Microbial Adhesion and Biofilm Formation on Bioactive Surfaces of Ti-35Nb-7Zr-5Ta Alloy Created by Anodization.

ABSTRACT: This study evaluated the microbial colonization (adhesion and biofilm) on modified surfaces of a titanium alloy, Ti-35Nb-7Zr-5Ta, anodized with Ca and P or F ions, with and without silver deposition. The chemical composition, surface topography, roughness (Ra), and surface free energy were evaluated before and after the surface modifications (anodizing). Adhesion and biofilm formation on saliva-coated discs by primary colonizing species (Streptococcus sanguinis, Streptococcus gordonii, Actinomyces naeslundii) and a periodontal pathogen (Porphyromonasgingivalis) were assessed. The surfaces of titanium alloys were modified after anodizing with volcano-shaped micropores with Ca and P or nanosized with F, both with further silver deposition. There was an increase in the Ra values after micropores formation; CaP surfaces became more hydrophilic than other surfaces, showing the highest polar component. For adhesion, no difference was detected for S. gordonii on all surfaces, and some differences were observed for the other three species. No differences were found for biofilm formation per species on all surfaces. However, S. gordonii biofilm counts on distinct surfaces were lower than S. sanguinis, A. naeslundii, and P. gingivalis on some surfaces. Therefore, anodized Ti-35Nb-7Zr-5Ta affected microbial adhesion and subsequent biofilm, but silver deposition did not hinder the colonization of these microorganisms.

SUBMITTER: Fais LMG

PROVIDER: S-EPMC8539148 | biostudies-literature | 2021 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Microbial Adhesion and Biofilm Formation on Bioactive Surfaces of Ti-35Nb-7Zr-5Ta Alloy Created by Anodization.

Fais Laiza Maria Grassi LMG de Sales Leite Luana L Reis Bárbara Araújo Dos BAD Ribeiro Ana Lúcia Roselino ALR Vaz Luis Geraldo LG Klein Marlise Inêz MI

Microorganisms 20211015 10

This study evaluated the microbial colonization (adhesion and biofilm) on modified surfaces of a titanium alloy, Ti-35Nb-7Zr-5Ta, anodized with Ca and P or F ions, with and without silver deposition. The chemical composition, surface topography, roughness (Ra), and surface free energy were evaluated before and after the surface modifications (anodizing). Adhesion and biofilm formation on saliva-coated discs by primary colonizing species (<i>Streptococcus sanguinis</i>, <i>Streptococcus gordonii< ...[more]

PMID: 34683474

Similar Datasets

Project description:BackgroundAlthough biomedical implants have been widely used in orthopedic treatments, two major clinical challenges remain to be solved, one is the bacterial infection resulting in biofilm formation, and the other is aseptic loosening during implantation due to over-activated osteoclastogenesis. These factors can cause many clinical issues and even lead to implant failure. Thus, it is necessary to endow implants with antibiofilm and aseptic loosening-prevention properties, to facilitate the integration between implants and bone tissues for successful implantation. To achieve this goal, this study aimed to develop a biocompatible titanium alloy with antibiofilm and anti-aseptic loosening dual function by utilizing gallium (Ga) as a component.MethodsA series of Ti-Ga alloys were prepared. We examined the Ga content, Ga distribution, hardness, tensile strength, biocompatibility, and anti-biofilm performance in vitro and in vivo. We also explored how Ga3+ ions inhibited the biofilm formation of Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) and osteoclast differentiation.ResultsThe alloy exhibited outstanding antibiofilm properties against both S. aureus and E. coli in vitro and decent antibiofilm performance against S. aureus in vivo. The proteomics results demonstrated that Ga3+ ions could disturb the bacterial Fe metabolism of both S. aureus and E. coli, inhibiting bacterial biofilm formation. In addition, Ti-Ga alloys could inhibit receptor activator of nuclear factor-κB ligand (RANKL)-dependent osteoclast differentiation and function by targeting iron metabolism, then suppressing the activation of the NF-κB signaling pathway, thus, showing their potential to prevent aseptic loosening.ConclusionThis study provides an advanced Ti-Ga alloy that can be used as a promising orthopedic implant raw material for various clinical scenarios. This work also revealed that iron metabolism is the common target of Ga3+ ions to inhibit biofilm formation and osteoclast differentiation.

