Development of Nickel- and Magnetite-Promoted Carbonized Cellulose Bead-Supported Bimetallic Pd-Pt Catalysts for Hydrogenation of Chlorate Ions in Aqueous Solution.

ABSTRACT: Cellulose grains were carbonized and applied as catalyst supports for nickel- and magnetite-promoted bimetallic palladium- and platinum-containing catalysts. The bimetallic spherical aggregates of Pd and Pt particles were created to enhance the synergistic effect among the precious metals during catalytic processes. As a first step, the cellulose bead-based supports were impregnated by nitrate salts of nickel and iron and carbonized at 973 K. After this step, the nickel was in an elemental state, while the iron was in a magnetite form in the corresponding supports. Then, Pd and Pt particles were deposited onto the supports and the catalyst surface; precious metal nanoparticles (10-20 nm) were clustered inside spherical aggregated particles 500-600 nm in size. The final bimetallic catalysts (i.e., Pd-Pt/CCB, Pd-Pt/Ni-CCB, and Pd-Pt/Fe₃O₄-CCB) were tested in hydrogenation of chlorate ions in the aqueous phase. For the nickel-promoted Pd-Pt catalyst, a >99% chlorate conversion was reached after 45 min at 80 °C. In contrast, the magnetite-promoted sample reached an 84.6% chlorate conversion after 3 h. Reuse tests were also carried out with the catalysts, and in the case of Pd-Pt/Ni-CCB after five cycles, the catalytic activity only decreased by ~7% which proves the stability of the system.

SUBMITTER: Sikora E

PROVIDER: S-EPMC8584269 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Efficient solvent-free hydrogenation of ketones over flame-prepared bimetallic Pt-Pd/ZrO(2) catalysts.

Project description:Named and flamed: Bimetallic Pt-Pd/ZrO(2) catalysts with different Pt/Pd atomic ratios and high dispersion of the metal nanoparticles are prepared by a single-step flame-spray pyrolysis. The catalysts show excellent activity and tunable product selectivity for the solvent-free hydrogenation of the ketone model compounds cyclopentanone and acetophenone.

| S-EPMC3796871 | biostudies-literature

Desorption of Furfural from Bimetallic Pt-Fe Oxides/Alumina Catalysts.

Project description:In this work, the desorption of furfural, which is a competitive intermediate during the production of biofuel and valuable aromatic compounds, was studied using pure alumina, as well as alumina impregnated with iron and platinum oxides both individually and in combination, using thermogravimetric analysis (TGA). The bimetallic sample exhibited the lowest desorption percentage for furfural. High-resolution transmission electron microscopy (HRTEM) imaging revealed the intimate connection between the iron and platinum oxide species on the alumina support. The mechanism of furfural desorption from the Pt-Fe/Al₂O₃ 0.5%-0.5% sample was determined using physisorbed furfural instead of chemisorbed furfural; this mechanism involved the oxidation of the C=O group on furfural by the catalyst. The oxide nanoparticles on γ-Al₂O₃ support helped to stabilize the furfural molecule on the surface.

| S-EPMC5453137 | biostudies-other

Controllable Synthesis of Surface Pt-Rich Bimetallic AuPt Nanocatalysts for Selective Hydrogenation Reactions.

Project description:Bimetallic nanocatalysts, with efficient and controllable catalytic performance, have a promising application in chemical production. In this study, surface Pt-rich bimetallic AuPt nanoparticles with different Pt/Au ratios were prepared and tested in selective hydrogenation reactions of substituted nitroaromatics. Au nanoparticles were first prepared with n-butyllithium as a rapid reducer, which were further used as seeds in the slow growth process of Pt atoms. Because of the employed sequential reduction method and the following atom diffusion, surface Pt-rich bimetallic AuPt nanoparticles were obtained. Compared with the uniform AuPt alloy nanocatalysts synthesized by the co-reduction method with n-butyllithium as the reducer and monometallic Pt nanocatalysts, the obtained surface Pt-rich AuPt bimetallic nanocatalysts presented an enhanced catalytic selectivity or activity. The performance enhancement is assigned to the optimized Au/Pt interaction in the surface Pt-rich bimetallic nanostructures. This work demonstrates that the optimization of the stoichiometry and construction of bimetallic materials is a feasible method to synthesize controllable and efficient nanocatalysts.

| S-EPMC6761762 | biostudies-literature

The promoted catalytic hydrogenation performance of bimetallic Ni-Co-B noncrystalline alloy nanotubes.

Project description:A noncrystalline Ni-B alloy in the shape of nanotubes has demonstrated its superior catalytic performance for some hydrogenation reactions. Remarkable synergistic effects have been observed in many reactions when bimetallic catalysts were used; however, bimetallic noncrystalline alloy nanotubes are far less investigated. Here, we report a simple acetone-assisted lamellar liquid crystal approach for synthesizing a series of bimetallic Ni-Co-B nanotubes and investigate their catalytic performances. The dilution effect of acetone on liquid crystals was characterized by small-angle X-ray diffraction (SAXRD) and scanning electron microscopy (SEM). The Ni/Co molar ratio of the catalyst was varied to study the composition, porous structure, electronic interaction, and catalytic efficiency. In the liquid-phase hydrogenation of p-chloronitrobenzene, the as-prepared noncrystalline alloy Ni-Co-B nanotubes exhibited higher catalytic activity and increased stability as compared to Ni-B and Co-B alloy nanotubes due to electronic interactions between the nickel and cobalt. The excellent hydrogenation performance of the Ni-Co-B nanotubes was attributed to their high specific surface area and the characteristic confinement effects, compared with Ni-Co-B nanoparticles.

| S-EPMC9070375 | biostudies-literature

Synthesis and hydrogenation application of Pt-Pd bimetallic nanocatalysts stabilized by macrocycle-modified dendrimer.

Project description:Different generations of poly(propylene imine) (G n -PPI) terminated with N-containing 15-membered triolefinic macrocycle (G n M) (n?=?2, 3, 4, 5) were prepared. The bimetallic nanoparticle catalysts G n M-(Pt x /Pd10-x ) (x?=?0, 3, 5, 7, 10) were prepared by the synchronous ligand-exchange reaction between G n M and the complexes of Pt(PPh3)4 and Pd(PPh3)4. The structure and catalytic properties of G n M-(Pt x /Pd10-x ) were characterized via Fourier transform infrared spectroscopy, 1H nuclear magnetic resonance spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, high-resolution transmission electron microscopy, energy-dispersive spectroscopy and inductively coupled plasma atomic emission spectroscopy. The novel bimetallic Pd-Pt nanoparticle catalysts stabilized by dendrimers (DSNs) present higher catalytic activities for the hydrogenation of dimeric acid (DA) than that of nitrile butadiene rubber (NBR). It can be concluded that bimetallic Pd-Pt DSNs possess alloying and synergistic electronic effects on account of the hydrogenation degree (HD) of DA and NBR. Furthermore, the HD of DA and NBR shows a remarkable decrease with the incremental generations (n) of G n M-(Pt3/Pd7) (n?=?2, 3, 4, 5).

| S-EPMC5750030 | biostudies-literature

Ruling Factors in Cinnamaldehyde Hydrogenation: Activity and Selectivity of Pt-Mo Catalysts.

Project description:To obtain selective hydrogenation catalysts with low noble metal content, two carbon-supported Mo-Pt bimetallic catalysts have been synthesized from two different molybdenum precursors, i.e., Na2MoO4 and (NH4)6Mo7O24. The results obtained by X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) combined with the presence and strength of acid sites clarified the different catalytic behavior toward cinnamaldehyde hydrogenation. After impregnating the carbon support with Mo precursors, each sample was used either as is or treated at 400 °C in N2 flow, as support for Pt nanoparticles (NPs). The heating treatment before Pt deposition had a positive effect on the catalytic performance. Indeed, TEM analyses showed very homogeneously dispersed Pt NPs only when they were deposited on the heat-treated Mo/C supports, and XPS analyses revealed an increase in both the exposure and reduction of Pt, which was probably tuned by different MoO3/MoO2 ratios. Moreover, the different acid properties of the catalysts resulted in different selectivity.

| S-EPMC7912768 | biostudies-literature

Atomically Dispersed Fe-Co Bimetallic Catalysts for the Promoted Electroreduction of Carbon Dioxide.

Project description:The electroreduction reaction of CO2 (ECO2RR) requires high-performance catalysts to convert CO2 into useful chemicals. Transition metal-based atomically dispersed catalysts are promising for the high selectivity and activity in ECO2RR. This work presents a series of atomically dispersed Co, Fe bimetallic catalysts by carbonizing the Fe-introduced Co-zeolitic-imidazolate-framework (C-Fe-Co-ZIF) for the syngas generation from ECO2RR. The synergistic effect of the bimetallic catalyst promotes CO production. Compared to the pure C-Co-ZIF, C-Fe-Co-ZIF facilitates CO production with a CO Faradaic efficiency (FE) boost of 10%, with optimal FECO of 51.9%, FEH2 of 42.4% at - 0.55 V, and CO current density of 8.0 mA cm-2 at - 0.7 V versus reversible hydrogen electrode (RHE). The H2/CO ratio is tunable from 0.8 to 4.2 in a wide potential window of - 0.35 to - 0.8 V versus RHE. The total FECO+H2 maintains as high as 93% over 10 h. The proper adding amount of Fe could increase the number of active sites and create mild distortions for the nanoscopic environments of Co and Fe, which is essential for the enhancement of the CO production in ECO2RR. The positive impacts of Cu-Co and Ni-Co bimetallic catalysts demonstrate the versatility and potential application of the bimetallic strategy for ECO2RR.

| S-EPMC8664923 | biostudies-literature

Fabrication of Biomass Derived Pt-Ni Bimetallic Catalyst and Its Selective Hydrogenation for 4-Nitrostyrene.

Project description:The hydrogenation products of aromatic molecules with reducible groups (such as C=C, NO2, C=O, etc.) are relatively critical intermediate compounds in fine chemicals, but how to accurately reduce only specific groups is still challenging. In this work, a bimetallic Pt-Ni/Chitin catalyst was prepared for the first time by using renewable biomass resource chitin as support. As the carrier, the chitin was constructed into porous nanofibrous microspheres through the sol-gel strategy, which was favorable for the adhesion of nano-metals and the exchange of reactive substances due to its large surface area, porous structure, and rich functional groups. Then the Pt-Ni/Chitin catalyst was applied to selective hydrogenation with the model substrate of 4-nitrostyrene. As the highly dispersed Pt-Ni NPs with abundant exposed active sites and the synergistic effect of bimetals, the Pt-Ni/Chitin catalyst could efficiently and selectively hydrogenate only NO2 or C=C with yields of ~99% and TOF of 660 h-1, as well as good stability. This utilization of biomass resources to build catalyst materials would be important for the green and sustainable chemistry.

| S-EPMC9457902 | biostudies-literature

Renewable Cyclopentanol From Catalytic Hydrogenation-Rearrangement of Biomass Furfural Over Ruthenium-Molybdenum Bimetallic Catalysts.

Project description:Biomass furfural-like compounds are chemicals that cannot be extracted from fossil materials, through which a large number of fine chemicals and fuel additives can be opened up, but one big efficiency problem during the transformation is the accumulation of oligomers. Here, we propose a novel and efficient Ru-Mo bimetallic catalyst for selective hydrogenation-rearrangement of furfural-like compounds. The result showed that an unprecedented rearrangement product selectivity of 89.1% to cyclopentanol was achieved under an optimized reaction condition over a 1%Ru-2.5%Mo/CNT catalyst reduced at 600°C. Subsequent characterization suggested that the catalyst presented with weak acidity and strong hydrogenation activity for the reaction, which not only ensures the smooth hydrogenation-rearrangement reaction but also inhibits the accumulation of furan polymers. These findings provide a convenient strategy to tune the catalytic performance of Mo-based catalysts by controlling the reduction and carburization conditions, which appear to be versatile for the rearrangement of furans and similar compounds.

| S-EPMC7775491 | biostudies-literature

Decoupling the electronic and geometric effects of Pt catalysts in selective hydrogenation reaction.

Project description:Decoupling the electronic and geometric effects has been a long cherished goal for heterogeneous catalysis due to their tangled relationship. Here, a novel orthogonal decomposition method is firstly proposed to settle this issue in p-chloronitrobenzene hydrogenation reaction on size- and shape-controlled Pt nanoparticles (NPs) carried on various supports. Results suggest Fermi levels of catalysts can be modulated by supports with varied work function (Wf). And the selectivity on Pt NPs of similar size and shape is linearly related with the Wf of support. Optimized Fermi levels of the catalysts with large Wf weaken the ability of Pt NPs to fill valence electrons into the antibonding orbital of C-Cl bond, finally suppressing the hydrodehalogenation side reaction. Foremost, the geometric effect is firstly spun off through orthogonal relation based on series of linear relationships over various sizes of Pt NPs reflecting the electronic effect. Moreover, separable nested double coordinate system is established to quantitatively evaluate the two effects.

| S-EPMC9213482 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data