Carbon-coated SnO₂ riveted on a reduced graphene oxide composite (C@SnO₂/RGO) as an anode material for lithium-ion batteries.

ABSTRACT: The research on graphene-based anode materials for high-performance lithium-ion batteries (LIBs) has been prevalent in recent years. In the present work, carbon-coated SnO₂ riveted on a reduced graphene oxide sheet composite (C@SnO₂/RGO) was fabricated using GO solution, SnCl₄, and glucose via a hydrothermal method after heat treatment. When the composite was exploited as an anode material for LIBs, the electrodes were found to exhibit a stable reversible discharge capacity of 843 mA h g^-1 at 100 mA g^-1 after 100 cycles with 99.5% coulombic efficiency (CE), and a specific capacity of 485 mA h g^-1 at 1000 mA g^-1 after 200 cycles; these values were higher than those for a sample without glucose (SnO₂/RGO) and a pure SnO₂ sample. The favourable electrochemical performances of the C@SnO₂/RGO electrodes may be attributed to the special double-carbon structure of the composite, which can effectively suppress the volume expansion of SnO₂ nanoparticles and facilitate the transfer rates of Li⁺ and electrons during the charge/discharge process.

SUBMITTER: Dai Y

PROVIDER: S-EPMC8695216 | biostudies-literature | 2021 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Carbon-coated SnO2 riveted on a reduced graphene oxide composite (C@SnO2/RGO) as an anode material for lithium-ion batteries.

Dai Yao Y Li Fu F Fu Yuan-Xiang YX Mo Dong-Chuan DC Lyu Shu-Shen SS

RSC advances 20210224 15

The research on graphene-based anode materials for high-performance lithium-ion batteries (LIBs) has been prevalent in recent years. In the present work, carbon-coated SnO2 riveted on a reduced graphene oxide sheet composite (C@SnO2/RGO) was fabricated using GO solution, SnCl4, and glucose via a hydrothermal method after heat treatment. When the composite was exploited as an anode material for LIBs, the electrodes were found to exhibit a stable reversible ...[more]

PMID: 35423388

Similar Datasets

Project description:Bagasse-derived carbon electrodes were developed by doping with nitrogen functional groups and compositing with high-capacity MnO2 nanoparticles (MnO2/NBGC). The bagasse-derived biochar was N-doped by refluxing in urea, followed by the deposition of MnO2 nanoparticles onto its porous surface via the hydrothermal reduction of KMnO4. Different initial KMnO4 loading concentrations (i.e. 5, 10, 40, and 100 mM) were applied to optimize the composite morphology and the corresponding electrochemical performance. Material characterization confirmed that the carbon composite has a mesoporous structure along with the dispersion of MnO2 nano-particles on the N-containing carbon surface. It was found that the 5-MnO2/NBGC sample exhibited the highest electrochemical performance with a reversible capacity of 760 mA h g-1 at a current density of 186 mA g-1. It delivered reversible capacities of 488 and 390 mA h g-1 in cycle tests at 372 and 744 mA g-1, respectively, for 150 cycles and presented good reversibility with nearly 100% coulombic efficiency. In addition, it could exert high capacities up to 388 and 301 mA h g-1 even under high current densities of 1860 and 3720 mA g-1, respectively. Moreover, most of the prepared composite products showed high rate capability with great reversibility up to more than 90% after testing at a high current density of 3720 mA g-1. The great electrochemical performance of the MnO2/NBGC nanocomposite electrode can be attributed to the synergistic impact of the hierarchical architecture of the MnO2 nanocrystals deposited on porous carbon and the capacitive effect of the N-containing defects within the carbon material. The nanostructure of the MnO2 particles deposited on porous carbon limits its large volume change during cycling and promotes good adhesion of MnO2 nanoparticles with the substrate. Meanwhile, the capacitive effect of the exposed N-functional groups enables fast ionic conduction and reduces interfacial resistance at the electrode interface.

Dataset Information

Carbon-coated SnO₂ riveted on a reduced graphene oxide composite (C@SnO₂/RGO) as an anode material for lithium-ion batteries.

Publications

Carbon-coated SnO<sub>2</sub> riveted on a reduced graphene oxide composite (C@SnO<sub>2</sub>/RGO) as an anode material for lithium-ion batteries.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets