Diphenolic Acid-Derived Hyperbranched Epoxy Thermosets with High Mechanical Strength and Toughness.

ABSTRACT: Diglycidyl ether of bisphenol A (DGEBA) is a kind of widely used epoxy resin, but its thermosets normally show high brittleness and poor impact resistance due to the intrinsic rigid aromatic rings, which limit its application greatly. To avoid this drawback, we proposed a method to prepare a series of hyperbranched epoxies (HBEPs) with different molecular weights. After HBEPs were cured with methyl tetrahydrophthalic anhydride (MTHPA), characterizations were carried out to evaluate the properties of the cured HBEP samples. Testing results indicate that the hyperbranched thermosets can achieve excellent mechanical strength and toughness (tensile strength: 89.2 MPa, bending strength: 129.6 MPa, elongation at break: 6.1%, toughness: 4.5 MJ m^-3, and impact strength: 6.7 kJ m^-2), which are superior to those of the thermosets of commercial DGEBA (tensile strength: 81.2 MPa, bending strength: 108.2 MPa, elongation at break: 3.0%, toughness: 1.5 MJ m^-3, and impact strength: 4.2 kJ m^-2). In addition, HBEP with the highest molecular weight and degree of branching shows the best comprehensive mechanical properties. All hyperbranched thermosets exhibit high glass-transition temperatures (T _g) and thermostability, which further illustrates the potential application value of HBEPs.

SUBMITTER: Xiao L

PROVIDER: S-EPMC8675157 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Enhancing the mechanical strength and toughness of epoxy resins with linear POSS nano-modifiers.

Project description:Glass transition temperature (T g) always deteriorates while improving the strength of epoxy resins which inherently suffer from brittleness. Herein, novel linear polyhedral oligomeric silsesquioxane (POSS)-epoxy nano-modifiers are synthesized with variable contents of POSS. The thermomechanical properties and chemical structure study of the POSS-epoxy indicates significant differences of the rigid POSS content in the linear nano-modifiers. By taking advantage of the synergistic effect of nanofillers and linear polymers, the modifiers disperse at the molecular level when POSS-epoxy is utilized as a co-curing agent for epoxy resins, allowing the applied force to be transferred into the polymer matrix. A good balance of T g, stiffness, and fracture toughness can be obtained. At 5 wt% of the nano-modifier, the resultant epoxy resins showed 27% enhancement in the Young's modulus relative to the neat epoxy. In addition, the T g and strength of epoxy thermosets are improved due to the increased cross-linking density, rough surface and tortuous path that resulted in good dispersion of energy during crack propagation.

| S-EPMC9419030 | biostudies-literature

Photopatternable Epoxy-Based Thermosets.

Project description:The present work provides a comparative study on the photopatterning of epoxy-based thermosets as a function of network structure and network mobility. Local switching of solubility properties by light of a defined wavelength is achieved by exploiting versatile o-nitrobenzyl ester (o-NBE) chemistry. o-NBE derivatives with terminal epoxy groups are synthetized and thermally cured with different types of cycloaliphatic anhydrides via nucleophilic ring opening reaction. By varying the structure of the anhydride, glass transition temperature (Tg) and surface hardness are adjusted over a broad range. Once the network has been formed, the photolysis of the o-NBE groups enables a well-defined degradation of the 3D network. Fourier transform infrared (FT-IR) spectroscopy studies demonstrate that cleavage rate and cleavage yield increase with rising mobility of the network, which is either facilitated by inherent network properties (Tg below room temperature) or a simultaneous heating of the thermosets above their Tg. The formation of soluble species is evidenced by sol-gel analysis, revealing that low-Tg networks are prone to secondary photoreactions at higher exposure doses, which lead to a re-crosslinking of the cleaved polymer chains. The change in solubility properties is exploited to inscribe positive tone micropatterns within the thermosets by photolithographic techniques. Contrast curves show that the resist performance of rigid networks is superior to flexible ones, with a contrast of 1.17 and a resolution of 8 µm.

| S-EPMC6695657 | biostudies-literature

Simultaneous reinforcement and toughness improvement of an epoxy-phenolic network with a hyperbranched polysiloxane modifier.

Project description:An epoxy-phenolic network is modified with hyperbranched polysiloxane (HBPSi). The addition of HBPSi-2, which has medium molecular weight, can significantly decrease the viscosity of the uncured epoxy-phenolic system and increase the crosslinking density and homogeneity of the cured crosslinking network. With 10% HBPSi-2, the mechanical properties of the samples are improved comprehensively: tensile modulus and maximum strength increase by 11.4% and 36.2%, respectively, while elongation at break and impact strength increase by 153.8% and 186.7%, respectively. The comprehensive improvements in the mechanical properties are attributed to combined effects of crosslinking density, network rigidity, cohesive density and the matrix-modifier compatibility. What is more, HBPSi-2 also significantly increases the char yield of the material and decreases the thermal weight loss rate, indicating an improved thermal stability. All these results may provide a new strategy for toughness and strength improvement of the epoxy-phenolic network.

| S-EPMC9080479 | biostudies-literature

Using Dicyclopentadiene-Derived Polyarylates as Epoxy Curing Agents To Achieve High T g and Low Dielectric Epoxy Thermosets.

Project description:To achieve high-T g and low-dielectric epoxy thermosets, four dicyclopentadiene-derived polyarylates (26-P, 26-M, 236-P, and 236-M) were prepared from 2,6-dimethyl (or 2,3,6-trimethyl) phenol-dicyclopentadiene adduct with terephthaloyl (or isophthaloyl) chloride by high-temperature solution polymerization. The resulting polyarylates, exhibiting active ester linkages (Ph-O-(C=O)-) are found to be reactive toward a commercial dicyclopentadiene phenol epoxy (HP7200) in the presence of some lone-pair electron-containing compounds. Five compounds including 4-dimethylaminopyridine (DMAP), imidazole, 2-methylimidazole, triphenylphosphine, and triphenylimidazole have been evaluated as a catalyst for the curing reactions. We found that DMAP, with the smallest pK b among them, is the best catalyst according to differential scanning calorimetry, infrared, and thermal analyses. The thermal and dielectric properties of the polyarylate/HP7200 thermosets are evaluated. We found that they exhibit a high T g characteristic (e.g., T g is 238 °C for DMAP-catalyzed, 236-P/HP7200 thermoset). Furthermore, because of the hydrophobic methyl and cycloaliphatic moieties, and the secondary hydroxyl-free structure, polyarylate/HP7200 thermosets show a relative low-dielectric constant of around 2.75 U. The detailed structure-properties relationship is discussed in this work.

| S-EPMC6641589 | biostudies-literature

Enhancing the Mechanical Toughness of Epoxy-Resin Composites Using Natural Silk Reinforcements.

Project description:Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.% Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50?°C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. The findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.

| S-EPMC5607334 | biostudies-literature

Development of Sustainable High Performance Epoxy Thermosets for Aerospace and Space Applications.

Project description:There is an imperative need to find sustainable ways to produce bisphenol A free, high performance thermosets for specific applications such as the space or aerospace areas. In this study, an aromatic tris epoxide, the tris(4-hydroxyphenyl)methane triglycidyl ether (THPMTGE), was selected to generate high crosslinked networks by its copolymerization with anhydrides. Indeed, the prepared thermosets show a gel content (GC) ~99.9% and glass transition values ranged between 167-196 °C. The thermo-mechanical properties examined by DMA analyses reveal the development of very hard materials with E' ~3-3.5 GPa. The thermosets' rigidity was confirmed by Young's moduli values which ranged between 1.25-1.31 GPa, an elongation at break of about 4-5%, and a tensile stress of ~35-45 MPa. The TGA analyses highlight a very good thermal stability, superior to 340 °C. The Limit Oxygen Index (LOI) parameter was also evaluated, showing the development of new materials with good flame retardancy properties.

| S-EPMC9785596 | biostudies-literature

Synthesis of a Degradable High-Performance Epoxy-Ended Hyperbranched Polyester.

Project description:Degradation and recycling of cured thermosetting epoxy resins are major challenges to the industry. Here, a low-viscosity, degradable epoxy-ended hyperbranched polyester (DEHP) is synthesized by a reaction between epichlorohydrin and a carboxyl-ended hyperbranched polyester (DCHP) obtained from an esterification between citric acid and maleic anhydride. The chemical structures of DCHP and DEHP were characterized by Fourier transform infrared and 1H NMR. DEHP has a positive effect on reinforcing and toughening of the diglycidyl ether of bisphenol-A (DGEBA). With an increase in the content and molecular weight of DEHP, the mechanical performances of the cured DEHP/DGEBA composites, including the tensile, flexural, and impact strengths, increase first and then decrease. The improvements on the tensile, flexural, and impact strengths were 34.2-43.4%, 35.6-48.1%, and 117.9-137.8%, respectively. Moreover, the DEHP also promotes degradation of the cured DEHP/DGEBA composites. The degree of degradation of the cured DEHP/DGEBA composites increases with an increase of the DEHP content and molecular weight. The composites containing 12 wt % DEHP can be degraded completely in only about 2 h at about 90 °C, compared with the degradation degree (35%) of cured DGEBA, indicating good degradation and recycling properties of the DEHP.

| S-EPMC6640995 | biostudies-literature

Cross-Linking and Evaluation of the Thermo-Mechanical Behavior of Epoxy Based Poly(ionic Liquid) Thermosets.

Project description:Poly(ionic liquids) (PILs) and ionenes are polymers containing ionic groups in their repeating units. The unique properties of these polymers render them as interesting candidates for a variety of applications, such as gas separation membranes and polyelectrolytes. Due to the vast number of possible structures, numerous synthesis protocols to produce monomers with different functional groups for task-specific PILs are reported in literature. A difunctional epoxy-IL resin was synthesized and cured with multifunctional amine and anhydride hardeners and the thermal and thermomechanical properties of the networks were assessed via differential scanning calorimetry and dynamic mechanical analysis. By the selection of suitable hardeners, the glass transition onset temperature (Tg,onset) of the resulting networks was varied between 18 °C and 99 °C. Copolymerization of epoxy-IL with diglycidyl ether of bisphenol A (DGEBA) led to a further increase of the Tg,onset. The results demonstrate the potential of epoxy chemistry for tailorable PIL networks, where the hardener takes the place of the ligands without requiring an additional synthesis step and can be chosen from a broad range of commercially available compounds.

| S-EPMC8620924 | biostudies-literature

Unmodified Silica Nanoparticles Enhance Mechanical Properties and Welding Ability of Epoxy Thermosets with Tunable Vitrimer Matrix.

Project description:Epoxy/silica thermosets with tunable matrix (vitrimers) were prepared by thermal curing of diglycidyl ether of bisphenol A (DGEBA) in the presence of a hardener-4-methylhexahydrophthalic anhydride (MHHPA), a transesterification catalyst-zinc acetylacetonate (ZAA), and 10-15 nm spherical silica nanoparticles. The properties of the resulting material were studied by tensile testing, thermomechanical and dynamic mechanical analysis. It is shown that at room temperature the introduction of 5-10 wt% of silica nanoparticles in the vitrimer matrix strengthens the material leading to the increase of the elastic modulus by 44% and the tensile stress by 25%. Simultaneously, nanoparticles enhance the dimensional stability of the material since they reduce the coefficient of thermal expansion. At the same time, the transesterification catalyst provides the thermoset with the welding ability at heating, when the chain exchange reactions are accelerated. For the first time, it was shown that the silica nanoparticles strengthen welding joints in vitrimers, which is extremely important, since it allows to repeatedly use products made of thermosets and heal defects in them. Such materials hold great promise for use in durable protective coatings, adhesives, sealants and many other applications.

| S-EPMC8467415 | biostudies-literature

Reprocessable Polybenzoxazine Thermosets with High Tgs and Mechanical Strength Retentions Using Boronic Ester Bonds as Crosslinkages.

Project description:In order to obtain reprocessable polybenzoxazine thermosets with high heat resistance and mechanical strength retentions, network structures without irreversible parts were constructed via crosslinking benzoxazine oligomers using boronic ester cross-linkers. Firstly, the benzoxazine monomer containing carbon-carbon double bonds was synthesized via the Mannich reaction. After thermal ring-opening polymerization, the benzoxazine oligomer containing carbon-carbon double bonds (OBZ) was yielded. Through the thiol-ene click reaction of the OBZ and dithiol cross-linker bearing boronic ester bonds, the polybenzoxazine thermosets using boronic ester bonds as crosslinkages (OBZ-BDB) were successfully synthesized. The structures of OBZ and OBZ-BDB were characterized by SEC, 1H NMR, and FT-IR measurements. Reprocessing experiments showed that OBZ-BDB has remarkable reprocessability. The retention rates of the tensile strengths through three generations of reprocessing were 98%, 95%, and 84%, respectively. Meanwhile, OBZ-BDB cross-linked by boronic ester bonds had brilliant thermal properties. The Tg of the original OBZ-BDB was 224 °C. With the increase of the reprocessing generations, the Tgs basically remained unchanged.

| S-EPMC9182748 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data