Confirmation of Calcium Phosphate Cement Biodegradation after Jawbone Augmentation around Dental Implants Using Three-Dimensional Visualization and Segmentation Software.

ABSTRACT: The use of autologous bone graft for oral rehabilitation of bone atrophy is considered the gold standard. However, the available grafts do not allow a fast loading of dental implants, as they require a long healing time before full functionality. Innovative bioactive materials provide an easy-to-use solution to this problem. The current study shows the feasibility of calcium phosphate cement paste (Paste-CPC) in the sinus. Long implants were placed simultaneously with the cement paste, and provisional prosthetics were also mounted in the same sessions. Final prosthetics and the full loading took place within the same week. Furthermore, the study shows for the first time the possibility to monitor not only healing progression using Cone Beam Computer tomography (CBCT) but also material retention, over two years, on a case study example. The segmented images showed a 30% reduction of the cement size and an increased mineralized tissue in the sinus. Mechanical testing was performed qualitatively using reverse torque after insertion and cement solidification to indicate clinical feasibility. Both functional and esthetic satisfaction remain unchanged after one year. This flowable paste encourages the augmentation procedure with less invasive measure through socket of removed implants. However, this limitation can be addressed in future studies.

SUBMITTER: Alkhasawnah Q

PROVIDER: S-EPMC8618138 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Proper horizontal and vertical thickness of the gingival connective tissue has been proven to be one of the success criteria in dental implant and reconstructive surgery. When thin tissue is found, gingiva augmentation methods can be used to increase the quality and volume of the tissue. Many methods have been described, among them pedicle soft-tissue flaps or autogenic tissue grafts. As an alternative to patients' own tissue, xenogenic materials can be used for grafting. The fundamental issue is to choose a material that will ensure the maximum therapeutic effect, while also minimizing the negative influence on the patient's health. The aim of this study was to compare gingival augmentation procedures using a palatal connective tissue graft (CTG) and an xenogenic soft-tissue substitute, Geistlich Mucograft (xenogeneic collagen matrix; CMX), and assess whether the timing of the graft surgery influences the clinical outcomes. The original study was a randomized control trial with a total of 75 implants placed. The patients received the soft-tissue thickening 3 months before the implant placement or 3 months after the implant placement (depending on the group). A connective tissue graft (CTG) or Geistlich Mucograft were used (depending on the group). For both the CTG and Geistlich Mucograft, better clinical outcomes were observed for maintaining the alveolar bone level and the thickness of the attached gingiva compared to the control group with no gingival augmentation. The Geistlich Mucograft showed good clinical performance in comparison to the control. Soft-tissue augmentation with the CTG before the implant placement was found to be most efficient method in terms of a stable increase of the tissue thickness since, throughout the entire observation period, the greatest increase of 1.035 mm (SD = 0.73 mm) in thickness was observed. Statistically important differences in the tissue thickness baseline compared after 5 years were observed for groups G1 vs. G2b (no augmentation vs. CTG before), G1 vs. G3b (no augmentation vs. CTG after) and for groups G2b vs. G3a (CTG before vs. CMX after).

Project description:In recent years, pure iron (Fe) has attracted significant attention as a promising biodegradable orthopedic implant material due to its excellent mechanical and biological properties. However, in physiological conditions, Fe has an extremely slow degradation rate with localized and irregular degradation, which is problematic for practical applications. In this study, we developed a novel combination of a nanostructured surface topography and galvanic reaction to achieve uniform and accelerated degradation of an Fe implant. The target-ion induced plasma sputtering (TIPS) technique was applied on the Fe implant to introduce biologically compatible and electrochemically noble tantalum (Ta) onto its surface and develop surface nano-galvanic couples. Electrochemical tests revealed that the uniformly distributed nano-galvanic corrosion cells of the TIPS-treated sample (nano Ta–Fe) led to relatively uniform and accelerated surface degradation compared to that of bare Fe. Furthermore, the mechanical properties of nano Ta–Fe remained almost constant during a long-term in vitro immersion test (~40 weeks). Biocompatibility was also assessed on surfaces of bare Fe and nano Ta–Fe using in vitro osteoblast responses through direct and indirect contact assays and an in vivo rabbit femur medullary cavity implantation model. The results revealed that nano Ta–Fe not only enhanced cell adhesion and spreading on its surface, but also exhibited no signs of cellular or tissue toxicity. These results demonstrate the immense potential of Ta-implanted surface nanostructures as an effective solution for the practical application of Fe-based orthopedic implants, ensuring long-term biosafety and clinical efficacy. Graphical abstract Image 1 Highlights • The degradation rate of nanostructured Fe implants was accelerated by TIPS technique.• Ta ions were accelerated strongly toward the Fe surface by TIPS process.• Nano Ta–Fe showed long-term mechanical stability and accelerated degradation rate.• Nanostructured Ta–Fe surface showed enhanced in vitro and in vivo cellular responses.• Ta-implanted Fe is a promising material for biodegradable orthopedic implants.

Dataset Information

Confirmation of Calcium Phosphate Cement Biodegradation after Jawbone Augmentation around Dental Implants Using Three-Dimensional Visualization and Segmentation Software.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets