SnO₂ Quantum Dots Distributed along V₂O₅ Nanobelts for Utilization as a High-Capacity Storage Hybrid Material in Li-Ion Batteries.

ABSTRACT: In this study, the facile synthesis of SnO₂ quantum dot (QD)-garnished V₂O₅ nanobelts exhibiting significantly enhanced reversible capacity and outstanding cyclic stability for Li⁺ storage was achieved. Electrochemical impedance analysis revealed strong charge transfer kinetics related to that of V₂O₅ nanobelts. The SnO₂ QD-garnished V₂O₅ nanobelts exhibited the highest discharge capacity of ca. 760 mAhg^-1 at a density of 441 mAg^-1 between the voltage ranges of 0.0 to 3.0 V, while the pristine V₂O₅ nanobelts samples recorded a discharge capacity of ca. 403 mAhg^-1. The high capacity of QD-garnished nanobelts was achieved as an outcome of their huge surface area of 50.49 m²g^-1 and improved electronic conductivity. Therefore, the as-presented SnO₂ QD-garnished V₂O₅ nanobelts synthesis strategy could produce an ideal material for application in high-performance Li-ion batteries.

SUBMITTER: Reddy IN

PROVIDER: S-EPMC8658980 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

One-step hydrothermal synthesis of graphene decorated V2O5 nanobelts for enhanced electrochemical energy storage.

Project description:Graphene-decorated V2O5 nanobelts (GVNBs) were synthesized via a low-temperature hydrothermal method in a single step. V2O5 nanobelts (VNBs) were formed in the presence of graphene oxide, a mild oxidant, which also enhanced the conductivity of GVNBs. From the electron energy loss spectroscopy analysis, the reduced graphene oxide (rGO) are inserted into the layered crystal structure of V2O5 nanobelts, which further confirmed the enhanced conductivity of the nanobelts. The electrochemical energy-storage capacity of GVNBs was investigated for supercapacitor applications. The specific capacitance of GVNBs was evaluated using cyclic voltammetry (CV) and charge/discharge (CD) studies. The GVNBs having V2O5-rich composite, namely, V3G1 (VO/GO = 3:1), showed superior specific capacitance in comparison to the other composites (V1G1 and V1G3) and the pure materials. Moreover, the V3G1 composite showed excellent cyclic stability and the capacitance retention of about 82% was observed even after 5000 cycles.

| S-EPMC4311251 | biostudies-literature

Improved Li storage performance in SnO2 nanocrystals by a synergetic doping.

Project description:Tin dioxide (SnO2) is a widely investigated lithium (Li) storage material because of its easy preparation, two-step storage mechanism and high specific capacity for lithium-ion batteries (LIBs). In this contribution, a phase-pure cobalt-doped SnO2 (Co/SnO2) and a cobalt and nitrogen co-doped SnO2 (Co-N/SnO2) nanocrystals are prepared to explore their Li storage behaviors. It is found that the morphology, specific surface area, and electrochemical properties could be largely modulated in the doped and co-doped SnO2 nanocrystals. Gavalnostatic cycling results indicate that the Co-N/SnO2 electrode delivers a specific capacity as high as 716 mAh g(-1) after 50 cycles, and the same outstanding rate performance can be observed in subsequent cycles due to the ionic/electronic conductivity enhancement by co-doping effect. Further, microstructure observation indicates the existence of intermediate phase of Li3N with high ionic conductivity upon cycling, which probably accounts for the improvements of Co-N/SnO2 electrodes. The method of synergetic doping into SnO2 with Co and N, with which the electrochemical performances is enhanced remarkably, undoubtedly, will have an important influence on the material itself and community of LIBs as well.

| S-EPMC4702176 | biostudies-literature

Controlled Hydrothermal Growth and Li+ Storage Performance of 1D VOx Nanobelts with Variable Vanadium Valence.