Project description:Bacterial infection of implants and prosthetic devices is one of the most common causes of implant failure. The nanostructured surface of biocompatible materials strongly influences the adhesion and proliferation of mammalian cells on solid substrates. The observation of this phenomenon has led to an increased effort to develop new strategies to prevent bacterial adhesion and biofilm formation, primarily through nanoengineering the topology of the materials used in implantable devices. While several studies have demonstrated the influence of nanoscale surface morphology on prokaryotic cell attachment, none have provided a quantitative understanding of this phenomenon. Using supersonic cluster beam deposition, we produced nanostructured titania thin films with controlled and reproducible nanoscale morphology respectively. We characterized the surface morphology; composition and wettability by means of atomic force microscopy, X-ray photoemission spectroscopy and contact angle measurements. We studied how protein adsorption is influenced by the physico-chemical surface parameters. Lastly, we characterized Escherichia coli and Staphylococcus aureus adhesion on nanostructured titania surfaces. Our results show that the increase in surface pore aspect ratio and volume, related to the increase of surface roughness, improves protein adsorption, which in turn downplays bacterial adhesion and biofilm formation. As roughness increases up to about 20 nm, bacterial adhesion and biofilm formation are enhanced; the further increase of roughness causes a significant decrease of bacterial adhesion and inhibits biofilm formation. We interpret the observed trend in bacterial adhesion as the combined effect of passivation and flattening effects induced by morphology-dependent protein adsorption. Our findings demonstrate that bacterial adhesion and biofilm formation on nanostructured titanium oxide surfaces are significantly influenced by nanoscale morphological features. The quantitative information, provided by this study about the relation between surface nanoscale morphology and bacterial adhesion points towards the rational design of implant surfaces that control or inhibit bacterial adhesion and biofilm formation.

Project description:ObjectivesThe present study aimed to evaluate the potential of the salivary pellicle (SP) formed on titanium (Ti) surfaces to modulate the formation of a biofilm composed of Streptococcus gordonii, Actinomyces naeslundii, Fusobacterium nucleatum, and Porphyromonas gingivalis.Materials and methodsTi substrates were incubated for 2 h with a pool of saliva samples obtained from 10 systemically and periodontally healthy subjects. Enamel substrates were included as a biological reference. Scanning electron microscopy (SEM) and Raman spectroscopy analysis were used to analyze the formation of the salivary pellicle. After the SP formation, the surfaces were incubated for 12 h with a mix of Streptococcus gordonii, Actinomyces naeslundii, Fusobacterium nucleatum, and Porphyromonas gingivalis. The number of bacterial cells attached to each surface was determined by the XTT assay while bacterial viability was analyzed by fluorescence microscopy using the LIVE/DEAD® BacLightTM kit.ResultsThe SEM and Raman spectroscopy analysis confirmed the presence of a salivary pellicle formed on the tested surfaces. Regarding the biofilm formation, the presence of the SP decreases the number of the bacterial cells detected in the test surfaces, compared with the uncover substrates. Even more, the SP-covered substrates showed similar bacterial counts in both Ti and enamel surfaces, meaning that the physicochemical differences of the substrates were less determinant than the presence of the SP. While on the SP-uncover substrates, differences in the bacterial adhesion patterns were directly related to the physicochemical nature of the substrates.ConclusionsThe salivary pellicle was the main modulator in the development of the biofilm consisting of representative oral bacteria on the Ti substrates.Clinical relevanceThe results of this study provide valuable information on the modulatory effect of the salivary pellicle on biofilm formation; such information allows us to understand better the events involved in the formation of oral biofilms on Ti dental implants.

Dataset Information

Microbial Adhesion and Biofilm Formation on Bioactive Surfaces of Ti-35Nb-7Zr-5Ta Alloy Created by Anodization.

Publications

Microbial Adhesion and Biofilm Formation on Bioactive Surfaces of Ti-35Nb-7Zr-5Ta Alloy Created by Anodization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets