Catalyst-Free Synthesis of Lignin Vitrimers with Tunable Mechanical Properties: Circular Polymers and Recoverable Adhesives.

ABSTRACT: Biobased circular materials are alternatives to fossil-based engineering plastics, but simple and material-efficient synthetic routes are needed for industrial scalability. Here, a series of lignin-based vitrimers built on dynamic acetal covalent networks with a gel content exceeding 95% were successfully prepared in a one-pot, thermally activated, and catalyst-free "click" addition of softwood kraft lignin (SKL) to poly(ethylene glycol) divinyl ether (PDV). The variation of the content of lignin from 28 to 50 wt % was used to demonstrate that the mechanical properties of the vitrimers can be widely tuned in a facile way. The lowest lignin content (28 wt %) showed a tensile strength of 3.3 MPa with 35% elongation at break, while the corresponding values were 50.9 MPa and 1.0% for the vitrimer containing 50 wt % of lignin. These lignin-based vitrimers also exhibited excellent performance as recoverable adhesives for different substrates such as aluminum and wood, with a lap shear test strength of 6.0 and 2.6 MPa, respectively. In addition, recyclability of the vitrimer adhesives showed preservation of the adhesion performance exceeding 90%, indicating a promising potential for their use in sustainable circular materials.

SUBMITTER: Moreno A

PROVIDER: S-EPMC8662642 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Closed-loop recycling of sulfur-rich polymers with tunable properties spanning thermoplastics, elastomers, and vitrimers.

Project description:The development of closed-loop recycling polymers that exhibit excellent performance is of great significance. Sulfur-rich polymers possessing excellent optical, thermal, and mechanical properties are promising candidates for chemical recycling but lack efficient synthetic strategies for achieving diverse structures. Herein, we report a universal synthetic strategy for producing polytrithiocarbonates, a class of sulfur-rich polymers, via the polycondensation of dithiols and dimethyl trithiocarbonate. This strategy has excellent compatibility with a wide range of monomers, including aliphatic, heteroatomic, and aromatic dithiols enabling the synthesis of polytrithiocarbonates with diverse structures. The present synthesis strategy offers a versatile platform for the construction of thermoplastics, elastomers, and vitrimers. Notably, these polytrithiocarbonates can be easily depolymerized via solvolysis into the corresponding monomers, which can be repolymerized to virgin polymers without changing the material properties.

| S-EPMC11001992 | biostudies-literature

Versatile Phosphate Diester-Based Flame Retardant Vitrimers via Catalyst-Free Mixed Transesterification.

Project description:We herein report a new vitrimer system integrated with UV curability, recyclability, and flame retardancy. Energy-efficiency, sustainability, and safety have been required features for next-generation polymer materials. Various attempts have been made to endow thermoset polymers with rapid prototyping capacity, recyclability, and flame retardancy. Thermoset vitrimers based on covalent adaptable networks (CANs) are recyclable and remoldable but are generally not UV curable or flame retardant. Here, we present a conceptually novel option to achieve fast exchange reactions in CANs via catalyst-free mixed transesterification of a UV curable phosphate diester-based acrylate cross-linker. In this system, the phosphate diesters serve as reversible covalent bonds, hydrogen bonding ligands, and flame-retardant structures, while acrylate groups serve as UV curable units as well as transesterification collaborators. After the facile UV curing, an intrinsic flame-retardant and mechanically strong dynamic network was achieved due to abundant hydrogen bonds between P-OH and C═O structures. Additionally, this highly cross-linked network exhibited an attractive recyclability even at temperatures lower than Tg. This phosphate diester-based mixed transesterification concept represents an efficient approach for developing multifunctional vitrimers and can also be generalized into other thermally cured polymer systems.

| S-EPMC7760087 | biostudies-literature

Catalyst-Free Cardanol-Based Epoxy Vitrimers for Self-Healing, Shape Memory, and Recyclable Materials.

Project description:Bio-based vitrimers present a promising solution to the issues associated with non-renewable and non-recyclable attributes of traditional thermosetting resins, showcasing extensive potential for diverse applications. However, their broader adoption has been hindered by the requirement for catalyst inclusion during the synthesis process. In this study, a cardanol-based curing agent with poly-hydroxy and tertiary amine structures was prepared by a clean synthetic method under the theory of click chemistry. The reaction of a cardanol-based curing agent with diglycidyl ether of bisphenol A formed catalyst-free, self-healing, and recyclable bio-based vitrimers. The poly-hydroxy and tertiary amine structures in the vitrimers promoted the curing of epoxy-carboxylic acid in the cross-linked network and served as internal catalysts of dynamic transesterification. In the absence of catalysts, the vitrimers network can achieve topological network rearrangement through dynamic transesterification, exhibiting excellent reprocessing performance. Moreover, the vitrimers exhibited faster stress relaxation (1500 s at 180 °C), lower activation energy (92.29 kJ·mol-1) and the tensile strength of the recycled material reached almost 100% of the original sample. This work offers a new method for preparing cardanol-based epoxy vitrimers that be used to make coatings, hydrogels, biomaterials, adhesives, and commodity plastics in the future.

| S-EPMC10857227 | biostudies-literature

Polybutadiene Vitrimers with Tunable Epoxy Ratios: Preparation and Properties.

Project description:Traditional crosslinked diene rubber has excellent thermal-mechanical properties and solvent resistance, yet it is incapable of being recycled via universal molding or injecting. Vitrimers, a new class of covalently crosslinked polymer networks, can be topologically rearranged with the associative exchange mechanism, endowing them with thermoplasticity. Introducing the concept of vitrimers into crosslinked networks for the recycling of rubbers is currently an attractive research topic. However, designing tailored rubber vitrimers still remains a challenge. Herein, polybutadiene (PB) vitrimers with different structures were prepared via partial epoxidation of double bonds and ring-opening esterification reactions. Their mechanical and relaxation properties were investigated. It was found that the increasing crosslinking density can increase tensile strength and activation energy for altering the network topology. The influence of side-group effects on their relaxation properties shows that an increase in the number of epoxy groups on the polybutadiene chain can increase the chance of an effective exchange of disulfide units. This work provides a simple network design which can tune vitrimer properties via altering the crosslinking density and side-group effects.

| S-EPMC8659766 | biostudies-literature

Novel and Integrated Process for the Valorization of Kraft Lignin to Produce Lignin-Containing Vitrimers

Project description:The valorization of lignin into value-added products

| S-EPMC9835646 | biostudies-literature

Sensing-triggered stiffness-tunable smart adhesives.

Project description:Artificial dry adhesives have exhibited great potential in the field of robotics. However, there is still a wide gap between bioinspired adhesives and living tissues, especially regarding the surface adaptability and switching ability of attachment/detachment. Here, we propose a sensing-triggered stiffness-tunable smart adhesive material, combining the functions of muscle tissues and sensing nerves rather than traditional biomimetic adhesive strategy that only focuses on structural geometry. Authorized by real-time perception of the interface contact state, conformal contact, shape locking, and active releasing are achieved by adjusting the stiffness based on the magnetorheological effect. Because of the fast switching of the magnetic field, a millisecond-level attachment/detachment response is successfully achieved, breaking the bottleneck of adhesive materials for high-speed manipulation. The innovative design can be applied to any toe's surface structure, opening up a previously unknown avenue for the development of adhesive materials.

| S-EPMC10017039 | biostudies-literature

Free radical polymers with tunable and selective bio- and chemical degradability.

Project description:A versatile synthetic strategy has been developed which enables the facile incorporation of cleavable functional groups, i.e., esters, thioesters, and disulfides, into the carbon-carbon backbone of vinyl-based polymers. Through the synthesis of novel cyclic monomers, RAFT-mediated radical ring-opening copolymerizations with traditional vinyl monomers such as methyl methacrylate, N,N-dimethylaminoethyl methacrylate, and 2-hydroxyethyl methacrylate lead to the introduction of controlled degradability into these widely used vinyl copolymer systems. An additional benefit of this strategy is the inherent versatility available through the incorporation of cyclic monomers containing diverse functional groups such as esters, thioesters, disulfides, and silyl ether units that allow degradation under basic/acidic, reductive, or enzymatic conditions. By integrating multiple, orthogonal cyclic monomers into linear copolymer backbones, well-defined systems with programmable degradation profiles are obtained which allows for tunable, selective, and stepwise degradation of the vinyl polymer backbones.

| S-EPMC2753401 | biostudies-literature

Colloidal Lignin Particles as Adhesives for Soft Materials.

Project description:Lignin has interesting functionalities to be exploited in adhesives for medicine, foods and textiles. Nanoparticles (NPs) < 100 nm coated with poly (L-lysine), PL and poly(L-glutamic acid) PGA were prepared from the laccase treated lignin to coat nanocellulose fibrils (CNF) with heat. NPs ca. 300 nm were prepared, β-casein coated and cross-linked with transglutaminase (Tgase) to agglutinate chamois. Size exclusion chromatography (SEC) and Fourier-transform infrared (FTIR) spectroscopy were used to characterize polymerized lignin, while zeta potential and dynamic light scattering (DLS) to ensure coating of colloidal lignin particles (CLPs). Protein adsorption on lignin was studied by quartz crystal microbalance (QCM). Atomic force microscopy (AFM) was exploited to examine interactions between different polymers and to image NPs with transmission electron microscopy (TEM). Tensile testing showed, when using CLPs for the adhesion, the stress improved ca. 10 and strain ca. 6 times compared to unmodified Kraft. For the β-casein NPs, the values were 20 and 8, respectively, and for the β-casein coated CLPs between these two cases. When NPs were dispersed in adhesive formulation, the increased Young's moduli confirmed significant improvement in the stiffness of the joints over the adhesive alone. Exploitation of lignin in nanoparticulate morphology is a potential method to prepare bionanomaterials for advanced applications.

| S-EPMC6315807 | biostudies-literature

Adhesion Improvement of Solvent-Free Pressure-Sensitive Adhesives by Semi-IPN Using Polyurethanes and Acrylic Polymers.

Project description:To improve the peel strength and holding time of polypropylene glycol (PPG)-based pressure-sensitive adhesives (PSAs), a semi-interpenetrating polymer network (semi-IPN) was prepared using acrylic polymers. In addition, to prevent air pollution due to volatile organic compound emissions and avoid the degradation of physical properties due to a residual solvent, the PPG-based semi-IPN PSAs were fabricated by an eco-friendly solvent-free method using an acrylic monomer instead of an organic solvent. PPG-based semi-IPN PSAs with different hard segment contents (2.9-17.2%) were synthesized; their holding time was found to depend on the hard segment contents. The peel strength was improved because of the formation of the semi-IPN structure. Moreover, the high degree of hard domain formation in the semi-IPN PSA, derived from the increase in the hard segment content using a chain extender, resulted in a holding time improvement. We believe that the as-prepared PSAs can be used in various applications that require high creep resistance.

| S-EPMC9571291 | biostudies-literature

Solvent-Free Esterification of Carboxylic Acids Using Supported Iron Oxide Nanoparticles as an Efficient and Recoverable Catalyst.

Project description:Supported iron oxide nanoparticles on mesoporous materials (FeNP@SBA-15) have been successfully utilized in the esterification of a variety carboxylic acids including aromatic, aliphatic, and long-chain carboxylic acids under convenient reaction conditions. The supported catalyst could be easily recovered after reaction completion and reused several times without any loss in activity after up to 10 runs.

| S-EPMC5456927 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data