Project description:One-dimensional (1D) vanadium oxide nanobelts (VOx NBs) with variable V valence, which include V3O7·H2O NBs, VO2 (B) NBs and V2O5 NBs, were prepared by a simple hydrothermal treatment under a controllable reductive environment and a following calcination process. Electrochemical measurements showed that all these VOx NBs can be adopted as promising cathode active materials for lithium ion batteries (LIBs). The Li+ storage mechanism, charge transfer property at the solid/electrolyte interface and Li+ diffusion characteristics for these as-synthesized 1D VOx NBs were systematically analyzed and compared with each other. The results indicated that V2O5 NBs could deliver a relatively higher specific discharge capacity (213.3 mAh/g after 50 cycles at 100 mA/g) and median discharge voltage (~2.68-2.71 V vs. Li/Li+) during their working potential range when compared to other VOx NBs. This is mainly due to the high V valence state and good crystallinity of V2O5 NBs, which are beneficial to the large Li+ insertion capacity and long-term cyclic stability. In addition, the as-prepared VO2 (B) NBs had only one predominant discharge plateau at the working potential window so that it can easily output a stable voltage and power in practical LIB applications. This work can provide useful references for the selection and easy synthesis of nanoscaled 1D vanadium-based cathode materials.

| S-EPMC6523597 | biostudies-literature

Lignin as a Binder Material for Eco-Friendly Li-Ion Batteries.

Project description:The industrial lignin used here is a byproduct from Kraft pulp mills, extracted from black liquor. Since lignin is inexpensive, abundant and renewable, its utilization has attracted more and more attention. In this work, lignin was used for the first time as binder material for LiFePO₄ positive and graphite negative electrodes in Li-ion batteries. A procedure for pretreatment of lignin, where low-molecular fractions were removed by leaching, was necessary to obtain good battery performance. The lignin was analyzed for molecular mass distribution and thermal behavior prior to and after the pretreatment. Electrodes containing active material, conductive particles and lignin were cast on metal foils, acting as current collectors and characterized using scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge cycles. Good reversible capacities were obtained, 148 mAh·g-1 for the positive electrode and 305 mAh·g-1 for the negative electrode. Fairly good rate capabilities were found for both the positive electrode with 117 mAh·g-1 and the negative electrode with 160 mAh·g-1 at 1C. Low ohmic resistance also indicated good binder functionality. The results show that lignin is a promising candidate as binder material for electrodes in eco-friendly Li-ion batteries.

| S-EPMC5456705 | biostudies-other

Self-Supported Fibrous Sn/SnO2@C Nanocomposite as Superior Anode Material for Lithium-Ion Batteries.

Project description:Low-cost and simple methods are constantly chased in order to produce less expensive lithium-ion batteries (LIBs) while possibly increasing the energy and power density as well as the volumetric capacity in order to boost a rapid decarbonization of the transport sector. Li alloys and tin-carbon composites are promising candidates as anode materials for LIBs both in terms of capacity and cycle life. In the present paper, electrospinning was employed in the preparation of Sn/SnOx@C composites, where tin and tin oxides were homogeneously dispersed in a carbonaceous matrix of carbon nanofibers. The resulting self-standing and light electrode showed a greatly enhanced performance compared to a conventional electrode based on the same starting materials that are simply mixed to obtain a slurry then deposited on a Cu foil. Fast kinetics were achieved with more than 90% of the reaction that resulted being surface-controlled, and stable capacities of about 300 mAh/g over 500 cycles were obtained at a current density of 0.5 A/g.

| S-EPMC8839326 | biostudies-literature

Amorphous cobalt silicate nanobelts@carbon composites as a stable anode material for lithium ion batteries.

Project description:During the past decade, tremendous attention has been given to the development of new electrode materials with high capacity to meet the requirements of electrode materials with high energy density in lithium ion batteries. Very recently, cobalt silicate has been proposed as a new type of high capacity anode material for lithium ion batteries. However, the bulky cobalt silicate demonstrates limited electrochemical performance. Nanostructure engineering and carbon coating represent two promising strategies to improve the electrochemical performance of electrode materials. Herein, we developed a template method for the synthesis of amorphous cobalt silicate nanobelts which can be coated with carbon through the deposition and thermal decomposition of phenol formaldehyde resin. Tested as an anode material, the amorphous cobalt silicate nanobelts@carbon composites exhibit a reversible high capacity of 745 mA h g-1 at a current density of 100 mA g-1, and a long life span of up to 1000 cycles with a stable capacity retention of 480 mA h g-1 at a current density of 500 mA g-1. The outstanding electrochemical performance of the composites indicates their high potential as an anode material for lithium ion batteries. The results here are expected to stimulate further research into transition metal silicate nanostructures for lithium ion battery applications.

| S-EPMC5510008 | biostudies-other

Exploration of Li-Organic Batteries Using Hexaphyrin as an Active Cathode Material.

Project description:Lithium-collaborating organic batteries (Li-[28]hexs) were investigated with [28]hexaphyrin(1.1.1.1.1.1) as an active electrode material. Each hexaphyrin of [28]Hex cathode ideally involved four electrons per unit cycle and performed a typical charge/discharge processes of Li-organic battery. Li-[28]Hex batteries set with fast charging rates showed reasonably stable charge and discharge performances over 200 cycles even though it caused incomplete (2~3 electrons) charge/discharge cycles due to failing the complete charging process. UV absorption changes of [28]hexaphyrin in CH2Cl2 were supplementary for the electrochemical oxidation, which performed a conversion from [28]hexaphyrin to [26]hexaphyrin.

| S-EPMC6651293 | biostudies-literature

Highly Ordered SnO2 Nanopillar Array as Binder-Free Anodes for Long-Life and High-Rate Li-Ion Batteries.

Project description:SnO2, a typical transition metal oxide, is a promising conversion-type electrode material with an ultrahigh theoretical specific capacity of 1494 mAh g-1. Nevertheless, the electrochemical performance of SnO2 electrode is limited by large volumetric changes (~300%) during the charge/discharge process, leading to rapid capacity decay, poor cyclic performance, and inferior rate capability. In order to overcome these bottlenecks, we develop highly ordered SnO2 nanopillar array as binder-free anodes for LIBs, which are realized by anodic aluminum oxide-assisted pulsed laser deposition. The as-synthesized SnO2 nanopillar exhibit an ultrahigh initial specific capacity of 1082 mAh g-1 and maintain a high specific capacity of 524/313 mAh g-1 after 1100/6500 cycles, outperforming SnO2 thin film-based anodes and other reported binder-free SnO2 anodes. Moreover, SnO2 nanopillar demonstrate excellent rate performance under high current density of 64 C (1 C = 782 mA g-1), delivering a specific capacity of 278 mAh g-1, which can be restored to 670 mAh g-1 after high-rate cycling. The superior electrochemical performance of SnO2 nanoarray can be attributed to the unique architecture of SnO2, where highly ordered SnO2 nanopillar array provided adequate room for volumetric expansion and ensured structural integrity during the lithiation/delithiation process. The current study presents an effective approach to mitigate the inferior cyclic performance of SnO2-based electrodes, offering a realistic prospect for its applications as next-generation energy storage devices.

| S-EPMC8156522 | biostudies-literature

Interfacial architecture for extra Li? storage in all-solid-state lithium batteries.

Project description:The performance of nanocomposite electrodes prepared by controlled ball-milling of TiS? and a Li?S-P?S? solid electrolyte (SE) for all-solid-state lithium batteries is investigated, focusing on the evolution of the microstructure. Compared to the manually mixed electrodes, the ball-milled electrodes exhibit abnormally increased first-charge capacities of 416 mA h g(-1) and 837 mA h g(-1) in the voltage ranges 1.5-3.0 V and 1.0-3.0 V, respectively, at 50 mA g(-1) and 30°C. The ball-milled electrodes also show excellent capacity retention of 95% in the 1.5-3.0 V range after 60 cycles as compared to the manually mixed electrodes. More importantly, a variety of characterization techniques show that the origin of the extra Li(+) storage is associated with an amorphous Li-Ti-P-S phase formed during the controlled ball-milling process.

| S-EPMC4085631 | biostudies-literature

Li-rich Li-Si alloy as a lithium-containing negative electrode material towards high energy lithium-ion batteries.

Project description:Lithium-ion batteries (LIBs) are generally constructed by lithium-including positive electrode materials, such as LiCoO2, and lithium-free negative electrode materials, such as graphite. Recently, lithium-free positive electrode materials, such as sulfur, are gathering great attention from their very high capacities, thereby significantly increasing the energy density of LIBs. Though the lithium-free materials need to be combined with lithium-containing negative electrode materials, the latter has not been well developed yet. In this work, the feasibility of Li-rich Li-Si alloy is examined as a lithium-containing negative electrode material. Li-rich Li-Si alloy is prepared by the melt-solidification of Li and Si metals with the composition of Li21Si5. By repeating delithiation/lithiation cycles, Li-Si particles turn into porous structure, whereas the original particle size remains unchanged. Since Li-Si is free from severe constriction/expansion upon delithiation/lithiation, it shows much better cyclability than Si. The feasibility of the Li-Si alloy is further examined by constructing a full-cell together with a lithium-free positive electrode. Though Li-Si alloy is too active to be mixed with binder polymers, the coating with carbon-black powder by physical mixing is found to prevent the undesirable reactions of Li-Si alloy with binder polymers, and thus enables the construction of a more practical electrochemical cell.

| S-EPMC4308695 | biostudies-literature