Fabrication of High Performance PVDF Hollow Fiber Membrane Using Less Toxic Solvent at Different Additive Loading and Air Gap.

ABSTRACT: Existing toxic solvents in the manufacturing of polymeric membranes have been raising concerns due to the risks of exposure to health and the environment. Furthermore, the lower tensile strength of the membrane renders these membranes unable to endure greater pressure during water treatment. To sustain a healthier ecosystem, fabrication of polyvinylidene fluoride (PVDF) hollow fiber membrane using a less toxic solvent, triethyl phosphate (TEP), with a lower molecular weight polyethylene glycol (PEG 400) (0-3 wt.%) additive were experimentally demonstrated via a phase inversion-based spinning technique at various air gap (10, 20 and 30 cm). Membrane with 2 wt.% of PEG 400 exhibited the desired ultrafiltration asymmetric morphology, while 3 wt.% PEG 400 resulting microfiltration. The surface roughness, porosity, and water flux performance increased as the loading of PEG 400 increased. The mechanical properties and contact angle of the fabricated membrane were influenced by the air gap where 20 cm indicate 2.91 MPa and 84.72°, respectively, leading to a stronger tensile and hydrophilicity surface. Lower toxicity TEP as a solvent helped in increasing the tensile properties of the membrane as well as producing an eco-friendly membrane towards creating a sustainable environment. The comprehensive investigation in this study may present a novel composition for the robust structure of polymeric hollow fiber membrane that is suitable in membrane technology.

SUBMITTER: Zakria HS

PROVIDER: S-EPMC8622764 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Improving the Performance of PVDF/PVDF-<i>g</i>-PEGMA Ultrafiltration Membranes by Partial Solvent Substitution with Green Solvent Dimethyl Sulfoxide during Fabrication.

Project description:Traditional organic solvents used in membrane manufacturing, such as dimethylformamide and tetrahydrofuran, are generally very hazardous and harmful to the environment and human health. Their total or partial substitution with green solvent dimethyl sulfoxide (DMSO) is proposed to fabricate membranes composed of poly(vinylidene fluoride) (PVDF) blended with PVDF-graft-poly(ethylene glycol) methyl ether methacrylate (PEGMA), with the purpose to accomplish a greener chemical process and enhance the membrane performance. Various organic solvent compositions were first investigated using the Hansen solubility theory, and the best mixture was thus applied experimentally. The membrane prepared by a ratio of N,N-dimethylacetamide/DMSO = 7:3 outperformed the membranes prepared by other solvent mixtures. This membrane showed high wetting behavior with the water contact angle declining from 71 to 7° in 18 s and a pure water flux reaching values larger than 700 L m-2 h-1 under 0.07 MPa applied hydraulic pressure. The membrane rejected sodium alginate at a rate of 87%, and nearly complete flux recovery was achieved following fouling and physical cleaning. The introduction of green chemistry concepts to PVDF/PVDF-g-PEGMA blended membranes is a step forward in the goal to increase the sustainability of membrane production.

| S-EPMC6882131 | biostudies-literature

Multifunctional nanocomposite hollow fiber membranes by solvent transfer induced phase separation.

Project description:The decoration of porous membranes with a dense layer of nanoparticles imparts useful functionality and can enhance membrane separation and anti-fouling properties. However, manufacturing of nanoparticle-coated membranes requires multiple steps and tedious processing. Here, we introduce a facile single-step method in which bicontinuous interfacially jammed emulsions are used to form nanoparticle-functionalized hollow fiber membranes. The resulting nanocomposite membranes prepared via solvent transfer-induced phase separation and photopolymerization have exceptionally high nanoparticle loadings (up to 50 wt% silica nanoparticles) and feature densely packed nanoparticles uniformly distributed over the entire membrane surfaces. These structurally well-defined, asymmetric membranes facilitate control over membrane flux and selectivity, enable the formation of stimuli responsive hydrogel nanocomposite membranes, and can be easily modified to introduce antifouling features. This approach forms a foundation for the formation of advanced nanocomposite membranes comprising diverse building blocks with potential applications in water treatment, industrial separations and as catalytic membrane reactors.

| S-EPMC5663856 | biostudies-literature

Ultrahigh loading dry-process for solvent-free lithium-ion battery electrode fabrication.

Project description:The current lithium-ion battery (LIB) electrode fabrication process relies heavily on the wet coating process, which uses the environmentally harmful and toxic N-methyl-2-pyrrolidone (NMP) solvent. In addition to being unsustainable, the use of this expensive organic solvent substantially increases the cost of battery production, as it needs to be dried and recycled throughout the manufacturing process. Herein, we report an industrially viable and sustainable dry press-coating process that uses the combination of multiwalled carbon nanotubes (MWNTs) and polyvinylidene fluoride (PVDF) as a dry powder composite and etched Al foil as a current collector. Notably, the mechanical strength and performance of the fabricated LiNi0.7Co0.1Mn0.2O2 (NCM712) dry press-coated electrodes (DPCEs) far exceed those of conventional slurry-coated electrodes (SCEs) and give rise to high loading (100 mg cm-2, 17.6 mAh cm-2) with impressive specific energy and volumetric energy density of 360 Wh kg-1 and 701 Wh L-1, respectively.

| S-EPMC10006413 | biostudies-literature

Melt Blown Fiber-Assisted Solvent-Free Device Fabrication at Low-Temperature.

Project description:In this paper, we propose a solvent-free device fabrication method using a melt-blown (MB) fiber to minimize potential chemical and thermal damages to transition-metal-dichalcogenides (TMDCs)-based semiconductor channel. The fabrication process is composed of three steps; (1) MB fibers alignment as a shadow mask, (2) metal deposition, and (3) lifting-up MB fibers. The resulting WSe2-based p-type metal-oxide-semiconductor (PMOS) device shows an ON/OFF current ratio of ~2 × 105 (ON current of ~-40 µA) and a remarkable linear hole mobility of ~205 cm2/V·s at a drain voltage of -0.1 V. These results can be a strong evidence supporting that this MB fiber-assisted device fabrication can effectively suppress materials damage by minimizing chemical and thermal exposures. Followed by an MoS2-based n-type MOS (NMOS) device demonstration, a complementary MOS (CMOS) inverter circuit application was successfully implemented, consisted of an MoS2 NMOS and a WSe2 PMOS as a load and a driver transistor, respectively. This MB fiber-based device fabrication can be a promising method for future electronics based on chemically reactive or thermally vulnerable materials.

| S-EPMC7763187 | biostudies-literature

Optimization of Nanofiltration Hollow Fiber Membrane Fabrication Process Based on Response Surface Method.

Project description:Layer-by-layer (LBL) self-assembly technology has become a new research hotspot in the fabrication of nanofiltration membranes in recent years. However, there is a lack of a systematic approach for the assessment of influencing factors during the membrane fabrication process. In this study, the process optimization of LBL deposition was performed by a two-step statistical method. The multiple linear regression was performed on the results of single-factor experiments to determine the major influencing factors on membrane performance, including the concentration of Poly (allylamine hydrochloride) (PAH), glutaraldehyde, and the NaCl concentration in PAH solution. The Box-Behnken response surface method was then used to analyze the interactions between the selected factors, while their correlation with the membrane performance was obtained by polynomial fitting. The R2 value of the regression models (0.97 and 0.94) was in good agreement with the adjusted R2 value (0.93 and 0.86), indicating that the quadratic response models were adequate enough to predict the membrane performance. The optimal process parameters were finally determined through dual-response surface analysis to achieve both high membrane permeability of 14.3 LMH·MPa-1 and MgSO4 rejection rate of 90.22%.

| S-EPMC9032820 | biostudies-literature

Continuous Fiber-Reinforced Aramid/PETG 3D-Printed Composites with High Fiber Loading through Fused Filament Fabrication.

Project description:Recent development in the field of additive manufacturing, also known as three-dimensional (3D) printing, has allowed for the incorporation of continuous fiber reinforcement into 3D-printed polymer parts. These fiber reinforcements allow for the improvement of the mechanical properties, but compared to traditionally produced composite materials, the fiber volume fraction often remains low. This study aims to evaluate the in-nozzle impregnation of continuous aramid fiber reinforcement with glycol-modified polyethylene terephthalate (PETG) using a modified, low-cost, tabletop 3D printer. We analyze how dimensional printing parameters such as layer height and line width affect the fiber volume fraction and fiber dispersion in printed composites. By varying these parameters, unidirectional specimens are printed that have an inner structure going from an array-like to a continuous layered-like structure with fiber loading between 20 and 45 vol%. The inner structure was analyzed by optical microscopy and Computed Tomography (µCT), achieving new insights into the structural composition of printed composites. The printed composites show good fiber alignment and the tensile modulus in the fiber direction increased from 2.2 GPa (non-reinforced) to 33 GPa (45 vol%), while the flexural modulus in the fiber direction increased from 1.6 GPa (non-reinforced) to 27 GPa (45 vol%). The continuous 3D reinforced specimens have quality and properties in the range of traditional composite materials produced by hand lay-up techniques, far exceeding the performance of typical bulk 3D-printed polymers. Hence, this technique has potential for the low-cost additive manufacturing of small, intricate parts with substantial mechanical performance, or parts of which only a small number is needed.

| S-EPMC8778918 | biostudies-literature

Synthesis and Polyelectrolyte Functionalization of Hollow Fiber Membranes Formed by Solvent Transfer Induced Phase Separation.

Project description:Ultrafiltration membranes are important porous materials to produce freshwater in an increasingly water-scarce world. A recent approach to generate porous membranes is solvent transfer induced phase separation (STrIPS). During STrIPS, the interplay of liquid-liquid phase separation and nanoparticle self-assembly results in hollow fibers with small surface pores, ideal structures for applications as filtration membranes. However, the underlying mechanisms of the membrane formation are still poorly understood, limiting the control over structure and properties. To address this knowledge gap, we study the nonequilibrium dynamics of hollow fiber structure evolution. Confocal microscopy reveals the distribution of nanoparticles and monomers during STrIPS. Diffusion simulations are combined with measurements of the interfacial elasticity to investigate the effect of the solvent concentration on nanoparticle stabilization. Furthermore, we demonstrate the separation performance of the membrane during ultrafiltration. To this end, polyelectrolyte multilayers are deposited on the membrane, leading to tunable pores that enable the removal of dextran molecules of different molecular weights (>360 kDa, >60 kDa, >18 kDa) from a feed water stream. The resulting understanding of STrIPS and the simplicity of the synthesis process open avenues to design novel membranes for advanced separation applications.

| S-EPMC9523618 | biostudies-literature

Fabrication and Characterisation of Stimuli Responsive Piezoelectric PVDF and Hydroxyapatite-Filled PVDF Fibrous Membranes.

Project description:Poly(vinylidene fluoride) has attracted interest from the biomaterials community owing to its stimuli responsive piezoelectric property and promising results for application in the field of tissue engineering. Here, solution blow spinning and electrospinning were employed to fabricate PVDF fibres and the variation in resultant fibre properties assessed. The proportion of piezoelectric β-phase in the solution blow spun fibres was higher than electrospun fibres. Fibre production rate was circa three times higher for solution blow spinning compared to electrospinning for the conditions explored. However, the solution blow spinning method resulted in higher fibre variability between fabricated batches. Fibrous membranes are capable of generating different cellular response depending on fibre diameter. For this reason, electrospun fibres with micron and sub-micron diameters were fabricated, along with successful inclusion of hydroxyapatite particles to fabricate stimuli responsive bioactive fibres.

| S-EPMC6571942 | biostudies-literature

Preparation and Characterization of TiO?-PVDF/PMMA Blend Membranes Using an Alternative Non-Toxic Solvent for UF/MF and Photocatalytic Application.

Project description:The approach of the present work is based on the use of poly (methylmethacrylate) (PMMA) polymer, which is compatible with PVDF and TiO? nanoparticles in casting solutions, for the preparation of nano-composites membranes using a safer and more compatible solvent. TiO? embedded poly (vinylidene fluoride) (PVDF)/PMMA photocatalytic membranes were prepared by phase inversion method. A non-solvent induced phase separation (NIPS) coupled with vapor induced phase separation (VIPS) was used to fabricate flat-sheet membranes using a dope solution consisting of PMMA, PVDF, TiO?, and triethyl phosphate (TEP) as an alternative non-toxic solvent. Membrane morphology was examined by scanning electron microscopy (SEM). Backscatter electron detector (BSD) mapping was used to monitor the inter-dispersion of TiO? in the membrane surface and matrix. The effects of polymer concentration, evaporation time, additives and catalyst amount on the membrane morphology and properties were investigated. Tests on photocatalytic degradation of methylene blue (MB) were also carried out using the membranes entrapped with different concentrations of TiO?. The results of this study showed that nearly 99% MB removal can be easily achieved by photocatalysis using TiO? immobilized on the membrane matrix. Moreover, it was observed that the quantity of TiO? plays a significant role in the dye removal.

| S-EPMC6412202 | biostudies-literature

A Complex Investigation of LATP Ceramic Stability and LATP+PVDF Composite Membrane Performance: The Effect of Solvent in Tape-Casting Fabrication.

Project description:Redox flow batteries (RFBs) are a prospective energy storage platform to mitigate the discrepancy between barely adjustable energy production and fluctuating demand. The energy density and affordability of RFBs can be improved significantly through the transition from aqueous systems to non-aqueous (NAq) due to their wider electrochemical stability window and better solubility of active species. However, the NAqRFBs suffer from a lack of effective membranes with high ionic conductivity (IC), selectivity (low permeability), and stability. Here, we for the first time thoroughly analyse the impact of tape-casting solvents (dimethylformamide-DMF; dimethylsulfoxide-DMSO; N-methyl-2-pyrrolidone-NMP) on the properties of the composite Li-conductive membrane (Li1.3Al0.3Ti1.7(PO4)3 filler within poly(vinylidene fluoride) binder-LATP+PVDF). We show that the prolonged exposure of LATP to the studied solvents causes slight morphological, elemental, and intrastructural changes, dropping ceramic's IC from 3.1 to 1.6-1.9 ∙ 10-4 S cm-1. Depending on the solvent, the final composite membranes exhibit IC of 1.1-1.7 ∙ 10-4 S cm-1 (comparable with solvent-treated ceramics) along with correlating permeability coefficients of 2.7-3.1 ∙ 10-7 cm2 min-1. We expect this study to complement the understanding of how the processes underlying the membrane fabrication impact its functional features and to stimulate further in-depth research of NAqRFB membranes.

| S-EPMC9965718 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data