Experimental Determination of Molecular Weight-Dependent Miscibility of PBAT/PLA Blends

ABSTRACT: Blends of poly(butylene adipate-co-terephthalate) (PBAT) and polylactide (PLA) have attracted the attention of academia and industry as a sustainable material. Unfortunately, this combination results in problems related to poor miscibility on the molecular level. This study mainly aims to determine the influence of molecular weights on the miscibility of PBAT/PLA blends. First, polymers with various molecular weights were obtained by the hydrolysis of PBAT and methanolysis of PLA. Second, the two components were solution-blended with different molecular weights and weight ratios. Third, each blend was heated to the molten state and subsequently stored at room temperature. Finally, the samples were tested using DSC and SEM. The thermal analysis indicated that the difference in glass transition temperature between both components decreased from about 91 °C to 57 °C and 0 °C, as the number-average molecular weights (Mn) decreased from 52/127 to 9.4/9 and 6.3/6.6 kg/mol. Moreover, the morphology changed from phase-separated with dispersed large particles gradually to uniform and homogeneous. This experimental work validated the trends predicted in the previous study, namely that PBAT/PLA blends changed the state from immiscible to partially miscible to fully miscible with decreasing Mn values. Moreover, we discussed the influencing factors such as weight ratio, temperature, and molecular structure on the miscibility. Based on the results, this work contributes to developing partially miscible and compatible blends without additives.

SUBMITTER: Su S

PROVIDER: S-EPMC8586918 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The addition of polyethylene glycol (PEG) chains to poly(lactic-co-glycolic acid) (PLGA) matrices is extensively used to modulate the biodegradation, drug loading and release, mechanical properties, and chemical stability of the original system. Multiple parameters, including the molecular weight, relative concentration, polarity, and solubility, affect the physicochemical properties of the polymer blend. Here, molecular dynamics simulations with the united-atom 2016H66 force field are used to model the behavior of PLGA and PEG chains and thus predict the overall physicochemical features of the resulting blend. First, the model accuracy is validated against fundamental properties of pure PLGA and PEG samples. In agreement with previous experimental and theoretical observations, the PLGA solubility results to be higher in acetonitrile than in water, with Flory parameters νACN = 0.63 ± 0.01 and νW = 0.21 ± 0.02, and the Young's modulus of PLGA and PEG equal to Y = 2.0 ± 0.43 and 0.32 ± 0.34 GPa, respectively. Next, four PEG/PLGA blending regimes are identified by varying the relative concentrations and molecular weights of the individual polymers. The computational results demonstrate that at low PEG concentrations (<8% w/w), homogeneous blends are generated for both low and high PEG molecular weights. In contrast, at comparable PEG and PLGA concentrations (∼50% w/w), short PEG chains are only partially miscible whereas long PEG chains segregate within the PLGA matrix. This behavior has been confirmed experimentally via differential scanning calorimetry and is in agreement with previous observations. Finally, the computed Young's modulus of PLGA/PEG blends is observed to decrease with the PEG content returning the lowest values for the partial and fully segregated regimens (Y ≈ 1.3 GPa). This work proposes a computational scheme for predicting the physicochemical properties of PLGA/PEG blends paving the way toward the rational design of polymer mixtures for biomedical applications.

Dataset Information

Experimental Determination of Molecular Weight-Dependent Miscibility of PBAT/PLA Blends

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets