material in various applications.

| S-EPMC7956836 | biostudies-literature

Fracture Toughness and Elastic Modulus of Epoxy-Based Nanocomposites with Dopamine-Modified Nano-Fillers.

Project description:This paper examines the effect of surface treatment and filler shape factor on the fracture toughness and elastic modulus of epoxy-based nanocomposite. Two forms of nanofillers, polydopamine-coated montmorillonite clay (D-clay) and polydopamine-coated carbon nanofibres (D-CNF) were investigated. It was found that Young's modulus increases with increasing D-clay and D-CNF loading. However, the fracture toughness decreases with increased D-clay loading but increases with increased D-CNF loading. Explanations have been provided with the aid of fractographic analysis using electron microscope observations of the crack-filler interactions. Fractographic analysis suggests that although polydopamine provides a strong adhesion between the fillers and the matrix, leading to enhanced elastic stiffness, the enhancement prohibits energy release via secondary cracking, resulting in a decrease in fracture toughness. In contrast, 1D fibre is effective in increasing the energy dissipation during fracture through crack deflection, fibre debonding, fibre break, and pull-out.

| S-EPMC5551819 | biostudies-other

Increasing Fracture Toughness and Transmittance of Transparent Ceramics using Functional Low-Thermal Expansion Coatings.

Project description:Transparent polycrystalline ceramics have the potential to enable applications no other materials can, but to do so their strength and toughness must be improved. However, surface strengthening treatments like those used for glasses have so far remained elusive. Here for the first time, we report on engineering unprecedented surface compression, of the magnitude achieved for ion-exchange strengthened glasses (~750?MPa) in transparent ceramics. This was achieved by applying functional, low thermal-expansion yttria coatings onto yttria-stabilized zirconia substrates and thermally treating. In some instances, the treatment more than doubled the fracture toughness while simultaneously increasing light transmittance.

| S-EPMC6199310 | biostudies-literature

3D Lamellar-Structured Graphene Aerogels for Thermal Interface Composites with High Through-Plane Thermal Conductivity and Fracture Toughness.

Project description: Not available

| S-EPMC8187529 | biostudies-literature

Highly Toughened Nanostructured Self-Assembled Epoxy-Based Material-Correlation Study between Nanostructured Morphology and Fracture Toughness-Impact Characteristics.

Project description:We present an efficient and effective method for preparing a novel self-assembled nanostructured material with high toughness and impact strength from a blend of di-glycidyl ether of bisphenol-A (DGEBA) and epoxidized poly(styrene-block-butadiene-block-styrene) (eSBS55) tri-block copolymer. The field emission scanning electron microscopy and transmission electron microscope results show the nanostructured morphological characteristics of the blends. This study achieved the highest fracture toughness, with a fracture toughness in the form of critical stress intensity factors (KIC) value of 2.54 MPa m1/2, in epoxy/block copolymer blends compared to previous works in the field. The impact strength also increased by 116% compared to neat epoxy. This is a major advancement in epoxy toughening due to the use of a single secondary phase. The resulting highly tough and impact-resistant material is a promising candidate for coating applications in industries such as flooring, building, aerospace, and automobiles.

| S-EPMC10097291 | biostudies-literature

Improvement of Fracture Toughness in Epoxy Nanocomposites through Chemical Hybridization of Carbon Nanotubes and Alumina.

Project description:The current study investigated the effect of adding a carbon nanotube-alumina (CNT-Al₂O₃) hybrid on the fracture toughness of epoxy nanocomposites. The CNT-Al₂O₃ hybrid was synthesised by growing CNTs on Al₂O₃ particles via the chemical vapour deposition method. The CNTs were strongly attached onto the Al₂O₃ particles, which served to transport and disperse the CNTs homogenously, and to prevent agglomeration in the CNTs. The experimental results demonstrated that the CNT-Al₂O₃ hybrid-filled epoxy nanocomposites showed improvement in terms of the fracture toughness, as indicated by an increase of up to 26% in the critical stress intensity factor, K1C, compared to neat epoxy.

| S-EPMC5503309 | biostudies-other

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Project description:Polyurethane is widely used to toughen epoxy resins due to its excellent comprehensive properties and compatibility. However, some demerits of polyurethanes limit their applications, such as the harsh storage condition of isocyanate-terminated polyurethane (ITPU), the limited amount of ITPU in epoxy resin, and using solvents during the preparation of polyurethane-modified epoxy resins. To address these issues, in this study, we reported a facile and green approach for preparing epoxy-terminated polyurethane (EPU)-modified epoxy resins with different EPU contents. It was found that the toughness of the epoxy resin was significantly improved after the addition of EPU. When the EPU content was 30 wt%, the elongation at break and toughness were improved by 358.36% and 73.56%, respectively. In comparison, the toughening effect of EPU outperformed that of ITPU. Moreover, the high content of EPU did not significantly decrease the glass transition temperature and had little effect on the thermal stability of the epoxy resin.

| S-EPMC10346895 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data