SrSnO₃-Assembled MWCNT Heterojunctions for Superior Hydrogen Production under Visible Light.

ABSTRACT: A one-step sol-gel method for SrSnO₃ nanoparticle synthesis and the incorporation of multi-walled carbon nanotubes (MWCNTs) to produce a SrSnO₃@MWCNT photocatalyst is presented. The incorporation of MWCNTs results in enhancement of structural, optical, and optoelectrical properties of SrSnO₃. The optimized 3.0% addition of MWCNTs results in light absorption enhancement and a reduction of the band gap from 3.68 to 2.85 eV. Upon application of the photocatalyst in the photocatalytic hydrogen production reaction, SrSnO₃@MWCNT-3.0% yields 4200 μmol g^-1 of H₂ in just 9 h with the use of 1.6 g L^-1 of the photocatalyst. SrSnO₃@MWCNT exhibits remarkable chemical and photocatalytic stability upon regeneration. Enhanced photocatalytic ability is attributed to improved surface properties and charge-carrier recombination suppression induced by the MWCNT addition. This study highlights the remarkable improvements in chemical and physical properties of semiconductors with MWCNT incorporation.

SUBMITTER: Kadi MW

PROVIDER: S-EPMC8600627 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

SrSnO3-Assembled MWCNT Heterojunctions for Superior Hydrogen Production under Visible Light.

Kadi Mohammad W MW Mohamed Reda M RM

ACS omega 20211105 45

A one-step sol-gel method for SrSnO3 nanoparticle synthesis and the incorporation of multi-walled carbon nanotubes (MWCNTs) to produce a SrSnO3@MWCNT photocatalyst is presented. The incorporation of MWCNTs results in enhancement of structural, optical, and optoelectrical properties of SrSnO3. The optimized 3.0% addition of MWCNTs results in light absorption enhancement and a reduction of the band gap from 3.68 to 2.85 eV. Upon application of the photocatalyst in ...[more]

PMID: 34805682

Similar Datasets

Project description:Graphitic carbon nitride (g-C₃N₄) and titanium dioxide (TiO₂) were chosen as a model system to investigate photocatalytic abilities of heterojunction system under UV and visible light conditions. The use of g-C₃N₄ has been shown to be effective in the reduction in recombination through the interaction between the two interfaces of TiO₂ and g-C₃N₄. A simple method of preparing g-C₃N₄ through the pyrolysis of melamine was employed, which was then added to undoped TiO₂ material to form the g-C₃N₄-TiO₂ system. These materials were then fully characterized by X-ray diffraction (XRD), Brunauer Emmett Teller (BET), and various spectroscopic techniques including Raman, X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), diffuse absorbance, and photoluminescence analysis. Photocatalysis studies were conducted using the model dye, rhodamine 6G utilizing visible and UV light irradiation. Raman spectroscopy confirmed that a composite of the materials was formed as opposed to a mixture of the two. Using XPS analysis, a shift in the nitrogen peak to that indicative of substitutional nitrogen was detected for all doped samples. This is then mirrored in the diffuse absorbance results, which show a clear decrease in band gap values for these samples, showing the effective band gap alteration achieved through this preparation process. When g-C₃N₄-TiO₂ samples were analyzed under visible light irradiation, no significant improvement was observed compared that of pure TiO₂. However, under UV light irradiation conditions, the photocatalytic ability of the doped samples exhibited an increased reactivity when compared to the undoped TiO₂ (0.130 min-1), with 4% g-C₃N₄-TiO₂ (0.187 min-1), showing a 43.9% increase in reactivity. Further doping to 8% g-C₃N₄-TiO₂ lead to a decrease in reactivity against rhodamine 6G. BET analysis determined that the surface area of the 4% and 8% g-C₃N₄-TiO₂ samples were very similar, with values of 29.4 and 28.5 m²/g, respectively, suggesting that the actual surface area is not a contributing factor. This could be due to an overloading of the system with covering of the active sites resulting in a lower reaction rate. XPS analysis showed that surface hydroxyl radicals and oxygen vacancies are not being formed throughout this preparation. Therefore, it can be suggested that the increased photocatalytic reaction rates are due to successful interfacial interactions with the g-C₃N₄-doped TiO₂ systems.

Dataset Information

SrSnO₃-Assembled MWCNT Heterojunctions for Superior Hydrogen Production under Visible Light.

Publications

SrSnO<sub>3</sub>-Assembled MWCNT Heterojunctions for Superior Hydrogen Production under Visible Light.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets