Magnetic composite of γ-Fe2O3 hollow sphere and palladium doped nitrogen-rich mesoporous carbon as a recoverable catalyst for C–C coupling reactions

ABSTRACT: In this article, palladated-magnetic nitrogen doped porous carbon was prepared from nano magnetic γ-Fe2O3 hollow sphere (h-Fe2O3) with high specific surface area and pore volume. To the purpose, initially h-Fe2O3 was prepared and covered with glucose via hydrothermal treatment with subsequent polymerization of organic shell. The polymerization of melamine-resorcinol–formaldehyde (MRF) was achieved in the presence of Cl-functionalized glucose coated h-Fe2O3 (h-Fe2O3@glu-MRF). Next, the prepared magnetic core–shell hollow sphere was palladated followed by carbonization to yield Pd@h-Fe2O3@C introducing more pores in its structure. The resulted compound, Pd@h-Fe2O3@C, was fully characterized, showing that carbonization process expressively increased the specific surface area. The resulted Pd@h-Fe2O3@C was successfully used for promoting C–C coupling reactions under mild reaction conditions as a heterogeneous catalyst and its activity was compared with some prepared control catalysts. This novel catalyst was magnetically separated simply by a magnet bar and recycled and reused at least in five consecutive runs, without considerable loss of its activity. It is note mentioning that, high recyclability with low Pd leaching are another gains of this protocol.

SUBMITTER: Malmir M

PROVIDER: S-EPMC8599472 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Hollow Mesoporous Fe2O3 Nanospindles/CNTs Composite: An Efficient Catalyst for High-Performance Li-O2 Batteries.

Project description:The design of mesoporous or hollow transition metal oxide/carbon hybrid catalysts is very important for rechargeable Li-O2 batteries. Here, spindle-like Fe2O3 with hollow mesoporous structure on CNTs backbones (Fe2O3-HMNS@CNT) are prepared by a facile hydrolysis process combined with low temperature calcination. Within this hybrid structure, the hollow interior and mesoporous shell of the Fe2O3 nanospindles provide high specific surface area and abundant catalytical active sites, which is also beneficial to facilitating the electrolyte infiltration and oxygen diffusion. Furthermore, the crisscrossed CNTs form a three-dimensional (3D) conductive network to accelerate and stabilize the electron transport, which leads to the decreasing internal resistance of electrode. As a cathodic catalyst for Li-O2 batteries, the Fe2O3-HMNS@CNT composite exhibits high specific capacity and excellent cycling stability (more than 100 cycles).

| S-EPMC6672713 | biostudies-literature

Sub-50 nm Iron-Nitrogen-Doped Hollow Carbon Sphere-Encapsulated Iron Carbide Nanoparticles as Efficient Oxygen Reduction Catalysts.

Project description:Sub-50 nm iron-nitrogen-doped hollow carbon sphere-encapsulated iron carbide nanoparticles (Fe3C-Fe,N/C) are synthesized by using a triblock copolymer of poly(styrene-b-2-vinylpyridine-b-ethylene oxide) as a soft template. Their typical features, including a large surface area (879.5 m2 g-1), small hollow size (≈16 nm), and nitrogen-doped mesoporous carbon shell, and encapsulated Fe3C nanoparticles generate a highly active oxygen reduction reaction (ORR) performance. Fe3C-Fe,N/C hollow spheres exhibit an ORR performance comparable to that of commercially available 20 wt% Pt/C in alkaline electrolyte, with a similar half-wave potential, an electron transfer number close to 4, and lower H2O2 yield of less than 5%. It also shows noticeable ORR catalytic activity under acidic conditions, with a high half-wave potential of 0.714 V, which is only 59 mV lower than that of 20 wt% Pt/C. Moreover, Fe3C-Fe,N/C has remarkable long-term durability and tolerance to methanol poisoning, exceeding Pt/C regardless of the electrolyte.

| S-EPMC6051398 | biostudies-literature

Synthesis of Mesoporous CuO Hollow Sphere Nanozyme for Paper-Based Hydrogen Peroxide Sensor.

Project description:Point-of-care monitoring of hydrogen peroxide is important due to its wide usage in biomedicine, the household and industry. Herein, a paper sensor is developed for sensitive, visual and selective detection of H2O2 using a mesoporous metal oxide hollow sphere as a nanozyme. The mesoporous CuO hollow sphere is synthesized by direct decomposition of copper-polyphenol colloidal spheres. The obtained mesoporous CuO hollow sphere shows a large specific surface area (58.77 m2/g), pore volume (0.56 cm3/g), accessible mesopores (5.8 nm), a hollow structure and a uniform diameter (~100 nm). Furthermore, they are proven to show excellent peroxidase-like activities with Km and Vmax values of 120 mM and 1.396 × 10-5 M·s-1, respectively. Such mesoporous CuO hollow spheres are then loaded on the low-cost and disposable filter paper test strip. The obtained paper sensor can be effectively used for detection of H2O2 in the range of 2.4-150 μM. This work provides a new kind of paper sensor fabricated from a mesoporous metal oxide hollow sphere nanozyme. These sensors could be potentially used in bioanalysis, food security and environmental protection.

| S-EPMC8392683 | biostudies-literature

Guanidinylated SBA-15/Fe3O4 mesoporous nanocomposite as an efficient catalyst for the synthesis of pyranopyrazole derivatives.

Project description:In this study, a novel mesoporous nanocomposite was fabricated in several steps. In this regard, SBA-15 was prepared by the hydrothermal method, next it was magnetized by in-situ preparation of Fe3O4 MNPs. After that, the as-prepared SBA-15/Fe3O4 functionalized with 3-minopropyltriethoxysilane (APTES) via post-synthesis approach. Then, the guanidinylated SBA-15/Fe3O4 was obtained by nucleophilic addition of APTES@SBA-15/Fe3O4 to cyanimide. The prepared nanocomposite exhibited excellent catalytic activity in the synthesis of dihydropyrano[2,3-c]pyrazole derivatives which can be related to its physicochemical features such as strong basic sites (presented in guanidine group), Lewis acid site (presented in Fe3O4), high porous structure, and high surface area. The characterization of the prepared mesoporous nanocomposite was well accomplished by different techniques such as FT-IR, EDX, FESEM, TEM, VSM, TGA, XRD and BET. Furthermore, the magnetic catalyst was reused at least six consequent runs without considerable reduction in its catalytic activity.

| S-EPMC8494731 | biostudies-literature

3D NiO hollow sphere/reduced graphene oxide composite for high-performance glucose biosensor.

Project description:The 3D NiO hollow sphere/reduced graphene oxide (rGO) composite was synthesized according to the coordinating etching and precipitating process by using Cu2O nanosphere/graphene oxide (GO) composite as template. The morphology, structure, and composition of the materials were characterized by SEM, TEM, HRTEM, XPS, and Raman spectra, and the electrochemical properties were studied by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and amperometry. Moreover, the electrochemical activity of the composite materials with different morphologies were also investigated, which indicating a better combination of the NiO hollow sphere and the rGO. Used as glucose sensing material, the 3D NiO hollow sphere/rGO composite modified electrode exhibits high sensitivity of ~2.04 mA mM-1 cm-2, quick response time of less than 5 s, good stability, selectivity, and reproducibility. Its application for the detection of glucose in human blood serum sample shows acceptable recovery and R.S.D.ValuesThe outstanding glucose sensing performance should be attributed to the unique 3D hierarchical porous superstructure of the composite, especially for its enhanced electron-transfer kinetic properties.

| S-EPMC5507916 | biostudies-literature

Tumor-targeted Gd-doped mesoporous Fe3O4 nanoparticles for T1/T2 MR imaging guided synergistic cancer therapy.

Project description:In this study, a novel intelligent nanoplatform to integrate multiple imaging and therapeutic functions for targeted cancer theranostics. The nanoplatform, DOX@Gd-MFe3O4 NPs, was constructed Gd-doped mesoporous Fe3O4 nanoparticles following with the doxorubicin (DOX) loading in the mesopores of the NPs. The DOX@Gd-MFe3O4 NPs exhibited good properties in colloidal dispersity, photothermal conversion, NIR triggered drug release, and high T1/T2 relaxicity rate (r1=9.64 mM-1s-1, r2= 177.71 mM-1s-1). Benefiting from the high MR contrast, DOX@Gd-MFe3O4 NPs enabled simultaneous T1/T2 dual-modal MR imagining on 4T1 bearing mice in vivo and the MR contrast effect was further strengthened by external magnetic field. In addition, the DOX@Gd-MFe3O4 NPs revealed the strongest inhibition to the growth of 4T1 in vitro and in vivo under NIR irradiation and guidance of external magnetic field. Moreover, biosafety was also validated by in vitro and in vivo tests. Thus, the prepared DOX@Gd-MFe3O4 NPs would provide a promising intelligent nanoplatform for dual-modal MR imagining guided synergistic therapy in cancer theranostics.

| S-EPMC8079076 | biostudies-literature

MOF-Derived CoSe2@N-Doped Carbon Matrix Confined in Hollow Mesoporous Carbon Nanospheres as High-Performance Anodes for Potassium-Ion Batteries.

Project description:In this work, a novel vacuum-assisted strategy is proposed to homogenously form Metal-organic frameworks within hollow mesoporous carbon nanospheres (HMCSs) via a solid-state reaction. The method is applied to synthesize an ultrafine CoSe2 nanocrystal@N-doped carbon matrix confined within HMCSs (denoted as CoSe2@NC/HMCS) for use as advanced anodes in high-performance potassium-ion batteries (KIBs). The approach involves a solvent-free thermal treatment to form a Co-based zeolitic imidazolate framework (ZIF-67) within the HMCS templates under vacuum conditions and the subsequent selenization. Thermal treatment under vacuum facilitates the infiltration of the cobalt precursor and organic linker into the HMCS and simultaneously transforms them into stable ZIF-67 particles without any solvents. During the subsequent selenization process, the "dual confinement system", composed of both the N-doped carbon matrix derived from the organic linker and the small-sized pores of HMCS, can effectively suppress the overgrowth of CoSe2 nanocrystals. Thus, the resulting uniquely structured composite exhibits a stable cycling performance (442 mAh g-1 at 0.1 A g-1 after 120 cycles) and excellent rate capability (263 mAh g-1 at 2.0 A g-1) as the anode material for KIBs.

| S-EPMC8187686 | biostudies-literature

Preparation of uniform magnetic recoverable catalyst microspheres with hierarchically mesoporous structure by using porous polymer microsphere template.

Project description:Merging nanoparticles with different functions into a single microsphere can exhibit profound impact on various applications. However, retaining the unique properties of each component after integration has proven to be a significant challenge. Our previous research demonstrated a facile method to incorporate magnetic nanoparticles into porous silica microspheres. Here, we report the fabrication of porous silica microspheres embedded with magnetic and gold nanoparticles as magnetic recoverable catalysts. The as-prepared multifunctional composite microspheres exhibit excellent magnetic and catalytic properties and a well-defined structure such as uniform size, high surface area, and large pore volume. As a result, the very little composite microspheres show high performance in catalytic reduction of 4-nitrophenol, special convenient magnetic separability, long life, and good reusability. The unique nanostructure makes the microspheres a novel stable and highly efficient catalyst system for various catalytic industry processes.

| S-EPMC4113952 | biostudies-literature

Highly Efficient Mesoporous Carbonaceous CeO2 Catalyst for Dephosphorylation.

Project description:Phosphorus is fast becoming a critical element, as the global supply and demand are reaching unsustainable levels. Herein, the synthesis, characterization, and applicability of a novel biomass-derived mesoporous carbonaceous material decorated with CeO2 (CeO2-S400) as an efficient catalyst for the dephosphorylation of 4-nitrophenyl phosphate disodium salt hexahydrate are reported. The presence and distribution of CeO2 are evidenced by inductively coupled plasma mass spectrometry (ICP-MS) (118.7 mg/g), high-resolution transmission electron microscopy (HRTEM), and energy dispersive X-ray (EDX) mapping. The apparent rate constant for the efficient catalysis of 4-nitrophenyl phosphate disodium salt hexahydrate was 0.097 ± 0.01 for CeO2-ES and 0.15 ± 0.03 min-1 for CeO2-S400, which followed first-order kinetics. Rate constants normalized by the catalytic loading (k m) were 80.84 and 15.00 g-1 min-1 for CeO2-ES and CeO2-S400, respectively, and the normalized rate constants with respect to surface area were 3.38 and 0.04 m-2 min-1 for CeO2-ES and CeO2-S400, respectively. This indicates that the presence of CeO2 nanoparticles has a catalytic effect on the dephosphorylation reaction.

| S-EPMC9260935 | biostudies-literature

Synthesis of 2D Nitrogen-Doped Mesoporous Carbon Catalyst for Oxygen Reduction Reaction.

Project description:2D nitrogen-doped mesoporous carbon (NMC) is synthesized by using a mesoporous silica film as hard template, which is then investigated as a non-precious metal catalyst for the oxygen reduction reaction (ORR). The effect of the synthesis conditions on the silica template and carbon is extensively investigated. In this work, we employ dual templates-viz. graphene oxide and triblock copolymer F127-to control the textural features of a 2D silica film. The silica is then used as a template to direct the synthesis of a 2D nitrogen-doped mesoporous carbon. The resultant nitrogen-doped mesoporous carbon is characterized by transmission electron microscopy (TEM), nitrogen ad/desorption isotherms, X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), and rotating disk electrode measurements (RDE). The electrochemical test reveals that the obtained 2D-film carbon catalyst yields a highly electrochemically active surface area and superior electrocatalytic activity for the ORR compared to the 3D-particle. The superior activity can be firstly attributed to the difference in the specific surface area of the two catalysts. More importantly, the 2D-film morphology makes more active sites accessible to the reactive species, resulting in a much higher utilization efficiency and consequently better activity. Finally, it is noted that all the carbon catalysts exhibit a higher ORR activity than a commercial Pt catalyst, and are promising for use in fuel cells.

| S-EPMC5459128 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data